CN109437702A - 基于无机纳米材料应用的文物库房门芯板制备方法 - Google Patents
基于无机纳米材料应用的文物库房门芯板制备方法 Download PDFInfo
- Publication number
- CN109437702A CN109437702A CN201811579165.3A CN201811579165A CN109437702A CN 109437702 A CN109437702 A CN 109437702A CN 201811579165 A CN201811579165 A CN 201811579165A CN 109437702 A CN109437702 A CN 109437702A
- Authority
- CN
- China
- Prior art keywords
- nano material
- inorganic nano
- door panel
- storage door
- cultural relics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种基于无机纳米材料应用的文物库房门芯板制备方法,所述芯板由无机纳米材料、减水剂、水、水泥及复合填充材料组成,将无机纳米材料、水和减水剂混合制得纳米材料泥浆;将所述纳米材料泥浆与水泥及复合填充材料按比例混合制成无机纳米材料增强的文物库房门芯板。因添加无机纳米材料,具有较大表面积,实现纳米材料矿粉与水化产物大量键合,有效改善混凝土中水泥石与骨料的界面结构,使混凝土强度、抗渗性与耐久性均得以提高。
Description
技术领域
本发明涉及文物库房门芯板设计技术领域,尤其涉及一种基于无机纳米材料应用的文物库房门芯板制备方法。
背景技术
文物库房门是博物馆库房中不可缺少的一部分,是文物安全的守护神。
文物库房门是需要按照《GB50348-2004安全防范工程技术规范》、《GB/T16571-2012博物馆和文物保护单位安全防范系统要求》、公共安全行业标准《GA/T143-1996金库门通用技术条件》及金融行业标准《JR/T001-2000金库门》而设计制造的,需要完全符合相关标准的要求及文博单位的使用需求。
文物库房门具备防盗、防火、防水、防烟等功能,满足“四防”要求。根据防暴力破坏时间和耐火极限的不同共分为四个等级,分别为C、B、A和M级(3、2、1和M级)。C级(3级)为最高级,依次递减。
要实现上述功能需要一款新材料与新工艺结合实现的新型门芯板来增强其安全性,传统的文物库房门芯板混凝土强度、抗渗性与耐久性均不够理想。
发明内容
本发明的目的在于提供一种基于无机纳米材料应用的文物库房门芯板制备方法,有效解决上述技术问题。
为有效解决上述技术问题,本发明采取的技术方案如下:
基于无机纳米材料应用的文物库房门芯板制备方法,该方法包括以下步骤:
(1)结构设定:所述芯板由无机纳米材料、减水剂、水、水泥及复合填充材料组成;
(2)制备步骤:
(2-1)制备纳米材料泥浆:将无机纳米材料、水和减水剂混合制得纳米材料泥浆;
(2-2)将所述纳米材料泥浆与水泥及复合填充材料按比例混合制成无机纳米材料增强的文物库房门芯板。
特别的,所述步骤还包括以下步骤:
所述无机纳米材料包括纳米二氧化硅、碳酸钙、三氧化二铝、二氧化钛、氧化铁及硅酸钙之一。
特别的,所述无机纳米材料包括纳米二氧化硅、碳酸钙、三氧化二铝、二氧化钛、氧化铁及硅酸钙中任意两种的混合材料。
特别的,所述步骤还包括以下步骤:
所述无机纳米材料的用量为水泥用量的0.2%-3.0%,纳米材料颗粒半径0.1-1.0微米,比表面积在50-500m2/g之间。
特别的,所述步骤还包括以下步骤:
所述减水剂包括聚羧酸盐、磺酸盐及脂肪族系之一。
特别的,所述步骤还包括以下步骤:
所述复合填充材料为细砂、石灰、珍珠岩、钢珠及弹簧的混合。
一种通过上述方法实现的文物库房门芯板,所述文物库房门芯板包括以下组成成分:
本发明的有益效果为:本发明提供的基于无机纳米材料应用的文物库房门芯板制备方法,添加无机纳米材料,具有较大表面积,实现纳米材料矿粉与水化产物大量键合,有效改善混凝土中水泥石与骨料的界面结构,使混凝土强度、抗渗性与耐久性均得以提高。
下面结合附图对本发明进行详细说明。
附图说明
图1是本发明工艺流程图。
具体实施方式
实施例1:
如图1所示,本实施例提供的基于无机纳米材料应用的文物库房门芯板制备方法:
基于无机纳米材料应用的文物库房门芯板制备方法,该方法包括以下步骤:
(1)结构设定:所述芯板由无机纳米材料、减水剂、水、水泥及复合填充材料组成;
(2)制备步骤:
(2-1)制备纳米材料泥浆:将无机纳米材料、水和减水剂混合制得纳米材料泥浆;
(2-2)将所述纳米材料泥浆与水泥及复合填充材料按比例混合制成无机纳米材料增强的文物库房门芯板。
申请人声明,所属技术领域的技术人员在上述实施例的基础上,将上述实施例某步骤,与发明内容部分的技术方案相组合,从而产生的新的方法,也是本发明的记载范围之一,本申请为使说明书简明,不再罗列这些步骤的其它实施方式。
本实施例具体加工步骤如下:
所述无机纳米材料包括纳米二氧化硅、碳酸钙、三氧化二铝、二氧化钛、氧化铁及硅酸钙之一。所述无机纳米材料包括纳米二氧化硅、碳酸钙、三氧化二铝、二氧化钛、氧化铁及硅酸钙中任意两种的混合材料。所述无机纳米材料的用量为水泥用量的0.2%-3.0%,纳米材料颗粒半径0.1-1.0微米,比表面积在50-500m2/g之间。所述减水剂包括聚羧酸盐、磺酸盐及脂肪族系之一。所述复合填充材料为细砂、石灰、珍珠岩、钢珠及弹簧的混合。
本实施例中区别于现有技术的技术路线为:
所述文物库房门芯板包括以下组成成分:
添加无机纳米材料,具有较大表面积,实现纳米材料矿粉与水化产物大量键合,有效改善混凝土中水泥石与骨料的界面结构,使混凝土强度、抗渗性与耐久性均得以提高。
申请人又一声明,本发明通过上述实施例来说明本发明的实现方法及装置结构,但本发明并不局限于上述实施方式,即不意味着本发明必须依赖上述方法及结构才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明所选用实现方法等效替换及步骤的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
本发明并不限于上述实施方式,凡采用与本发明相似结构及其方法来实现本发明目的的所有实施方式均在本发明保护范围之内。
Claims (7)
1.基于无机纳米材料应用的文物库房门芯板制备方法,其特征在于,该方法包括以下步骤:
(1)结构设定:所述芯板由无机纳米材料、减水剂、水、水泥及复合填充材料组成;
(2)制备步骤:
(2-1)制备纳米材料泥浆:将无机纳米材料、水和减水剂混合制得纳米材料泥浆;
(2-2)将所述纳米材料泥浆与水泥及复合填充材料按比例混合制成无机纳米材料增强的文物库房门芯板。
2.根据权利要求1所述基于无机纳米材料应用的文物库房门芯板制备方法,其特征在于,所述步骤还包括以下步骤:
所述无机纳米材料包括纳米二氧化硅、碳酸钙、三氧化二铝、二氧化钛、氧化铁及硅酸钙之一。
3.根据权利要求2所述基于无机纳米材料应用的文物库房门芯板制备方法,其特征在于,
所述无机纳米材料包括纳米二氧化硅、碳酸钙、三氧化二铝、二氧化钛、氧化铁及硅酸钙中任意两种的混合材料。
4.根据权利要求1所述基于无机纳米材料应用的文物库房门芯板制备方法,其特征在于,所述步骤还包括以下步骤:
所述无机纳米材料的用量为水泥用量的0.2%-3.0%,纳米材料颗粒半径0.1-1.0微米,比表面积在50-500m2/g之间。
5.根据权利要求1所述基于无机纳米材料应用的文物库房门芯板制备方法,其特征在于,所述步骤还包括以下步骤:
所述减水剂包括聚羧酸盐、磺酸盐及脂肪族系之一。
6.根据权利要求1所述基于无机纳米材料应用的文物库房门芯板制备方法,其特征在于,所述步骤还包括以下步骤:
所述复合填充材料为细砂、石灰、珍珠岩、钢珠及弹簧的混合。
7.一种通过权利要求1所述方法实现的文物库房门芯板,其特征在于,所述文物库房门芯板包括以下组成成分: