CN109572299A - A kind of process recipes of New model production sandstone sculpture - Google Patents
A kind of process recipes of New model production sandstone sculpture Download PDFInfo
- Publication number
- CN109572299A CN109572299A CN201811641012.7A CN201811641012A CN109572299A CN 109572299 A CN109572299 A CN 109572299A CN 201811641012 A CN201811641012 A CN 201811641012A CN 109572299 A CN109572299 A CN 109572299A
- Authority
- CN
- China
- Prior art keywords
- parts
- gypsum
- sculpture
- fiber filament
- sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of process recipes of New model production sandstone sculpture, the mixture includes the raw material of following parts by weight: 6-10 parts of resin, 35-50 parts of quartz sand, 60-80 parts of fiber filament, 70-90 parts of flax silk, 150-250 parts of cement, 30-50 parts of catalyst, 20-50 parts of curing agent, surplus is color essence.The process recipes of its sandstone sculpture are the following steps are included: S1, sculpture mud mould: gypsum and water are modulated into the state of congee；S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, it is all cut with scissors to 1-2mm length, gypsum and water reconcile uniform, it is put into 1-2mm flax silk and fiber filament, a small amount of mountain flour is added to reconcile uniformly, starts to enclose on the surface of mud mould to modulate gypsum, it is ensured that mud film is completely covered in gypsum.The sculpture that the present invention produces is not indeformable easily broken, increases service life of the products, improves production efficiency, reduces cost.
Description
Technical field
The invention belongs to fiber preparation process technical field more particularly to a kind of techniques of New model production sandstone sculpture
Preparation method.
Background technique
Traditional sandstone sculpture mold can only produce a product every time, cannot replicated product repeatedly, product cannot batch
Production, sandstone product surface have de- husky phenomenon, and sandstone excessively relies on natural colored, and texture excessively relies on natural mineral resources, makes
It is single at color, it is larger to manufacture cost input, and finished product is heavier, increases transport and installation cost, such as bending strength, product
It when comparing book, easily snaps off, it may appear that ultraviolet light effect is poor, and the time has grown product and has been easy discoloration, and the production cycle is long, raw
The defects of production low efficiency, needs 24 hours or so that depanning could be completed, and sandrock effect is unobvious, and the service life of product is short.
Summary of the invention
The present invention in view of the above technical problems, provides a kind of process recipes of New model production sandstone sculpture.
The technical scheme adopted by the invention is as follows: a kind of process recipes of New model production sandstone sculpture, the mixing
Material includes the raw material of following parts by weight:
6-10 parts of resin, 35-50 parts of quartz sand, 60-80 parts of fiber filament, 70-90 parts of flax silk, 150-250 parts of cement, catalyst
30-50 parts, 20-50 parts of curing agent, surplus is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 1-2mm length, gypsum and water are reconciled uniformly, are put into 1-2mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts
It is enclosed on the surface of mud mould and modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely,
Gypsum surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1-2 hour, is collapsible die after gypsum sets, mold, which turns over, have been made
At；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, according to required presentation
Color, addition color accurate adjustment system is uniform, reconciles uniformly white cement is added；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 2% and modulates uniformly, add curing agent
3.5% modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, spreading one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing to 1-2 hour, solidify product, and then with demoulding knob is pulled, slightly firmly product is just deviate from
Mold, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
Preferably, the sculpture is made of mixture, and the mixture includes the raw material of following parts by weight:
7-9 parts of resin, 44-46 parts of quartz sand, 69-71 parts of fiber filament, 84-86 parts of flax silk, 199-201 parts of cement, catalyst 44-
46 parts, 34-36 parts of curing agent, surplus is color essence.
Preferably, the sculpture is made of mixture, and the mixture includes the raw material of following parts by weight:
It is 8 parts of resin, 45 parts of quartz sand, 70 parts of fiber filament, 85 parts of flax silk, 20 parts of cement, 45 parts of catalyst, 35 parts of curing agent, remaining
Amount is color essence.
Preferably, in the step S1, flax silk and fiber filament are all cut with scissors to 2mm length.
Preferably, it in the step S8, waits to 1.5 hours, solidifies product.
Preferably, in the step S1, the ratio of gypsum and water is 1:10.
The invention has the benefit that
1, this invention die sinking, which uses flax silk, fiber filament, fiber cloth, mountain flour, ties mold more with different production methods
It is real secured, duplication production product can be recycled, while saving material and turning over mold opening cost processed, mold is not hard durable fragile
Damage, it is indeformable, it can be persistently stored, production cost greatly reduces for producer, also functions to the effect of protection environment；
2, present invention employs the materials such as resin, flax silk, fiber filament, white cement, color essence.Resin adds flax silk and fiber filament, plays
Pulling force effect keeps product not easy to crack, and white cement carries the solidification degree of finished product, keeps product more solid hard, solves system
The noncondensing disadvantage of product long-time during work.Color accurate adjustment is added and produces required color, decolourizes supplemented with conventional sandstone
The problem of, color essence and resin quartz sand hybrid modulation, the long-time that can guarantee the quality will not fade；
3, the present invention joined stainless steel cloth (325 mesh silks: 0.035mm, hole: 0.045mm) in sandstone production, rise to product
Integrity degree has been arrived, it is indeformable, it is not easily broken, the time limit that product uses is increased, production efficiency is improved, reduces production cost,
The effect more close to natural sandstone is increased, the more abundant beauty of sculpture effect is made.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment 1
A kind of process recipes of New model production sandstone sculpture, sculpture are made of mixture, and mixture includes following parts by weight
Raw material:
It is 6 parts of resin, 35 parts of quartz sand, 60 parts of fiber filament, 70 parts of flax silk, 150 parts of cement, 30 parts of catalyst, 20 parts of curing agent, remaining
Amount is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 2mm length, gypsum and water are reconciled uniformly, are put into 2mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts in mud
The surface of mould, which is enclosed, modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely, in gypsum
Surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1.5 hours, is collapsible die after gypsum sets, and mold turns over system and completes；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, according to required presentation
Color, addition color accurate adjustment system is uniform, reconciles uniformly white cement is added；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 1% and modulates uniformly, add curing agent 2%
Modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, spreading one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing to 4 hours, solidify product, and then with demoulding knob is pulled, slightly firmly product just deviates from mould
Tool, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
Embodiment 2
A kind of process recipes of New model production sandstone sculpture, sculpture are made of mixture, and mixture includes following parts by weight
Raw material:
It is 7 parts of resin, 44 parts of quartz sand, 69 parts of fiber filament, 84 parts of flax silk, 199 parts of cement, 44 parts of catalyst, 34 parts of curing agent, remaining
Amount is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 1.5mm length, gypsum and water are reconciled uniformly, are put into 1.5mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts
It is enclosed on the surface of mud mould and modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely,
Gypsum surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1.3 hours, is collapsible die after gypsum sets, mold, which turns over, have been made
At；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, according to required presentation
Color, addition color accurate adjustment system is uniform, reconciles uniformly white cement is added；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 1.5% and modulates uniformly, add curing agent
2.5% modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, spreading one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing to 3.5 hours, solidify product, and then with demoulding knob is pulled, slightly firmly product is just deviate from
Mold, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
Embodiment 3
A kind of process recipes of New model production sandstone sculpture, sculpture are made of mixture, and mixture includes following parts by weight
Raw material:
It is 8 parts of resin, 45 parts of quartz sand, 70 parts of fiber filament, 85 parts of flax silk, 20 parts of cement, 45 parts of catalyst, 35 parts of curing agent, remaining
Amount is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 2mm length, gypsum and water are reconciled uniformly, are put into 2mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts in mud
The surface of mould, which is enclosed, modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely, in gypsum
Surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1.5 hours, is collapsible die after gypsum sets, and mold turns over system and completes；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, according to required presentation
Color, addition color accurate adjustment system is uniform, reconciles uniformly white cement is added；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 2% and modulates uniformly, add curing agent
3.5% modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, spreading one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing to 4 hours, solidify product, and then with demoulding knob is pulled, slightly firmly product just deviates from mould
Tool, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
Embodiment 4
A kind of process recipes of New model production sandstone sculpture, sculpture are made of mixture, and mixture includes following parts by weight
Raw material:
It is 9 parts of resin, 46 parts of quartz sand, 71 parts of fiber filament, 86 parts of flax silk, 201 parts of cement, 46 parts of catalyst, 36 parts of curing agent, remaining
Amount is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 1.5mm length, gypsum and water are reconciled uniformly, are put into 1.5mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts
It is enclosed on the surface of mud mould and modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely,
Gypsum surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1.2 hours, is collapsible die after gypsum sets, mold, which turns over, have been made
At；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, according to required presentation
Color, addition color accurate adjustment system is uniform, reconciles uniformly white cement is added；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 2.5% and modulates uniformly, add curing agent
3.5% modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, spreading one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing to 3.6 hours, solidify product, and then with demoulding knob is pulled, slightly firmly product is just deviate from
Mold, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
Embodiment 5
A kind of process recipes of New model production sandstone sculpture, sculpture are made of mixture, and mixture includes following parts by weight
Raw material:
10 parts of resin, 50 parts of quartz sand, 80 parts of fiber filament, 90 parts of flax silk, 250 parts of cement, 50 parts of catalyst, 50 parts of curing agent,
Surplus is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 1.8mm length, gypsum and water are reconciled uniformly, are put into 1.8mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts
It is enclosed on the surface of mud mould and modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely,
Gypsum surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1.9 hours, is collapsible die after gypsum sets, mold, which turns over, have been made
At；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, according to required presentation
Color, addition color accurate adjustment system is uniform, reconciles uniformly white cement is added；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 3% and modulates uniformly, add curing agent 5%
Modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, spreading one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing to 4 hours, solidify product, and then with demoulding knob is pulled, slightly firmly product just deviates from mould
Tool, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
This invention die sinking, which uses flax silk, fiber filament, fiber cloth, mountain flour, makes mold more with different production methods
Solid securely to recycle duplication production product, while saving material and turning over mold opening cost processed, mold is hard durable to be not easy
Breakage, it is indeformable, it can be persistently stored, production cost greatly reduces for producer, also functions to the effect of protection environment.The present invention
Using materials such as resin, flax silk, fiber filament, white cement, color essences.Resin adds flax silk and fiber filament, plays pulling force effect, makes to produce
Product are not easy to crack, and white cement carries the solidification degree of finished product, keep product more solid hard, it is long to solve product in manufacturing process
Time noncondensing disadvantage.The problem of color accurate adjustment produces required color, decolourizes supplemented with conventional sandstone, color essence and tree is added
Rouge quartz sand hybrid modulation, can guarantee the quality will not fade for a long time.The present invention joined stainless steel cloth (325 in sandstone production
Mesh silk: 0.035mm, hole: 0.045mm), integrity degree is played to product, it is indeformable, it is not easily broken, increase the year that product uses
Limit, improves production efficiency, reduces production cost, increase the effect more close to natural sandstone, make sculpture effect more
Abundant beauty.
5 embodiments of the invention are described in detail above, but the content is only preferable implementation of the invention
Example, should not be considered as limiting the scope of the invention.It is all according to all the changes and improvements made by the present patent application range
Deng should still be within the scope of the patent of the present invention.
Claims (6)
1. a kind of process recipes of New model production sandstone sculpture, which is characterized in that the sculpture is made of mixture, described
Mixture includes the raw material of following parts by weight:
6-10 parts of resin, 35-50 parts of quartz sand, 60-80 parts of fiber filament, 70-90 parts of flax silk, 150-250 parts of cement, catalyst
30-50 parts, 20-50 parts of curing agent, surplus is color essence.
The process recipes of its sandstone sculpture the following steps are included:
S1, sculpture mud mould: gypsum and water are modulated into the state of congee；
S2, counter mold: S1 is prepared into pure calcium plaster and is uniformly sprayed on mud mould surface, flax silk and fiber filament, is all cut with scissors
To 1-2mm length, gypsum and water are reconciled uniformly, are put into 1-2mm flax silk and fiber filament, and a small amount of mountain flour is added and reconciles uniformly, starts
It is enclosed on the surface of mud mould and modulates gypsum, it is ensured that mud film is completely covered in gypsum, in the case where gypsum does not parch completely,
Gypsum surface layer spreads one layer of fiber filament, brushes one layer of calcium plaster, waits 1-2 hour, is collapsible die after gypsum sets, mold, which turns over, have been made
At；
S3, cleaning mold: mold prepared by S2 washes with water completely, paints demoulding wax oil；
S4, modulation sandstone material: resin, quartz sand, flax silk and fiber filament are modulated uniformly, further according to required presentation
Color, addition color accurate adjustment system is uniform, adds white cement and reconciles uniformly；
S5, casting sandstone: it according to the material for needing to pour into mold every time, adds catalyst 1%-3% modulation uniformly, adds curing agent
2%-5% modulation uniformly, first pours into a part in mold less, levelling with scraper plate；
S6, it is put into steel wire: pouring layer overlay stainless (steel) wire in the mold after sandstone, repaving one layer of quartz mortar；
It is S7, levelling: to levelling by the die surface of step S6, press with hand and pat solid, rearward shaken hands plus demoulding；
S8, demoulding: standing 1-2 hour, solidify product, and then with demoulding knob is pulled, slightly firmly product just deviates from mould
Tool, product just successfully complete by counter；
S9, product cleaning: it is cleaned by surface of the clear water to product；
S10, installation: scene splicing is repaired: the single product after cleaning being transported to scene, single product is spliced one
It rises.
2. a kind of process recipes of New model production sandstone sculpture according to claim 1, which is characterized in that the carving
Modeling is made of mixture, and the mixture includes the raw material of following parts by weight:
7-9 parts of resin, 44-46 parts of quartz sand, 69-71 parts of fiber filament, 84-86 parts of flax silk, 199-201 parts of cement, catalyst 44-
46 parts, 34-36 parts of curing agent, surplus is color essence.
3. a kind of process recipes of New model production sandstone sculpture according to claim 1, which is characterized in that the carving
Modeling is made of mixture, and the mixture includes the raw material of following parts by weight:
It is 8 parts of resin, 45 parts of quartz sand, 70 parts of fiber filament, 85 parts of flax silk, 20 parts of cement, 45 parts of catalyst, 35 parts of curing agent, remaining
Amount is color essence.
4. a kind of process recipes of New model production sandstone sculpture according to claim 1, which is characterized in that the step
In rapid S2, flax silk and fiber filament are all cut with scissors to 2mm length.
5. a kind of process recipes of New model production sandstone sculpture according to claim 1, which is characterized in that the step
In rapid S8, waits to 1.5 hours, solidify product.
6. a kind of process recipes of New model production sandstone sculpture according to claim 1, which is characterized in that the step
In rapid S1, the ratio of gypsum and water is 1:10.