CN207862254U - A kind of low dyestripping voltage antistatic PET protection film - Google Patents

A kind of low dyestripping voltage antistatic PET protection film Download PDF

Info

Publication number
CN207862254U
CN207862254U CN201721446056.5U CN201721446056U CN207862254U CN 207862254 U CN207862254 U CN 207862254U CN 201721446056 U CN201721446056 U CN 201721446056U CN 207862254 U CN207862254 U CN 207862254U
Authority
CN
China
Prior art keywords
pet
antistatic
sensitive adhesive
low
pressure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201721446056.5U
Other languages
Chinese (zh)
Inventor
陈新江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hanano Material Science And Technology Co Ltdsuzhou
Original Assignee
Hanano Material Science And Technology Co Ltdsuzhou
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hanano Material Science And Technology Co Ltdsuzhou filed Critical Hanano Material Science And Technology Co Ltdsuzhou
Priority to CN201721446056.5U priority Critical patent/CN207862254U/en
Application granted granted Critical
Publication of CN207862254U publication Critical patent/CN207862254U/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model discloses a kind of low dyestripping voltage antistatic PET protection films.The low dyestripping voltage antistatic PET protection film includes PET base material, pressure-sensitive adhesive layer and the antistatic PET release film set gradually along direction initialization; the antistatic PET release films include PET release films and the anti-static coating for being set to a PET release films at least side surface, and the PET base material is also equipped with anti-static coating with the opposite facing side surface of pressure-sensitive adhesive layer.On the one hand the low dyestripping voltage antistatic PET protection film of the utility model can be effectively reduced in protective film production process, electrostatic that is that release film generates during uncoiling and can building up by making release film with anti-static function;On the other hand this structure is also beneficial to during actually using protective film, and electrostatic can be guided during removing release film, the dyestripping voltage of protective film can be made to accomplish by above effect minimum, application prospect is extensive.

Description

A kind of low dyestripping voltage antistatic PET protection film
Technical field
The utility model is related to a kind of PET protection film more particularly to a kind of low dyestripping voltage antistatic PET protection films, belong to In protective film of electronic product field.
Background technology
Transparent anti static PET protection film has been widely used for touch panel (TP, the Touch of touch screen factory now Panel processing procedure) and shipment protection.
Currently, global touch screen market development is getting faster, and industry size is in rapid growth.In smart mobile phone, tablet electricity The multi-field applications such as brain, stylus electricity, wearable device, onboard system, information management system can deepen continuously.It touches simultaneously Screen technology also develops to directions such as multiple point touching, enlargement and thin lightweights, the antistatic work(of this auxiliary material being also used for Requirements at the higher level, the protective film that especially TP shipment uses can be proposed, it is desirable that it there must be excellent anti-static function, avoid It is final remove caused charge breakdown TP when protective film and caused by lose.
Traditional antistatic PET protection film, is that polyurethane contact adhesive is coated in PET base material, and then laminating PET is release Film.In order to avoid touch screen producer it is final remove protective film carry out it is lower examine together or when assembling procedure, because protective film is torn Glue-line usually is designed to have certain by the functional assemblies such as the electronic component in electrostatic breakdown or damage TP except generation The anti-protective film of the pressure sensitive adhesive of anti-static function, i.e. glue.Also there is portioned product in view of right caused by electrostatic in actual use simultaneously The adverse effect of actual job also has and does the dual anti-protective film that film forming is anti-and glue is anti-in PET base material surface coating antistatic backing Scheme.
But, with the development of touch screen technology, more and more touch screen factory feedbacks, even with dual anti-protection Film also will produce a certain proportion of bad functional test that can interfere with TP and lead to occur NG's when operation is examined at the scene Phenomenon.Its disadvantage is that electrostatic when can not avoid removing release film generates, when carrying out dyestripping voltage tester, in room temperature condition, A4 Size dimension, dyestripping voltage are more than 1kV.Its main cause is as follows, and process for using of the protective film for TP shipment protection is:First Corresponding protective film is die-cut to suitable size, the guarantor that then field operation person will be die cut according to the gauge size of touch screen Release film in protection film structure removes (process will produce very big electrostatic), and will be fitted to glue-line needs TP panel areas to be protected Domain, then quality restriction personnel can to TP carry out functional test, pack shipment after the assay was approved.Therefore, traditional antistatic PET protection film, the electrostatic generated when removing release film when can not solve field operation doing plastic and resisting.
Utility model content
It is existing to overcome the main purpose of the utility model is to provide a kind of low dyestripping voltage antistatic PET protection film Deficiency in technology.
For realization foregoing purpose, the technical solution adopted in the utility model includes:
The utility model embodiment provides a kind of low dyestripping voltage antistatic PET protection film comprising along direction initialization PET base material, pressure-sensitive adhesive layer and the antistatic PET release films set gradually, the antistatic PET release films include PET release films And it is set to the anti-static coating of a PET release films at least side surface.
One of preferably, the PET base material is also equipped with anti-with the opposite facing side surface of pressure-sensitive adhesive layer Electrostatic coating.
Further, the pressure-sensitive adhesive layer includes antistatic polyurethane modified pressure-sensitive adhesive layer or acrylic modified pressure-sensitive adhesive Layer.
Further, the pressure-sensitive adhesive layer includes including the pressure sensitive adhesive substrate of antistatic agent and being set to described pressure-sensitive The anti-static coating of a matrix layer at least side surface.
Further, the PET base material includes PET polyester films.
Further, the thickness of the PET base material is 36~75 μm.
Further, the thickness of the anti-static coating is not more than 1 μm, impedance 105~1011Ω。
Further, the thickness of the antistatic PET release films is 36~75 μm, impedance 105~1011Ω。
Further, the dry glue thickness of the pressure-sensitive adhesive layer is 5~15 μm.
Further, at ambient temperature, when peeling force is 0.3~5g, A4 paper sizes, the low dyestripping voltage antistatic The dyestripping voltage of PET protection film is less than 500V.
Compared with prior art, include the advantages of the utility model:
Low dyestripping voltage antistatic PET protection film provided by the utility model is by making release film with antistatic work( Can, on the one hand it can effectively reduce in protective film production process, it is that release film generates during uncoiling and can build up Electrostatic;On the other hand this structure is also beneficial to during actually using protective film, and electrostatic can remove release film mistake It is guided in journey, the dyestripping voltage of protective film can be made to accomplish by above effect minimum, application prospect is extensive.
Description of the drawings
Fig. 1 is a kind of structural representation of low dyestripping voltage antistatic PET protection film in one exemplary embodiments of the utility model Figure.
Fig. 2 shows for a kind of structure of low dyestripping voltage antistatic PET protection film in another exemplary embodiments of the utility model It is intended to.
Reference numeral:1-PET polyester films, 2- polyurethane pressure sensitive glue-lines, 3-PET release films, 4- anti-static coatings.
Specific implementation mode
In view of deficiency in the prior art, inventor is able to propose that this practicality is new through studying for a long period of time and largely putting into practice The technical solution of type as follows will be further explained the technical solution, its implementation process and principle etc..
A kind of low dyestripping voltage antistatic PET protection film that the one side of the utility model embodiment provides comprising PET base material, pressure-sensitive adhesive layer and the antistatic PET release films set gradually along direction initialization, the antistatic PET release films include PET release films and the anti-static coating for being set to a PET release films at least side surface.
In view of caused by electrostatic in actual use to the adverse effect of actual job, one of preferably, The PET base material is also equipped with anti-static coating with the opposite facing side surface of pressure-sensitive adhesive layer, and it is anti-to do film forming.
Further, the pressure-sensitive adhesive layer includes antistatic polyurethane modified pressure-sensitive adhesive layer or acrylic modified pressure-sensitive adhesive Layer.
Further, the pressure-sensitive adhesive layer includes including the pressure sensitive adhesive substrate of antistatic agent and being set to described pressure-sensitive The anti-static coating of a matrix layer at least side surface.In electrostatic breakdown or damage TP in order to avoid removing generation because of protective film The functional assemblies such as electronic component, the pressure sensitive adhesive that the utility model is designed to glue-line to have certain anti-static function, i.e., The anti-protective film of glue.
Further, the PET base material includes PET polyester films.
Further, the thickness of the PET base material is 36~75 μm.
Further, the thickness of the anti-static coating is not more than 1 μm, impedance 105~1011Ω。
Further, the thickness of the antistatic PET release films is 36~75 μm, impedance 105~1011Ω。
Further, the dry glue thickness of the pressure-sensitive adhesive layer is 5~15 μm.
Further, when dyestripping voltage tester, at ambient temperature, when peeling force is 0.3~5g, A4 paper sizes are described The dyestripping voltage of low dyestripping voltage antistatic PET protection film is less than 500V.
Refering to Figure 1, the low dyestripping voltage antistatic PET protection film includes anti-static coating 4, PET bases successively Material (that is, PET polyester films 1), pressure-sensitive adhesive layer (that is, polyurethane contact adhesive 2), anti-static coating 4 and PET release films 3, i.e., it is anti- The layer upper surface antistatic of electrostatic PET release films.
It please refers to shown in Fig. 2, the low dyestripping voltage antistatic PET protection film includes anti-static coating 4, PET bases successively Material (that is, PET polyester films 1), pressure-sensitive adhesive layer (that is, polyurethane pressure sensitive glue-line 2), PET release films 3 and anti-static coating 4, i.e., The non-layer upper surface antistatic of antistatic PET release films.
The technical solution of the utility model is further explained below in conjunction with several embodiments and attached drawing.
Embodiment 1
The structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:PET base material, 36~75 μm of thickness;Poly- ammonia Ester or acrylic modified pressure-sensitive adhesive, dry glue thickness are 5~15 μm;Anti-static coating;PET release films (i.e. antistatic PET release films Layer upper surface antistatic), impedance 105~1011Ω, thickness are 50 μm.
Embodiment 2
The structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:PET base material, 36~75 μm of thickness;Poly- ammonia Ester or acrylic modified pressure-sensitive adhesive, dry glue thickness are 5~15 μm;PET release films;Anti-static coating (i.e. antistatic PET release films Non- layer upper surface antistatic), impedance 105~1011Ω, thickness are 50 μm.
Embodiment 3
The structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:PET base material, 36~75 μm of thickness;It is anti-quiet Voltolisation urethane or acrylic modified pressure-sensitive adhesive, dry glue thickness are 5~15 μm;Anti-static coating;PET release films (i.e. antistatic PET The layer upper surface antistatic of release film), impedance 105~1011Ω, thickness are 50 μm.
Embodiment 4
The structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:PET base material, 36~75 μm of thickness;It is anti-quiet Voltolisation urethane or acrylic modified pressure-sensitive adhesive, dry glue thickness are 5~15 μm;PET release films;Anti-static coating (i.e. antistatic PET The non-layer upper surface antistatic of release film), impedance 105~1011Ω, thickness are 50 μm.
Embodiment 5
As shown in Figure 1, the structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:Anti-static coating 4 is thick Degree is less than or equal to 1 μm;PET polyester films 1,36~75 μm of thickness;Polyurethane pressure sensitive glue-line 2, dry glue thickness are 5~15 μm;It is anti- Electrostatic coating 4;PET release films 3 (the layer upper surface antistatic of i.e. antistatic PET release films), impedance 105~1011Ω, thickness 50 μm。
Embodiment 6
As shown in Fig. 2, the structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:Anti-static coating 4 is thick Degree is less than or equal to 1 μm;PET polyester films 1,36~75 μm of thickness;Polyurethane pressure sensitive glue-line 2, dry glue thickness are 5~15 μm;PET Release film 3;Anti-static coating 4 (the non-layer upper surface antistatic of i.e. antistatic PET release films), impedance 105~1011Ω, thickness are 50μm。
Embodiment 7
The structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:Anti-static coating, thickness are less than or equal to 1 μ m;PET base material, 36~75 μm of thickness;Antistatic polyurethane or acrylic modified pressure-sensitive adhesive, dry glue thickness are 5~15 μm;It is anti-quiet Electrocoat;PET release films (the layer upper surface antistatic of i.e. antistatic PET release films), impedance 105~1011Ω, thickness are 50 μm.
Embodiment 8
The structure of the low dyestripping voltage antistatic PET protection film of the present embodiment is:Anti-static coating, thickness are less than or equal to 1 μ m;PET base material, 36~75 μm of thickness;Antistatic polyurethane or acrylic modified pressure-sensitive adhesive, dry glue thickness are 5~15 μm;PET from Type film;Anti-static coating (the non-layer upper surface antistatic of i.e. antistatic PET release films), impedance 105~1011Ω, thickness are 50 μm.
In conclusion the low dyestripping voltage antistatic PET protection film of the utility model is by making release film with anti- On the one hand electrostatic function can effectively reduce in protective film production process, that release film generates during uncoiling and can be by The electrostatic gradually accumulated;On the other hand this structure is also beneficial to during actually using protective film, electrostatic can remove from It is guided in type membrane process, the dyestripping voltage of protective film can be made to accomplish by above effect minimum, application prospect is extensive.
It should be appreciated that above-described embodiment is only the technical concepts and features for illustrating the utility model, it is ripe its object is to allow The personage for knowing technique can understand the content of the utility model and implement according to this, can not limit the utility model with this Protection domain.It is all according to equivalent change or modification made by the spirit of the present invention essence, should all cover in the utility model Within protection domain.

Claims (6)

1. a kind of low dyestripping voltage antistatic PET protection film, it is characterised in that include the PET bases set gradually along direction initialization Material, pressure-sensitive adhesive layer and antistatic PET release films, the antistatic PET release films include PET release films and are set to described The anti-static coating of PET release film both side surfaces, the PET base material are also equipped with anti-with the opposite facing side surface of pressure-sensitive adhesive layer Electrostatic coating, wherein the pressure-sensitive adhesive layer is selected from antistatic polyurethane modified pressure-sensitive adhesive layer or acrylic modified pressure-sensitive adhesive layer, institute It states pressure-sensitive adhesive layer and includes and include the pressure sensitive adhesive substrate of antistatic agent and be set to a pressure sensitive adhesive substrate at least side surface Anti-static coating;Also, when at ambient temperature, peeling force is 0.3~5g, the low dyestripping voltage antistatic PET protections The dyestripping voltage of film is less than 500V.
2. low dyestripping voltage antistatic PET protection film according to claim 1, it is characterised in that:The PET base material includes PET polyester films.
3. the low dyestripping voltage antistatic PET protection film according to claim 1, any one of 2, it is characterised in that:It is described The thickness of PET base material is 36~75 μm.
4. the low dyestripping voltage antistatic PET protection film according to claim 1, any one of 2, it is characterised in that:It is described The thickness of anti-static coating is not more than 1 μm, impedance 105~1011Ω。
5. the low dyestripping voltage antistatic PET protection film according to claim 1, any one of 2, it is characterised in that:It is described The thickness of antistatic PET release films is 36~75 μm, impedance 105~1011Ω。
6. the low dyestripping voltage antistatic PET protection film according to claim 1, any one of 2, it is characterised in that:It is described The dry glue thickness of pressure-sensitive adhesive layer is 5~15 μm.
CN201721446056.5U 2017-11-02 2017-11-02 A kind of low dyestripping voltage antistatic PET protection film Active CN207862254U (en)