CN109371499A - A kind of plant modified dacron fabric and preparation method thereof - Google Patents
A kind of plant modified dacron fabric and preparation method thereof Download PDFInfo
- Publication number
- CN109371499A CN109371499A CN201811273783.5A CN201811273783A CN109371499A CN 109371499 A CN109371499 A CN 109371499A CN 201811273783 A CN201811273783 A CN 201811273783A CN 109371499 A CN109371499 A CN 109371499A
- Authority
- CN
- China
- Prior art keywords
- modified dacron
- parts
- modifying agent
- preparation
- plant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of plant modified dacron fabric and preparation method thereof, and raw material includes polyester resin, acid fiber by polylactic, modifying agent, polyester resin, acid fiber by polylactic, modifying agent mass ratio be 80-100:24-27:4-4.8.Modifying agent is mixed with by plant extracts, glutathione, chitin, linseed oil according to 5:3:2:9；Plant extracts is the one or more of wormwood, peppermint, motherwort, honeysuckle.Modified dacron fabric of the present invention is suitable for fabric, lining, the shoes and hats etc. of outdoor dress ornament.
Description
Technical field
The present invention relates to a kind of plant modified dacron fabrics and preparation method thereof, belong to textile technology field.
Background technique
Dacron intensity with higher and elastic recovery capability, strong durable, wash and wear.Terylene is to close fine fabric
The best fabric of middle heat resistance has thermoplasticity, can manufacture accordion-pleated skirt, rivel is lasting.The light resistance of dacron is preferable, but compares
Acrylic fibers are poor；Resistance to various chemicals are functional.Acid, alkali are all little to its extent of the destruction, while not being afraid of mould, are not afraid of and damage by worms.
Although polyester fabric sucting wet air permeability is bad, personal clothes are made, dress is uncomfortable.But it is used to make gym suit, account
Paulin, outdoor mountain-climbing clothes, mountain-climbing packet, climbing boot etc. are still very favorite by consumer.
Most modified dacron technologies, which are all put forth effort on, in the prior art improves its comfort, enhances that it is soft, affine, ventilative,
And the performances such as antibacterial, radiation protection.Such as copper ion modified terylene, silver ion modified dacron, silk gum modified dacron.
A kind of modified polyester fibre of prior art CN201710722020.3, comprising: polyester fiber ontology, silver fiber, bamboo
Carbon fibe and protein fibre, wherein the polyester fiber ontology accounts for a kind of modified polyester fibre mass percent
35%-50%, the silver fiber accounts for a kind of 10%-16% of modified polyester fibre mass percent, the bamboo charcoal
Fiber accounts for a kind of 20%-25% of modified polyester fibre mass percent, and the protein fibre accounts for described one kind
The 20%-24% of modified polyester fibre mass percent.By the above-mentioned means, improve polyster fibre dyeing and hygroscopicity difference lack
Point improves the flexibility of polyester fiber, and skin affinity, while also having radiation protection and antibacterial effect.
A kind of production technology of copper ion modified polyester staple fiber socks of prior art CN201810241886.7 is passed through
Socks, margin to seam and setting process are knitted in the selection of raw material, complete the production technology of copper ion modified polyester staple fiber socks；Advantage
Be: the present invention can assign the stronger gas permeability of socks, no by selecting copper ion modified polyester staple fiber in raw material
Easy pilling, prolonged endurable, socks surfacing, smooth, antibacterial bacteriostatic.
A kind of silk gum modified dacron Rachael blanket of prior art CN201710952490.9, the silk gum modified dacron are drawn
She Er woollen blanket is antistatic, the antibacterial dacron Rachael blanket that fiber surface is grafted with sericin, and preparation step includes that alkali subtracts
Amount, elargol prepare and are modified.Polyester raschel blanket is modified using the fulmargin containing antistatic agent, obtains silk gum
Modified dacron Rachael blanket has good antistatic, antibacterial and comfort property.
Rarely has pure plant modified dacron in the modified dacron fabric of the prior art, to further increase the resistance to of its face liber
Photosensitiveness, mosquito repellent, insect prevention technical report.
Summary of the invention
The problem to be solved in the present invention is against the above deficiency, to provide a kind of plant modified dacron fabric and its preparation side
Method, to realize following goal of the invention: making polyester fabric have preferable mosquito repellent, insect prevention performance, good light resistance is preferably suitable
It closes it and is used for outdoor dress ornament, luggage, shoes and hats etc..
In order to solve the above technical problems, the technical solution adopted by the present invention is as follows:
A kind of plant modified dacron fabric, raw material include polyester resin, acid fiber by polylactic, modifying agent, polyester resin, polylactic acid
Fiber, modifying agent mass ratio be 80-100:24-27:4-4.8；The modifying agent is by plant extracts, glutathione, chitin
Matter, linseed oil are mixed with according to 5:3:2:9；The plant extracts is wormwood, peppermint, motherwort, honeysuckle
It is one or more of.
A kind of plant modified dacron fabric, raw material further include following components: sodium alginate, lubricant, α-sorb
Alcohol, oleic acid.
A kind of plant modified dacron fabric, raw material includes following components in parts by weight: 80-100 parts of polyester resin,
24-27 parts of acid fiber by polylactic, 4-4.8 parts of modifying agent, 14-17 parts of sodium alginate, 1-1.5 parts of lubricant, α -4-5 parts of sorbierite,
4-5 parts of oleic acid；
The polyester resin: fineness is 60 mesh, water content≤0.2%；
The acid fiber by polylactic: fibre number is 1.5 denier, fibre length 0.3-0.45mm；
The sodium alginate: fineness is 80 mesh, viscosity 200-300 mpa.s, moisture content 10-12%, calcium content 0.3%；
The lubricant: stearic acid vinyl ester and calcium stearate are mixed according to the mass ratio of 4:1；
The plant extracts: active principle content 96.5%, 100% logical sieves with 100 mesh sieve；
The glutathione: active principle content 98%, 100% passes through 200 meshes.
A kind of preparation method of plant modified dacron fabric, comprising the following steps:
Step 1: the preparation of modifying agent: plant extracts, glutathione, chitin, linseed oil are mixed according to 5:3:2:9,
Open stirring, mixing speed 1000rpm, mixing time 1h；After stirring, mixed liquor is subjected to microwave treatment, the microwave
Processing: power 250w, treatment temperature are 52 DEG C, and the processing time is 70s, and number of processes is 3 times, interval time 2min；Microwave
After processing, mixed liquor is heated into 30min under the conditions of 85-89 DEG C, obtains modifying agent.
Step 2: the preparation of modified dacron master batch: polyester resin being heated to 298 DEG C, opens stirring, stirring rate is
1200rpm is added modifying agent, persistently stirs 2.5h；Then cooling is prepared into modified dacron master batch.
Step 3: the preparation of spinning solution: by modified dacron master batch and acid fiber by polylactic, sodium alginate, α-sorbierite, oleic acid
Mixing, is heated to 310 DEG C, heating time 50min, stirring rate 200rpm；Lubricant is added in side stirring, side；It is melted
Melt spinning solution.
Step 4: spinning
Spinning solution is imported in manifold, fiber is sprayed from the hole of spinneret, and the hole cross section of spinneret is equilateral triangle,
Extrusion temperature is 257 DEG C, and subsequently into coagulating bath, coagulation bath temperature is 60-65 DEG C, the concentration of ethylene methacrylic pyridine in coagulating bath
For 45-47%, internal circulating load 60-65kL/h；Obtain fibre bundle.
Step 5: drawing-off oils
It obtains fibre bundle and carries out 4 drawing-offs, draw ratio is respectively 1:1.08,1:1.21,1:1.15,1:1.05；After drawing-off, give
Fibre bundle sprays finish, and it is compound that the finish is that polyethylene glycol laurate, tripalmitin are prepared with mass ratio 5:3
Finish.
Fibre bundle drying after oiling, is curled at cooling, and plant modified dacron is obtained.
Step 6: weaving
The plant modified dacron prepared using step 5 weaves fabric.
It will be put into after fabric in plasma treatment instrument, be passed through the argon gas that pressure is 32Pa and carry out plasma treatment, plasma
The processing time 2 minutes.
Then determine drying and shaping, obtain plant modified dacron fabric.
The invention adopts the above technical scheme, compared with prior art, has the advantages that
(1) plant modified dacron fabric finished product of the present invention: there is apparent repelling effect, it is 90-93.5% that mosquito, which walks quickly and keeps away rate,；Water
After washing 10 times, mosquito walks quickly and keeps away rate still up to 80-87%.
(2) when the addition number of modifying agent is in 3.5-4, degradation temperature is set as 55 DEG C, and intensity of illumination is set as
0.95W/m2, after irradiating 300h, strength retention is higher, especially when it is 4 that number, which is added, reach peak value, fabric fibre
Strength retention is up to 85.6%.
(3) plant modified dacron fabric finished product of the present invention: there is apparent insect prevention performance, through testing, ant walks quickly and keeps away rate and reaches
95-97.2%；After washing 10 times, ant walks quickly and keeps away rate still up to 90-93%.
(4) plant modified dacron fabric finished product of the present invention: antistatic property is good, and continuous friction 500 times does not play electrostatic；It is suitable
For garment material.
Polyester fabric is set to have preferable mosquito repellent, insect prevention performance, meanwhile, there is apparent wear-resisting, antistatic performance, especially
Dress ornament, luggage, shoes and hats for being used suitable for outdoor sports, excursion, mountain climbing expedition etc. etc..
Specific embodiment
It should be appreciated that preferred embodiments described herein are only used to illustrate and explain the present invention, it is not used to limit this
Invention.
A kind of plant modified dacron fabric of embodiment 1
Its raw material includes following components in parts by weight: 80 parts of polyester resin, 25 parts of acid fiber by polylactic, 4.4 parts of modifying agent, alginic acid
14 parts of sodium, 1 part of lubricant, 5 parts of α-sorbierite, 4.5 parts of oleic acid；
The polyester resin: fineness is 60 mesh, water content≤0.2%；
The acid fiber by polylactic: fibre number is 1.5 denier, fibre length 0.3-0.45mm；
The modifying agent is mixed with by plant extracts, glutathione, chitin, linseed oil according to 5:3:2:9.
The sodium alginate: fineness is 80 mesh, viscosity 200-300 mpa.s, moisture content 10-12%, calcium content 0.3%；
The lubricant: stearic acid vinyl ester and calcium stearate are mixed according to the mass ratio of 4:1；
The plant extracts 100% is logical to be sieved with 100 mesh sieve；The plant extracts is wormwood extract.
The glutathione: active principle content 98%, 100% passes through 200 meshes.
A kind of plant modified dacron fabric of embodiment 2
Identical with embodiment 1, only change following: the raw material of fabric includes following components in parts by weight: 90 parts of polyester resin, poly- cream
27 parts of sour fiber, 4 parts of modifying agent, 15 parts of sodium alginate, 1.4 parts of lubricant, 4 parts of α-sorbierite, 4 parts of oleic acid.
A kind of plant modified dacron fabric of embodiment 3
Identical with embodiment 1, only change following: the raw material of fabric includes following components in parts by weight: 100 parts of polyester resin gathers
24 parts of acid fiber, 4.8 parts of modifying agent, 17 parts of sodium alginate, 1.5 parts of lubricant, 4.5 parts of α-sorbierite, 5 parts of oleic acid.
A kind of preparation method of the plant modified dacron fabric of embodiment 4
According to the composition of raw materials of embodiment 1-3, follow the steps below:
Step 1: the preparation of modifying agent: plant extracts, glutathione, chitin, linseed oil are mixed according to 5:3:2:9,
Open stirring, mixing speed 1000rpm, mixing time 1h；After stirring, mixed liquor is subjected to microwave treatment, the microwave
Processing: power 250w, treatment temperature are 52 DEG C, and the processing time is 70s, and number of processes is 3 times, interval time 2min；Microwave
After processing, mixed liquor is heated into 30min under the conditions of 85-89 DEG C, obtains modifying agent.
Step 2: the preparation of modified dacron master batch: polyester resin being heated to 298 DEG C, opens stirring, stirring rate is
1200rpm is added modifying agent, persistently stirs 2.5h；Then cooling is prepared into modified dacron master batch.
Step 3: the preparation of spinning solution: by modified dacron master batch and acid fiber by polylactic, sodium alginate, α-sorbierite, oleic acid
Mixing, is heated to 310 DEG C, heating time 50min, stirring rate 200rpm；Lubricant is added in side stirring, side；It is melted
Melt spinning solution.
Step 4: spinning
Spinning solution is imported in manifold, fiber is sprayed from the hole of spinneret, and the hole cross section of spinneret is equilateral triangle,
Extrusion temperature is 257 DEG C, and subsequently into coagulating bath, coagulation bath temperature is 60-65 DEG C, the concentration of ethylene methacrylic pyridine in coagulating bath
It is 46%, internal circulating load 60-65kL/h；Obtain fibre bundle.
Step 5: drawing-off oils
It obtains fibre bundle and carries out 4 drawing-offs, draw ratio is respectively 1:1.08,1:1.21,1:1.15,1:1.05；After drawing-off, give
Fibre bundle sprays finish, and it is compound that the finish is that polyethylene glycol laurate, tripalmitin are prepared with mass ratio 5:3
Finish.
Fibre bundle drying after oiling, is curled at cooling, and plant modified dacron is obtained.
Step 6: weaving
The plant modified dacron prepared using step 5 weaves fabric.
It will be put into after fabric in plasma treatment instrument, be passed through the argon gas that pressure is 32Pa and carry out plasma treatment, plasma
The processing time 2 minutes.
Then determine drying and shaping, obtain plant modified dacron fabric.
Comparative example 1
The raw material of fabric of use includes following weight parts component: identical with embodiment 1, only change following: the raw material of fabric includes
Following components in parts by weight: 90 parts of polyester resin, 27 parts of acid fiber by polylactic, 4 parts of modifying agent, 15 parts of sodium alginate, lubricant 1.4
Part, 4 parts of α-sorbierite, 4 parts of oleic acid.
The modifying agent is mixed with by glutathione, chitin according to 3:2.
Preparation method: it is same as Example 4, only change following steps:
Step 1: the preparation of modifying agent: glutathione, chitin being mixed according to 3:2, open stirring, mixing speed is
1000rpm, mixing time 1h；Mixed liquor is heated into 30min under the conditions of 85-89 DEG C, obtains modifying agent.
Step 5: drawing-off oils
It obtains fibre bundle and carries out 4 drawing-offs, draw ratio is respectively 1:1.08,1:1.21,1:1.15,1:1.05；
It by fibre bundle drying, cooling, curls, obtains modified dacron.
Comparative example 2
The raw material of fabric of use includes following weight parts component: identical with embodiment 1, only change following: the raw material of fabric includes
Following components in parts by weight: 90 parts of polyester resin, 27 parts of acid fiber by polylactic, 4 parts of modifying agent, 15 parts of sodium alginate, lubricant 1.4
Part, 4 parts of α-sorbierite, 4 parts of oleic acid.
The modifying agent is mixed with by plant extracts, linseed oil according to 5:9.
Preparation method: it is same as Example 4, only change following steps:
Step 1: the preparation of modifying agent: plant extracts, linseed oil being mixed according to 5:9, open stirring, mixing speed is
1000rpm, mixing time 1h；Mixed liquor is heated into 30min under the conditions of 85-89 DEG C, obtains modifying agent.
Step 5: drawing-off oils
It obtains fibre bundle and carries out 4 drawing-offs, draw ratio is respectively 1:1.08,1:1.21,1:1.15,1:1.05；
It by fibre bundle drying, cooling, curls, obtains modified dacron.
Through testing, the technical indicator testing result of embodiment 1-3 and comparative example 1-2 are shown in Table 1；
Table 1
The present invention tests the calculating to rate of walking quickly and keeping away using the meter in GB/T 28408-2012 protective clothes insect prevention standard
What calculation method carried out.
Embodiment 5 is in order to further test modifying agent of the invention to the shadow of polyester fabric fiber prepared by the present invention
It rings, is tested as follows:
Using the method for embodiment 2, only changes the number of the addition of modifying agent, test its influence to index of correlation of the present invention.
Test method:
Modified dacron fabric prepared by the present invention has good anti-aging property: the polyester fabric fibers of preparation is placed in always
Change in testing machine, is uniformly dispersed, degradation temperature is set as 55 DEG C, and intensity of illumination is set as 0.95W/m2, after irradiating 300h,
The strength retention for detecting its fiber, is specifically shown in Table 2；
Table 2
As can be seen from the above table, during the present invention prepares polyester fabric, illumination of the modifying agent of use to polyester fabric fiber
Strength retention, mosquito and the rate of walking quickly and keeping away of ant have large effect, especially when the addition number of modifying agent is in 3.5-4
When, degradation temperature is set as 55 DEG C, and intensity of illumination is set as 0.95W/m2, after irradiating 300h, strength retention is higher, special
It is not to reach peak value, conservation rate 85.6% when it is 4 that number, which is added,.
Unless specifically indicated, ratio of the present invention is mass ratio, and the percentage is mass percent.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (9)
1. a kind of plant modified dacron fabric, it is characterised in that: raw material includes polyester resin, acid fiber by polylactic, modifying agent, terylene
Resin, acid fiber by polylactic, modifying agent mass ratio be 80-100:24-27:4-4.8；The modifying agent is by plant extracts, paddy
The sweet peptide of Guang, chitin, linseed oil are mixed with according to 5:3:2:9；The plant extracts is wormwood, peppermint, benefit mother
Careless, honeysuckle one or more.
2. a kind of plant modified dacron fabric according to claim 1, it is characterised in that: its raw material further includes following groups
Point: sodium alginate, lubricant, α-sorbierite, oleic acid.
3. a kind of plant modified dacron fabric according to claim 1, it is characterised in that: raw material includes following weight parts group
Point: 80-100 parts of polyester resin, 24-27 parts of acid fiber by polylactic, 4-4.8 parts of modifying agent, 14-17 parts of sodium alginate, lubricant 1-
1.5 parts, α -4-5 parts of sorbierite, 4-5 parts of oleic acid.
4. a kind of plant modified dacron fabric according to claim 1, it is characterised in that:
The polyester resin: fineness is 60 mesh, water content≤0.2%；
The acid fiber by polylactic: fibre number is 1.5 denier, fibre length 0.3-0.45mm.
5. a kind of plant modified dacron fabric according to claim 1, it is characterised in that: the sodium alginate: fineness is
80 mesh, viscosity 200-300 mpa.s, moisture content 10-12%, calcium content 0.3%；
The lubricant: stearic acid vinyl ester and calcium stearate are mixed according to the mass ratio of 4:1.
6. a kind of preparation method of plant modified dacron fabric, it is characterised in that: the preparation step including modifying agent；
The preparation of the modifying agent: plant extracts, glutathione, chitin, linseed oil are mixed according to 5:3:2:9, opened
Open stirring, mixing speed 1000rpm, mixing time 1h；After stirring, mixed liquor is subjected to microwave treatment, at the microwave
Reason: power 250w, treatment temperature are 52 DEG C, and the processing time is 70s, and number of processes is 3 times, interval time 2min；At microwave
After reason, mixed liquor is heated into 30min under the conditions of 85-89 DEG C, obtains modifying agent.
7. a kind of preparation method of plant modified dacron fabric according to claim 7, it is characterised in that: further include being modified
Dacron master grain step；
The modified dacron master batch: being heated to 298 DEG C for polyester resin, opens stirring, and stirring rate 1200rpm is added
Modifying agent persistently stirs 2.5h.
8. a kind of preparation method of plant modified dacron fabric according to claim 7, it is characterised in that: further include spinning
The preparation step of liquid；
The preparation of the spinning solution: modified dacron master batch is mixed with acid fiber by polylactic, sodium alginate, α-sorbierite, oleic acid,
It is heated to 310 DEG C, heating time 50min, stirring rate 200rpm.
9. a kind of preparation method of plant modified dacron fabric according to claim 7, it is characterised in that: further include spinning
With drawing-off oiling step；
The spinning: fiber is 257 DEG C from spinneret extrusion temperature, and coagulation bath temperature is 60-65 DEG C, methyl second in coagulating bath
The concentration of annulated pyridine is 45-47%, internal circulating load 60-65kL/h；
The drawing-off: pass through 4 drawing-offs, draw ratio is respectively 1:1.08,1:1.21,1:1.15,1:1.05；
Described oils: it is compound that the finish used is that polyethylene glycol laurate, tripalmitin are prepared with mass ratio 5:3
Finish.