CN101088781A

CN101088781A - Process of making glass etching and silver plating ornament picture

Info

Publication number: CN101088781A
Application number: CNA2006100318537A
Authority: CN
Inventors: 李建保
Original assignee: Individual
Current assignee: Individual
Priority date: 2006-06-18
Filing date: 2006-06-18
Publication date: 2007-12-19

Abstract

The glass etching and silver plating ornament picture is made on glass carrier and through the technological process includes the steps of picture design, white-and-black film making, silk screen photosensitizing plate making, printing with anticorrosive ink, soaking in etching solution, washing, silver plating, sealing with lacquer, framing, etc. The picture making process is simple, fast, low in cost and suitable for mechanical production, and the glass etching and silver plating ornament picture has excellent visual effect and strong stereo feeling, and may be used as decoration in household, hotel, etc.

Description

A kind of method of making glass etching and silver plating ornament picture

[technical field] the present invention relates to a kind of preparation method of Glass Craft, is a kind of method of making glass etching and silver plating ornament picture specifically.

[background technology] is present, and the reception room of constituent parts, meeting room, office and family generally all are provided with decoration painting, in order to increase serious, graceful, the create an aesthetic feeling of its occasion.Currently marketed decoration be decorated with lacquer painting, copperplate etching, woodcut, ceramic drawing, on glass with lacquer draw a picture, glass sand carve and paint etc., but up to the present also do not find to do the glass etching and silver plating decoration painting of carrier with glass.And the glass etching and silver plating decoration painting, lifelike image, svelteness, elegance, third dimension is strong.A lot of art workers wish to find a kind of method of making this glass etching and silver plating ornament picture, produce more more beautiful glass etching and silver plating ornament pictures, to satisfy the ever-increasing aesthetic feeling demand of people.

The kind in [summary of the invention] horn of plenty art work market, improve the quality class of glass decoration picture, the purpose of this invention is to provide a kind of method of making glass etching and silver plating ornament picture, the art worker can produce in enormous quantities solemnly, graceful, glass etching and silver plating ornament picture that aesthetic feeling is good so that make, and satisfies people's culture life and the artistic market demand to high-grade glass etching silver plating ornament picture.

For solving its technical problem, the technical solution adopted in the present invention is: the preparation method of this glass etching and silver plating ornament picture comprises the steps:

1. cut blocks for printing: required image is scribed with engraving machine or be made by handwork black and white paper or film film, made the silk screen version by silk screen sensitization then;

2. serigraphy: the silk screen version of image will be arranged, be printed on certain one side of transparency glass plate, by serigraphy through air dry in 40～50 hours with corrosion-resistanting ink;

3. glass etching: will be printed on the glass of screen image, and be placed in the corrosion liquid pool that 55 degree hydrofluoric acid add 50% water and soaked 30～60 minutes;

4. clean:,, rinse well with clear water then and dry earlier with 5% sodium hydroxide solution immersion 5～8 minutes with the etched glass plate that image is arranged;

5. silver-plated: as with mechanical or manual etching to be had the face glass of image indenture, plate mercury or aluminize and get final product;

6. primer spray: with the image of silver coated or aluminium lamination, spraying one deck priming paint or multiple colored lacquer, in order to sealing and decorative picture, anti-oxidation.

7. frame up: will be through etching, silver-plated, glass plate after spraying paint, level and smooth one side is positive, it is the back side that the one side of image indenture and silver coating is arranged, and loads onto metal or wooden picture frame is finished product.

The beneficial effects of the utility model are: 1. because the present invention adopts serigraphy on glass plate image, carry out pickling etching, silver-plated then, with comparing of past with silver plating mirror plating word, the prepared image complexity of the present invention, exquisiteness, svelteness grace, exquisiteness, third dimension is strong, be adapted at glass etching and comprise picture, mural painting, figure painting, landscape painting, flower-and-bird painting, this decoration painting mainly plays decoration function with the lines daring and resolution, can enrich the kind of decoration painting.

2. be carrier because of the present invention adopts glass, the transparency of utilizing glass with silver-plated brightness set off mutually, make picture lines, indenture seem bright especially, has very strong visual impact, can make the lines of Chinese painting (simple, straight-forward style of writing) embodying incisively and vividly picture reach a kind of very high artistic state.

3. because method of the present invention all can adopt machine and manual the cooperation to complete, therefore become picture speed fast, product cost is low, is fit to produce in enormous quantities.

[specific embodiment] the present invention is further described below in conjunction with embodiment.

Embodiment 1: the production method of tempering glass carved art picture, it comprises the steps:

The glass that 1. will be used for the handicraft picture carrier carries out tempering, to increase strength of glass, prevents breakage;

2. with the picture proof of handicraft picture, be printed on the safety glass with screen process press;

3. will be printed on the armorplate glass of handicraft picture, and be immersed in 55 degree hydrofluoric acid and add in the pond of corrosive liquid of water 50%, soak time is 30～60 minutes;

4. clean: the armorplate glass elder generation after soaking soaked 5 minutes with 5% sodium hydroxide solution, rinsed well with clear water and dried;

5. silver-plated: as the on glass of image indenture to be arranged by acid corrosion, aluminizing or silver-plated with the vacuum machine;

6. the imaging surface of silver or aluminium lamination is arranged in spraying plating, spray one deck protective paint again;

7. frame up: make picture frame with metal or timber, the front of picture frame is the glass surface of etching not, and the back side of picture frame is also established one deck baffle for cross and be sprayed with the glass another side of protective paint through etching at the back side of picture frame.

Embodiment 2: on the etching glass figure, use the traditional-handwork silver-coating method, it comprises the steps:

1. image draft design: with required image picture computer engraving machine, engraving is made black and white paper, also can be made into film film;

2. screen printing: with 200～300 purpose terylene silk nets with canopy net machine or manual canopy net on framework, in the darkroom, the silk screen that cleans up is scraped the last layer photoresists uniformly, again the image draft or the film are layered on the photoresists, with ultraviolet lamp box sensitization 8～12 minutes, flushing was dried stand-by then;

3. serigraphy: on smooth print station, the silk screen plate after the sensitization is layered on need draw a picture on glass, corrosion-resistanting ink is scraped on glass plate equably air dry through silk screen plate with scraper through 40～50 hours;

4. glass etching: in the anticorrosion pond of plastics, the corrosive liquid of the glass plate of scraping printing ink being put into 55 degree hydrofluoric acid and adding water 50% soaked 50 minutes;

5. clean: will glass plate take out earlier with 5% sodium hydroxide solution immersion 5 minutes, rinse well with clear water again and dry through soaking;

6. silver-plated: after adding water 500 gram dissolvings with stannous chloride 3 grams earlier, need wash with the glass picture, to be plated with aquae destillata flushing one time again, add aquae destillata 600 grams by every square metre of picture with the sour silver of 3 gram pins and mix 50 milliliters in back repeated hydrogenation sodium oxide molybdena 1 gram, water, add ammoniacal liquor 1.5cc again silver nitrate is dissolved into transparency liquid fully, add glucose solution then, and to the glass picture of horizontal positioned, after 20 minutes the mercury outside the picture is removed, dried and get final product;

7. primer spray: with anti-oxidation mirror finish sprayed protection, or with 150 degree temperature mirror baking vanish protections;

8. finished product is decorated: the picture behind silver-plated, the stop-off lacquer is framed up, picture is viewed and admired as decorative picture conversely.

Claims

1, a kind of method of making glass etching and silver plating ornament picture is characterized in that it comprises the steps:

2, method according to claim 1, it is characterized in that: described screen printing be with 200～300 purpose terylene silk nets with canopy net machine or manual canopy net on framework, in the darkroom, the silk screen that cleans up is scraped the last layer photoresists uniformly, again the image draft or the film are layered on the photoresists, with ultraviolet lamp box sensitization 8～12 minutes, flushing was dried stand-by then.

3, method according to claim 1, it is characterized in that: described serigraphy is on smooth print station, silk screen plate after the sensitization is layered on need draw a picture on glass, corrosion-resistanting ink is scraped on glass plate equably air dry through silk screen plate with scraper through 40～50 hours.

4, method according to claim 1, it is characterized in that: described craft is silver-plated to be after adding water 500 gram dissolvings with stannous chloride 3 grams earlier, need wash with the glass picture, to be plated with aquae destillata flushing one time again, add aquae destillata 600 grams by every square metre of picture with the sour silver of 3 gram pins and mix 50 milliliters in back repeated hydrogenation sodium oxide molybdena 1 gram, water, add ammoniacal liquor 1.5cc again silver nitrate is dissolved into transparency liquid fully, add glucose solution then, and to the glass picture of horizontal positioned, after 20 minutes the mercury outside the picture is removed, dried and get final product.