CN106747144A - A kind of single ply waterproofing decoration mortar - Google Patents
A kind of single ply waterproofing decoration mortar Download PDFInfo
- Publication number
- CN106747144A CN106747144A CN201710041176.5A CN201710041176A CN106747144A CN 106747144 A CN106747144 A CN 106747144A CN 201710041176 A CN201710041176 A CN 201710041176A CN 106747144 A CN106747144 A CN 106747144A
- Authority
- CN
- China
- Prior art keywords
- single ply
- ply waterproofing
- gypsum plaster
- complexing agent
- building gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of single ply waterproofing decoration mortar, it is made up of following raw material：Ordinary portland cement, double quick alumina cement, quartz sand and oozes brilliant coating complexing agent at building gypsum plaster, the ordinary portland cement, double quick alumina cement, quartz sand, building gypsum plaster and oozes brilliant coating complexing agent mass ratio and is：14~18:2~4:16~20:0.8~1.2:1~3.The single ply waterproofing decoration mortar is applied between building flooring, ground, cistern, underground structure, planted roof, kitchen lavatory and the rigidity of civil air defense constructions and installations, rail-road bridge, subway tunnel and hydraulic engineering is impervious（Self-healing）Waterproof, meets, back side.Using its thick bottom of rendering it is low the characteristics of can be preferably moulding to being carried out outside mortar, play decorative effect, possess high practical value.
Description
Technical field
The present invention relates to home health care field, specially a kind of far infrared heating cobblestone sole massage blanket.
Background technology
Mortar be it is architectural lay bricks use cohere material, by a certain proportion of sand and cementing material（Cement, lime
Cream, clay etc.）Add water into, be also mortar, also make mortar.Mortar is by Binder Materials（Cement, lime, clay etc.）With thin bone
Material（Sand）The mix that adds water is formed.Conventional has cement mortar, mixed mortar（Or it is cement-lime mortar）, lime mortar and clay
Mortar.
According to composition material, ordinary mortar can also be divided into:1. lime mortar.Made according to a certain ratio by lime paste, Sha Heshui
Into, be generally used for intensity requirement it is not high, by moist masonry and coat of plaster；2. cement mortar.By cement, sand and water by certain
Proportioning is made, and is generally used for masonry in wet environment or water, metope or ground etc.；3. mixed mortar.In cement or lime sand
Appropriate admixture such as flyash, diatomite etc. is filled in slurry to be made, to save cement or lime consumption, and improve mortar and it is easy
Property.Conventional mixed mortar has cement-lime mortar, cement clay mortar and lime clay mortar etc..
Waterproof mortar is called cationic chloroprene latex water-proof and anti-corrosive material.Cationic chloroprene latex is a kind of high polymer point
The modified based high molecular water-tight corrosion-proof system of son.By being introduced into mouthful epoxy resin modified latex acceding state neoprene latex and poly-
The high polymer latex that acrylate, synthetic rubber, various emulsifying agents, modified latex etc. are constituted.Add base-material and appropriate chemistry
Auxiliary agent and inserts, through plasticating, knead, the macromolecule water-proof and anti-corrosive material that the operation such as calendering is added.From imported material
With domestic high-quality auxiliary material, according to the quality product of national sector standard highest ranking written instructions production, national Research of Comfortable House is pushed away
Recommend product.Long lifespan, easy construction, long period of soaking in water the life-span more than 50 years.Existing waterproof mortar is in work progress
In generally occur that waterproof mortar elongation parameter reaches, the problem that tensile strength is not reached, meanwhile, water sand slurry construction after also
The phenomenon for often shrinking.
The content of the invention
It is applied to building flooring, ground, cistern, underground structure, plantation it is an object of the invention to provide one kind
Between roofing, kitchen lavatory and civil air defense constructions and installations, rail-road bridge, subway tunnel and hydraulic engineering rigidity it is impervious（Self-healing）Waterproof, meet,
Back side can new waterproof mortar, to solve the problems, such as to propose in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme：A kind of single ply waterproofing decoration mortar, by following raw material
Composition：Ordinary portland cement, double quick alumina cement, quartz sand and oozes brilliant coating complexing agent at building gypsum plaster, and the ordinary portland cement is double
Fast alumina cement, quartz sand and oozes brilliant coating complexing agent mass ratio and is building gypsum plaster：14~18:2~4:16~20:0.8~1.2:
1~3。
Preferably, it is made up of following raw material：Ordinary portland cement, double quick alumina cement, quartz sand and oozes brilliant painting at building gypsum plaster
Material complexing agent, the ordinary portland cement, double quick alumina cement, quartz sand and oozes brilliant coating complexing agent mass ratio and is building gypsum plaster：
16：3：18：1：2.
Preferably, quartz sand is crushed by the small blocks of the broken 20-40mm of raw material quartz mine, obtains particle diameter 70-100 purposes
Quartz sand.
Preferably, building gypsum plaster after 3~18min of ardealite grinding by obtaining after the particle that particle diameter is 35~55 μm in temperature
2~8h is calcined in the environment of 100~230 DEG C of degree and obtains the building gypsum plaster that particle diameter is 15~35 μm.
Preferably, brilliant coating complexing agent is oozed for mass ratio is 50：15：5：5：5：1：1：1：5 high activity silica, it is living
Change modenite, anhydrous sodium sulfate, sodium metaaluminate, magnesium hydroxide, high-efficiency water-reducing agent of poly-carboxylic acid, redispersable latex powder, hydroxypropyl
Ylmethyl cellulose ether and inorganic gel.
Preferably, the smearing thickness of single ply waterproofing decoration mortar is 1.0mm, and the ratio of adding water of single ply waterproofing decoration mortar is
1：0.25~0.3.
Compared with prior art, the beneficial effects of the invention are as follows：The single ply waterproofing decoration mortar be applied to building flooring,
Between ground, cistern, underground structure, planted roof, kitchen lavatory and civil air defense constructions and installations, rail-road bridge, subway tunnel and water conservancy work
The rigidity of journey is impervious（Self-healing）Waterproof, meets, back side.Using its thick bottom of rendering it is low the characteristics of can be to being carried out outside mortar
It is preferably moulding, decorative effect is played, possess high practical value.
Specific embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model of present invention protection
Enclose.
Embodiment 1
The present invention provides a kind of technical scheme：A kind of single ply waterproofing decoration mortar, is made up of following raw material：Ordinary portland cement, double quick
Alumina cement, quartz sand and oozes brilliant coating complexing agent at building gypsum plaster, the ordinary portland cement, double quick alumina cement, quartz sand,
Building gypsum plaster and ooze brilliant coating complexing agent mass ratio and be：14~18:2~4:16~20:0.8~1.2:1~3.
Quartz sand therein is crushed by the small blocks of the broken 20-40mm of raw material quartz mine, obtains the stone of particle diameter 70-100 mesh
Sand.Building gypsum plaster by obtained after 3~18min of ardealite grinding after the particle that particle diameter is 35~55 μm temperature 100~
2~8h is calcined in the environment of 230 DEG C and obtains the building gypsum plaster that particle diameter is 15~35 μm.Brilliant coating complexing agent is oozed for mass ratio is
50：15：5：5：5：1：1：1：5 high activity silica, activates modenite, anhydrous sodium sulfate, sodium metaaluminate, hydroxide
Magnesium, high-efficiency water-reducing agent of poly-carboxylic acid, redispersable latex powder, hydroxypropyl methyl cellulose ether and inorganic gel.Single ply waterproofing is decorated
The smearing thickness of mortar is 1.0mm, and the ratio that adds water of single ply waterproofing decoration mortar is 1：0.25~0.3.
The single ply waterproofing decoration mortar is applied to building flooring, ground, cistern, underground structure, planted roof, kitchen
Between lavatory and civil air defense constructions and installations, rail-road bridge, subway tunnel and hydraulic engineering rigidity it is impervious（Self-healing）Waterproof, meets, back side
.
Embodiment 2
On the basis of embodiment 1, a kind of single ply waterproofing decoration mortar is made up of following raw material：Ordinary portland cement, double quick high alumina water
Mud, quartz sand and oozes brilliant coating complexing agent, the ordinary portland cement, double quick alumina cement, quartz sand, paring stone at building gypsum plaster
Cream powder and ooze brilliant coating complexing agent mass ratio and be：16：3：18：1：2.
Quartz sand therein is crushed by the small blocks of the broken 25-35mm of raw material quartz mine, obtains the stone of particle diameter 80-90 mesh
Sand.Building gypsum plaster after ardealite grinding 10min by obtaining after the particle that particle diameter is 40~50 μm in 150~200 DEG C of temperature
In the environment of calcine 4~6h obtain the building gypsum plaster that particle diameter is 20~30 μm.
And brilliant coating complexing agent is oozed for mass ratio is 50：15：5：5：5：1：1：1：5 high activity silica, activation
Modenite, anhydrous sodium sulfate, sodium metaaluminate, magnesium hydroxide, high-efficiency water-reducing agent of poly-carboxylic acid, redispersable latex powder, hydroxypropyl
Methyl cellulose ether and inorganic gel.The smearing thickness of single ply waterproofing decoration mortar be 1.0mm, single ply waterproofing decoration mortar plus
Water ratio is 1：0.28.Further reduction paints thickness, using the thick bottom of its rendering it is low the characteristics of can be to being carried out more outside mortar
Good is moulding, plays decorative effect, possesses high practical value.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding can carry out various changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (6)
1. a kind of single ply waterproofing decoration mortar, it is characterised in that：It is made up of following raw material：Ordinary portland cement, double quick alumina cement, stone
Sand, building gypsum plaster and oozes brilliant coating complexing agent, the ordinary portland cement, double quick alumina cement, quartz sand, building gypsum plaster and
Oozing brilliant coating complexing agent mass ratio is：14~18:2~4:16~20:0.8~1.2:1~3.
2. a kind of single ply waterproofing decoration mortar according to claim 1, it is characterised in that：It is made up of following raw material：General silicon
Cement, double quick alumina cement, quartz sand and oozes brilliant coating complexing agent at building gypsum plaster, the ordinary portland cement, double quick high alumina water
Mud, quartz sand and oozes brilliant coating complexing agent mass ratio and is building gypsum plaster：16：3：18：1：2.
3. a kind of single ply waterproofing decoration mortar according to claim 1 and 2, it is characterised in that：The quartz sand is by raw material
The small blocks of the broken 20-40mm of quartz mine, crush, and obtain the quartz sand of particle diameter 70-100 mesh.
4. a kind of single ply waterproofing decoration mortar according to claim 1 and 2, it is characterised in that：The building gypsum plaster by
Obtain calcining 2 in the environment of 100~230 DEG C of temperature after the particle that particle diameter is 35~55 μm after 3~18min of ardealite grinding
~8h obtains the building gypsum plaster that particle diameter is 15~35 μm.
5. a kind of single ply waterproofing decoration mortar according to claim 1 and 2, it is characterised in that：It is described to ooze brilliant coating complexing
Agent is that mass ratio is 50：15：5：5：5：1：1：1：5 high activity silica, activates modenite, anhydrous sodium sulfate, inclined aluminium
Sour sodium, magnesium hydroxide, high-efficiency water-reducing agent of poly-carboxylic acid, redispersable latex powder, hydroxypropyl methyl cellulose ether and inorganic gel.
6. a kind of single ply waterproofing decoration mortar according to claim 1 and 2, it is characterised in that：The single ply waterproofing decoration
The smearing thickness of mortar is 1.0mm, and the ratio that adds water of single ply waterproofing decoration mortar is 1：0.25~0.3.