CN102587124B - Manufacturing method of bamboo fiber and polyester-nylon fiber interweaved fabric as well as fabric - Google Patents
Manufacturing method of bamboo fiber and polyester-nylon fiber interweaved fabric as well as fabric Download PDFInfo
- Publication number
- CN102587124B CN102587124B CN201210046899.1A CN201210046899A CN102587124B CN 102587124 B CN102587124 B CN 102587124B CN 201210046899 A CN201210046899 A CN 201210046899A CN 102587124 B CN102587124 B CN 102587124B
- Authority
- CN
- China
- Prior art keywords
- fabric
- bamboo
- described fabric
- finishing agent
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a manufacturing method of a bamboo fiber and polyester-nylon fiber interweaved fabric as well as the fabric, belonging to the technical field of bamboo fiber weaving. The manufacturing method of the bamboo fiber and polyester-nylon fiber interweaved fabric comprises the following steps of: (1) weaving the fabric, dipping the fabric by adopting a finishing agent and drying; (2) cooling the fabric after drying; and (3) dipping the fabric by adopting an after finishing agent and setting the fabric, wherein during fabric weaving, warps are yarns formed by twisting one or more than one strand of bamboo fiber and wefts are yarns formed by twisting one or more than one strand of polyester-nylon. The bamboo fiber and polyester-nylon fiber interweaved fabric manufactured by using the method disclosed by the invention has the advantages of good crease resistant performance, low shrinkage and good wearability.
Description
Technical field
The present invention relates to bamboo fibre and manufacture method and the fabric of washing bright and beautiful fiber interwoven fabric, belong to bamboo fibre textile technology field.
Background technology
Along with people's going deep into bamboo fibre understanding, the consumer groups of bamboo fibre are also expanding gradually, from white collar several years ago, to present blue collar, spread gradually, in knitting and family, spin field, the total amount of bamboo fiber products has been created new peak in recent years, and its market share amount is also equally matched with cotton product.When obtaining encouraging success, further developing of the industry also run into bottleneck, and because of intensity, shrink and the reason such as well-pressed, it is to be difficult at present the technical barrier of capturing that bamboo fibre marches to other field of textiles.The patent No. is 201020295706.2 Chinese utility model patent, family's textile fabric that a kind of bamboo fibre and model blending and cotton fiber interweave is disclosed, although this patented technology still belongs to house, spin field, also can say that this patented technology marches a technique direction is provided to other field of textiles for bamboo fibre.Application number is 200810136352.4 Chinese invention patent, a kind of interwoven and weaving method thereof of washing bright and beautiful filament and bamboo fibre disclosed, described interwoven is washed bright and beautiful fiber single hole silk by 20D～30D super fine denier and is interwoven as parallel as warp, bamboo fiber yarn, described super fine denier is washed bright and beautiful fiber single hole silk composition and is accounted for 15%～25% of interwoven gross weight, and described bamboo fiber yarn composition accounts for 75%～85% of interwoven gross weight.The cloth cover of this interwoven is retaining on the basis of the advantages such as antibacterial, high ventilative, the high moisture absorption of bamboo fiber yarn, wear-resisting, not balling-up, has also strengthened exquisiteness sense and the drapability of fabric, is applicable to fashion material.But the technical problem that this fabric can't solve is crease-resistant, shrink.
Summary of the invention
The object of the invention is the manufacture method that a kind of bamboo fibre is provided and washs bright and beautiful fiber interwoven fabric for solving the problems of the technologies described above.The fabric making by the method, except having the advantage of bamboo fibre, also has advantages of that the good washing shrinkage of wrinkle resistance is low.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing;
2. after dry processing, described fabric is cooled to room temperature;
3. adopt post-finishing agent to flood described fabric, then adopt heating rate to surpass 10 ℃/s and temperature and be no more than the PULSE HEATING mode of 160 ℃ to the processing that formalizes of described fabric;
Described finishing agent is that bamboo vinegar content is not less than 30% ethanolic solution;
Described post-finishing agent is that bamboo vinegar content is not less than 70% the aqueous solution;
The described dry heating-up temperature that is treated to is the heat drying of 78～120 ℃;
While weaving fabric, the yarn that warp adopts one or more strands of bamboo fibres to form by twisting, parallel adopts one or more strands ofly to be washed bright and beautiful fiber and forms yarn by twisting.
In technique scheme of the present invention, adopted that 2 dry methods of 2 dippings have obtained that wrinkle resistance is good, washing shrinkage, bamboo fibre and the shuttle-woven fabric of washing bright and beautiful fiber that low wearability is good.These 2 times dipping has adopted different finishing agents, and dry method and object are also different.Dipping has adopted bamboo vinegar content to be not less than 30% ethanolic solution first, and the ethanol in this solution has not only promoted the infiltration of bamboo vinegar, also the pH value of this solution is promoted, and common fabric is unstable and easy damaged at sour environment performance.The dry temperature that adopted is the heat drying mode of 78～120 ℃ first, adopts this method ethanol promptly can be evaporated and removes from fabric.Applicant thinks, the more high easier locking of the performance by fabric of temperature is not yet handled well due to fabric now, therefore should not adopt excessive temperature, and 120 ℃ and following be a comparatively suitable temperature section.In the 2nd dipping, applicant has obviously strengthened bamboo vinegar content, and has adopted the aqueous solution of bamboo vinegar.Because easily also easily evaporation of infiltration of ethanol, can take away part bamboo vinegar during evaporation, now adopted still more the bamboo vinegar of higher concentration.In dry for the second time, namely step during 3. described setting is processed, is processed the wrinkle resistance of described fabric is promoted significantly by described setting.Aspect the wrinkle resistance of fabric, the free ironing full cotton shirt technology of Younger of take in prior art is outstanding figure, and the technical way of Younger is that cotton fabric is sprayed after exempting to press finishing agent and processed through hot iron.Cotton fabric through this special high-temperature process can obtain good wrinkle resistance.Applicant uses for reference the wrinkle resistance that this method wishes to obtain bamboo fibre fabric, because the relative cotton fiber of heat resistance of bamboo fibre is very different, add that this to exempt to press finishing agent larger than expection to the destruction of bamboo fibre, applicant delivers to Younger technique center by bamboo fiber woven fabric and has done and exempt to press after processing, finds that this fabric almost lost wearability.Applicant is according to the own characteristic of bamboo fibre, by of the prior art, exempt to press finishing agent and replace with described post-finishing agent, then adopting heating rate to surpass the technical scheme that 10 ℃/s and temperature be no more than the PULSE HEATING of 160 ℃ processes bamboo fiber woven fabric, the wrinkle resistance of described fabric is greatly improved, and does not almost lose the wearability of this fabric.Through measuring, the fabric making by the present invention is after having carried out artificial group wrinkle, the instant recovery rate of fold is more than 75%, the fabric that the Chinese invention patent that is 200810136352.4 by application number on year-on-year basis makes, and the instant recovery rate of fold increases approximately 50 percentage points.
By step effort 3., also make the washing shrinkage of described fabric obtain effective control; After tested, without step processing 3., a washing shrinkage of described fabric approaches 10%, and permanent washing shrinkage will be over 12% through prediction.And the fabric making through the inventive method, washing shrinkage is lower than 5%.
Describedly washing bright and beautiful fiber and refer to, is to take the fabric of island-in-sea type compound silk that mode that polyamide fibre is island as extra large terylene makes through spinning technique.Islands-in-sea bicomponent fibre is that two kinds of incompatible polymers are fully mixed to the blended fiber that rear melt spinning stretches and manufactures, and wherein a kind of polymers compositions (being called island phase) is scattered in another kind of polymers compositions (being called marine facies) with the form of fine staple fibre (being called fibril).Islands-in-sea type fibre also claims fibril-matrix type composite fibre, and a kind of island phase component is fibrillar structure, and another kind of marine facies component is impalpable structure.In cross-sectional direction, the component of fibrillar structure is embedded in impalpable structure component, and like island formal distribution, on fiber is longitudinal, the polymer of two kinds of components is intensive, dispersed continuously.From whole fiber, it has fineness and the length of conventional fibre.Islands-in-sea type fibre is a kind of main method of manufacturing superfine fibre, with chemical solvent, " sea " composition is dissolved, and just can obtain the superfine fibre of the boundling shape that radical is numerous.The quantity on described island can Shi16 island, 18 Dao Huo 24 islands etc.
As technique scheme preferably, step 2. and 3., also comprises fabric modification procedure: adopt Cryogenic air atmosphere plasma to carry out modification to described fabric.
Adopt Cryogenic air atmosphere plasma to carry out, after modification, having increased substantially the infiltration rate of post-finishing agent to described fabric, although the microstructure fiber of face liber is approximate before and after processing, water-wet performance is greatly improved.
As technique scheme preferably, after described face weave completes, first carry out preshrunk and then carry out 1. described dipping and dry processing of step.
Because bamboo fibre easily contracts, and in graticule, warp is bamboo fibre, and parallel is not bamboo fibre, and therefore the warp-wise shrinkage ratio broadwise of described fabric is shunk significantly many; Applicant has first adopted the technical scheme of preshrinking process effectively to solve through the large technical problem of broadwise difference in shrinkage.
As technique scheme preferably, when weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface.
Bamboo fibre phase commute fuzz balls, so applicant is hidden in bamboo fibre by technique the inside of fabric, to obtain the raising of fabric anti-pilling property.
As technique scheme preferably, described post-finishing agent comprises that bamboo vinegar and general formula are HO(C
2h
4o)
a-(C
3h
6o) b-(C
2h
4o)
athe auxiliary agent of H, the content of described auxiliary agent is not less than 0.1%.
Another object of the present invention is to provide a kind of fabric according to the manufacture method of above-mentioned fabric, and the radial density of described fabric is 170～175 pieces/inch, 80～85 pieces/inch of latitudinal densities; Fabric ultimate strength >=240N; Washing shrinkage≤5%.
As technique scheme preferably, described fabric is jacquard fabrics, described jacquard fabrics is by the bamboo fiber yarn as warp is proposed from described fabric interior section, the fabric with patterning forming on described fabric surface.
As technique scheme preferably, satin weave fabric during described fabric, described satin weave is five piece three and flies satin or five piece two and fly satin.
In sum, the present invention has following beneficial effect:
Use bamboo fibre that the inventive method makes and wash bright and beautiful fiber interwoven fabric and have advantages of that wrinkle resistance is good, washing shrinkage is low, wearability good.
The specific embodiment
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the modification that there is no creative contribution as required after reading this description, but as long as within the scope of claim of the present invention, are all subject to the protection of Patent Law.
embodiment mono-
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing;
2. after dry processing, described fabric is cooled to room temperature;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 11 ℃/s and temperature are that the PULSE HEATING mode of 100 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 30%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 70%;
The described dry heating-up temperature that is treated to is the heat drying of 78 ℃;
While weaving fabric, the yarn that warp adopts one bamboo fibre to form by twisting, parallel adopts one to wash the yarn that bright and beautiful fiber forms by twisting.
The fabric making by said method, its ultimate strength >=240N; Washing shrinkage≤5%.
embodiment bis-
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing;
2. after dry processing, described fabric is cooled to room temperature, adopts Cryogenic air atmosphere plasma to carry out modification to described fabric;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 12 ℃/s and temperature are that the PULSE HEATING mode of 120 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 35%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 75%;
The described dry heating-up temperature that is treated to is the heat drying of 85 ℃;
While weaving fabric, the yarn that warp adopts bifilar bamboo fibre to form by twisting, parallel adopts the bifilar yarn that bright and beautiful fiber forms by twisting of washing.
The fabric making by said method, its ultimate strength >=240N; Washing shrinkage≤5%.
embodiment tri-
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, described fabric is carried out to preshrunk processing, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing;
2. after dry processing, described fabric is cooled to room temperature, adopts Cryogenic air atmosphere plasma to carry out modification to described fabric;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 15 ℃/s and temperature are that the PULSE HEATING mode of 120 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 40%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 75%;
The described dry heating-up temperature that is treated to is the heat drying of 90 ℃;
While weaving fabric, warp adopts three strands of high-count yarns that bamboo fibre forms by twisting, and parallel adopts three strands and washs the yarn that bright and beautiful fiber forms by twisting.
The fabric making by said method, its ultimate strength >=300N; Washing shrinkage≤3%.The radial density of described fabric is 175 pieces/inch, 85 pieces/inch of latitudinal densities.
embodiment tetra-
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, described fabric is carried out to preshrunk processing, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing; When weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface;
2. after dry processing, described fabric is cooled to room temperature, adopts Cryogenic air atmosphere plasma to carry out modification to described fabric;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 15 ℃/s and temperature are that the PULSE HEATING mode of 150 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 45%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 70%;
The described dry heating-up temperature that is treated to is the heat drying of 100 ℃;
While weaving fabric, warp adopts three strands of high-count yarns that bamboo fibre forms by twisting, and parallel adopts three strands and washs the yarn that bright and beautiful fiber forms by twisting.
The fabric making by said method, its ultimate strength >=300N; Washing shrinkage≤3%.The radial density of described fabric is 175 pieces/inch, 85 pieces/inch of latitudinal densities.
embodiment five
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, described fabric is carried out to preshrunk processing, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing; When weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface;
2. after dry processing, described fabric is cooled to room temperature, adopts Cryogenic air atmosphere plasma to carry out modification to described fabric;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 15 ℃/s and temperature are that the PULSE HEATING mode of 150 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 45%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 70%; In described post-finishing agent, also contain Poloxamer, described Poloxamer is that general formula is HO(C
2h
4o)
a-(C
3h
6o) b-(C
2h
4o)
athe auxiliary agent of H, in the present embodiment, a is that 12, b is 20, and the mean molecule quantity of this auxiliary agent is 2090～2360, and the content of described auxiliary agent is 0.2%;
The described dry heating-up temperature that is treated to is the heat drying of 100 ℃;
While weaving fabric, warp adopts three strands of high-count yarns that bamboo fibre forms by twisting, and parallel adopts three strands and washs the yarn that bright and beautiful fiber forms by twisting.
The fabric making by said method, its ultimate strength >=300N; Washing shrinkage≤3%.The radial density of described fabric is 175 pieces/inch, 85 pieces/inch of latitudinal densities.Described fabric is jacquard fabrics, and described jacquard fabrics is by the bamboo fiber yarn as warp is proposed from described fabric interior section, the fabric with patterning forming on described fabric surface.Described fabric is five piece three and flies satin tissue fabric.
embodiment six
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, described fabric is carried out to preshrunk processing, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing; When weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface;
2. after dry processing, described fabric is cooled to room temperature, adopts Cryogenic air atmosphere plasma to carry out modification to described fabric;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 18 ℃/s and temperature are that the PULSE HEATING mode of 160 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 45%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 75%; In described post-finishing agent, also contain Poloxamer, described Poloxamer is that general formula is HO(C
2h
4o)
a-(C
3h
6o) b-(C
2h
4o)
athe auxiliary agent of H, in the present embodiment, a is that 64, b is 37, and the mean molecule quantity of this auxiliary agent is 6840～8830, and the content of described auxiliary agent is 0.3%;
The described dry heating-up temperature that is treated to is the heat drying of 120 ℃;
While weaving fabric, warp adopts three strands of high-count yarns that bamboo fibre forms by twisting, and parallel adopts three strands and washs the Compact-spun Yarn: that bright and beautiful fiber forms by twisting.
The fabric making by said method, its ultimate strength >=300N; Washing shrinkage≤3%.The radial density of described fabric is 170 pieces/inch, 80 pieces/inch of latitudinal densities.Described fabric is jacquard fabrics, and described jacquard fabrics is by the bamboo fiber yarn as warp is proposed from described fabric interior section, the fabric with patterning forming on described fabric surface.Described fabric is five piece two and flies satin tissue fabric.
embodiment seven
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, described fabric is carried out to preshrunk processing, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing; When weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface;
2. after dry processing, described fabric is cooled to room temperature, adopts Cryogenic air atmosphere plasma to carry out modification to described fabric;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 16 ℃/s and temperature are that the PULSE HEATING mode of 140 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 50%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 70%; In described post-finishing agent, also contain Poloxamer, described Poloxamer is that general formula is HO(C
2h
4o)
a-(C
3h
6o) b-(C
2h
4o)
athe auxiliary agent of H, in the present embodiment, a is that 101, b is 56, and the mean molecule quantity of this auxiliary agent is 9840～14600, and the content of described auxiliary agent is 0.5%;
The described dry heating-up temperature that is treated to is the heat drying of 100 ℃;
While weaving fabric, warp adopts three strands of high-count yarns that bamboo fibre forms by twisting, and parallel adopts three strands and washs the yarn that bright and beautiful fiber forms by twisting.
The fabric making by said method, its ultimate strength >=300N; Washing shrinkage≤3%.The radial density of described fabric is 175 pieces/inch, 85 pieces/inch of latitudinal densities.Described fabric is jacquard fabrics, and described jacquard fabrics is by the bamboo fiber yarn as warp is proposed from described fabric interior section, the fabric with patterning forming on described fabric surface.Described fabric is five piece two and flies satin tissue fabric.
embodiment eight
Bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, described fabric is carried out to preshrunk processing, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing; When weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface;
2. after dry processing, described fabric is cooled to room temperature;
3. adopt post-finishing agent to flood described fabric, then adopting heating rate is that 20 ℃/s and temperature are that the PULSE HEATING mode of 160 ℃ is to the processing that formalizes of described fabric;
Described finishing agent is the ethanolic solution of bamboo vinegar content 35%;
Described post-finishing agent is the aqueous solution of bamboo vinegar content 85%; In described post-finishing agent, also contain Poloxamer, described Poloxamer is that general formula is HO(C
2h
4o)
a-(C
3h
6o) b-(C
2h
4o)
athe auxiliary agent of H, in the present embodiment, a is that 79, b is 28, and the mean molecule quantity of this auxiliary agent is 7680～9510, and the content of described auxiliary agent is 1.5%;
The described dry heating-up temperature that is treated to is the heat drying of 120 ℃;
While weaving fabric, the high-count yarn that warp adopts bifilar bamboo fibre to form by twisting, parallel adopts the bifilar Compact-spun Yarn: that bright and beautiful fiber forms by twisting of washing.
The fabric making by said method, its ultimate strength >=300N; Washing shrinkage≤3%.The radial density of described fabric is 170 pieces/inch, 85 pieces/inch of latitudinal densities.Described fabric is jacquard fabrics, and described jacquard fabrics is by the bamboo fiber yarn as warp is proposed from described fabric interior section, the fabric with patterning forming on described fabric surface.
It is to carry out by GB/T 3923.1 that ultimate strength of the present invention is measured.Washing shrinkage of the present invention is as all referred to permanent washing shrinkage without specializing, and permanent washing shrinkage refers to the shrinkage of measuring when fabric no longer shrinks after repeatedly washing.
Claims (7)
1. bamboo fibre and the manufacture method of washing bright and beautiful fiber interwoven fabric, comprise the following steps:
1. weave fabric, adopt finishing agent to carry out impregnation process to described fabric, be then dried processing;
2. after dry processing, described fabric is cooled to room temperature;
3. adopt post-finishing agent to flood described fabric, then adopt heating rate to surpass 10 ℃/s and temperature and be no more than the PULSE HEATING mode of 160 ℃ to the processing that formalizes of described fabric;
Described finishing agent is that bamboo vinegar content is not less than 30% ethanolic solution;
Described post-finishing agent is that bamboo vinegar content is not less than 70% the aqueous solution;
The described dry heating-up temperature that is treated to is the heat drying of 78～120 ℃;
While weaving fabric, the yarn that warp adopts one or more strands of bamboo fibres to form by twisting, parallel adopts one or more strands ofly to be washed bright and beautiful fiber and forms yarn by twisting;
Described post-finishing agent comprises that bamboo vinegar and general formula are HO(C
2h
4o)
a-(C
3h
6o)
b-(C
2h
4o)
athe auxiliary agent of H, the content of described auxiliary agent is not less than 0.1%;
When a is that 12, b is 20, the mean molecule quantity of auxiliary agent is 2090～2360;
When a is that 64, b is 37, the mean molecule quantity of auxiliary agent is 6840～8830;
When a is that 101, b is 56, the mean molecule quantity of auxiliary agent is 9840～14600;
When a is that 79, b is 28, the mean molecule quantity of auxiliary agent is 7680～9510.
2. bamboo fibre according to claim 1 and the manufacture method of washing bright and beautiful fiber interwoven fabric, is characterized in that, step 2. and 3., also comprises fabric modification procedure: adopt Cryogenic air atmosphere plasma to carry out modification to described fabric.
3. bamboo fibre according to claim 1 and the manufacture method of washing bright and beautiful fiber interwoven fabric, is characterized in that: after described face weave completes, first carry out preshrunk and then carry out 1. described dipping and dry processing of step.
4. bamboo fibre according to claim 1 and the manufacture method of washing bright and beautiful fiber interwoven fabric, is characterized in that: when weaving described fabric, adopt satin weave technique that warp is hidden in to described fabric inner, make parallel float on described fabric surface.
5. the fabric being made by above-mentioned arbitrary claim, is characterized in that: the warp-wise density of described fabric is 170～175 pieces/inch, 80～85 pieces/inch of latitudinal densities; Fabric ultimate strength >=240N; Washing shrinkage≤5%.
6. fabric according to claim 5, it is characterized in that: described fabric is jacquard fabrics, described jacquard fabrics is by the bamboo fiber yarn as warp is proposed from described fabric interior section, the fabric with patterning forming on described fabric surface.
7. fabric according to claim 6, is characterized in that: described fabric is satin weave fabric, and described satin weave is five piece three and flies satin or five piece two and fly satin.