CN109537400A - A kind of reflective type chinampa playing mark action - Google Patents
A kind of reflective type chinampa playing mark action Download PDFInfo
- Publication number
- CN109537400A CN109537400A CN201811439261.8A CN201811439261A CN109537400A CN 109537400 A CN109537400 A CN 109537400A CN 201811439261 A CN201811439261 A CN 201811439261A CN 109537400 A CN109537400 A CN 109537400A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- base cloth
- reflective
- artificial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the reflective type chinampas that one kind can play mark action, including plastic feet and artificial turf, artificial turf include base cloth, artificial grass filaments and adhesive layer；Artificial grass filaments include following components: basic resin, Masterbatch, reflective masterbatch, coupling agent, auxiliary agent, luminescent powder TYY-4E, dispersing agent, negative ion powder, filler；Adhesive layer is formed by adhesive brushing in base cloth bottom end, and adhesive includes following components: EVA resin, phenolic resin, phthalic anhydride, polytetrahydrofuran, chain extender, isocyanates, Nano carbon white N20, defoaming agent, curing agent, emulsifier, is denaturalized dressing agent；There is chinampa of the present invention good reflective can play marked effect, and the lawn has good heat-resisting, corrosion-resistant, ageing-resistant performance, and long service life, it is convenient to be easy to use.
Description
Technical field
The present invention relates to a kind of lawns, and in particular to one kind can play the reflective type chinampa of mark action, belong to artificial
Lawn technical field.
Background technique
In recent years, with chinampa technology develop, chinampa stability, lawn maintenance, resistance to sliding and
Appearance luster etc. is significantly improved, and increasingly close to natural lawn, thus is applied to movement more and more, stops
The fields such as not busy, decoration.
Due to the extensive use of chinampa, for the chinampa technical research with various correlation functions such as fire
If carrying out for the bitter edible plant is during turf production by the way that matt material is added to original such as with the chinampa of matt
Material, which is modified the surface for being allowed to smooth, has the effect of diffusing reflection to reach not dazzling；It is logical such as low-temperature artificial lawn
It crosses to be added in raw material and there is the filler of infrared external reflection function to achieve the purpose that reduce lawn temperature；Antistatic artificial lawn
It is to spray antistatic solution on chinampa surface to reach antistatic effect；But there are no a nights on the market at present
Car bulb can be reflected, the chinampa of marked effect is played, it is therefore desirable to develop one kind for roadside, this is conducive to
Safeguard that the reflective type chinampa of night traffic safety becomes those skilled in the art's technical problem urgently to be resolved.
Summary of the invention
The technical problem to be solved by the present invention is to the shortcomings that overcoming the prior art, the reflective of mark action can be played by providing
Type chinampa, which there is good reflective can play marked effect, and the lawn is with good heat-resisting, resistance to
Burn into ageing-resistant performance, long service life, it is convenient to be easy to use.
In order to solve the above technical problems, the present invention provides a kind of reflective type chinampa that can play mark action, including
Plastic feet and the artificial turf being contained in plastic feet, artificial turf include that base cloth, tufting are artificial on base cloth
Careless silk and the adhesive layer for being set to base cloth bottom end；
Artificial grass filaments are to be reversed into double-stranded strip grass silk, and several circular holes, each circular hole are evenly equipped on base cloth
Two semicircle orifices are separated by being placed in the fixed strip among circular hole, artificial grass filaments pass through two semicircle orifices and are placed on base cloth,
Wherein:
Artificial grass filaments include following components according to the mass fraction:
Basic resin: 60-95 parts, Masterbatch: 1-5 parts, reflective masterbatch: 4-10 parts, coupling agent: 1-5 parts, auxiliary agent: 0.2-
4.8 parts, TYY-4E:5-7 parts of luminescent powder, dispersing agent: 1-5 parts, negative ion powder: 1-5 parts, filler: 1-5 parts；
Basic resin is the mixture of vinylite and plexiglass；Reflective masterbatch is that glass is micro-
Pearl；Coupling agent is silane coupling agent；Auxiliary agent includes the mixture of antioxidant 1010, light stabilizer 770, spin finish aid；Dispersing agent
For the mixture of polypropylene wax and oxidized polyethylene wax；Filler is powdered whiting or talcum powder；
Adhesive layer is formed by adhesive brushing in base cloth bottom end, and adhesive includes following components according to the mass fraction:
EVA resin: 5-20 parts, phenolic resin: 15-35 parts, phthalic anhydride: 5-15 parts, polytetrahydrofuran: 5-15
Part, chain extender: 2-5 parts, isocyanates: 6-12 parts, N20:2-4 parts of Nano carbon white, defoaming agent: 3-6 parts, curing agent: 10-14
Part, emulsifier: 4-7 parts, denaturation dressing agent: 1-3 parts；
EVA resin is the copolymer of ethylene Yu comonomer vinyl acetate, wherein the weight percent of monomer vinyl acetate
Content is 38%, and the mass percent of ethylene is 62%；Chain extender is 1,4- butanediol；Defoaming agent is melamine；Curing agent
For one of m-phenylene diamine (MPD), diethylenetriamine, polyamide；Emulsifier is dodecyl sodium sulfate；Denaturation dressing agent is hydrogen-oxygen
Change one of sodium, disodium hydrogen phosphate or the chloro- 2- propyl alcohol of 1,3- bis-.
The technical solution that the present invention further limits are as follows:
In aforementioned reflective type chinampa, plastic feet includes pedestal holding tank and edge, and edge is from pedestal holding tank
Top surrounding extends internally, and the side of pedestal holding tank is equipped with stay hook, and the pedestal holding tank other side is equipped with fixed ring, bottom
The bottom of seat holding tank is equipped with several drainage holes.
In aforementioned reflective type chinampa, base cloth is overlapped by polypropylene woven cloth, non-woven fabrics and Gauze from top to down
It forms.
In aforementioned reflective type chinampa, adhesive the preparation method is as follows:
O-phthalic is added in the four-hole boiling flask equipped with electric mixing device, heating device, thermometer and vacuum inlet
Acid anhydrides and polytetrahydrofuran are heated to 100-110 degrees Celsius, and chain extender is then added and quickly stirs, stirs 10-20min
After isocyanates is added, continue to stir, EVA resin and phenolic resin be then added and stirs evenly, it is white that nanometer is added while stirring
Carbon black N20, defoaming agent, curing agent, emulsifier, denaturation dressing agent, obtain adhesive after mixing evenly.
In aforementioned reflective type chinampa, reflective type chinampa the preparation method is as follows:
Step (1) prepares artificial grass filaments:
Basic resin, reflective masterbatch, coupling agent are blended to granulation on the twin screw extruder and are prepared into reflective master batch, is squeezed out
Temperature is 150-250 degrees Celsius, then send into stirred tank reflective master batch, Masterbatch, auxiliary agent and filler and uniformly stirring is blended
Speed is 100-150r/min, and luminescent powder TYY-4E, dispersing agent, negative ion powder, coupling agent is then added into stirred tank again, after
Continuous stirring, mixing speed 200-300r/min is squeezed out after stirring evenly, wire drawing is prepared into careless silk semi-finished product, extrusion molding
Temperature is controlled at 150-300 degrees Celsius, is reversed two-by-two in every careless silk semi-finished product and is bonded into double-stranded strip grass silk and obtains
To finished product grass silk, multiple finished synthetic's grass silks are flocked together, and it is stand-by to form cluster artificial grass filaments；
The artificial grass filaments that step (2) prepares are worn in the air from a semicircle of base cloth to another semicircle orifice, are then existed
Tufting has the base cloth bottom coating gluing dosage form of artificial grass filaments artificial grass filaments are fixed on base cloth at adhesive layer to be formed
Artificial turf is placed in plastic feet by artificial turf, and is fixed for use by the edge on plastic feet；
Each plastic feet for accommodating artificial turf is passed through the fixed hook and fixed ring of plastic feet two sides by step (3)
It connects to form chinampa.
The beneficial effects of the present invention are:
Phthalic anhydride is used in the present invention for the polyalcohol of acid, instead of adipic acid, the properties of product of synthesis
It is excellent, polyurethane elastomer is made using polyalcohol, chain extender, isocyanates, with preferable weatherability, adhesive strength
Height, elasticity is good, with the excellent adhesive of forming properties, extends the service life of chinampa.
The reflective type chinampa of the present invention has good reflection function, can reflect car bulb, play marked effect,
Be conducive to safeguard night traffic safety.
Artificial grass filaments in the present invention are interspersed on base cloth by two semicircle orifices, installation, convenient disassembly, convenient for solid
It is fixed, each artificial turf is connected using plastic feet, dismantles easy for installation, reduction labor intensity.
There is reflective type chinampa of the invention good reflective can play marked effect, and the lawn has well
Heat-resisting, corrosion-resistant, ageing-resistant performance, long service life, it is convenient to be easy to use, and preparation process is simple, without in addition
Equipment is purchased, can be completed using existing equipment.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution of the present invention is clearly and completely described, it is clear that
Described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Embodiment 1
One kind provided in this embodiment can play the reflective type chinampa of mark action, including plastic feet and be contained in modeling
Expect that the artificial turf in pedestal, artificial turf include that base cloth, tufting artificial grass filaments and are set to base cloth bottom on base cloth
The adhesive layer at end；
Base cloth is formed by stacking by polypropylene woven cloth, non-woven fabrics and Gauze from top to down, and artificial grass filaments are to be reversed into
Double-stranded strip grass silk, is evenly equipped with several circular holes on base cloth, and each circular hole is by the fixed strip point that is placed among circular hole
Two semicircle orifices are divided into, artificial grass filaments pass through two semicircle orifices and are placed on base cloth；
Plastic feet includes pedestal holding tank and edge, and edge extends internally from the top surrounding of pedestal holding tank,
The side of pedestal holding tank is equipped with stay hook, and the pedestal holding tank other side is equipped with fixed ring, and the bottom of pedestal holding tank is equipped with number
A drainage hole, in which:
Artificial grass filaments include following components according to the mass fraction:
Basic resin: 70 parts, reflective masterbatch glass microballoon: 5 parts, auxiliary agent: 0.2 part, TYY-4E:5 parts of luminescent powder, dispersion
Agent: 2 parts, negative ion powder: 1 part, filler: 1 part；
Basic resin is the mixture of vinylite and plexiglass；Auxiliary agent includes antioxidant
1010, the mixture of light stabilizer 770, spin finish aid；Dispersing agent is the mixture of polypropylene wax and oxidized polyethylene wax；Filler
For powdered whiting；
Adhesive layer is formed by adhesive brushing in base cloth bottom end, and adhesive includes following components according to the mass fraction:
EVA resin: 10 parts, phenolic resin: 15 parts, phthalic anhydride: 8 parts, polytetrahydrofuran: 5 parts, thickener: 1
Part, chain extender: 2 parts, isocyanates: 6 parts, B2500:1 parts of anti-aging agent, N20:2 parts of Nano carbon white, defoaming agent: 3 parts, solidification
Agent: 10 parts, emulsifier: 4 parts, preservative: 2 parts, denaturation dressing agent: 3 parts, fire retardant: 1 part；
EVA resin is the copolymer of ethylene Yu comonomer vinyl acetate, wherein the weight percent of monomer vinyl acetate
Content is 38%, and the mass percent of ethylene is 62%；Thickener is hydroxymethyl cellulose；Chain extender is 1,4- butanediol；Disappear
Infusion is melamine；Curing agent is m-phenylene diamine (MPD)；Emulsifier is dodecyl sodium sulfate；Preservative is formic acid；Denaturation modification
Agent is sodium hydroxide；Fire retardant is phosphotriester.
Adhesive the preparation method is as follows:
O-phthalic is added in the four-hole boiling flask equipped with electric mixing device, heating device, thermometer and vacuum inlet
Acid anhydrides and polytetrahydrofuran are heated to 100 degrees Celsius, and chain extender is then added and quickly stirs, and are added after stirring 10min different
Cyanate continues to stir, and EVA resin then is added and phenolic resin stirs evenly, and thickener, anti-aging agent are added while stirring
B2500, Nano carbon white N20, defoaming agent, curing agent, emulsifier, preservative, denaturation dressing agent, fire retardant, after mixing evenly
Obtain adhesive.
Reflective type chinampa the preparation method is as follows:
Step (1) prepares artificial grass filaments:
Basic resin, reflective masterbatch, coupling agent are blended to granulation on the twin screw extruder and are prepared into reflective master batch, is squeezed out
Temperature is 150 degrees Celsius, then send into stirred tank reflective master batch, auxiliary agent and filler and is blended uniformly, mixing speed 100r/
Then min is added luminescent powder TYY-4E, dispersing agent, negative ion powder into stirred tank again, continues to stir, mixing speed 200r/
Min, is prepared into careless silk semi-finished product through extrusion, wire drawing after stirring evenly, and extrusion molding temperature is controlled at 150 degrees Celsius, at every
Careless silk semi-finished product reverse two-by-two to be bonded into double-stranded strip grass silk and obtains finished product grass silk, and multiple finished synthetic's grass silks are gathered
Gathering together, it is stand-by to form cluster artificial grass filaments；
The artificial grass filaments that step (2) prepares are worn in the air from a semicircle of base cloth to another semicircle orifice, are then existed
Tufting has the base cloth bottom coating gluing dosage form of artificial grass filaments artificial grass filaments are fixed on base cloth at adhesive layer to be formed
Artificial turf is placed in plastic feet by artificial turf, and is fixed for use by the edge on plastic feet；
Each plastic feet for accommodating artificial turf is passed through the fixed hook and fixed ring of plastic feet two sides by step (3)
It connects to form chinampa.
Embodiment 2
One kind provided in this embodiment can play the reflective type chinampa of mark action, including plastic feet and be contained in modeling
Expect that the artificial turf in pedestal, artificial turf include that base cloth, tufting artificial grass filaments and are set to base cloth bottom on base cloth
The adhesive layer at end；
Base cloth is formed by stacking by polypropylene woven cloth, non-woven fabrics and Gauze from top to down, and artificial grass filaments are to be reversed into
Double-stranded strip grass silk, is evenly equipped with several circular holes on base cloth, and each circular hole is by the fixed strip point that is placed among circular hole
Two semicircle orifices are divided into, artificial grass filaments pass through two semicircle orifices and are placed on base cloth；
Plastic feet includes pedestal holding tank and edge, and edge extends internally from the top surrounding of pedestal holding tank,
The side of pedestal holding tank is equipped with stay hook, and the pedestal holding tank other side is equipped with fixed ring, and the bottom of pedestal holding tank is equipped with number
A drainage hole, in which:
Artificial grass filaments include following components according to the mass fraction:
Basic resin: 95 parts, Masterbatch: 5 parts, reflective masterbatch glass microballoon: 10 parts, silane coupling agent: 5 parts, auxiliary agent: 5
Part, TYY-4E:7 parts of luminescent powder, dispersing agent: 5 parts, negative ion powder: 2 parts, filler: 3 parts；
Basic resin is the mixture of vinylite and plexiglass；Auxiliary agent includes antioxidant
1010, the mixture of light stabilizer 770, spin finish aid；Dispersing agent is the mixture of polypropylene wax and oxidized polyethylene wax；Filler
For talcum powder；
Adhesive layer is formed by adhesive brushing in base cloth bottom end, and adhesive includes following components according to the mass fraction:
EVA resin: 20 parts, phenolic resin: 30 parts, phthalic anhydride: 15 parts, polytetrahydrofuran: 10 parts, thickener: 3
Part, chain extender: 5 parts, isocyanates: 12 parts, B2500:3 parts of anti-aging agent, N20:4 parts of Nano carbon white, defoaming agent: 6 parts, solidification
Agent: 14 parts, emulsifier: 7 parts, preservative: 5 parts, denaturation dressing agent: 3 parts, fire retardant: 2 parts；
EVA resin is the copolymer of ethylene Yu comonomer vinyl acetate, wherein the weight percent of monomer vinyl acetate
Content is 38%, and the mass percent of ethylene is 62%；Thickener is hydroxymethyl cellulose；Chain extender is 1,4- butanediol；Disappear
Infusion is melamine；Curing agent is polyamide；Emulsifier is dodecyl sodium sulfate；Preservative is formic acid；It is denaturalized dressing agent
For in the chloro- 2- propyl alcohol of 1,3- bis-；Fire retardant is phosphotriester.
Adhesive the preparation method is as follows:
O-phthalic is added in the four-hole boiling flask equipped with electric mixing device, heating device, thermometer and vacuum inlet
Acid anhydrides and polytetrahydrofuran are heated to 110 degrees Celsius, and chain extender is then added and quickly stirs, and are added after stirring 20min different
Cyanate continues to stir, and EVA resin then is added and phenolic resin stirs evenly, and thickener, anti-aging agent are added while stirring
B2500, Nano carbon white N20, defoaming agent, curing agent, emulsifier, preservative, denaturation dressing agent, fire retardant, after mixing evenly
Obtain adhesive.
Reflective type chinampa the preparation method is as follows:
Step (1) prepares artificial grass filaments:
Basic resin, reflective masterbatch, coupling agent are blended to granulation on the twin screw extruder and are prepared into reflective master batch, is squeezed out
Temperature is 250 degrees Celsius, then send into stirred tank reflective master batch, Masterbatch, auxiliary agent and filler and is blended uniformly, mixing speed
For 150r/min, luminescent powder TYY-4E, dispersing agent, negative ion powder, coupling agent is then added into stirred tank again, continues to stir,
Mixing speed is 300r/min, is prepared into careless silk semi-finished product through extrusion, wire drawing after stirring evenly, and the control of extrusion molding temperature exists
It 300 degrees Celsius, is reversed two-by-two in every careless silk semi-finished product and is bonded into double-stranded strip grass silk and obtains finished product grass silk, it will be more
A finished synthetic's grass silk flocks together, and to form cluster artificial grass filaments stand-by；
The artificial grass filaments that step (2) prepares are worn in the air from a semicircle of base cloth to another semicircle orifice, are then existed
Tufting has the base cloth bottom coating gluing dosage form of artificial grass filaments artificial grass filaments are fixed on base cloth at adhesive layer to be formed
Artificial turf is placed in plastic feet by artificial turf, and is fixed for use by the edge on plastic feet；
Each plastic feet for accommodating artificial turf is passed through the fixed hook and fixed ring of plastic feet two sides by step (3)
It connects to form chinampa.
Based on the embodiment in invention, those of ordinary skill in the art are obtained without creative efforts
Every other embodiment, shall fall within the protection scope of the present invention.
Claims (5)
1. one kind can play the reflective type chinampa of mark action, including plastic feet and the pedaline being contained in plastic feet
Skin, the artificial turf include artificial grass filaments on base cloth of base cloth, tufting and the gluing for being set to base cloth bottom end
Oxidant layer；
The artificial grass filaments are to be reversed into double-stranded strip grass silk, are evenly equipped with several circular holes on the base cloth, each
Circular hole is separated into two semicircle orifices by being placed in the fixed strip among circular hole, and the artificial grass filaments pass through two semicircle orifices and are placed in bottom
In base fabric, in which:
The artificial grass filaments include following components according to the mass fraction:
Basic resin: 60-95 parts, Masterbatch: 1-5 parts, reflective masterbatch: 4-10 parts, coupling agent: 1-5 parts, auxiliary agent: 0.2-4.8
Part, TYY-4E:5-7 parts of luminescent powder, dispersing agent: 1-5 parts, negative ion powder: 1-5 parts, filler: 1-5 parts；
The basic resin is the mixture of vinylite and plexiglass；The reflective masterbatch is
Glass microballoon；The coupling agent is silane coupling agent；The auxiliary agent includes that antioxidant 1010, light stabilizer 770, spinning help
The mixture of agent；The dispersing agent is the mixture of polypropylene wax and oxidized polyethylene wax；The filler is heavy carbonic acid
Calcium or talcum powder；
The adhesive layer is formed by adhesive brushing in base cloth bottom end, and the adhesive includes following according to the mass fraction
Component:
EVA resin: 5-20 parts, phenolic resin: 15-35 parts, phthalic anhydride: 5-15 parts, polytetrahydrofuran: 5-15 parts, expand
Chain agent: 2-5 parts, isocyanates: 6-12 parts, N20:2-4 parts of Nano carbon white, defoaming agent: 3-6 parts, curing agent: 10-14 parts, cream
Agent: 4-7 parts, denaturation dressing agent: 1-3 parts；
The EVA resin is the copolymer of ethylene Yu comonomer vinyl acetate, wherein the weight percent of monomer vinyl acetate
It is 38% than content, the mass percent of ethylene is 62%；The chain extender is 1,4- butanediol；The defoaming agent is melamine
Amine；The curing agent is one of m-phenylene diamine (MPD), diethylenetriamine, polyamide；The emulsifier is dodecyl sodium sulfate；
The denaturation dressing agent is one of sodium hydroxide, disodium hydrogen phosphate or the chloro- 2- propyl alcohol of 1,3- bis-.
2. the reflective type chinampa according to claim 1 for playing mark action, it is characterised in that: the plastic feet
Including pedestal holding tank and edge, the edge extends internally from the top surrounding of pedestal holding tank, and the pedestal accommodates
The side of slot is equipped with stay hook, and the pedestal holding tank other side is equipped with fixed ring, and the bottom of pedestal holding tank is equipped with several drainage holes.
3. the reflective type chinampa according to claim 1 for playing mark action, it is characterised in that: the base cloth is extremely
It is formed by stacking under above by polypropylene woven cloth, non-woven fabrics and Gauze.
4. the reflective type chinampa according to claim 1 for playing mark action, it is characterised in that: the adhesive
The preparation method is as follows:
Phthalic anhydride is added in the four-hole boiling flask equipped with electric mixing device, heating device, thermometer and vacuum inlet
And polytetrahydrofuran, it is heated to 100-110 degrees Celsius, chain extender is then added and quickly stirs, is added after stirring 10-20min
Enter isocyanates, continue to stir, EVA resin then is added and phenolic resin stirs evenly, Nano carbon white is added while stirring
N20, defoaming agent, curing agent, emulsifier are denaturalized dressing agent, obtain adhesive after mixing evenly.
5. the reflective type chinampa according to claim 1 for playing mark action, it is characterised in that: the reflective type people
Make lawn the preparation method is as follows:
Step (1) prepares artificial grass filaments:
Basic resin, reflective masterbatch, coupling agent are blended to granulation on the twin screw extruder and are prepared into reflective master batch, extrusion temperature
It is 150-250 degrees Celsius, then reflective master batch, Masterbatch, auxiliary agent and filler is sent into stirred tank and are blended uniformly, mixing speed
For 100-150r/min, luminescent powder TYY-4E, dispersing agent, negative ion powder, coupling agent is then added into stirred tank again, continues to stir
It mixes, mixing speed 200-300r/min, is squeezed out after stirring evenly, wire drawing is prepared into careless silk semi-finished product, extrusion molding temperature
Control is reversed two-by-two in every careless silk semi-finished product at 150-300 degrees Celsius and is bonded into double-stranded strip grass silk and obtains into
Product grass silk, multiple finished synthetic's grass silks are flocked together, and it is stand-by to form cluster artificial grass filaments；
The artificial grass filaments that step (2) prepares are worn in the air from a semicircle of base cloth to another semicircle orifice, then in tufting
Have artificial grass filaments base cloth bottom coating gluing dosage form artificial grass filaments are fixed on base cloth at adhesive layer formed it is artificial
Artificial turf is placed in plastic feet by turf, and is fixed for use by the edge on plastic feet；
Step (3) connects each plastic feet for accommodating artificial turf by the fixed hook of plastic feet two sides with fixed ring
Get up to form chinampa.