CN109435397A - A kind of new-energy automobile radiation protection new material - Google Patents
A kind of new-energy automobile radiation protection new material Download PDFInfo
- Publication number
- CN109435397A CN109435397A CN201811371113.7A CN201811371113A CN109435397A CN 109435397 A CN109435397 A CN 109435397A CN 201811371113 A CN201811371113 A CN 201811371113A CN 109435397 A CN109435397 A CN 109435397A
- Authority
- CN
- China
- Prior art keywords
- parts
- new
- raw material
- energy automobile
- radiation protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of new-energy automobile radiation protection new materials; it is related to radiation protection new material technology field; including radiation-proof film, the radiation-proof film is successively made of adsorption layer, counterdie, antiradiation coating and protective layer outward the side of abutting glass for vehicle window.New-energy automobile radiation protection new material, by being provided with PE protective film, effectively antiradiation coating can be protected, prevent the unexpected of antiradiation coating from scratching, it avoids pad pasting from being damaged and the phenomenon that anti-radiation performance variation occurs, by using ethyl alcohol, with the use of polyvinyl alcohol, sodium citrate, deionized water, antiradiation agent, nano-titanium dioxide, silane coupling agent, water-base epoxy tree, levelling agent and defoaming agent, can the pad pasting with shielding property effectively be reached with the use of preparation by more materials, to improve the shielding property of new-energy automobile pad pasting, solve the problems, such as that existing new-energy automobile pad pasting shielding property is poor.
Description
Technical field
The present invention relates to radiation protection new material technology field, specially a kind of new-energy automobile radiation protection new material.
Background technique
New energy is also known as unconventional energy resource, refers to the various energy forms except traditional energy, refers to and just starts to develop and use
Or actively study, need the energy promoted, such as solar energy, geothermal energy, wind energy, ocean energy, biomass energy and nuclear fusion energy
Generally refer to the renewable energy developed and used on the basis of new technology Deng, new energy, including solar energy, biomass energy,
Thermal cycle etc. between wind energy, geothermal energy, wave energy, ocean current energy and tide energy and ocean surface and deep layer, in addition, also
Hydrogen Energy, biogas, alcohol, methanol etc., and the energy such as coal, petroleum, natural gas, water energy utilized extensively, referred to as conventional energy
Source, new-energy automobile, which refers to, uses unconventional vehicle fuel as a source of power, the dynamic Control of comprehensive vehicle and driving side
The advanced technology in face, the advanced automobile with new technology, new construction of the technical principle of formation, electric car is new-energy automobile
One kind.
Automobile adhesive film is exactly that thin film shape object is sticked on vehicle front and rear windshield, side window glass and skylight,
And this layer film shape object is also referred to as solar film or is called thermal isolation film, but the radiation protection in use of existing automobile adhesive film
Performance price differential, causes car to receive radiation for a long time, and chronic exposure is brought very to can early be in very big life child to human body to user
Mostly than necessary trouble, as the poor new-energy automobile pad pasting of this shielding property is gradually difficult to meet the need of users
It asks.
Summary of the invention
It is new the object of the invention is in order to make up for the deficiencies of the prior art, provide a kind of new-energy automobile radiation protection
Material, it has the advantages that radiation protection, solves the problems, such as that existing new-energy automobile pad pasting shielding property is poor.
The present invention is in order to solve the above technical problems, provide the following technical solutions: a kind of new-energy automobile radiation protection green wood
Material, including radiation-proof film, the radiation-proof film is by the side of abutting glass for vehicle window outward successively by adsorption layer, counterdie, anti-
Radiation coating and protective layer composition.
Preferably, the formula of the antiradiation coating includes following components: ethyl alcohol in terms of mass fraction: 60 parts, polyethylene
Alcohol: 5 parts, sodium citrate: 10 parts, deionized water: 50 parts, antiradiation agent: 5-10 parts, nano-titanium dioxide: 5-10 parts, silane is even
Connection agent: 8-10 parts, aqueous epoxy resins: 60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3 parts.
Preferably, the preparation method of the antiradiation coating includes the following steps:
The ethyl alcohol of corrresponding quality part, polyvinyl alcohol, sodium citrate, antiradiation agent, nano-titanium dioxide are added to deionization by S1
In water, disperse 10-30min under the conditions of 300-500rpm, obtains first part of raw material.
S2 reacts 30min under the conditions of 300-500rpm, obtains after silane coupling agent is added dropwise dropwise into first part of raw material
To second part of raw material.
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material.
Third part raw material is added in hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm, obtains the
Four parts of raw materials.
Levelling agent and defoaming agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain antiradiation coating painting
Material.
Preferably, the counterdie is non-woven fabrics or carbon fiber, and counterdie a layer thickness is 4-8 μm.
Preferably, the adsorption layer is silicone resin, and adsorption layer a layer thickness is 10-15 μm.
Preferably, the protective layer is PE film, and PE a layer thickness is 5-10 μm.
Compared with prior art, this kind of new-energy automobile radiation protection new material have it is following the utility model has the advantages that
1, the present invention can effectively protect vehicle glass by being provided with Carbon fibe counterdie, and reducing radiation-proof film makes
With to the damage of glass body, avoiding counterdie from occurring the phenomenon that scratching glass body in use in the process, pass through setting
There is PE protective film, effectively antiradiation coating can be protected, prevent radiation-proof film from occurring radiation protection in use
It unexpected the phenomenon that scratching of coating, avoids radiation-proof film from being damaged and the phenomenon that anti-radiation performance variation occurs.
2, counterdie and glass body effectively can be carried out adhesion, prevent the automobile by the present invention by being provided with adsorption layer
There is the phenomenon that radiation-proof film is separated with glass body in use in pad pasting, and the present invention is logical by using ethyl alcohol, matches
Close using polyvinyl alcohol, sodium citrate, deionized water, antiradiation agent, nano-titanium dioxide, silane coupling agent, water-base epoxy tree,
Levelling agent and defoaming agent effectively can reach the pad pasting with shielding property with the use of preparation by more materials, to mention
The shielding property of high new-energy automobile pad pasting, solves that existing new-energy automobile pad pasting shielding property is poor to ask
Topic.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1
A kind of new-energy automobile radiation protection new material, the formula of the antiradiation coating is in terms of mass fraction comprising with the following group
Point: ethyl alcohol: 60 parts, polyvinyl alcohol: 5 parts, sodium citrate: 10 parts, deionized water: 50 parts, antiradiation agent: 5-10 parts, nanometer two
Titanium oxide: 5-10 parts, silane coupling agent: 8-10 parts, aqueous epoxy resins: 60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3
Part.
The antiradiation coating preparation method includes the following steps:
S1, by 5 parts of 10 parts of 5 parts of 60 parts of ethyl alcohol, polyvinyl alcohol, sodium citrate, the antiradiation agent, nanometer titanium dioxide of corrresponding quality part
10 parts of titanium are add to deionized water, and disperse 10-30min under the conditions of 300-500rpm, obtain first part of raw material.
S2 reacts under the conditions of 300-500rpm after being added dropwise 10 parts of silane coupling agent dropwise into first part of raw material
30min obtains second part of raw material.
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material.
Third part raw material is added in 60 parts of hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm, obtains
To the 4th part of raw material.
2 parts and 3 parts of defoaming agent of levelling agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain radiation protection
Coated coating.
Embodiment 2
A kind of new-energy automobile radiation protection new material, the antiradiation coating formula include following components in terms of mass fraction:
Ethyl alcohol: 60 parts, polyvinyl alcohol: 5 parts, sodium citrate: 10 parts, deionized water: 50 parts, antiradiation agent: 5-10 parts, nanometer titanium dioxide
Titanium: 5-10 parts, silane coupling agent: 8-10 parts, aqueous epoxy resins: 60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3 parts.
The antiradiation coating preparation method includes the following steps:
S1, by 5 parts of 10 parts of 5 parts of 60 parts of ethyl alcohol, polyvinyl alcohol, sodium citrate, the antiradiation agent, nanometer titanium dioxide of corrresponding quality part
10 parts of titanium are add to deionized water, and disperse 10-30min under the conditions of 300-500rpm, obtain first part of raw material.
S2 reacts under the conditions of 300-500rpm after being added dropwise 10 parts of silane coupling agent dropwise into first part of raw material
30min obtains second part of raw material.
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material.
Third part raw material is added in 70 parts of hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm, obtains
To the 4th part of raw material.
2 parts and 3 parts of defoaming agent of levelling agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain radiation protection
Coated coating.
Embodiment 3
A kind of new-energy automobile radiation protection new material, the antiradiation coating formula include following components in terms of mass fraction:
Ethyl alcohol: 60 parts, polyvinyl alcohol: 5 parts, sodium citrate: 10 parts, deionized water: 50 parts, antiradiation agent: 5-10 parts, nanometer titanium dioxide
Titanium: 5-10 parts, silane coupling agent: 8-10 parts, aqueous epoxy resins: 60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3 parts.
The antiradiation coating preparation method includes the following steps:
S1, by 10 parts of 10 parts of 5 parts of 60 parts of ethyl alcohol, polyvinyl alcohol, sodium citrate, the antiradiation agent, nano-silica of corrresponding quality part
Change 10 parts of titanium to be add to deionized water, disperses 10-30min under the conditions of 300-500rpm, obtain first part of raw material.
S2 reacts under the conditions of 300-500rpm after being added dropwise 10 parts of silane coupling agent dropwise into first part of raw material
30min obtains second part of raw material.
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material.
Third part raw material is added in 80 parts of hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm, obtains
To the 4th part of raw material.
2 parts and 3 parts of defoaming agent of levelling agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain radiation protection
Coated coating.
Embodiment 4
A kind of new-energy automobile radiation protection new material, the antiradiation coating formula include following components in terms of mass fraction:
Ethyl alcohol: 60 parts, polyvinyl alcohol: 5 parts, sodium citrate: 10 parts, deionized water: 50 parts, antiradiation agent: 5-10 parts, nanometer titanium dioxide
Titanium: 5-10 parts, silane coupling agent: 8-10 parts, aqueous epoxy resins: 60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3 parts.
The antiradiation coating preparation method includes the following steps:
S1, by 10 parts of 10 parts of 5 parts of 60 parts of ethyl alcohol, polyvinyl alcohol, sodium citrate, the antiradiation agent, nano-silica of corrresponding quality part
Change 10 parts of titanium to be add to deionized water, disperses 10-30min under the conditions of 300-500rpm, obtain first part of raw material.
S2 reacts under the conditions of 300-500rpm after being added dropwise 10 parts of silane coupling agent dropwise into first part of raw material
30min obtains second part of raw material.
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material.
Third part raw material is added in 90 parts of hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm, obtains
To the 4th part of raw material.
2 parts and 3 parts of defoaming agent of levelling agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain radiation protection
Coated coating
Embodiment 5
A kind of new-energy automobile radiation protection new material, the antiradiation coating formula include following components in terms of mass fraction:
Ethyl alcohol: 60 parts, polyvinyl alcohol: 5 parts, sodium citrate: 10 parts, deionized water: 50 parts, antiradiation agent: 5-10 parts, nanometer titanium dioxide
Titanium: 5-10 parts, silane coupling agent: 8-10 parts, aqueous epoxy resins: 60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3 parts.
The antiradiation coating preparation method includes the following steps:
S1, by 10 parts of 10 parts of 5 parts of 60 parts of ethyl alcohol, polyvinyl alcohol, sodium citrate, the antiradiation agent, nano-silica of corrresponding quality part
Change 10 parts of titanium to be add to deionized water, disperses 10-30min under the conditions of 300-500rpm, obtain first part of raw material.
S2 reacts under the conditions of 300-500rpm after being added dropwise 10 parts of silane coupling agent dropwise into first part of raw material
30min obtains second part of raw material.
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material.
Third part raw material is added in 100 parts of hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm,
Obtain the 4th part of raw material.
2 parts and 3 parts of defoaming agent of levelling agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain radiation protection
Coated coating.
In the prior art antiradiation coating coating the preparation method is as follows:
S1: prepare dove powder, aluminium powder and nano aluminium oxide.
S2: dove powder, aluminium powder and nano aluminium oxide 1:1:2 in mass ratio be sufficiently mixed, arrive raw material 1.
S3: well-mixed raw material 1 is fabricated to antiradiation coating.
Working principle: in use, first raw material is weighed portioning, according to a certain percentage by ethyl alcohol, polyvinyl alcohol, lemon
Sour sodium, antiradiation agent, nano-titanium dioxide are add to deionized water, and 10-30min is dispersed under the conditions of 300-500rpm, then
After silane coupling agent is added dropwise dropwise, 30min is reacted in continuation under the conditions of 300-500rpm, then uses ball mill grinding 20-
Radiation protective layer slurry is made in 30min;Radiation protective layer slurry is added to the radiation protective layer slurry obtained in aqueous epoxy resins,
After dispersing 20-30min under the conditions of 800rpm, levelling agent and defoaming agent are added, continues to disperse 20-30min, obtains radiation protection painting
Coating, the present invention is logical by using ethyl alcohol, is used cooperatively polyvinyl alcohol, sodium citrate, deionized water, antiradiation agent, nanometer
Titanium dioxide, silane coupling agent, water-base epoxy tree, levelling agent and defoaming agent, can be effectively by more materials with the use of system
It is standby to reach the pad pasting with shielding property, to improve the shielding property of new-energy automobile pad pasting, solve existing new
The energy automobile problem poor with pad pasting shielding property.
In the description of the present invention, the terms "include", "comprise" or its any other variant are intended to nonexcludability
Include so that include a series of elements process, method, article or equipment not only include those elements, but also
Including other elements that are not explicitly listed, or further include for this process, method, article or equipment intrinsic want
Element.It should be noted that, in this document, the relational terms of such as " first ", " second " or the like are used merely to an entity
Or operation is distinguished with another entity or operation, is existed without necessarily requiring or implying between these entities or operation
Any actual relationship or order.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of new-energy automobile radiation protection new material, it is characterised in that: including radiation-proof film, the radiation-proof film by
The side for being close to glass for vehicle window is successively made of adsorption layer, counterdie, antiradiation coating and protective layer outward.
2. a kind of new-energy automobile radiation protection new material according to claim 1, it is characterised in that: the radiation protection applies
The formula of layer includes following components: ethyl alcohol in terms of mass fraction: 60 parts, polyvinyl alcohol: and 5 parts, sodium citrate: 10 parts, deionization
Water: 50 parts, antiradiation agent: 5-10 parts, nano-titanium dioxide: 5-10 parts, silane coupling agent: 8-10 parts, aqueous epoxy resins:
60-100 parts, levelling agent: 1-2 parts, defoaming agent: 2-3 parts.
3. a kind of new-energy automobile radiation protection new material according to claim 2, it is characterised in that: the radiation protection applies
The preparation method of layer includes the following steps:
The ethyl alcohol of corrresponding quality part, polyvinyl alcohol, sodium citrate, antiradiation agent, nano-titanium dioxide are added to deionization by S1
In water, disperse 10-30min under the conditions of 300-500rpm, obtains first part of raw material;
S2 reacts 30min under the conditions of 300-500rpm after silane coupling agent is added dropwise dropwise into first part of raw material, obtains
Two parts of raw materials;
Radiation protective layer slurry is made with second part of raw material 20-30min of ball mill grinding in S3, obtains third part raw material;
Third part raw material is added in hydrotropism's epoxy resin by S4, after dispersing 20-30min under the conditions of 800rpm, obtains the 4th part
Raw material;
Levelling agent and defoaming agent are added into the 4th part of raw material by S5, continue to disperse 20-30min, obtain antiradiation coating coating.
4. a kind of new-energy automobile radiation protection new material according to claim 1, it is characterised in that: the counterdie is nothing
Woven fabric or carbon fiber, and counterdie a layer thickness is 4-8 μm.
5. a kind of new-energy automobile radiation protection new material according to claim 1, it is characterised in that: the adsorption layer is
Silicone resin, and adsorption layer a layer thickness is 10-15 μm.
6. a kind of new-energy automobile radiation protection new material according to claim 1, it is characterised in that: the protective layer is
PE film, and PE a layer thickness is 5-10 μm.