CN107499052A - A kind of preparation method of roller coat pattern aluminum sheet - Google Patents
A kind of preparation method of roller coat pattern aluminum sheet Download PDFInfo
- Publication number
- CN107499052A CN107499052A CN201710910767.1A CN201710910767A CN107499052A CN 107499052 A CN107499052 A CN 107499052A CN 201710910767 A CN201710910767 A CN 201710910767A CN 107499052 A CN107499052 A CN 107499052A
- Authority
- CN
- China
- Prior art keywords
- preparation
- printed layer
- aluminum
- roller coat
- aluminum sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of roller coat pattern aluminum sheet, comprise the following steps that：(1) Aluminum sheets foil of the surface microstructure average area more than 1.0 square millimeters is produced；(2) Aluminum sheets foil is pre-processed, is sequentially cleaning, degreasing, passivation, cleaning, drying, cooling；(3) traction positioning is unreeled；(4) four stamps, four drying are carried out on aluminum strip passivation layer and are cooled into printed layer four times；(5) the transparent area enamelled coating of stamp is as above protected in printed layer；(6) winding traction positioning.The present invention by four printing operations, after in printed layer addition protection stamp top coat layer, both make it that product surface was bright and clean neat, it is also possible that decorative pattern is hardly damaged, floral designs are lively, have preferable beautifying and decorating to act on.
Description
Technical field
The present invention relates to a kind of preparation method of roller coat pattern aluminum sheet, belong to aluminium surface processing technology field.
Background technology
With the raising of living standard, people to the demand of material in addition to practicality, with greater need for pursue it is attractive in appearance and
Enjoy the life of high-quality.Aluminium and its aluminum alloy materials are widely used in the curtain wall of building, interior wall, furred ceiling, buckle, door
Many aspects such as window, column, it is also used for the shell of various household electrical appliance, equipment, instrument, instrument, bin etc..At present, aluminium sheet table
The plane decorative pattern in face is all and manufactured, this plane figure colour list by Coating Processes or using nature pass schedule
One, outward appearance lacks aesthetic feeling, lacks diversity.
The content of the invention
The present invention is to solve the above problems, the invention provides a kind of preparation method of roller coat pattern aluminum sheet.Specific steps
It is as follows：(1) Aluminum sheets foil of the surface microstructure average area more than 1.0 square millimeters is produced；(2) Aluminum sheets foil is carried out
Pretreatment, is sequentially cleaning, degreasing, passivation, cleaning, drying, cooling；(3) traction positioning is unreeled；(4) in aluminum strip passivation layer
The upper stamp four times of progress four times, which is dried four times, is cooled into printed layer；(5) clear finish of stamp is as above protected in printed layer
Layer；(6) winding traction positioning.
The beneficial effects of the invention are as follows：The present invention by four printing operations, after in printed layer addition protection stamp
Top coat layer, both make it that product surface was bright and clean neat, it is also possible that decorative pattern is hardly damaged, floral designs are lively, there is preferable U.S.
Change decoration function.
Embodiment
A kind of preparation method of roller coat pattern aluminum sheet, comprises the following steps in order：
(1) Aluminum sheets foil of the surface microstructure average area more than 1.0 square millimeters is produced；
(2) Aluminum sheets foil is pre-processed, is sequentially cleaning, degreasing, passivation, cleaning, drying, cooling；
(3) traction positioning is unreeled；
(4) four stamps, four drying are carried out on aluminum strip passivation layer and are cooled into printed layer four times；
(5) the transparent area enamelled coating of stamp is as above protected in printed layer；
(6) winding traction positioning.
Specific embodiment described herein is only to spirit explanation for example of the invention.Technology belonging to the present invention is led
The technical staff in domain can be made various modifications or supplement to described specific embodiment or be replaced using similar mode
Generation, but without departing from the spiritual of the present invention or surmount scope defined in appended claims.
Claims (3)
1. a kind of preparation method of roller coat pattern aluminum sheet, it is characterised in that comprise the following steps that：(1) production surface microstructure is averaged
Aluminum sheets foil of the area more than 1.0 square millimeters；(2) Aluminum sheets foil is pre-processed, be sequentially cleaning, degreasing,
Passivation, cleaning, drying, cooling；(3) traction positioning is unreeled；(4) four stamps, four drying four are carried out on aluminum strip passivation layer
It is secondary to be cooled into printed layer；(5) the transparent area enamelled coating of stamp is as above protected in printed layer；(6) winding traction positioning.
2. the preparation method of a kind of roller coat pattern aluminum sheet according to claim 1, it is characterised in that described in step (4)
Printed layer thickness be 2-4 μm.
3. the preparation method of a kind of roller coat pattern aluminum sheet according to claim 1, it is characterised in that described in step (5)
Top coat layer thickness be 8-16 μm.