CN106094430A - A kind of vacuum aluminum-coated device for forming pattern and operational approach thereof - Google Patents
A kind of vacuum aluminum-coated device for forming pattern and operational approach thereof Download PDFInfo
- Publication number
- CN106094430A CN106094430A CN201610704940.8A CN201610704940A CN106094430A CN 106094430 A CN106094430 A CN 106094430A CN 201610704940 A CN201610704940 A CN 201610704940A CN 106094430 A CN106094430 A CN 106094430A
- Authority
- CN
- China
- Prior art keywords
- pattern
- curved baffle
- film
- vacuum aluminum
- netted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of vacuum aluminum-coated device for forming pattern and operational approach thereof, including laser photocomposing machine, ultraviolet silk-screen printer, netted curved baffle and vacuum aluminum-plating machine, laser photocomposing machine is for making the Fei Er film of required transparent pattern, netted curved baffle uses exotic material, its surface-coated has extraordinary photosensitive material, Fei Er film plaster is attached on netted curved baffle, ultraviolet silk-screen printer is for being just exposed Fei Er film, the extraordinary photosensitive resin being attached on netted curved baffle is solidify to form pattern, aluminize under cylinder by what the figuratum netted curved baffle of tool was placed in vacuum aluminum-plating machine, the just vacuum aluminum ion chamber to lower section.The present invention uses the pattern web plate of making to be placed in vacuum aluminum-plating machine to carry out pattern and aluminize, and each equipment of employing is simple, and cost of manufacture is low, and plant maintenance is convenient, and maintenance cost is low, and the present invention also has simple in construction, feature convenient to operation.
Description
Technical field
The present invention relates to a kind of vacuum aluminum-coated device for forming pattern and operational approach thereof, belong to vacuum aluminum-coated printing
Equipment technical field.
Background technology
In existing vacuum aluminum-coated pattern typography, special equipment is usually used to carry out pattern making of aluminizing, its equipment
Expensive, cost of manufacture is high, and cost of equipment maintenance is high.
Summary of the invention
The technical problem to be solved in the present invention is: provide a kind of vacuum aluminum-coated device for forming pattern and operation side thereof
Method, equipment is simple, and cost of manufacture is low, and plant maintenance is convenient, and maintenance cost is low, to solve problems of the prior art.
The technical scheme that the present invention takes is: a kind of vacuum aluminum-coated device for forming pattern, including laser photocomposing machine,
Ultraviolet silk-screen printer, netted curved baffle and vacuum aluminum-plating machine, laser photocomposing machine is for making the phenanthrene of required black and white pattern
Woods film, netted curved baffle uses exotic material, and its surface-coated has extraordinary sensitive material, film film plaster to be attached to netted
On curved baffle, ultraviolet silk-screen printer, for being just exposed film film, will be attached on netted curved baffle
Extraordinary sensitive material solidify to form pattern, and will lose at light and rinse out, and figuratum for tool netted curved baffle is placed in vacuum
Aluminize under cylinder in aluminum-spraying machine, the just vacuum aluminum ion chamber to lower section.
Preferably, above-mentioned netted curved baffle uses resistant to elevated temperatures steel wire to be made, and between its steel wire, spacing is 0.2-
0.25mm。
A kind of operational approach of the vacuum aluminum-coated device for forming pattern, the method comprises the following steps:
(1) pattern film production: use the required pattern made of laser photocomposing machine input, produce the film glue of black and white pattern
Sheet；
(2) netted curved baffle makes: coating spy on the netted curved baffle using steel wire diameter to be 0.2-0.25mm making
Planting sensitive material material, sensitive material coating thickness is 0.3mm；
(3) film film of the band transparent pattern in step (1) is fitted on netted curved baffle, use ultraviolet silk-screen to shine
Film film is exposed by version eedle, and after exposure, solidification at light is shown in by the extraordinary sensitive material on netted curved baffle, loses light
Place rinses out, it is thus achieved that with the netted curved baffle penetrating pattern；
(4) aluminize under cylinder by be installed in vacuum aluminum-plating machine with figuratum netted curved baffle, start vacuum aluminum-plating machine,
Aluminum, under heating in vacuum, becomes aluminium ion after being heated to design temperature, opens the baffle plate on aluminium ion chamber, and aluminium ion is upwards
Volatilization, penetrates pattern position, thus forms, aluminizing, pattern of aluminizing on figure base material.
Beneficial effects of the present invention: compared with prior art, the present invention uses the pattern web plate of making to be placed in vacuum aluminum-coated
Carrying out pattern in machine to aluminize, each equipment of employing is simple, and cost of manufacture is low, and plant maintenance is convenient, and maintenance cost is low, efficient solution
The problem that present in prior art of having determined, equipment auxiliary, cost of manufacture height, plant maintenance inconvenience and maintenance cost are high, the present invention
Also there is simple in construction, feature convenient to operation.
Accompanying drawing explanation
Fig. 1 is the process structure schematic diagram of the present invention；
Fig. 2 is the film exposure apparatus structure schematic diagram of the present invention；
Fig. 3 is the vacuum aluminum-plating machine netted curved baffle junction structural representation of the present invention.
In figure, 1-laser photocomposing machine, 2-ultraviolet silk-screen printer, the netted curved baffle of 3-, 4-vacuum aluminum-plating machine, 5-is luxuriant and rich with fragrance
Your film, 6-aluminizes cylinder, 7-vacuum aluminum ion chamber, 8-baffle plate.
Detailed description of the invention
Below in conjunction with the accompanying drawings and the present invention is described further by specific embodiment.
Embodiment 1: as shown in Figure 1-Figure 3, a kind of vacuum aluminum-coated device for forming pattern, including laser photocomposing machine 1,
Ultraviolet silk-screen printer 2, netted curved baffle 3 and vacuum aluminum-plating machine 4, laser photocomposing machine 1 is used for making required transparent pattern
Film film 5, netted curved baffle 3 uses exotic material, and its surface-coated has extraordinary sensitive material, film film 5 to paste
Being attached on netted curved baffle 3, ultraviolet silk-screen printer 2, for being just exposed film film 5, will be attached to netted song
Light partially cured formation pattern is shown in by extraordinary sensitive material on face baffle plate 3, and will lose at light and rinse out, and will have figuratum net
What shape curved baffle 3 was placed in vacuum aluminum-plating machine 4 aluminize cylinder 6 times, the just vacuum aluminum ion chamber 7 to lower section.
Preferably, above-mentioned netted curved baffle 3 uses resistant to elevated temperatures steel wire to be made, and between its steel wire, spacing is 0.2-
0.25mm。
Embodiment 2: the operational approach of a kind of vacuum aluminum-coated device for forming pattern, the method comprises the following steps:
(1) pattern film production: use the required pattern made of laser photocomposing machine input, produce the film glue of black and white pattern
Sheet；
(2) netted curved baffle makes: coating spy on the netted curved baffle using steel wire diameter to be 0.2-0.25mm making
Planting photosensitive material, photosensitive resin coating thickness is 0.3mm；
(3) film film of the band black and white pattern in step (1) is fitted on netted curved baffle, use ultraviolet silk-screen to shine
Film film is exposed by version eedle, and after exposure, solidification at light is shown in by the extraordinary sensitive material on netted curved baffle, loses light
Place rinses out, it is thus achieved that with the netted curved baffle penetrating pattern；
(4) aluminize under cylinder by be installed in vacuum aluminum-plating machine with figuratum netted curved baffle, start vacuum aluminum-plating machine,
Aluminum, under heating in vacuum, becomes aluminium ion after being heated to design temperature, opens the baffle plate on aluminium ion chamber, and aluminium ion is upwards
Volatilization, penetrates pattern position, thus forms, aluminizing, pattern of aluminizing on figure base material.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
Those familiar with the art, in the technical scope that the invention discloses, can readily occur in change or replace, should contain
Covering within protection scope of the present invention, therefore, protection scope of the present invention should be as the criterion with described scope of the claims.
Claims (3)
1. the vacuum aluminum-coated device being used for forming pattern, it is characterised in that: include laser photocomposing machine (1), ultraviolet silk-screen
Printer (2), netted curved baffle (3) and vacuum aluminum-plating machine (4), laser photocomposing machine (1) is for making required black and white pattern
Film film (5), netted curved baffle (3) uses exotic material, and its surface-coated has extraordinary sensitive material, film film
(5) being attached on netted curved baffle (3), ultraviolet silk-screen printer (2), will for being just exposed film film (5)
The extraordinary sensitive material being attached on netted curved baffle (3) solidify to form pattern, and will lose at light and rinse out, and will have figure
The netted curved baffle (3) of case is placed under the cylinder of aluminizing (6) in vacuum aluminum-plating machine (4), just the vacuum aluminum ion chamber to lower section
(7).
A kind of vacuum aluminum-coated device for forming pattern the most according to claim 1, it is characterised in that: netted curved surface keeps off
Plate (3) uses resistant to elevated temperatures steel wire to be made, and between its steel wire, spacing is 0.2-0.25mm.
3., according to the operational approach of the arbitrary described a kind of vacuum aluminum-coated device for forming pattern of claim 1-2, it is special
Levy and be: the method comprises the following steps:
(1) pattern film production: use the required pattern made of laser photocomposing machine input, produce the film glue of black and white pattern
Sheet；
(2) netted curved baffle makes: coating spy on the netted curved baffle using steel wire diameter to be 0.2-0.25mm making
Planting sensitive material, sensitive material coating thickness is 0.3mm；
(3) film film of the band black and white pattern in step (1) is fitted on netted curved baffle, use ultraviolet silk-screen to shine
Film film is exposed by version eedle, and after exposure, the extraordinary photosensitive material on netted curved baffle is shown in solidification at light, no
See and rinse out at light, it is thus achieved that with the netted curved baffle penetrating pattern；
(4) aluminize under cylinder by be installed in vacuum aluminum-plating machine with figuratum netted curved baffle, start vacuum aluminum-plating machine,
Aluminum, under heating in vacuum, becomes aluminium ion after being heated to design temperature, opens the baffle plate on aluminium ion chamber, and aluminium ion is upwards
Volatilization, penetrates pattern position, thus forms, aluminizing, pattern of aluminizing on figure base material.