CN109588160B - 高防尘长效转光五层共挤大棚膜及制备方法 - Google Patents
高防尘长效转光五层共挤大棚膜及制备方法 Download PDFInfo
- Publication number
- CN109588160B CN109588160B CN201811558653.6A CN201811558653A CN109588160B CN 109588160 B CN109588160 B CN 109588160B CN 201811558653 A CN201811558653 A CN 201811558653A CN 109588160 B CN109588160 B CN 109588160B
- Authority
- CN
- China
- Prior art keywords
- master batch
- layer
- dustproof
- greenhouse film
- light conversion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于农膜制备技术领域,具体的涉及一种高防尘长效转光五层共挤大棚膜及制备方法。本发明所述的高防尘长效转光五层共挤大棚膜包括外层、次外层、中层、次内层和内层,外层和次外层是大棚膜的流滴层,中层是大棚膜的保温层,内层和次内层是大棚膜的长寿层;其中,在次内层中添加转光母料,内层中添加防尘母料。该高防尘长效转光五层共挤大棚膜,除具备流滴功能外,还兼备转光功能和防尘功能;本发明所述的制备方法科学合理、简单易行;采用本发明所述的高防尘长效转光五层共挤大棚膜覆盖的大棚,具有作物生长快、坐果好、结果多、抗逆性强、早熟、增产、品质好的优点。
Description
技术领域
本发明属于农膜制备技术领域,具体的涉及一种高防尘长效转光五层共挤大棚膜及制备方法。
背景技术
目前,我国塑料农膜产量和消费量已经位居世界前列,而且农用薄膜市场正逐步向高端领域发展,由常规3层向5层结构发展已经成为农用薄膜行业的普遍共识,并且农膜正在朝着多功能性发展;“菜篮子”工程是增加农民收入的重要途径,也是稳定物价、稳定市场、保障人民生活需要的基础条件,随着全国各地“菜篮子”工程的建设,设施蔬菜生产规模的持续扩大,棚室内茎叶菜种植比例明显上升;不需要蓄热的避雨栽培面积也越来越大;另外,消费者对产品质量的要求越来越高,例如茎叶菜鲜嫩度的要求、口感的要求;生产者则对改善作业环境的意识日益增强,希望能在相对舒适的环境里进行种植。这就导致市场迫切需要新一代多功能大棚膜的出现。
现在市场上存在防尘功能和转光功能的大棚膜,但是它们的防尘、转光及流滴消雾功能不能共存,只能存在三种功能中的一种或两种;为克服上述缺点,亟需开发功能更为全面的大棚膜。
发明内容
本发明的目的是克服现有技术的不足,提供一种高防尘长效转光五层共挤大棚膜。该大棚膜除具备流滴、消雾等常规功能外,还具备防尘功能和长效转光功能;本发明同时提供了其制备方法,该制备方法科学合理、简单易行。
本发明所述的高防尘长效转光五层共挤大棚膜,包括外层、次外层、中层、次内层和内层,外层和次外层是大棚膜的流滴层,中层是大棚膜的保温层,内层和次内层是大棚膜的长寿层;其中,在次内层中添加转光母料,内层中添加防尘母料。
其中:
大棚膜内层为具有防尘功能的长寿层,次内层为具有转光功能的长寿层,中层为保温层,外层为流滴消雾层,次外层为流滴消雾层。
外层、次外层、中层、次内层、内层生产原料由如下重量百分比的原料制成:
以重量分数计,内层由如下原料组成:
聚乙烯原料 80%
长寿母料 10%
防尘母料 10%;
以重量分数计,次内层由如下原料组成:
聚乙烯原料 87%
长寿母料 10%
转光母料 3%;
以重量分数计,中层由如下原料组成:
以重量分数计,外层由如下原料组成:
EVA 80%
长寿母料 10%
流滴消雾母料 10%;
以重量分数计,次外层由如下原料组成:
其中,长寿母料、流滴消雾母料、保温母料、防尘母料、转光母料由如下重量百分比的原料制成:
以重量分数计,长寿母料由如下原料组成:
以重量分数计,流滴消雾母料由如下原料组成:
聚乙烯粉料 83%-85%
流滴剂 14%-16%
液体消雾剂 1%。
以重量分数计,保温母料由如下原料组成:
聚乙烯粉料 81%-84%
流滴剂 12%-14%
保温剂 4%-5%;
以重量分数计,防尘母料由如下原料组成:
以重量分数计,转光母料由如下原料组成:
聚乙烯粉料 90-95%
转光剂 5-10%。
聚乙烯原料是指由低密度聚乙烯、线性低密度聚乙烯或茂金属聚乙烯三种原料中的一种或多种按所需比例组成的基础原料;大棚膜内层的聚乙烯原料由低密度聚乙烯和茂金属聚乙烯按3:7的质量比混合;大棚膜次内层的聚乙烯原料由低密度聚乙烯和茂金属聚乙烯按7:3的质量比混合;大棚膜中层的聚乙烯原料是100%低密度聚乙烯;大棚膜次外层的聚乙烯原料是100%低密度聚乙烯;大棚膜外层无聚乙烯原料。
聚乙烯粉料是磨成粉状的聚乙烯原料。
流滴剂为脂肪酸多元醇酯、脂肪酸聚氧乙烯酯或聚氧乙烯烷基胺中的一种或多种。
流滴剂优选是LY-8(临安助剂化工有限公司)。
光稳定剂为622(北京天罡助剂有限公司)或光稳定剂944(北京天罡助剂有限公司)中的一种。
抗氧剂为1010(天津利安隆新材料股份有限公司)或抗氧剂168(天津利安隆新材料股份有限公司)中的一种。
紫外线吸收剂为UV-531(天津天大)或UV-630(北京天罡助剂有限公司)中的一种。
液体消雾剂是台湾丰笙TS-403氟表面活性剂。
保温剂为高岭土、硅藻土或滑石粉中的一种;润滑剂为硬脂酸锌类润滑剂;分散剂为脂肪族酰胺类分散剂;偶联剂为钛酸酯偶联剂。
分散剂优选己烯基双硬脂酰胺(青岛集思材料有限公司);偶联剂优选TMC-201(山东佰仟化工有限公司)。
防尘助剂为是抗静电剂,防静电剂为ATMER 129-MB。
转光剂为有机合成类稀土转光剂,稀土成分为三氧化二铕,有机成分为邻羟基苯甲酸。
本发明所述的高防尘长效转光五层共挤大棚膜的制备方法,具体包括以下步骤:
首先按照外层、次外层、中层、次内层、内层的配方将各种原料倒入电动搅拌机,将原料搅拌均匀,然后原料通过吸料机吸入挤出机的料斗中,原料经过各层(外层、次外层、中层、次内层、内层)机筒的剪切加热再经过机筒的连接体到达机头,工人将塑化好从机头挤出的原料提起到达牵引,同时进行吹胀,膜经过牵引再进行收卷,形成成品。
本发明所述的高防尘长效转光五层共挤大棚膜的制备工艺流程图如附图1所示。
其中:
长寿母料、保温母料、流滴消雾母料、防尘母料和转光母料的制备方法分别为:
(1)长寿母料的制备
使用高速混合机将聚乙烯粉料、光稳定剂、抗氧剂和紫外线吸收剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得长寿母料;
(2)保温母料的制备
使用高速混合机将聚乙烯粉料、流滴剂和保温剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得保温母料;
(3)流滴消雾母料的制备
使用高速混合机将聚乙烯粉料、流滴剂和液体消雾剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得流滴消雾母料;
(4)防尘母料的制备
使用高速混合机将聚乙烯粉料、润滑剂、分散剂、偶联剂和防尘助剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得防尘母料;
(5)转光母料的制备
使用高速混合机将聚乙烯粉料和转光剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得转光母料。
本发明是通过选取最合适助剂,保证各种助剂之间是协同作用,互相之间没有负面影响的前提下,调配新型配方工艺,经过大量的试验(大田试验及实验室试验),最大程度利用防尘助剂和转光助剂的功能,同时利用五层共挤大棚膜配方的灵活性,使五层配方中每一层的功能性单一且高效。经大量实验及科学论证流滴剂、液体消雾剂和防尘助剂都是析出性功能产品,只能迁移到膜的表面后才能起作用,转光剂不需要迁移到膜表面,在膜的内层就能起到转光的作用,同时流滴剂、液体消雾剂、转光剂、防尘助剂之间是有相互抑制的作用,不能同时放到一层当中,综合理论及实践结合,得出配方。
本发明所述的高防尘长效转光五层共挤大棚膜是五层层共挤设备完成,并且利用的是翻棚生产的技术完成。
本发明通过新型添加方式,做到农膜同时具备了流滴消雾功能、转光功能、防尘功能;本发明同时提供了高防尘长效转光五层共挤大棚膜的制备方法,该制备方法科学合理、简单易行。
高防尘长效转光五层共挤大棚膜在防尘性方面,加工薄膜过程中在塑料原料中加入防静电剂或对薄膜进行表面处理使其表面不易拈污灰尘,保持透明度,利于作物光合作用的进行及作物、植物的生长。其次对于膜的转光性,在生产SPAPO大棚膜的原材料中添加“转光功能性母料”,当阳光透过“转光膜”时,阳光中的紫外线(会灼伤植物组织)和绿光(会被植物反射而损失)被膜中的“转光母料”吸收转换,释放出对植物生长有利的蓝光和红光,使棚内的蓝色和红色光谱成分增加,提高了光能利用率。应用结果表明,采用“转光膜”覆盖的大棚,作物生长快、坐果好、结果多、抗逆性强、早熟、增产、品质好的优点。
本发明与现有技术相比,具有以下有益效果:
(1)本发明所述的高防尘长效转光五层共挤大棚膜,除具备流滴功能外,还兼备转光功能和防尘功能;本发明所述的制备方法科学合理、简单易行。
(2)采用本发明所述的高防尘长效转光五层共挤大棚膜覆盖的大棚,具有作物生长快、坐果好、结果多、抗逆性强、早熟、增产、品质好的优点。
附图说明
图1是本发明高防尘长效转光五层共挤大棚膜的制备工艺流程图。
具体实施方式
以下结合实施例对本发明作进一步描述。
实施例1
本实施例1所述的内层、次内层、中层、外层、次外层大棚膜配比按照配方所给比例添加,具体是:
大棚膜内层配比:80%聚乙烯原料(200kg)+10%长寿母料(25kg)+10%防尘母料(25kg)(合计250kg倒入混料机混合均匀),其中聚乙烯原料由低密度聚乙烯和茂金属聚乙烯按3:7的质量比混合;
大棚膜次内层配比:87%聚乙烯原料(217.5kg)+10%长寿母料(25kg)+3%转光母料(7.5kg)(合计250kg倒入混料机混合均匀),其中聚乙烯原料由低密度聚乙烯和茂金属聚乙烯按7:3的质量比混合;
大棚膜中层配比:70%聚乙烯原料(175kg)+20%EVA(50kg)+5%保温母料(12.5kg)+5%流滴消雾母料(12.5kg)(合计250kg倒入混料机混合均匀),其中聚乙烯原料是100%低密度聚乙烯;
大棚膜外层配比:80%EVA(200kg)+10%长寿母料(25kg)+10%流滴消雾母料(25kg)(合计250kg倒入混料机混合均匀);
大棚膜次外层配比:20%聚乙烯原料(50kg)+60%EVA(150kg)+10%流滴消雾母料(25kg)+10%流滴消雾母料(25kg)(合计250kg倒入混料机混合均匀),其中聚乙烯原料是100%低密度聚乙烯。
所述的长寿母料每包重量是25kg,是由如下重量的原料制成:
所述的保温母料每包重量是25kg,是由如下重量的原料制成:
聚乙烯粉料(齐鲁石化有限公司7042) 20.25kg
流滴剂(临安助剂化工有限公司LY-8) 3.5kg
保温剂(广州亿峰科技有限公司滑石粉) 1.25kg。
所述的流滴消雾母料每包重量是25kg,是由如下重量的原料制成:
聚乙烯粉料(齐鲁石化有限公司7042) 20.75kg
流滴剂(临安助剂化工有限公司LY-8) 4kg
液体消雾剂(大连锦隆化工有限公司TS-403) 0.25kg。
所述的防尘母料每包重25kg,是由如下重量的原料制成:
所述的转光母料每包重25kg,是由如下重量的原料制成:
聚乙烯粉料 22.5kg
有机合成稀土转光剂(湖南师范大学) 2.5kg。
高防尘长效转光五层共挤大棚膜的制备方法,步骤如下:
首先按照外层、次外层、中层、次内层、内层的配方将各种原料倒入电动搅拌机,将原料搅拌均匀,然后原料通过吸料机吸入挤出机的料斗中,原料经过各层(外层、次外层、中层、次内层、内层)机筒的剪切加热再经过机筒的连接体到达机头,工人将塑化好从机头挤出的原料提起到达牵引,同时进行吹胀,膜经过牵引再进行收卷,形成成品。
其中,长寿母料、保温母料、流滴消雾母料、防尘母料和转光母料的制备方法分别为:
(1)长寿母料的制备
使用高速混合机将聚乙烯粉料、流滴剂、光稳定剂、抗氧剂、紫外线吸收剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得长寿母料;
(2)保温母料的制备
使用高速混合机将聚乙烯粉料、流滴剂、保温剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得保温母料;
(3)流滴消雾母料的制备
使用高速混合机将聚乙烯粉料、流滴剂、消雾剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得流滴母料;
(4)防尘母料的制备
使用高速混合机将聚乙烯粉料、润滑剂、分散剂、偶联剂、防尘助剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得防尘母料;
(5)转光母料的制备
使用高速混合机将聚乙烯粉料、转光助剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得转光母料。
原料经过五层层共挤吹塑机组吹塑成型,即得。
调整下料比,按照内层1,次内层1,中层1,次外层1,外层1的下料比例按流程吹膜生产。工艺温度设置按照表1所示。
表1吹塑成型温度(℃)
实施例2
本实施例2所述的内层、次内层、中层、外层、次外层大棚膜配比按照配方所给比例添加,具体是:大棚膜内层、次内层、中层、外层及次外层的配比均与实施例1相同。
所述的长寿母料、保温母料和流滴消雾母料每包重量均是25kg,配比均匀实施例1相同。
所述的防尘母料每包重25kg,是由如下重量的原料制成:
所述的转光母料每包重25kg,是由如下重量的原料制成:
聚乙烯粉料 23.75kg
有机合成稀土转光剂(湖南师范大学) 1.25kg。
实施例2所述的高防尘长效转光五层共挤大棚膜的制备方法与实施例1相同。
实施例3
本实施例3所述的内层、次内层、中层、外层、次外层大棚膜配比按照配方所给比例添加,具体是:大棚膜内层、次内层、中层、外层及次外层的配比均与实施例1相同。
所述的长寿母料、保温母料和流滴消雾母料每包重量均是25kg,配比均匀实施例1相同。
所述的防尘母料每包重25kg,是由如下重量的原料制成:
所述的转光母料每包重25kg,是由如下重量的原料制成:
聚乙烯粉料 23kg
有机合成稀土转光剂(湖南师范大学) 2kg。
实施例3所述的高防尘长效转光五层共挤大棚膜的制备方法与实施例1相同。
对比例1
本对比例1配方选取配方中不添加防尘母料和转光母料,母料缺失部分由聚乙烯原料代替;大棚膜内层配比:90%聚乙烯原料+10%长寿母料(倒入混料机混合均匀);大棚膜次内层配比:90%聚乙烯原料+10%长寿母料(倒入混料机混合均匀);大棚膜中层、次外层和外层配比均同实施例1;长寿母料、保温母料、流滴消雾母料配比均匀实施例1相同;制备方法与实施例1相同。
对比例2
本对比例2选取配方中防尘母料和转光母料同时放到薄膜内层(棚的外层),大棚膜内层配比:77%聚乙烯原料+10%长寿母料+10%防尘母料+3%转光母料(倒入混料机混合均匀);大棚膜次内层配比:90%聚乙烯原料+10%长寿母料(合计250kg倒入混料机混合均匀);大棚膜中层、次外层和外层配比均同实施例1;长寿母料、保温母料、流滴消雾母料、防尘母料和转光母料配比均匀实施例1相同;制备方法与实施例1相同。
对比例3
本对比例3配方选取配方中转光母料放到薄膜的中层,防尘母料放在大棚膜内层(棚的外层);大棚膜内层配比:同实例1;次内层配比:90%聚乙烯原料+10%长寿母料(合计250kg倒入混料机混合均匀);中层配比:67%聚乙烯原料+20%EVA+5%保温母料+5%流滴消雾母料+3%转光母料;大棚膜次外层和外层配比均同实施例1;长寿母料、保温母料、流滴消雾母料、防尘母料和转光母料配比均匀实施例1相同;制备方法与实施例1相同。
对比例4
本对比例4选取配方中转光母料放到薄膜的次外层,防尘母料放在大棚膜内层(棚的外层);大棚膜次内层配比:90%聚乙烯原料+10%长寿母料;大棚膜次外层配比:17%聚乙烯原料+60%EVA+10%长寿母料+10%流滴消雾母料+3%转光母料(合计250kg倒入混料机混合均匀)。
大棚膜内层、中层和外层配比均同实施例1;长寿母料、保温母料、流滴消雾母料、防尘母料和转光母料配比均匀实施例1相同;制备方法与实施例1相同。
对比例5
本对比例5配方选取配方中转光母料放到薄膜的外层,防尘母料放在大棚膜内层(棚的外层);大棚膜内层配比:同实例1;大棚膜次内层配比:90%聚乙烯原料+10%长寿母料(合计250kg倒入混料机混合均匀);大棚膜中层配比:同实例1;大棚膜次外层配比:同实例1;大棚膜外层配比:77%EVA+10%长寿母料+10%流滴消雾母料+3%转光母料(合计250kg倒入混料机混合均匀)。
长寿母料、保温母料、流滴消雾母料、防尘母料、转光母料均同实例1;制备方法与实施例1相同。
依据农用大棚膜国标测试其机械性能,产品不同部位机械性能及透光率雾度值测试结果见表2,产品规格型号为10000mm*0.12mm。
表2实施例1-3和对比例1-5产品机械性能及透光率雾度值测试结果
测试结果看膜的各项性能均是优秀。
为了测试本发明所述的高防尘长效转光大棚膜的性能,进行实验室模拟对比试验:
试验条件:持续水浴(60℃);持续氙灯照射;
恒量:转光母料添加量;
变量:外中内三层转光母料添加比例。
散射效果、有效成分检测情况如下表3:
表3大棚膜转光效果及转光中助剂含量检测
表4流滴消雾水浴试验
表5防尘试验
经过一系列测试,实施例1和对比例1-5的流滴消雾效果看,防尘母料和转光母料的添加未对其功能产生影响,所以防尘母料和转光母料在哪一层添加都不会影响流滴消雾功能;实施例1和对比例2,理论上防尘母料(抗静电母料)放到膜的内层(棚的外层)是显而易见的,通过对比例2看出防尘助剂和转光助剂有相互抑制的作用;从转光性看出,对比例3-5,转光剂放到中层、次外层和外层,转光助剂的含量有明显变化,表明是流滴消雾剂的析出带走了转光助剂。综上所述,本发明中所述的添加方式是最优添加方式,能够使棚膜满同时具备流滴消雾、防尘和转光功能。
Claims (8)
4.根据权利要求1所述的高防尘长效转光五层共挤大棚膜,其特征在于:聚乙烯原料是指由低密度聚乙烯、线性低密度聚乙烯或茂金属聚乙烯三种原料中的一种或多种按所需比例组成的基础原料;大棚膜内层的聚乙烯原料由低密度聚乙烯和茂金属聚乙烯按3:7的质量比混合;大棚膜次内层的聚乙烯原料由低密度聚乙烯和茂金属聚乙烯按7:3的质量比混合;大棚膜中层的聚乙烯原料是100%低密度聚乙烯;大棚膜次外层的聚乙烯原料是100%低密度聚乙烯。
5.根据权利要求2所述的高防尘长效转光五层共挤大棚膜,其特征在于:聚乙烯粉料是磨成粉状的聚乙烯原料;流滴剂为脂肪酸多元醇酯、脂肪酸聚氧乙烯酯或聚氧乙烯烷基胺中的一种或多种;光稳定剂为622或944中的一种;抗氧剂为1010或168中的一种;紫外线吸收剂为UV-531或UV-630中的一种;液体消雾剂是台湾丰笙TS-403氟表面活性剂。
6.根据权利要求3所述的高防尘长效转光五层共挤大棚膜,其特征在于:保温剂为高岭土、硅藻土或滑石粉中的一种;润滑剂为硬脂酸锌类润滑剂;分散剂为脂肪族酰胺类分散剂;偶联剂为钛酸酯偶联剂;防尘助剂为是防静电剂,防静电剂为ATMER 129-MB;转光剂为有机合成类稀土转光剂,稀土成分为三氧化二铕,有机成分为邻羟基苯甲酸。
7.一种权利要求1所述的高防尘长效转光五层共挤大棚膜的制备方法,其特征在于:具体包括以下步骤:
首先按照外层、次外层、中层、次内层、内层的配方将各种原料倒入电动搅拌机,将原料搅拌均匀,然后原料通过吸料机吸入挤出机的料斗中,原料经过各层机筒的剪切加热再经过机筒的连接体到达机头,工人将塑化好从机头挤出的原料提起到达牵引,同时进行吹胀,膜经过牵引再进行收卷,形成成品。
8.根据权利要求7所述的高防尘长效转光五层共挤大棚膜的制备方法,其特征在于:原料中长寿母料、保温母料、流滴消雾母料、防尘母料和转光母料原料的制备方法分别如下:
(1)长寿母料的制备
使用高速混合机将聚乙烯粉料、光稳定剂、抗氧剂和紫外线吸收剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得长寿母料;
(2)保温母料的制备
使用高速混合机将聚乙烯粉料、流滴剂和保温剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得保温母料;
(3)流滴消雾母料的制备
使用高速混合机将聚乙烯粉料、流滴剂和液体消雾剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得流滴消雾母料;
(4)防尘母料的制备
使用高速混合机将聚乙烯粉料、润滑剂、分散剂、偶联剂和防尘助剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得防尘母料;
(5)转光母料的制备
使用高速混合机将聚乙烯粉料和转光剂按照比例高速混合后,加入密炼机捏合,再由喂料机喂入双螺杆挤出机,经水环或水下切粒,制得转光母料。