CN109338498A - A kind of production method of nice and cool nylon fibre - Google Patents
A kind of production method of nice and cool nylon fibre Download PDFInfo
- Publication number
- CN109338498A CN109338498A CN201811187999.XA CN201811187999A CN109338498A CN 109338498 A CN109338498 A CN 109338498A CN 201811187999 A CN201811187999 A CN 201811187999A CN 109338498 A CN109338498 A CN 109338498A
- Authority
- CN
- China
- Prior art keywords
- chinlon
- degrees celsius
- nice
- section
- cooling masterbatch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of production methods of nice and cool nylon fibre, include the following steps: that 1) cooling masterbatch and chinlon 6 section are dried；2) cooling masterbatch is added using master batch output syringe pump, with chinlon 6 section mixed melting according to a certain percentage；3) spinning: the melt of melting is extruded from spinneret orifice, is frozen into silk；4) manufactured fiber is successively carried out to draw-teisting, twists afterwards, compress and wash drying, thermal finalization, balance, rewinding and packaging.In the step 1), drying temperature is 100-105 degrees Celsius, drying time 3-5h；In the step 2), the weight ratio of cooling masterbatch and chinlon 6 section is 1:10-20；In the step 3), spinning temperature is 270-275 degrees Celsius；In the step 4), draft temperature is 70-75 degrees Celsius.The production method of nice and cool nylon fibre of the invention, by the way that cooling masterbatch is added, the nylon fibre produced has excellent nice and cool performance.
Description
Technical field
The present invention relates to a kind of production methods of nice and cool nylon fibre, belong to synthetic fibers production technical field.
Background technique
Polyamide Yarns is a kind of textile fabric, there is the multiple types such as monofilament, strand, special yarn, compared to the gloss of silk broadcloth
For degree, Polyamide Yarns fabric sheen is poor, the feeling as coated coating of wax matter, while being rubbed back and forth with hand, can feel
Abrasive feel between fabric.
In daily life, this fabric is currently used primarily in production sportswear, scarf etc., is still had an optimistic view of by people.It is curing
Aspect is treated, is mainly used for making bandage.Polyamide Yarns product is mainly for the production of trimming cloth.Other have light with 118DFDY and FDY
All kinds of extraordinary material compositions such as TRIANGLE PROFILE, extraordinary silk, Polyamide Yarns match woven fabric, and small lot multi items strike a bargain opposite
It is more active.
With the continuous progress of science and technology with the characteristics of the continuous improvement of living standard, natural fiber or chemical fibre yarn and
Traditional spinning method for genuine has been difficult to meet people to the higher level demands such as comfort, the functionality of dress ornament, bis- (or more) components
Silk (or fiber) compound resultant yarn technology just comes into being and has become one of the main contents of domestic new technology at present.
With the raising of material conditions, the rich increasing of product, people to the functional requirement of functional fiber increasingly
Height, for example during the broiling summer, people develop the meaning of nice and cool nylon fibre very there is an urgent need to wear nice and cool clothes
It is great.
Summary of the invention
The purpose of the present invention is to overcome the deficiencies of the prior art, provides a kind of production method of nice and cool nylon fibre.
The production method of nice and cool nylon fibre of the invention, includes the following steps:
1) cooling masterbatch and chinlon 6 section are dried；
2) cooling masterbatch is added using master batch output syringe pump, with chinlon 6 section mixed melting according to a certain percentage；
3) spinning: the melt of melting is extruded from spinneret orifice, is frozen into silk；
4) manufactured fiber is successively carried out to draw-teisting, twists afterwards, compress and wash drying, thermal finalization, balance, rewinding and packaging.
In the step 1), drying temperature is 100-105 degrees Celsius, drying time 3-5h；
In the step 2), the weight ratio of cooling masterbatch and chinlon 6 section is 1:10-20；
In the step 3), spinning temperature is 270-275 degrees Celsius；
In the step 4), draft temperature is 70-75 degrees Celsius.
The production method of nice and cool nylon fibre of the invention, by the way that cooling masterbatch is added, the nylon fibre produced has
Excellent nice and cool performance.
Specific embodiment
Embodiment 1
The production method of nice and cool nylon fibre of the invention, includes the following steps:
1) cooling masterbatch and chinlon 6 section are dried；
2) cooling masterbatch is added using master batch output syringe pump, with chinlon 6 section mixed melting according to a certain percentage；
3) spinning: the melt of melting is extruded from spinneret orifice, is frozen into silk；
4) manufactured fiber is successively carried out to draw-teisting, twists afterwards, compress and wash drying, thermal finalization, balance, rewinding and packaging.
In the step 1), drying temperature is 100 degrees Celsius, drying time 3h；
In the step 2), the weight ratio of cooling masterbatch and chinlon 6 section is 1:10；
In the step 3), spinning temperature is 270 degrees Celsius；
In the step 4), draft temperature is 70 degrees Celsius.
Embodiment 2
The production method of nice and cool nylon fibre of the invention, includes the following steps:
1) cooling masterbatch and chinlon 6 section are dried；
2) cooling masterbatch is added using master batch output syringe pump, with chinlon 6 section mixed melting according to a certain percentage；
3) spinning: the melt of melting is extruded from spinneret orifice, is frozen into silk；
4) manufactured fiber is successively carried out to draw-teisting, twists afterwards, compress and wash drying, thermal finalization, balance, rewinding and packaging.
In the step 1), drying temperature is 105 degrees Celsius, drying time 5h；
In the step 2), the weight ratio of cooling masterbatch and chinlon 6 section is 1:20；
In the step 3), spinning temperature is 275 degrees Celsius；
In the step 4), draft temperature is 75 degrees Celsius.
Embodiment 3
The production method of nice and cool nylon fibre of the invention, includes the following steps:
1) cooling masterbatch and chinlon 6 section are dried；
2) cooling masterbatch is added using master batch output syringe pump, with chinlon 6 section mixed melting according to a certain percentage；
3) spinning: the melt of melting is extruded from spinneret orifice, is frozen into silk；
4) manufactured fiber is successively carried out to draw-teisting, twists afterwards, compress and wash drying, thermal finalization, balance, rewinding and packaging.
In the step 1), drying temperature is 103 degrees Celsius, drying time 4h；
In the step 2), the weight ratio of cooling masterbatch and chinlon 6 section is 1:15；
In the step 3), spinning temperature is 272 degrees Celsius；
In the step 4), draft temperature is 72 degrees Celsius.
Claims (1)
1. a kind of production method of nice and cool nylon fibre, which comprises the steps of:
1) cooling masterbatch and chinlon 6 section are dried；
2) cooling masterbatch is added using master batch output syringe pump, with chinlon 6 section mixed melting according to a certain percentage；
3) spinning: the melt of melting is extruded from spinneret orifice, is frozen into silk；
4) manufactured fiber is successively carried out to draw-teisting, twists afterwards, compress and wash drying, thermal finalization, balance, rewinding and packaging；
In the step 1), drying temperature is 100-105 degrees Celsius, drying time 3-5h；
In the step 2), the weight ratio of cooling masterbatch and chinlon 6 section is 1:10-20；
In the step 3), spinning temperature is 270-275 degrees Celsius；
In the step 4), draft temperature is 70-75 degrees Celsius.