CN108977922A - A kind of production method of modified nylon long filament - Google Patents
A kind of production method of modified nylon long filament Download PDFInfo
- Publication number
- CN108977922A CN108977922A CN201810907699.8A CN201810907699A CN108977922A CN 108977922 A CN108977922 A CN 108977922A CN 201810907699 A CN201810907699 A CN 201810907699A CN 108977922 A CN108977922 A CN 108977922A
- Authority
- CN
- China
- Prior art keywords
- modified nylon
- master batch
- production method
- long filament
- winding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of production method of modified nylon long filament, include the following steps: 1) to send by vacuum feeder to flour mill and crush, obtain premix using graphene powder, PA6 slice and auxiliary agent as raw material；Premix is subjected to melt blending extruding pelletization by double screw extruder, disperses graphene uniform, obtains modified nylon master batch；2) spinning, the winding that oils, balance and stretching are successively carried out to modified nylon master batch, obtain modified nylon fiber filament；In the step 2), spinning temperature is 260-265 degrees Celsius；In the step 2), winding speed 400-450rpm；In the step 2), tensile speed 600-650rpm.The production method of modified nylon long filament of the invention is granulated by being blended, obtains modified master batch, and the nylon fibre produced has excellent uvioresistant, far infrared, anti-microbial property.
Description
Technical field
The present invention relates to a kind of production methods of modified nylon long filament, belong to synthetic fibers production technical field.
Background technique
Polyamide Yarns is a kind of textile fabric, there is the multiple types such as monofilament, strand, special yarn, compared to the gloss of silk broadcloth
For degree, Polyamide Yarns fabric sheen is poor, the feeling as coated coating of wax matter, while being rubbed back and forth with hand, can feel
Abrasive feel between fabric.
In daily life, this fabric is currently used primarily in production sportswear, scarf etc., is still had an optimistic view of by people.It is curing
Aspect is treated, is mainly used for making bandage.Polyamide Yarns product is mainly for the production of trimming cloth.Other have light with 118DFDY and FDY
All kinds of extraordinary material compositions such as TRIANGLE PROFILE, extraordinary silk, Polyamide Yarns match woven fabric, and small lot multi items strike a bargain opposite
It is more active.
With the continuous progress of science and technology with the characteristics of the continuous improvement of living standard, natural fiber or chemical fibre yarn and
Traditional spinning method for genuine has been difficult to meet people to the higher level demands such as comfort, the functionality of dress ornament, bis- (or more) components
Silk (or fiber) compound resultant yarn technology just comes into being and has become one of the main contents of domestic new technology at present.
The fast light and heat-resistant stability of polyamide fibre is poor, in the application easy flavescence embrittlement, dyeing and printing fabric fugitive color, uses
It strongly declines to a great extent long afterwards, seriously affects its service life.Nylon fibre is modified to improve its sun-resistant ageing properties
For expanding having very important significance using field for polyamide fibre.
Summary of the invention
The purpose of the present invention is to overcome the deficiencies of the prior art, provides a kind of production method of modified nylon long filament.
The production method of modified nylon long filament of the invention, includes the following steps:
1) it using graphene powder, PA6 slice and auxiliary agent as raw material, is sent by vacuum feeder to flour mill and is crushed, premixed
Material；Premix is subjected to melt blending extruding pelletization by double screw extruder, disperses graphene uniform, obtains modified nylon
Master batch；
2) spinning, the winding that oils, balance and stretching are successively carried out to modified nylon master batch, obtain modified nylon fiber filament.
In the step 2), spinning temperature is 260-265 degrees Celsius.
In the step 2), winding speed 400-450rpm.
In the step 2), tensile speed 600-650rpm.
The production method of modified nylon long filament of the invention is granulated by being blended, obtains modified master batch, the polyamide fibre produced
Fiber has excellent uvioresistant, far infrared, anti-microbial property.
Specific embodiment
Embodiment 1
The production method of modified nylon long filament of the invention, includes the following steps:
1) it using graphene powder, PA6 slice and auxiliary agent as raw material, is sent by vacuum feeder to flour mill and is crushed, premixed
Material；Premix is subjected to melt blending extruding pelletization by double screw extruder, disperses graphene uniform, obtains modified nylon
Master batch；
2) spinning, the winding that oils, balance and stretching are successively carried out to modified nylon master batch, obtain modified nylon fiber filament.
In the step 2), spinning temperature is 260 degrees Celsius.
In the step 2), winding speed 400rpm.
In the step 2), tensile speed 600rpm.
Embodiment 2
The production method of modified nylon long filament of the invention, includes the following steps:
1) it using graphene powder, PA6 slice and auxiliary agent as raw material, is sent by vacuum feeder to flour mill and is crushed, premixed
Material；Premix is subjected to melt blending extruding pelletization by double screw extruder, disperses graphene uniform, obtains modified nylon
Master batch；
2) spinning, the winding that oils, balance and stretching are successively carried out to modified nylon master batch, obtain modified nylon fiber filament.
In the step 2), spinning temperature is 265 degrees Celsius.
In the step 2), winding speed 450rpm.
In the step 2), tensile speed 650rpm.
Claims (1)
1. a kind of production method of modified nylon long filament, which comprises the steps of:
1) it using graphene powder, PA6 slice and auxiliary agent as raw material, is sent by vacuum feeder to flour mill and is crushed, premixed
Material；Premix is subjected to melt blending extruding pelletization by double screw extruder, disperses graphene uniform, obtains modified nylon
Master batch；
2) spinning, the winding that oils, balance and stretching are successively carried out to modified nylon master batch, obtain modified nylon fiber filament；
In the step 2), spinning temperature is 260-265 degrees Celsius；
In the step 2), winding speed 400-450rpm；
In the step 2), tensile speed 600-650rpm.