CN110055860A - A kind of manufacture craft of antibacterial artificial turf - Google Patents
A kind of manufacture craft of antibacterial artificial turf Download PDFInfo
- Publication number
- CN110055860A CN110055860A CN201810047455.7A CN201810047455A CN110055860A CN 110055860 A CN110055860 A CN 110055860A CN 201810047455 A CN201810047455 A CN 201810047455A CN 110055860 A CN110055860 A CN 110055860A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- artificial turf
- mixture
- manufacture craft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to chinampa technical fields, and in particular to a kind of manufacture craft of antibacterial artificial turf；Its ingredient includes: antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide, defoaming agent, polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate；Wherein, the nitrogen-atoms in polyvinylpyrrolidone and silver form complex bonds, and polyvinylpyrrolidone is fixed on a nanometer silver surface, it is wrapped up, provides effective steric hindrance, nano silver is made not reunite, to keep Nano silver grain more stable, the concentration of Nano silver grain is increased；Polyvinylpyrrolidone-nano silver composite material is blended with copper nitrate and zinc nitrate, and the addition of copper ion and zinc ion can play synergistic effect with nano silver, enhances its antibacterial effect.
Description
Technical field
The present invention relates to chinampa technical fields, and in particular to a kind of manufacture craft of antibacterial artificial turf.
Background technique
In the U.S., artificial grass fibre material used in most of chinampa is high-grade nylon material, also there is use
Multi-component fibre, infiltration and impermeable two kinds can also be divided into without filling husky chinampa.This lawn exactly likes naturally in shape
Lawn partially has one layer of shock-absorbing airfoam cushion layer, and there are many different density and thickness for shock suction layer.Due to really slapping at home
The producer for holding chinampa laying technology is few, and mostly foreign technology, therefore, special when laying does not fill husky chinampa
It is not to be laid with shock-absorbing airfoam cushion layer to have to be completed by external expert.One layer of smooth pitch is spread under shock-absorbing foam to make
Based on, based on pitch will spread rubble, sand and cobble further below, and the construction of drainage system therein is most critical
Link.In addition, such chinampa is had to during the installation process using pedaline special-purpose machinery, especially one
It is even more important in the laying installation on athletic ground that is a little professions or involving great expense, otherwise will be unable to reach levelling of the land and
The requirement of evenness, for example, hockey of Beijing Lu Cheng sports techniques institute on 2008 Olympic Games hockey court ground
And part in order to which the places such as the packaged type pedaline, the piece pedaline that meet special demands all must be strictly by requirements above
It constructs.
Traditional chinampa does not have anti-microbial property, not can solve the bacteria growth problems of chinampa.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of manufacture crafts of antibacterial artificial turf, not only have good
Good antibacterial effect, and easy to operate, lower production costs.
In order to achieve the above object, the present invention is achieved by the following technical programs:
A kind of manufacture craft of antibacterial artificial turf, ingredient by weight: 25-37 parts of antibacterial colorant master batch, auxiliary agent
18-26 parts, 19-27 parts of basic resin, 14-32 parts of adhesive, polyvinylpyrrolidone -16-21 parts of nano silver composite material, nitre
Sour copper 11-19 parts, 13-19 parts of zinc nitrate and 17-29 parts of defoaming agent.
Preferably, a kind of manufacture craft of antibacterial artificial turf, preparation method includes the following steps:
A, stirred tank is added in antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide and defoaming agent to be blended uniformly, is obtained
Mixture A；Stirred tank is added in polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate to be blended uniformly, is obtained mixed
Close material B；
B, the mixture B in step a is adjusted to 7.0-8.0 with PH regulator, obtains mixture C；
C, stirred tank is added in mixture A and mixture C to be blended into uniformly, obtains mixture D；
D, mixture D is squeezed out, wire drawing through extruder, prepares artificial grass filaments；
E, artificial grass filaments tufting is formed into base fabric semi-finished product lawn, semi-finished product lawn base cloth backside is covered with gluing
Antibacterial artificial turf is made in agent.
Preferably, the mixing speed in the step a is 250r/min.
Preferably, the PH regulator in the step b is the buffer solution of sodium dihydrogen phosphate and disodium hydrogen phosphate.
Preferably, the mixing time in the step c is 1h.
Preferably, the temperature setting of the extruder in the step d is 120-160 DEG C.
The utility model has the advantages that
A kind of manufacture craft of antibacterial artificial turf prepared by the present invention, nitrogen-atoms and silver-colored shape in polyvinylpyrrolidone
At complex bonds, polyvinylpyrrolidone is fixed on a nanometer silver surface, is wrapped up, and provides effective steric hindrance, makes nanometer
Silver is not reunited, to keep Nano silver grain more stable, increases the concentration of Nano silver grain；Polyvinylpyrrolidone-
Nano silver composite material is blended with copper nitrate and zinc nitrate, and copper ion can rise with nano silver with the addition of zinc ion and cooperate with work
With enhancing its antibacterial effect；After blending adjust PH to 7.0-8.0, facilitate polyvinylpyrrolidone-nano silver composite material with
Copper nitrate and zinc nitrate are more fully mixed；This technological operation is simple, lower production costs.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1:
A kind of manufacture craft of antibacterial artificial turf, ingredient by weight: 25 parts of antibacterial colorant master batch, auxiliary agent 21
Part, 19 parts of basic resin, 20 parts of adhesive, 17 parts of polyvinylpyrrolidone-nano silver composite material, 11 parts of copper nitrate, nitric acid
13 parts and 17 parts of defoaming agent of zinc.
A kind of manufacture craft of antibacterial artificial turf, preparation method includes the following steps:
A, stirred tank is added in antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide and defoaming agent to be blended uniformly, is obtained
Mixture A；Stirred tank is added in polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate to be blended uniformly, is obtained mixed
Close material B；
B, the mixture B in step a is adjusted to 7.0 with PH regulator, obtains mixture C；
C, stirred tank is added in mixture A and mixture C to be blended into uniformly, obtains mixture D；
D, mixture D is squeezed out, wire drawing through extruder, prepares artificial grass filaments；
E, artificial grass filaments tufting is formed into base fabric semi-finished product lawn, semi-finished product lawn base cloth backside is covered with gluing
Antibacterial artificial turf is made in agent.
Mixing speed in step a is 250r/min.
PH regulator in step b is the buffer solution of sodium dihydrogen phosphate and disodium hydrogen phosphate.
Mixing time in step c is 1h.
The temperature setting of extruder in step d is 120 DEG C.
Embodiment 2:
A kind of manufacture craft of antibacterial artificial turf, ingredient by weight: 33 parts of antibacterial colorant master batch, auxiliary agent 24
Part, 24 parts of basic resin, 14 parts of adhesive, 19 parts of polyvinylpyrrolidone-nano silver composite material, 17 parts of copper nitrate, nitric acid
17 parts and 25 parts of defoaming agent of zinc.
A kind of manufacture craft of antibacterial artificial turf, preparation method includes the following steps:
A, stirred tank is added in antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide and defoaming agent to be blended uniformly, is obtained
Mixture A；Stirred tank is added in polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate to be blended uniformly, is obtained mixed
Close material B；
B, the mixture B in step a is adjusted to 7.0 with PH regulator, obtains mixture C；
C, stirred tank is added in mixture A and mixture C to be blended into uniformly, obtains mixture D；
D, mixture D is squeezed out, wire drawing through extruder, prepares artificial grass filaments；
E, artificial grass filaments tufting is formed into base fabric semi-finished product lawn, semi-finished product lawn base cloth backside is covered with gluing
Antibacterial artificial turf is made in agent.
Mixing speed in step a is 250r/min.
PH regulator in step b is the buffer solution of sodium dihydrogen phosphate and disodium hydrogen phosphate.
Mixing time in step c is 1h.
The temperature setting of extruder in step d is 135 DEG C.
Embodiment 3:
A kind of manufacture craft of antibacterial artificial turf, ingredient by weight: 29 parts of antibacterial colorant master batch, auxiliary agent 18
Part, 21 parts of basic resin, 26 parts of adhesive, 18 parts of polyvinylpyrrolidone-nano silver composite material, 14 parts of copper nitrate, nitric acid
15 parts and 21 parts of defoaming agent of zinc.
A kind of manufacture craft of antibacterial artificial turf, preparation method includes the following steps:
A, stirred tank is added in antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide and defoaming agent to be blended uniformly, is obtained
Mixture A；Stirred tank is added in polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate to be blended uniformly, is obtained mixed
Close material B；
B, the mixture B in step a is adjusted to 8.0 with PH regulator, obtains mixture C；
C, stirred tank is added in mixture A and mixture C to be blended into uniformly, obtains mixture D；
D, mixture D is squeezed out, wire drawing through extruder, prepares artificial grass filaments；
E, artificial grass filaments tufting is formed into base fabric semi-finished product lawn, semi-finished product lawn base cloth backside is covered with gluing
Antibacterial artificial turf is made in agent.
Mixing speed in step a is 250r/min.
PH regulator in step b is the buffer solution of sodium dihydrogen phosphate and disodium hydrogen phosphate.
Mixing time in step c is 1h.
The temperature setting of extruder in step d is 145 DEG C.
Embodiment 4:
A kind of manufacture craft of antibacterial artificial turf, ingredient by weight: 37 parts of antibacterial colorant master batch, auxiliary agent 26
Part, 27 parts of basic resin, 32 parts of adhesive, 21 parts of polyvinylpyrrolidone-nano silver composite material, 19 parts of copper nitrate, nitric acid
19 parts and 29 parts of defoaming agent of zinc.
A kind of manufacture craft of antibacterial artificial turf, preparation method includes the following steps:
A, stirred tank is added in antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide and defoaming agent to be blended uniformly, is obtained
Mixture A；Stirred tank is added in polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate to be blended uniformly, is obtained mixed
Close material B；
B, the mixture B in step a is adjusted to 8.0 with PH regulator, obtains mixture C；
C, stirred tank is added in mixture A and mixture C to be blended into uniformly, obtains mixture D；
D, mixture D is squeezed out, wire drawing through extruder, prepares artificial grass filaments；
E, artificial grass filaments tufting is formed into base fabric semi-finished product lawn, semi-finished product lawn base cloth backside is covered with gluing
Antibacterial artificial turf is made in agent.
Mixing speed in step a is 250r/min.
PH regulator in step b is the buffer solution of sodium dihydrogen phosphate and disodium hydrogen phosphate.
Mixing time in step c is 1h.
The temperature setting of extruder in step d is 160 DEG C.
In above embodiments, embodiment 2 is most preferred embodiment, and anti-microbial property is best.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (6)
1. a kind of manufacture craft of antibacterial artificial turf, which is characterized in that its ingredient by weight: antibacterial colorant master batch 25-
37 parts, 18-26 parts of auxiliary agent, 19-27 parts of basic resin, 14-32 parts of adhesive, polyvinylpyrrolidone-nano silver composite material
16-21 parts, 11-19 parts of copper nitrate, 13-19 parts of zinc nitrate and 17-29 parts of defoaming agent.
2. a kind of manufacture craft of antibacterial artificial turf according to claim 1, which is characterized in that preparation method includes
Following steps:
A, stirred tank is added in antibacterial colorant master batch, auxiliary agent, basic resin, magnesium hydroxide and defoaming agent to be blended uniformly, must mixed
Expect A；Stirred tank is added in polyvinylpyrrolidone-nano silver composite material, copper nitrate and zinc nitrate to be blended uniformly, obtains mixture
B；
B, the mixture B in step a is adjusted to 7.0-8.0 with PH regulator, obtains mixture C；
C, stirred tank is added in mixture A and mixture C to be blended into uniformly, obtains mixture D；
D, mixture D is squeezed out, wire drawing through extruder, prepares artificial grass filaments；
E, artificial grass filaments tufting is formed into base fabric semi-finished product lawn, semi-finished product lawn base cloth backside is covered with adhesive,
Antibacterial artificial turf is made.
3. a kind of manufacture craft of antibacterial artificial turf according to claim 2, it is characterised in that: in the step a
Mixing speed is 250r/min.
4. a kind of manufacture craft of antibacterial artificial turf according to claim 2, it is characterised in that: in the step b
PH regulator is the buffer solution of sodium dihydrogen phosphate and disodium hydrogen phosphate.
5. a kind of manufacture craft of antibacterial artificial turf according to claim 2, it is characterised in that: in the step c
Mixing time is 1h.
6. a kind of manufacture craft of antibacterial artificial turf according to claim 2, it is characterised in that: in the step d
The temperature setting of extruder is 120-160 DEG C.