CN109487984A - 一种环保回收石子再利用地板及其制备方法 - Google Patents
一种环保回收石子再利用地板及其制备方法 Download PDFInfo
- Publication number
- CN109487984A CN109487984A CN201811111239.0A CN201811111239A CN109487984A CN 109487984 A CN109487984 A CN 109487984A CN 201811111239 A CN201811111239 A CN 201811111239A CN 109487984 A CN109487984 A CN 109487984A
- Authority
- CN
- China
- Prior art keywords
- stone
- substrate cavity
- floor
- turquoise
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保回收石子再利用的地板，包括基材腔体、涂覆于基材腔体外表面的油漆层以及包覆于基材腔体内的填充层，所述填充层是由小米石和绿松石通过胶粘剂相互粘连而形成的填充层；同时本发明还公开了一种环保回收石子再利用地板的制备方法：首先将小米石和绿松石粉碎；然后小米石和绿松石与胶粘剂注入基材腔体；其次将基材腔体自然烘干，并用砂光机打磨基材腔体；最后对基材腔体上漆，晾干。本发明制备地板过程简单方便，制备的地板不仅防水，结实稳定，耐磨，而且将废石子重新利用，环保，利用率高。
Description
技术领域
本发明属于地板及地板生产制造技术领域，特别是涉及一种环保回收石子再利用地板的制备方法。
背景技术
随着人们生活水平的不断提高，地板在室内地面装修中得到看广泛应用，同时人们也追求更加节能环保的地板，但实现节能环保一直是地板制造的短板。
因此，如何利用废弃材料制造节能环保的地板成为本领域人员研究的重点。
发明内容
本发明的目的就是提供一种环保回收石子再利用地板的制备方法，能完全解决上述现有技术的不足之处。
本发明的目的通过下述技术方案来实现：
一种环保回收石子再利用的地板，包括基材腔体、涂覆于基材腔体外表面的油漆层以及包覆于基材腔体内的填充层，所述填充层是由小米石和绿松石通过胶粘剂相互粘连而形成的填充层。
作为优选，所述基材腔体为密闭方体，基材腔体下表面开设有与基材腔体内腔相通的凹槽。
作为优选，所述胶粘剂是由以下组分及质量百分比的原料制成：天然3L橡胶80%-90%、交联剂2%-5%、增粘剂5%-10%、硫化剂3%-5%。
一种环保回收石子再利用地板的制备方法，包括以下步骤：
1）将小米石和绿松石粉碎；
2)将粉碎后的小米石和绿松石与胶粘剂边混合，边从基材腔体上的凹槽注入基材腔体内腔；
3）将注满小米石和绿松石的基材腔体自然烘干，并用砂光机将基材腔体表面打磨光滑；
4）对打磨后基材腔体表面涂抹油漆，待油漆晾干后即可。
作为优选，所述步骤2）中往基材腔体内边注入小米石和绿松石，边摇动基材腔体，使小米石和绿松石均匀布满基材腔体内腔。
与现有技术相比，本发明的有益效果在于：
本发明制备地板的方法简单方便，制备的地板不仅防水，结实稳定，耐磨，而且将废石子重新利用，环保，利用率高。
附图说明
图1是本发明的结构示意图；
图2是本发明的纵截面剖图。
附图标记：1-基材腔体，2-油漆层，3-填充层，4-凹槽。
具体实施方式
下面结合具体实施例和附图对本发明作进一步的说明。
实施例一
如图1至图2所示，一种环保回收石子再利用的地板，包括基材腔体1、涂覆于基材腔体外表面的油漆层2以及包覆于基材腔体内的填充层3，填充层3是由小米石和绿松石通过胶粘剂相互粘连而形成，胶粘剂是由以下组分及质量百分比的原料制成：天然3L橡胶80%，交联剂5%，增粘剂10%，硫化剂5%，基材腔体为密闭方体，基材腔体下表面开设有与基材腔体内腔相通的凹槽4，基材腔体是由以下组分及质量份的原料组成：聚氯乙烯树脂60-80份、玻璃纤维20-35份、固化剂2-5份、阻燃剂3-7份、钙锌稳定剂5-10份和废弃橡胶10-15份，油漆层是由以下组分和质量份的原料制成的油漆涂刷而成：烃乙基纤维素20-40份、水溶树脂5-10份、硼砂2-6份、松香酚醛树脂5-10份和茉莉花3-5份。
实施例二
如图1至图2所示，一种环保回收石子再利用的地板，包括基材腔体1、涂覆于基材腔体外表面的油漆层2以及包覆于基材腔体内的填充层3，填充层3是由小米石和绿松石通过胶粘剂相互粘连而形成，胶粘剂是由以下组分及质量百分比的原料制成：天然3L橡胶85%、交联剂4%、增粘剂8%、硫化剂4%，基材腔体为密闭方体，基材腔体下表面开设有与基材腔体内腔相通的凹槽4，基材腔体是由以下组分及质量份的原料组成：聚氯乙烯树脂70份、玻璃纤维25份、固化剂3份、阻燃剂5份、钙锌稳定剂8份、废弃橡胶13份，油漆层是由以下组分和质量份的原料制成的油漆涂刷而成：烃乙基纤维素30份、水溶树脂6份、硼砂4份、松香酚醛树脂7份和茉莉花4份。
实施例三
如图1至图2所示，一种环保回收石子再利用的地板，包括基材腔体1、涂覆于基材腔体外表面的油漆层2以及包覆于基材腔体内的填充层3，填充层3是由小米石和绿松石通过胶粘剂相互粘连而形成，胶粘剂是由以下组分及质量百分比的原料制成：天然3L橡胶90%、交联剂5%、增粘剂10%、硫化剂5%，基材腔体为密闭方体，基材腔体下表面开设有与基材腔体内腔相通的凹槽4，基材腔体是由以下组分及质量份的原料组成：聚氯乙烯树脂75份、玻璃纤维30份、固化剂4份、阻燃剂6份、钙锌稳定剂9份、废弃橡胶14份，油漆层是由以下组分和质量份的原料制成的油漆涂刷而成：烃乙基纤维素35份、水溶树脂8份、硼砂5份、松香酚醛树脂9份和茉莉花4.5份。
同时本发明还公开了上述实施例1-3中任一种环保回收石子再利用地板的制备方法，包括以下步骤：
1）将小米石和绿松石粉碎；
2)将粉碎后的小米石和绿松石与胶粘剂边混合，边从基材腔体上的凹槽注入基材腔体内腔，在往基材腔体内边注入小米石和绿松石，边摇动基材腔体，使小米石和绿松石均匀布满基材腔体内腔；
3）将注满小米石和绿松石的基材腔体自然烘干，并用砂光机将基材腔体表面打磨光滑；
4）对打磨后基材腔体表面涂抹油漆，待油漆晾干后即可。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种环保回收石子再利用的地板，其特征在于：包括基材腔体（1）、涂覆于基材腔体（1）外表面的油漆层（2）以及包覆于基材腔体（1）内的填充层（3），所述填充层（3）是由小米石和绿松石通过胶粘剂相互粘连而形成的填充层。
2.根据权利要求1所述的一种环保回收石子再利用的地板，其特征在于：所述基材腔体（1）为密闭方体，基材腔体（1）下表面开设有与基材腔体（1）内腔相通的凹槽（4）。
3.根据权利要求1所述的一种环保回收石子再利用的地板，其特征在于：所述胶粘剂是由以下组分及质量百分比的原料制成：天然3L橡胶80%-90%、交联剂2%-5%、增粘剂5%-10%、硫化剂3%-5%。
4.根据权利要求1～3中任一所述的一种环保回收石子再利用地板的制备方法，其特征在于：包括以下步骤：
1）将小米石和绿松石粉碎；
2)将粉碎后的小米石和绿松石与胶粘剂边混合，边从基材腔体上的凹槽注入基材腔体内腔；
3）将注满小米石和绿松石的基材腔体自然烘干，并用砂光机将基材腔体表面打磨光滑；
4）对打磨后基材腔体表面涂抹油漆，待油漆晾干后即可。
5.根据权利要求4所述的一种环保回收石子再利用地板的制备方法，其特征在于：所述步骤2）中往基材腔体内边注入小米石和绿松石，边摇动基材腔体，使小米石和绿松石均匀布满基材腔体内腔。