CN109574606A - A kind of antibacterial environment protection gap filler for building - Google Patents
A kind of antibacterial environment protection gap filler for building Download PDFInfo
- Publication number
- CN109574606A CN109574606A CN201811630946.0A CN201811630946A CN109574606A CN 109574606 A CN109574606 A CN 109574606A CN 201811630946 A CN201811630946 A CN 201811630946A CN 109574606 A CN109574606 A CN 109574606A
- Authority
- CN
- China
- Prior art keywords
- parts
- gap filler
- environment protection
- protection gap
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterial environment protection gap fillers for building, its raw material includes following components by weight: 25-30 parts of portland cement, 0.5-1 parts of high alumina cement, 55-70 parts of filler, 1-2 parts of antimildew and antibacterial agent, 1.5-3 parts of waterproofing agent, 1-5 parts of pigment, 1-2 parts of lubricant, 0.5-2 parts of levelling agent, 1-2 parts of antioxidant, antibacterial environment protection gap filler for building, it has cohesive force strong in use, antimildew and antibacterial, sterilizing environmental protection, it is anti-oxidant and not blistering, crack is not generated and is fallen off, it is bright-colored colorful, good water-proof effect, the features such as easy to use, there are also splendid decorative effects for this antibacterial environment protection gap filler for building, the requirement of high-end tiles fitting-out work can be met, coloration is high, exquisite in texture, suitable for the ceramic tile of most of type and the seam of stone material, it can To enhance the decorative effect of plane materiel, after water mixed construction, have certain flexibility, waterproofness and inoxidizability, the swell-shrinking deformation between plate can be prevented, to extend the service life of facing.
Description
Technical field
The present invention relates to technical field of construction and decoration materials more particularly to a kind of antibacterial environment protection gap fillers for building.
Background technique
After exterior walls of buildings sticks ceramic tile, need to be filled the gap between ceramic tile, gap filler meets well
Such requirement, gap filler is also at caulking agent, jointing agent is claimed, for filling up the ceramic tile or natural stone that are attached on wall or floor
Between joint filler, match gap filler appropriate suitable for indoor and outdoors, matched with ornament materials such as ceramic tile, stone materials,
There is provided bonding, the antiseepage etc. between beautiful surface and facing brick body, additionally it is possible to reduce entire wall or floor covering
Interior stress protects tile base layer material to negatively affect from mechanical failure and water penetration into whole building bring, but tradition
Gap filler there is very big problem, do not have the effect of antimildew and antibacterial sterilization, gap location bacterium easy to breed when use occurs mould
Become, bring health threat to the life of personnel, material harmful components are too many, can not accomplish environment protecting, easy to oxidize and blistering
Phenomenon is serious, and color is single, be easy to produce crack and fall off, waterproof effect it is bad.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of antibacterial environment protection proposed is for building
Gap filler,
To achieve the goals above, present invention employs following technical solutions:
A kind of antibacterial environment protection gap filler for building, raw material includes following components by weight: portland cement 25-30
Part, 0.5-1 parts of high alumina cement, 55-70 parts of filler, 1-2 parts of antimildew and antibacterial agent, 1.5-3 parts of waterproofing agent, 1-5 parts of pigment, lubricant
1-2 parts, 0.5-2 parts of levelling agent, 1-2 parts of antioxidant.
As a preferred technical solution of the present invention, the filler is one kind of quartz sand, calcium carbonate and dolomite dust.
As a preferred technical solution of the present invention, the antimildew and antibacterial agent is organic copper salt or electrodeless salt copper sulphate
It is one or two kinds of.
As a preferred technical solution of the present invention, the antioxidant is one kind of L-AA or sulphite
Or two kinds.
As a preferred technical solution of the present invention, the lubricant is aluminium-magnesium silicate thixotropic lubricant.
As a preferred technical solution of the present invention, the levelling agent is one kind of polyacrylic acid or carboxymethyl cellulose
Or it is a variety of.
As a preferred technical solution of the present invention, the waterproofing agent is inorganic aluminate water-proof agent.
As a preferred technical solution of the present invention, the raw material further includes 1-5 parts of defoaming agent by weight.
As a preferred technical solution of the present invention, the defoaming agent is silicone emulsion, higher alcohols are fatty acid ester compounded
Object or polypropylene glycerol aether it is one or more.
As a preferred technical solution of the present invention, the pigment is the one or two of titanium oxide or iron oxide.
Beneficial to benefit: in the present invention, it has strong cohesive force, antimildew and antibacterial, sterilizing environmental protection, anti-oxidant and not in use
Blistering, do not generate crack and fall off, bright-colored colorful, good water-proof effect, it is easy to use the features such as, this antibacterial environment protection building
With gap filler, there are also splendid decorative effects, can meet the requirement of high-end tiles fitting-out work, and coloration height, is applicable in exquisite in texture
In the ceramic tile of most of type and the seam of stone material, the decorative effect of plane materiel can be enhanced, after water mixed construction, have certain
Flexibility, waterproofness and inoxidizability, the swell-shrinking deformation between plate can be prevented, to extend the service life of facing.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment one
Production is cleaned up and is dried with reactor tank, by 25 parts of portland cement, 1 part of high alumina cement, 55 parts of quartz sand,
1 part of organic copper salt, 1.5 parts of inorganic aluminate water-proof agent, 1 part of titanium oxide, 1 part of aluminium-magnesium silicate thixotropic lubricant, polyacrylic acid 0.5
Part, 1 part of L-AA, 1 part of silicone emulsion, aluminium-magnesium silicate thixotropic lubricant form a kind of be known as when being only more than minimum external force
Just flowable yield value, this makes gap filler during joint filling without producing sagging or sliding phenomenon, shape when use
At slurry, add pigment after will not cause to precipitate, pigment will not be generated and secreted out, organic copper salt can be good at preventing micro- life
Object causes the occurrence of mouldy, and electrodeless salt copper sulphate is very stable at normal temperatures and pressures, does not deliquesce, and can play good sterilization
Effect, the gap filler added with inorganic aluminate water-proof agent, the capillary porosity formed in gap filler hardening process and aquaporin, tool
There is the repellency of extremely strong hydrophobicity and moisture, thus assign gap filler very strong waterproof performance, silicone emulsion, higher alcohols fat
Acid esters compound or polypropylene glycerol aether make gap filler surface tension be lower than the surface tension of gas-liquid bubble, inhibit the generation of bubble
Or the bubble that has generated is eliminated, and by weight configuring, after the completion of configuration, the reactor tank that is delivered to by conveying pipeline in blender
In, stirring motor is opened, is uniformly mixed each ingredient by stirring rod, after mixing, discharging is packaged into bag up to product is gone out.
Embodiment two
Production is cleaned up and is dried with reactor tank, by 30 parts of portland cement, 1 part of high alumina cement, 70 parts of quartz sand,
2 parts of organic copper salt, 3 parts of inorganic aluminate water-proof agent, 5 parts of titanium oxide, 2 parts of aluminium-magnesium silicate thixotropic lubricant, 2 parts of polyacrylic acid, L-
1 part of the fatty acid ester compounded object of 2 parts of ascorbic acid, higher alcohols, by weight configuring, aluminium-magnesium silicate thixotropic lubricant forms a kind of title
Ability flowable yield value when to be only more than minimum external force, this makes gap filler during joint filling without producing sagging
Or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate pigment and secrete out after adding pigment, organic copper
Salt can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is very stable at normal temperatures and pressures, not damp
Solution, can play good bactericidal effect, the gap filler added with inorganic aluminate water-proof agent is formed in gap filler hardening process
Capillary porosity and aquaporin, with extremely strong hydrophobicity and moisture repellency, to assign gap filler very strong waterproofness
Can, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether make gap filler surface tension lower than gas-liquid bubble
Surface tension inhibits the generation of bubble or eliminates the bubble generated, after the completion of configuration, is delivered in blender by conveying pipeline
Reactor tank in, open stirring motor, each ingredient is uniformly mixed by stirring rod, after mixing, discharging be packaged into bag i.e.
Obtain product.
Embodiment three
Production is cleaned up and is dried with reactor tank, by 25 parts of portland cement, 1 part of high alumina cement, 55 parts of calcium carbonate,
1 part of electrodeless salt copper sulphate, 1.5 parts of inorganic aluminate water-proof agent, 1 part of iron oxide, 1 part of aluminium-magnesium silicate thixotropic lubricant, carboxymethyl are fine
Plain 0.5 part, 1 part of sulphite, 1 part of polypropylene glycerol aether are tieed up, by weight configuring, aluminium-magnesium silicate thixotropic lubricant forms one
Ability flowable yield value when kind is known as only being more than minimum external force, this makes gap filler during joint filling without producing
Sagging or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate pigment and secrete out, have after adding pigment
Machine mantoquita can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is very stable at normal temperatures and pressures,
It does not deliquesce, good bactericidal effect can be played, the gap filler added with inorganic aluminate water-proof agent, in gap filler hardening process
The capillary porosity of formation and aquaporin, the repellency with extremely strong hydrophobicity and moisture, so that it is very strong anti-to assign gap filler
Aqueous energy, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether make gap filler surface tension lower than gas-liquid
The surface tension of bubble inhibits the generation of bubble or eliminates the bubble generated, after the completion of configuration, is delivered to stirring by conveying pipeline
In reactor tank in device, stirring motor is opened, is uniformly mixed each ingredient by stirring rod, after mixing, discharging is packaged into
Bag is up to product out.
Example IV
Production is cleaned up and dried with reactor tank, by 30 parts of portland cement, 0.5 part of high alumina cement, calcium carbonate 70
Part, 2 parts of organic copper salt, 3 parts of inorganic aluminate water-proof agent, 5 parts of titanium oxide, 2 parts of aluminium-magnesium silicate thixotropic lubricant, carboxymethyl cellulose
0.5 part, 1 part of sulphite, 3 parts of polypropylene glycerol aether, by weight configuring, aluminium-magnesium silicate thixotropic lubricant forms a kind of title
Ability flowable yield value when to be only more than minimum external force, this makes gap filler during joint filling without producing sagging
Or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate pigment and secrete out after adding pigment, organic copper
Salt can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is very stable at normal temperatures and pressures, not damp
Solution, can play good bactericidal effect, the gap filler added with inorganic aluminate water-proof agent is formed in gap filler hardening process
Capillary porosity and aquaporin, with extremely strong hydrophobicity and moisture repellency, to assign gap filler very strong waterproofness
Can, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether make gap filler surface tension lower than gas-liquid bubble
Surface tension inhibits the generation of bubble or eliminates the bubble generated, after the completion of configuration, is delivered in blender by conveying pipeline
Reactor tank in, open stirring motor, each ingredient is uniformly mixed by stirring rod, after mixing, discharging be packaged into bag i.e.
Obtain product
Embodiment five
Production is cleaned up and dried with reactor tank, by 25 parts of portland cement, 0.5 part of high alumina cement, dolomite dust
55 parts, 1 part of electrodeless salt copper sulphate, 1.5 parts of inorganic aluminate water-proof agent, 1 part of iron oxide, 1 part of aluminium-magnesium silicate thixotropic lubricant, poly- third
0.5 part of olefin(e) acid, 1 part of L-AA, 5 parts of polypropylene glycerol aether, by weight configuring, aluminium-magnesium silicate thixotropic lubricant is formed
One kind is known as when being only more than minimum external force just flowable yield value, this make gap filler during joint filling without
Producing sagging or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate pigment and secrete out after adding pigment,
Organic copper salt can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is very steady at normal temperatures and pressures
It is fixed, it does not deliquesce, good bactericidal effect can be played, the gap filler added with inorganic aluminate water-proof agent was hardened in gap filler
The capillary porosity formed in journey and aquaporin, the repellency with extremely strong hydrophobicity and moisture, so that it is very strong to assign gap filler
Waterproof performance, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether are lower than gap filler surface tension
The surface tension of gas-liquid bubble inhibits the generation of bubble or eliminates the bubble generated, after the completion of configuration, is delivered to by conveying pipeline
In reactor tank in blender, stirring motor is opened, is uniformly mixed each ingredient by stirring rod, after mixing, spout bag
Bag is dressed up up to product is gone out.
Embodiment six
Production is cleaned up and dried with reactor tank, by 25 parts of portland cement, 1 part of high alumina cement, dolomite dust 70
Part, 2 parts of electrodeless salt copper sulphate, 3 parts of inorganic aluminate water-proof agent, 3 parts of iron oxide, 2 parts of aluminium-magnesium silicate thixotropic lubricant, polyacrylic acid
2 parts, 2 parts of L-AA, 2 parts of the fatty acid ester compounded object of higher alcohols, by weight configuring, aluminium-magnesium silicate thixotropic lubricant is formed
One kind is known as when being only more than minimum external force just flowable yield value, this make gap filler during joint filling without
Producing sagging or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate pigment and secrete out after adding pigment,
Organic copper salt can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is very steady at normal temperatures and pressures
It is fixed, it does not deliquesce, good bactericidal effect can be played, the gap filler added with inorganic aluminate water-proof agent was hardened in gap filler
The capillary porosity formed in journey and aquaporin, the repellency with extremely strong hydrophobicity and moisture, so that it is very strong to assign gap filler
Waterproof performance, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether are lower than gap filler surface tension
The surface tension of gas-liquid bubble inhibits the generation of bubble or eliminates the bubble generated, after the completion of configuration, is delivered to by conveying pipeline
In reactor tank in blender, stirring motor is opened, is uniformly mixed each ingredient by stirring rod, after mixing, spout bag
Bag is dressed up up to product is gone out.
Embodiment seven
Production is cleaned up and dried with reactor tank, by 28 parts of portland cement, 0.5 part of high alumina cement, dolomite dust
60 parts, it is 1.5 parts of electrodeless salt copper sulphate, 2 parts of inorganic aluminate water-proof agent, 3 parts of iron oxide, 1.5 parts of aluminium-magnesium silicate thixotropic lubricant, poly-
1 part of acrylic acid, 1.5 parts of L-AA, 5 parts of the fatty acid ester compounded object of higher alcohols, by weight configuring, aluminium-magnesium silicate thixotroping is moistened
Lubrication prescription formed it is a kind of be known as when being only more than minimum external force just flowable yield value, this make gap filler during joint filling and
It is not in produce sagging or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate face after adding pigment
Material is secreted out, and organic copper salt can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is in normal temperature and pressure
Under it is very stable, do not deliquesce, good bactericidal effect can be played, the gap filler added with inorganic aluminate water-proof agent, in gap filler
The capillary porosity formed in hardening process and aquaporin, the repellency with extremely strong hydrophobicity and moisture, to assign joint filling
The very strong waterproof performance of agent, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether make gap filler surface
Power is lower than the surface tension of gas-liquid bubble, inhibits the generation of bubble or eliminates the bubble generated, after the completion of configuration, passes through conveying pipeline
It is delivered in the reactor tank in blender, opens stirring motor, uniformly mixed each ingredient by stirring rod, after mixing,
Discharging is packaged into bag up to product is gone out.
Embodiment eight
Production is cleaned up and dried with reactor tank, by 25 parts of portland cement, 1 part of high alumina cement, dolomite dust 55
Part, 1 part of electrodeless salt copper sulphate, 1.5 parts of inorganic aluminate water-proof agent, 1 part of iron oxide, 1 part of aluminium-magnesium silicate thixotropic lubricant, polypropylene
Sour 0.5 part, 1 part of L-AA, 1 part of the fatty acid ester compounded object of higher alcohols, by weight configuration, aluminium-magnesium silicate thixotropic lubricant
Formed it is a kind of be known as when being only more than minimum external force just flowable yield value, this make gap filler during joint filling without
There is producing sagging or sliding phenomenon, the slurry that when use is formed will not cause to precipitate, will not generate pigment and secrete after adding pigment
Out, organic copper salt can be good at preventing microorganism from causing the occurrence of mouldy, and electrodeless salt copper sulphate is at normal temperatures and pressures very
Stablize, do not deliquesce, good bactericidal effect can be played, the gap filler added with inorganic aluminate water-proof agent is hardened in gap filler
The capillary porosity formed in the process and aquaporin, the repellency with extremely strong hydrophobicity and moisture, to assign gap filler very
Strong waterproof performance, the fatty acid ester compounded object of silicone emulsion, higher alcohols or polypropylene glycerol aether keep gap filler surface tension low
In the surface tension of gas-liquid bubble, inhibits the generation of bubble or eliminate the bubble generated, after the completion of configuration, conveyed by conveying pipeline
In reactor tank into blender, stirring motor is opened, is uniformly mixed each ingredient by stirring rod, after mixing, discharging
Bag is packaged into up to product is gone out.
Benefit of the invention: in use it have cohesive force strong, antimildew and antibacterial, sterilizing environmental protection, it is anti-oxidant and not blistering,
Do not generate crack and fall off, bright-colored colorful, good water-proof effect, it is easy to use the features such as, it is coloration height, exquisite in texture, applicable
In the ceramic tile of most of type and the seam of stone material, the decorative effect of plane materiel can be enhanced, after water mixed construction, have certain
Flexibility, waterproofness and inoxidizability, the swell-shrinking deformation between plate can be prevented, to extend the service life of facing.
Claims (10)
1. a kind of antibacterial environment protection gap filler for building, it is characterised in that: its raw material includes following components by weight: silicate cement
25-30 parts of mud, 0.5-1 parts of high alumina cement, 55-70 parts of filler, 1-2 parts of antimildew and antibacterial agent, 1.5-3 parts of waterproofing agent, pigment 1-5
Part, 1-2 parts of lubricant, 0.5-2 parts of levelling agent, 1-2 parts of antioxidant.
2. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the filler is quartz
One kind of sand, calcium carbonate or dolomite dust.
3. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the antimildew and antibacterial agent is
The one or two of organic copper salt or electrodeless salt copper sulphate.
4. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the antioxidant is L-
The one or two of ascorbic acid or sulphite.
5. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the lubricant is silicic acid
Magnalium thixotropic lubricant.
6. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the levelling agent is poly- third
Olefin(e) acid or carboxymethyl cellulose it is one or more.
7. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the waterproofing agent is inorganic
Aluminate water-proof agent.
8. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the raw material is by weight
It further include 1-5 parts of defoaming agent.
9. a kind of antibacterial environment protection gap filler for building according to claim 7, it is characterised in that: the defoaming agent is emulsification
The fatty acid ester compounded object of silicone oil, higher alcohols or polypropylene glycerol aether it is one or more.
10. a kind of antibacterial environment protection gap filler for building according to claim 1, it is characterised in that: the pigment is oxidation
The one or two of titanium or iron oxide.