CN109397964A - A kind of production method that metal wood sense is drawn - Google Patents
A kind of production method that metal wood sense is drawn Download PDFInfo
- Publication number
- CN109397964A CN109397964A CN201811351332.9A CN201811351332A CN109397964A CN 109397964 A CN109397964 A CN 109397964A CN 201811351332 A CN201811351332 A CN 201811351332A CN 109397964 A CN109397964 A CN 109397964A
- Authority
- CN
- China
- Prior art keywords
- aluminium sheet
- processing
- drawn
- production method
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production methods that a kind of metal wood sense is drawn, include the following steps: a, aluminium sheet cutting: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and cutting processing is carried out to aluminium sheet using cutting machine, by aluminium sheet preparatory processing to required size;B, it polishes: carrying out polishing processing using aluminium sheet sander to the surface of aluminum plate after cutting, side, edges and corners are completed in a step.Beneficial effect is: the present invention is using metal as material, using wood grain as background color, writing or local printing are carried out on wood grain, pass through setting off for wood grain background color, entire picture is allowed to seem graceful, it is pure and fresh free from vulgarity, it is fresh and new to people's one kind, the same impression of poem, and with the breath of dense Chinese traditional culture in 5000, to make entire product have dense artistic feeling, entire decoration space is allowed to be filled with art atmosphere and cultural spirit everywhere, to set off out the high-end grade and culture of owner.
Description
Technical field
The present invention relates to adornment field, the production method drawn more particularly to a kind of metal wood sense.
Background technique
With the improvement of living standards, more and more people like parlor, room, company wall on hang up several width and draw
Make, paintings content is different or scenery with hills and waters or wild beast or landscape or personage, can not only intersperse room, moreover it is possible to personal taste is improved,
Promote personal makings.
But decoration painting product currently on the market generally use paper or printed matter production, and background color full page is all a face
Color is displayed without elegant natural style, and the printing of typically full page, level fuzzy, appreciation effect are bad.
Summary of the invention
The object of the invention is that providing a kind of production method that metal wood sense is drawn to solve the above-mentioned problems.
The present invention through the following technical solutions to achieve the above objectives:
A kind of production method that metal wood sense is drawn, includes the following steps:
A, aluminium sheet is cut: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and is carried out using cutting machine to aluminium sheet
Cutting processing, by aluminium sheet preparatory processing to required size;
B, it polishes: is beaten using aluminium sheet sander the surface of aluminum plate after cutting, side, edges and corners are completed in a step
Mill processing guarantees that surface of aluminum plate bright degree is high, remains without flash, non-oxidation;
C, pretreatment cleaning: to via the b step, treated that aluminium sheet cleans, cleaning process are as follows: first to aluminium sheet into
Row ungrease treatment removes the greasy dirt of surface of aluminum plate by alkaline degreaser, rinses the degreasing of surface of aluminum plate after degreasing with tap water
Liquid, rinse bath are designed as circulating water cleaning, avoid secondary pollution;
D, it dries: being dried using industrial microwave oven drying machine to via the aluminium sheet after step c cleaning, guarantee aluminium sheet table
Face noresidue, without washmarking;
E, it sprays: by the surface of aluminum plate spray-applied primer after being dried in the Step d;
F, a high-temperature baking: high-temperature baking will be carried out by the aluminium sheet for completing spraying in the step e, guarantees spray painting close attachment
On the surface of aluminium sheet, avoid falling off;
G, it vacuumizes thermal transfer processing: carrying out vacuumizing thermal transfer to by the aluminium sheet after progress high-temperature baking in the f step
Required pattern, is fixed on the surface of aluminium sheet by reason;
H, uv is printed: being printed to via the aluminium sheet after g step processing, without making a plate, one-step print is completed, and is made
Aluminium sheet pattern color after the g step process is beautiful abundant, wear-resistant, antiultraviolet;
I, required traditional Chinese Painting or other colour images the drafting of traditional Chinese Painting or other colour images: are plotted to the h step
On treated finished product, the basic drafting operation of works is completed;
J, it sprays Lacquer finish: carrying out coating hood light processing to via the finished product after the i step process, can protect table of the invention
Complexion paint layer, applique improve top coat layer gloss and dicoration;
K, secondary high-temperature toasts: will carry out secondary high-temperature baking by the finished product after j step processing, guarantees the drying of finished product
Property, avoids that deformation occurs;
L, it finally frames up: frame will be tumbled in by the finished surface after processing in the k step, complete final assembly of the invention and make
Industry.
Further, in a step, cutting processing is carried out to aluminium sheet using laser cutting machine, guarantees that notch is smooth, protects
Aluminium sheet is demonstrate,proved without bending and notch.
Further, in the step c, the detergent that cleaning aluminium sheet uses is alkaline detergent.
Further, in the Step d, the temperature of drying is maintained at 90-95 DEG C, drying time 15-30min.
Further, in the step e, spray painting uses powder spray, and average film thickness is 40-60 μm.
Further, in the f step, a high-temperature baking temperature is 200-250 DEG C, and the baking duration is 30-
35min。
Further, in the k step, secondary high-temperature baking temperature is 150-200 DEG C, and the baking duration is 10-
15min。
Further, in the l step, external installation frame is mounted together with aluminium sheet interference fit.
The beneficial effects of the present invention are: the present invention is using metal as material, and using wood grain as background color, book is carried out on wood grain
It writes or local printing by setting off for wood grain background color allows entire picture to seem graceful, it is pure and fresh free from vulgarity, give a kind of ear of people
Mesh one is new, the same impression of poem, and with the breath of dense Chinese traditional culture in 5000, so that there have entire product to be dense
Artistic feeling allows entire decoration space to be filled with art atmosphere and cultural spirit everywhere, to set off out the high-end grade of owner
With culture.
Specific embodiment
Embodiment one:
A kind of production method that metal wood sense is drawn, includes the following steps:
A, aluminium sheet is cut: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and is carried out using cutting machine to aluminium sheet
Cutting processing, by aluminium sheet preparatory processing to required size;
B, it polishes: is beaten using aluminium sheet sander the surface of aluminum plate after cutting, side, edges and corners are completed in a step
Mill processing guarantees that surface of aluminum plate bright degree is high, remains without flash, non-oxidation;
C, pretreatment cleaning: to via the b step, treated that aluminium sheet cleans, cleaning process are as follows: first to aluminium sheet into
Row ungrease treatment removes the greasy dirt of surface of aluminum plate by alkaline degreaser, rinses the degreasing of surface of aluminum plate after degreasing with tap water
Liquid, rinse bath are designed as circulating water cleaning, avoid secondary pollution;
D, it dries: being dried using industrial microwave oven drying machine to via the aluminium sheet after step c cleaning, guarantee aluminium sheet table
Face noresidue, without washmarking;
E, it sprays: by the surface of aluminum plate spray-applied primer after being dried in the Step d;
F, a high-temperature baking: high-temperature baking will be carried out by the aluminium sheet for completing spraying in the step e, guarantees spray painting close attachment
On the surface of aluminium sheet, avoid falling off;
G, it vacuumizes thermal transfer processing: carrying out vacuumizing thermal transfer to by the aluminium sheet after progress high-temperature baking in the f step
Required pattern, is fixed on the surface of aluminium sheet by reason;
H, uv is printed: being printed to via the aluminium sheet after g step processing, without making a plate, one-step print is completed, and is made
Aluminium sheet pattern color after the g step process is beautiful abundant, wear-resistant, antiultraviolet;
I, required traditional Chinese Painting or other colour images the drafting of traditional Chinese Painting or other colour images: are plotted to the h step
On treated finished product, the basic drafting operation of works is completed;
J, it sprays Lacquer finish: carrying out coating hood light processing to via the finished product after the i step process, can protect table of the invention
Complexion paint layer, applique improve top coat layer gloss and dicoration;
K, secondary high-temperature toasts: will carry out secondary high-temperature baking by the finished product after j step processing, guarantees the drying of finished product
Property, avoids that deformation occurs;
L, it finally frames up: frame will be tumbled in by the finished surface after processing in the k step, complete final assembly of the invention and make
Industry.
In the present embodiment, in a step, cutting processing is carried out to aluminium sheet using laser cutting machine, guarantees that notch is smooth,
Guarantee aluminium sheet without bending and notch.
In the present embodiment, in the step c, the detergent that cleaning aluminium sheet uses is alkaline detergent.
In the present embodiment, in the Step d, the temperature of drying is maintained at 90 DEG C, drying time 15min.
In the present embodiment, in the step e, spray painting uses powder spray, and average film thickness is 40 μm.
In the present embodiment, in the f step, a high-temperature baking temperature is 200 DEG C, and the baking duration is 30min.
In the present embodiment, in the k step, secondary high-temperature baking temperature is 150 DEG C, and the baking duration is 10min.
In the present embodiment, in the l step, external installation frame is mounted together with aluminium sheet interference fit.
Embodiment two:
A kind of production method that metal wood sense is drawn, includes the following steps:
A, aluminium sheet is cut: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and is carried out using cutting machine to aluminium sheet
Cutting processing, by aluminium sheet preparatory processing to required size;
B, it polishes: is beaten using aluminium sheet sander the surface of aluminum plate after cutting, side, edges and corners are completed in a step
Mill processing guarantees that surface of aluminum plate bright degree is high, remains without flash, non-oxidation;
C, pretreatment cleaning: to via the b step, treated that aluminium sheet cleans, cleaning process are as follows: first to aluminium sheet into
Row ungrease treatment removes the greasy dirt of surface of aluminum plate by alkaline degreaser, rinses the degreasing of surface of aluminum plate after degreasing with tap water
Liquid, rinse bath are designed as circulating water cleaning, avoid secondary pollution;
D, it dries: being dried using industrial microwave oven drying machine to via the aluminium sheet after step c cleaning, guarantee aluminium sheet table
Face noresidue, without washmarking;
E, it sprays: by the surface of aluminum plate spray-applied primer after being dried in the Step d;
F, a high-temperature baking: high-temperature baking will be carried out by the aluminium sheet for completing spraying in the step e, guarantees spray painting close attachment
On the surface of aluminium sheet, avoid falling off;
G, it vacuumizes thermal transfer processing: carrying out vacuumizing thermal transfer to by the aluminium sheet after progress high-temperature baking in the f step
Required pattern, is fixed on the surface of aluminium sheet by reason;
H, uv is printed: being printed to via the aluminium sheet after g step processing, without making a plate, one-step print is completed, and is made
Aluminium sheet pattern color after the g step process is beautiful abundant, wear-resistant, antiultraviolet;
I, required traditional Chinese Painting or other colour images the drafting of traditional Chinese Painting or other colour images: are plotted to the h step
On treated finished product, the basic drafting operation of works is completed;
J, it sprays Lacquer finish: carrying out coating hood light processing to via the finished product after the i step process, can protect table of the invention
Complexion paint layer, applique improve top coat layer gloss and dicoration;
K, secondary high-temperature toasts: will carry out secondary high-temperature baking by the finished product after j step processing, guarantees the drying of finished product
Property, avoids that deformation occurs;
L, it finally frames up: frame will be tumbled in by the finished surface after processing in the k step, complete final assembly of the invention and make
Industry.
In the present embodiment, in a step, cutting processing is carried out to aluminium sheet using laser cutting machine, guarantees that notch is smooth,
Guarantee aluminium sheet without bending and notch.
In the present embodiment, in the step c, the detergent that cleaning aluminium sheet uses is alkaline detergent.
In the present embodiment, in the Step d, the temperature of drying is maintained at 93 DEG C, drying time 20min.
In the present embodiment, in the step e, spray painting uses powder spray, and average film thickness is 45 μm.
In the present embodiment, in the f step, a high-temperature baking temperature is 220 DEG C, and the baking duration is 33min.
In the present embodiment, in the k step, secondary high-temperature baking temperature is 180 DEG C, and the baking duration is 10min.
In the present embodiment, in the l step, external installation frame is mounted together with aluminium sheet interference fit.
Embodiment three:
A kind of production method that metal wood sense is drawn, includes the following steps:
A, aluminium sheet is cut: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and is carried out using cutting machine to aluminium sheet
Cutting processing, by aluminium sheet preparatory processing to required size;
B, it polishes: is beaten using aluminium sheet sander the surface of aluminum plate after cutting, side, edges and corners are completed in a step
Mill processing guarantees that surface of aluminum plate bright degree is high, remains without flash, non-oxidation;
C, pretreatment cleaning: to via the b step, treated that aluminium sheet cleans, cleaning process are as follows: first to aluminium sheet into
Row ungrease treatment removes the greasy dirt of surface of aluminum plate by alkaline degreaser, rinses the degreasing of surface of aluminum plate after degreasing with tap water
Liquid, rinse bath are designed as circulating water cleaning, avoid secondary pollution;
D, it dries: being dried using industrial microwave oven drying machine to via the aluminium sheet after step c cleaning, guarantee aluminium sheet table
Face noresidue, without washmarking;
E, it sprays: by the surface of aluminum plate spray-applied primer after being dried in the Step d;
F, a high-temperature baking: high-temperature baking will be carried out by the aluminium sheet for completing spraying in the step e, guarantees spray painting close attachment
On the surface of aluminium sheet, avoid falling off;
G, it vacuumizes thermal transfer processing: carrying out vacuumizing thermal transfer to by the aluminium sheet after progress high-temperature baking in the f step
Required pattern, is fixed on the surface of aluminium sheet by reason;
H, uv is printed: being printed to via the aluminium sheet after g step processing, without making a plate, one-step print is completed, and is made
Aluminium sheet pattern color after the g step process is beautiful abundant, wear-resistant, antiultraviolet;
I, required traditional Chinese Painting or other colour images the drafting of traditional Chinese Painting or other colour images: are plotted to the h step
On treated finished product, the basic drafting operation of works is completed;
J, it sprays Lacquer finish: carrying out coating hood light processing to via the finished product after the i step process, can protect table of the invention
Complexion paint layer, applique improve top coat layer gloss and dicoration;
K, secondary high-temperature toasts: will carry out secondary high-temperature baking by the finished product after j step processing, guarantees the drying of finished product
Property, avoids that deformation occurs;
L, it finally frames up: frame will be tumbled in by the finished surface after processing in the k step, complete final assembly of the invention and make
Industry.
In the present embodiment, in a step, cutting processing is carried out to aluminium sheet using laser cutting machine, guarantees that notch is smooth,
Guarantee aluminium sheet without bending and notch.
In the present embodiment, in the step c, the detergent that cleaning aluminium sheet uses is alkaline detergent.
In the present embodiment, in the Step d, the temperature of drying is maintained at 95 DEG C, drying time 25min.
In the present embodiment, in the step e, spray painting uses powder spray, and average film thickness is 50 μm.
In the present embodiment, in the f step, a high-temperature baking temperature is 250 DEG C, and the baking duration is 35min.
In the present embodiment, in the k step, secondary high-temperature baking temperature is 200 DEG C, and the baking duration is 15min.
In the present embodiment, in the l step, external installation frame is mounted together with aluminium sheet interference fit.
Example IV:
A kind of production method that metal wood sense is drawn, includes the following steps:
A, aluminium sheet is cut: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and is carried out using cutting machine to aluminium sheet
Cutting processing, by aluminium sheet preparatory processing to required size;
B, it polishes: is beaten using aluminium sheet sander the surface of aluminum plate after cutting, side, edges and corners are completed in a step
Mill processing guarantees that surface of aluminum plate bright degree is high, remains without flash, non-oxidation;
C, pretreatment cleaning: to via the b step, treated that aluminium sheet cleans, cleaning process are as follows: first to aluminium sheet into
Row ungrease treatment removes the greasy dirt of surface of aluminum plate by alkaline degreaser, rinses the degreasing of surface of aluminum plate after degreasing with tap water
Liquid, rinse bath are designed as circulating water cleaning, avoid secondary pollution;
D, it dries: being dried using industrial microwave oven drying machine to via the aluminium sheet after step c cleaning, guarantee aluminium sheet table
Face noresidue, without washmarking;
E, it sprays: by the surface of aluminum plate spray-applied primer after being dried in the Step d;
F, a high-temperature baking: high-temperature baking will be carried out by the aluminium sheet for completing spraying in the step e, guarantees spray painting close attachment
On the surface of aluminium sheet, avoid falling off;
G, it vacuumizes thermal transfer processing: carrying out vacuumizing thermal transfer to by the aluminium sheet after progress high-temperature baking in the f step
Required pattern, is fixed on the surface of aluminium sheet by reason;
H, uv is printed: being printed to via the aluminium sheet after g step processing, without making a plate, one-step print is completed, and is made
Aluminium sheet pattern color after the g step process is beautiful abundant, wear-resistant, antiultraviolet;
I, required traditional Chinese Painting or other colour images the drafting of traditional Chinese Painting or other colour images: are plotted to the h step
On treated finished product, the basic drafting operation of works is completed;
J, it sprays Lacquer finish: carrying out coating hood light processing to via the finished product after the i step process, can protect table of the invention
Complexion paint layer, applique improve top coat layer gloss and dicoration;
K, secondary high-temperature toasts: will carry out secondary high-temperature baking by the finished product after j step processing, guarantees the drying of finished product
Property, avoids that deformation occurs;
L, it finally frames up: frame will be tumbled in by the finished surface after processing in the k step, complete final assembly of the invention and make
Industry.
In the present embodiment, in a step, cutting processing is carried out to aluminium sheet using laser cutting machine, guarantees that notch is smooth,
Guarantee aluminium sheet without bending and notch.
In the present embodiment, in the step c, the detergent that cleaning aluminium sheet uses is alkaline detergent.
In the present embodiment, in the Step d, the temperature of drying is maintained at 95 DEG C, drying time 30min.
In the present embodiment, in the step e, spray painting uses powder spray, and average film thickness is 60 μm.
In the present embodiment, in the f step, a high-temperature baking temperature is 250 DEG C, and the baking duration is 35min.
In the present embodiment, in the k step, secondary high-temperature baking temperature is 200 DEG C, and the baking duration is 15min.
In the present embodiment, in the l step, external installation frame is mounted together with aluminium sheet interference fit.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, and the above embodiments and description only describe originals of the invention
Reason, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes and improvements
It all fall within the protetion scope of the claimed invention.
Claims (8)
1. the production method that a kind of metal wood sense is drawn, characterized by the following steps:
A, aluminium sheet is cut: selection aluminium sheet of the surface without obvious scratch, aluminium sheet model 7075, and is carried out using cutting machine to aluminium sheet
Cutting processing, by aluminium sheet preparatory processing to required size;
B, it polishes: is beaten using aluminium sheet sander the surface of aluminum plate after cutting, side, edges and corners are completed in a step
Mill processing guarantees that surface of aluminum plate bright degree is high, remains without flash, non-oxidation;
C, pretreatment cleaning: to via the b step, treated that aluminium sheet cleans, cleaning process are as follows: first to aluminium sheet into
Row ungrease treatment removes the greasy dirt of surface of aluminum plate by alkaline degreaser, rinses the degreasing of surface of aluminum plate after degreasing with tap water
Liquid, rinse bath are designed as circulating water cleaning, avoid secondary pollution;
D, it dries: being dried using industrial microwave oven drying machine to via the aluminium sheet after step c cleaning, guarantee aluminium sheet table
Face noresidue, without washmarking;
E, it sprays: by the surface of aluminum plate spray-applied primer after being dried in the Step d;
F, a high-temperature baking: high-temperature baking will be carried out by the aluminium sheet for completing spraying in the step e, guarantees spray painting close attachment
On the surface of aluminium sheet, avoid falling off;
G, it vacuumizes thermal transfer processing: carrying out vacuumizing thermal transfer to by the aluminium sheet after progress high-temperature baking in the f step
Required pattern, is fixed on the surface of aluminium sheet by reason;
H, uv is printed: being printed to via the aluminium sheet after g step processing, without making a plate, one-step print is completed, and is made
Aluminium sheet pattern color after the g step process is beautiful abundant, wear-resistant, antiultraviolet;
I, required traditional Chinese Painting or other colour images the drafting of traditional Chinese Painting or other colour images: are plotted to the h step
On treated finished product, the basic drafting operation of works is completed;
J, it sprays Lacquer finish: carrying out coating hood light processing to via the finished product after the i step process, can protect table of the invention
Complexion paint layer, applique improve top coat layer gloss and dicoration;
K, secondary high-temperature toasts: will carry out secondary high-temperature baking by the finished product after j step processing, guarantees the drying of finished product
Property, avoids that deformation occurs;
L, it finally frames up: frame will be tumbled in by the finished surface after processing in the k step, complete final assembly of the invention and make
Industry.
2. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: in a step, use
Laser cutting machine carries out cutting processing to aluminium sheet, guarantees that notch is smooth, guarantees aluminium sheet without bending and notch.
3. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: in the step c, cleaning
The detergent that aluminium sheet uses is alkaline detergent.
4. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: in the Step d, drying
Temperature be maintained at 90-95 DEG C, drying time 15-30min.
5. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: in the step e, spray painting
Using powder spray, average film thickness is 40-60 μm.
6. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: in the f step, once
High-temperature baking temperature is 200-250 DEG C, and the baking duration is 30-35min.
7. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: secondary in the k step
High-temperature baking temperature is 150-200 DEG C, and the baking duration is 10-15min.
8. the production method that a kind of metal wood sense according to claim 1 is drawn, it is characterised in that: external in the l step
Installation frame is mounted together with aluminium sheet interference fit.