CN102587124A - Manufacturing method of bamboo fiber and polyester-nylon fiber interweaved fabric as well as fabric - Google Patents
Manufacturing method of bamboo fiber and polyester-nylon fiber interweaved fabric as well as fabric Download PDFInfo
- Publication number
- CN102587124A CN102587124A CN2012100468991A CN201210046899A CN102587124A CN 102587124 A CN102587124 A CN 102587124A CN 2012100468991 A CN2012100468991 A CN 2012100468991A CN 201210046899 A CN201210046899 A CN 201210046899A CN 102587124 A CN102587124 A CN 102587124A
- Authority
- CN
- China
- Prior art keywords
- lining
- fabric
- finishing agent
- bamboo
- adopt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a manufacturing method of a bamboo fiber and polyester-nylon fiber interweaved fabric as well as the fabric, belonging to the technical field of bamboo fiber weaving. The manufacturing method of the bamboo fiber and polyester-nylon fiber interweaved fabric comprises the following steps of: (1) weaving the fabric, dipping the fabric by adopting a finishing agent and drying; (2) cooling the fabric after drying; and (3) dipping the fabric by adopting an after finishing agent and setting the fabric, wherein during fabric weaving, warps are yarns formed by twisting one or more than one strand of bamboo fiber and wefts are yarns formed by twisting one or more than one strand of polyester-nylon. The bamboo fiber and polyester-nylon fiber interweaved fabric manufactured by using the method disclosed by the invention has the advantages of good crease resistant performance, low shrinkage and good wearability.
Description
Technical field
The present invention relates to bamboo fibre and manufacturing approach and the lining of washing bright and beautiful fiber interweaving lining, belong to the bamboo fibre textile technology field.
Background technology
Along with people's is goed deep into bamboo fibre understanding; The consumer groups of bamboo fibre are also enlarging gradually; Spread to present blue collar gradually from white collar several years ago; In the knitting and tame field of spinning, the total amount of bamboo fibre product has been created new peak in recent years, and its market occupancy volume is also equally matched with the cotton product.When obtaining encouraging success, further developing of the industry also run into bottleneck, and because of intensity, shrink and reason such as well-pressed, it is to be difficult to the technical barrier of capturing at present that bamboo fibre marches to other field of textiles.The patent No. is 201020295706.2 Chinese utility model patent; The tame textile fabric that a kind of bamboo fibre and model blending and cotton fiber interweave is disclosed; Spin the field although this patented technology still belongs to house, we can say that also this patented technology is that bamboo fibre marches to other field of textiles a technique direction is provided.Application number is 200810136352.4 Chinese invention patent; A kind of interweave cloth and weaving method thereof of washing bright and beautiful filament and bamboo fibre disclosed; The said cloth that interweaves is washed bright and beautiful fiber single hole silk by 20D～30D super fine denier and is interwoven as parallel as warp, bamboo fibre yarn; Said super fine denier is washed bright and beautiful fiber single hole silk composition and is accounted for 15%～25% of the cloth gross weight that interweaves, and said bamboo fibre yarn composition accounts for 75%～85% of the cloth gross weight that interweaves.The cloth cover of this cloth that interweaves has also been strengthened the exquisiteness sense and the drapability of fabric on the basis that keeps advantages such as antibiotic, high ventilative, the high moisture absorption of bamboo fibre yarn, wear-resisting, not balling-up, be applicable to fashion material.But the technical problem that this lining can't solve is crease-resistant, shrink.
Summary of the invention
The objective of the invention is the manufacturing approach that a kind of bamboo fibre is provided and washs bright and beautiful fiber interweaving lining for solving the problems of the technologies described above.The lining that makes through this method also has the low advantage of the good washing shrinkage of wrinkle resistance except that the advantage with bamboo fibre.
Above-mentioned technical purpose of the present invention is achieved through following technical scheme:
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, adopt finishing agent that said lining is carried out impregnation process, carry out dried then;
2. after the dried, said lining is cooled to room temperature;
3. adopt post-finishing agent that said lining is flooded, adopt heating rate to surpass 10 ℃/s and temperature then and be no more than 160 ℃ PULSE HEATING mode the processing that formalizes of said lining;
Said finishing agent is not less than 30% ethanolic solution for Bamboo vinegar solution content;
Said post-finishing agent is not less than 70% the aqueous solution for Bamboo vinegar solution content;
Said dried is that heating-up temperature is 78～120 ℃ a heat drying;
When weaving lining, the yarn that warp adopts one or multiply bamboo fibre to form through twisting, parallel adopt one or multiply to wash bright and beautiful fiber and form yarn through twisting.
In the technique scheme of the present invention, adopted the method for 2 dryings of 2 dippings to obtain that wrinkle resistance is good, washing shrinkage, bamboo fibre and the shuttle-woven fabric of washing bright and beautiful fiber that low wearability is good.These 2 times dipping has adopted different finishing agents, and dry method and purpose are also different.Dipping has adopted Bamboo vinegar solution content to be not less than 30% ethanolic solution first, and the ethanol in this solution has not only promoted the infiltration of Bamboo vinegar solution, and also the pH value with this solution promotes, common lining unstable properties and easy damaged in sour environment.The dry first temperature that adopted is 78～120 ℃ a heat drying mode, adopts this method can ethanol promptly be evaporated from lining and removes.The applicant thinks, the high more easier performance locking with lining of temperature because this moment, lining still was untreated, therefore should not be adopted excessive temperature, and 120 ℃ and following be a comparatively suitable temperature section.In the 2nd time flooded, the applicant had obviously strengthened Bamboo vinegar solution content, and has adopted the aqueous solution of Bamboo vinegar solution.Because ethanol also evaporation easily of infiltration easily can be taken away the part Bamboo vinegar solution during evaporation, adopted the Bamboo vinegar solution of higher concentration still more this moment.In second time drying, during the 3. described setting of step is just handled, handle to make that the wrinkle resistance of said lining is promoted significantly through said setting.Aspect the wrinkle resistance of lining, the free ironing full cotton shirt technology with Younger in the prior art is the outstanding figure, and the major technique means of Younger are to handle through hot iron after the cotton fabric sprinkling is exempted to press finishing agent.Cotton fabric through this special high-temperature process can obtain good wrinkle resistance.The applicant uses for reference the wrinkle resistance that this method hopes to obtain bamboo fibre fabric; Because the relative cotton fiber of heat resistance of bamboo fibre is very different; Add that this to exempt to press finishing agent bigger than expection to the destruction of bamboo fibre; The applicant with bamboo fiber woven fabric deliver to the Younger technique center done exempt to press processing after, find that this lining almost lost wearability.The applicant is according to the own characteristic of bamboo fibre; Exempt to press finishing agent and replace with said post-finishing agent of the prior art; Adopting heating rate to surpass the technical scheme that 10 ℃/s and temperature be no more than 160 ℃ PULSE HEATING then handles bamboo fiber woven fabric; Make the wrinkle resistance of said lining be greatly improved, and almost do not lose the wearability of this lining.Through measuring; The lining that makes through the present invention is after having carried out artificial group wrinkle; The instant recovery rate of fold is more than 75%, is the lining that 200810136352.4 Chinese invention patent makes through application number on year-on-year basis, and the instant recovery rate of fold increases about 50 percentage points.
Through step effort 3., also make the washing shrinkage of said lining obtain effective control; Through test, without step processing 3., a washing shrinkage of said lining is near 10%, and permanent washing shrinkage will be above 12% through prediction.And the lining that process the inventive method makes, washing shrinkage is lower than 5%.
Saidly washing bright and beautiful fiber and be meant, is to be that extra large terylene is the fabric of island-in-sea type compound silk that the mode on island is processed through spinning technique with polyamide fibre.Islands-in-sea bicomponent fibre is fully to mix the blended fiber that the back melt spinning stretches and makes to two kinds of incompatible polymers, and wherein a kind of polymers compositions (being called the island phase) is scattered in the another kind of polymers compositions (being called marine facies) with the form of fine staple fibre (being called fibril).Islands-in-sea type fibre is also claimed fibril-matrix type composite fibre, and a kind of island phase component is a fibrillar structure, and another kind of marine facies component is an impalpable structure.Component at fibrillar structure on the cross-sectional direction is embedded on the impalpable structure component, distributes intensive continuously, the even dispersion of polymer of two kinds of components on fiber is vertical like the island form.From whole fiber, it has the fineness and the length of conventional fibre.Islands-in-sea type fibre is a kind of main method of making superfine fibre, dissolves " sea " composition with chemical solvent, just can obtain the superfine fibre of the numerous boundling shape of radical.The quantity on said island can be 16 islands, 18 islands or 24 islands etc.
Preferred as technique scheme, step also comprise the lining modification procedure: adopt Cryogenic air atmosphere plasma that said lining is carried out modification 2. and 3..
After adopting Cryogenic air atmosphere plasma that said lining is carried out modification, increased substantially the infiltration rate of post-finishing agent, though the microstructure fiber of face liber is approximate before and after handling, the water-wet performance is greatly improved.
Preferred as technique scheme after said face weave is accomplished, carries out preshrunk earlier and carries out 1. described dipping of step and dried then.
Because bamboo fibre is prone to contract, and in the graticule, warp is a bamboo fibre, parallel is not a bamboo fibre, and therefore the warp-wise shrinkage ratio broadwise of said lining is shunk significantly many; The applicant has adopted the technical scheme of preshrinking process to solve effectively through the big technical problem of broadwise difference in shrinkage earlier.
Preferred as technique scheme, when weaving said lining, it is inner to adopt satin weave technology that warp is hidden in said lining, makes parallel float on said lining surface.
Bamboo fibre phase commute fuzz balls, so the applicant is hidden in the inside of lining through technology with bamboo fibre, to obtain the raising of lining anti-pilling property.
Preferred as technique scheme, said post-finishing agent comprises that Bamboo vinegar solution and general formula are HO (C
2H
4O)
a-(C
3H
6O) b-(C
2H
4O)
aThe auxiliary agent of H, the content of said auxiliary agent is not less than 0.1%.
Another object of the present invention is that the manufacturing approach according to above-mentioned lining provides a kind of lining, and the radial density of said lining is 170～175 pieces/inch, 80～85 pieces/inch of latitudinal densities; Lining ultimate strength>=240N; Washing shrinkage≤5%.
Preferred as technique scheme, said lining is a jacquard fabrics, said jacquard fabrics is through proposing from said lining interior section as the bamboo fibre yarn of warp, at the lining with patterning of said lining surface formation.
Satin weave lining when preferred as technique scheme, said lining, said satin weave are five piece three and fly satin or five piece two and fly satin.
In sum, the present invention has following beneficial effect:
Use bamboo fibre that the inventive method makes and wash bright and beautiful fiber interweaving lining and have the advantage that wrinkle resistance is good, washing shrinkage is low, wearability is good.
The specific embodiment
This specific embodiment only is to explanation of the present invention; It is not a limitation of the present invention; Those skilled in the art can make the modification that does not have creative contribution to present embodiment as required after reading this specification, but as long as in claim scope of the present invention, all receive the protection of Patent Law.
Embodiment one
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, adopt finishing agent that said lining is carried out impregnation process, carry out dried then;
2. after the dried, said lining is cooled to room temperature;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 11 ℃/s and temperature are that 100 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 30%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 70%;
Said dried is that heating-up temperature is 78 ℃ a heat drying;
When weaving lining, the yarn that warp adopts one bamboo fibre to form through twisting, parallel adopt one to wash the yarn that bright and beautiful fiber forms through twisting.
Through the lining that said method makes, its ultimate strength>=240N; Washing shrinkage≤5%.
Embodiment two
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, adopt finishing agent that said lining is carried out impregnation process, carry out dried then;
2. after the dried, said lining is cooled to room temperature, adopts Cryogenic air atmosphere plasma that said lining is carried out modification;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 12 ℃/s and temperature are that 120 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 35%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 75%;
Said dried is that heating-up temperature is 85 ℃ a heat drying;
When weaving lining, the yarn that warp adopts bifilar bamboo fibre to form through twisting, parallel adopt the bifilar yarn that bright and beautiful fiber forms through twisting of washing.
Through the lining that said method makes, its ultimate strength>=240N; Washing shrinkage≤5%.
Embodiment three
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, said lining is carried out preshrunk handle, adopt finishing agent that said lining is carried out impregnation process, carry out dried then;
2. after the dried, said lining is cooled to room temperature, adopts Cryogenic air atmosphere plasma that said lining is carried out modification;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 15 ℃/s and temperature are that 120 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 40%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 75%;
Said dried is that heating-up temperature is 90 ℃ a heat drying;
When weaving lining, the high-count yarn that warp adopts three strands of bamboo fibres to form through twisting, parallel adopt three strands to wash the yarn that bright and beautiful fiber forms through twisting.
Through the lining that said method makes, its ultimate strength>=300N; Washing shrinkage≤3%.The radial density of said lining is 175 pieces/inch, 85 pieces/inch of latitudinal densities.
Embodiment four
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, said lining is carried out preshrunk handle, adopt finishing agent that said lining is carried out impregnation process, carry out dried then; When weaving said lining, adopt satin weave technology that warp is hidden in said lining inside, make parallel float on said lining surface;
2. after the dried, said lining is cooled to room temperature, adopts Cryogenic air atmosphere plasma that said lining is carried out modification;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 15 ℃/s and temperature are that 150 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 45%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 70%;
Said dried is that heating-up temperature is 100 ℃ a heat drying;
When weaving lining, the high-count yarn that warp adopts three strands of bamboo fibres to form through twisting, parallel adopt three strands to wash the yarn that bright and beautiful fiber forms through twisting.
Through the lining that said method makes, its ultimate strength>=300N; Washing shrinkage≤3%.The radial density of said lining is 175 pieces/inch, 85 pieces/inch of latitudinal densities.
Embodiment five
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, said lining is carried out preshrunk handle, adopt finishing agent that said lining is carried out impregnation process, carry out dried then; When weaving said lining, adopt satin weave technology that warp is hidden in said lining inside, make parallel float on said lining surface;
2. after the dried, said lining is cooled to room temperature, adopts Cryogenic air atmosphere plasma that said lining is carried out modification;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 15 ℃/s and temperature are that 150 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 45%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 70%; Also contain Poloxamer in the said post-finishing agent, said Poloxamer is that general formula is HO (C
2H
4O)
a-(C
3H
6O) b-(C
2H
4O)
aThe auxiliary agent of H, a is 12 in the present embodiment, and b is 20, and the mean molecule quantity of this auxiliary agent is 2090～2360, and the content of said auxiliary agent is 0.2%;
Said dried is that heating-up temperature is 100 ℃ a heat drying;
When weaving lining, the high-count yarn that warp adopts three strands of bamboo fibres to form through twisting, parallel adopt three strands to wash the yarn that bright and beautiful fiber forms through twisting.
Through the lining that said method makes, its ultimate strength>=300N; Washing shrinkage≤3%.The radial density of said lining is 175 pieces/inch, 85 pieces/inch of latitudinal densities.Said lining is a jacquard fabrics, and said jacquard fabrics is through will propose the lining with patterning that forms on said lining surface as the bamboo fibre yarn of warp from said lining interior section.Said lining is five piece three and flies satin and organize lining.
Embodiment six
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, said lining is carried out preshrunk handle, adopt finishing agent that said lining is carried out impregnation process, carry out dried then; When weaving said lining, adopt satin weave technology that warp is hidden in said lining inside, make parallel float on said lining surface;
2. after the dried, said lining is cooled to room temperature, adopts Cryogenic air atmosphere plasma that said lining is carried out modification;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 18 ℃/s and temperature are that 160 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 45%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 75%; Also contain Poloxamer in the said post-finishing agent, said Poloxamer is that general formula is HO (C
2H
4O)
a-(C
3H
6O) b-(C
2H
4O)
aThe auxiliary agent of H, a is 64 in the present embodiment, and b is 37, and the mean molecule quantity of this auxiliary agent is 6840～8830, and the content of said auxiliary agent is 0.3%;
Said dried is that heating-up temperature is 120 ℃ a heat drying;
When weaving lining, the high-count yarn that warp adopts three strands of bamboo fibres to form through twisting, parallel adopt three strands to wash the compact spinning line that bright and beautiful fiber forms through twisting.
Through the lining that said method makes, its ultimate strength>=300N; Washing shrinkage≤3%.The radial density of said lining is 170 pieces/inch, 80 pieces/inch of latitudinal densities.Said lining is a jacquard fabrics, and said jacquard fabrics is through will propose the lining with patterning that forms on said lining surface as the bamboo fibre yarn of warp from said lining interior section.Said lining is five piece two and flies satin and organize lining.
Embodiment seven
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, said lining is carried out preshrunk handle, adopt finishing agent that said lining is carried out impregnation process, carry out dried then; When weaving said lining, adopt satin weave technology that warp is hidden in said lining inside, make parallel float on said lining surface;
2. after the dried, said lining is cooled to room temperature, adopts Cryogenic air atmosphere plasma that said lining is carried out modification;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 16 ℃/s and temperature are that 140 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 50%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 70%; Also contain Poloxamer in the said post-finishing agent, said Poloxamer is that general formula is HO (C
2H
4O)
a-(C
3H
6O) b-(C
2H
4O)
aThe auxiliary agent of H, a is 101 in the present embodiment, and b is 56, and the mean molecule quantity of this auxiliary agent is 9840～14600, and the content of said auxiliary agent is 0.5%;
Said dried is that heating-up temperature is 100 ℃ a heat drying;
When weaving lining, the high-count yarn that warp adopts three strands of bamboo fibres to form through twisting, parallel adopt three strands to wash the yarn that bright and beautiful fiber forms through twisting.
Through the lining that said method makes, its ultimate strength>=300N; Washing shrinkage≤3%.The radial density of said lining is 175 pieces/inch, 85 pieces/inch of latitudinal densities.Said lining is a jacquard fabrics, and said jacquard fabrics is through will propose the lining with patterning that forms on said lining surface as the bamboo fibre yarn of warp from said lining interior section.Said lining is five piece two and flies satin and organize lining.
Embodiment eight
Bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, said lining is carried out preshrunk handle, adopt finishing agent that said lining is carried out impregnation process, carry out dried then; When weaving said lining, adopt satin weave technology that warp is hidden in said lining inside, make parallel float on said lining surface;
2. after the dried, said lining is cooled to room temperature;
3. adopt post-finishing agent that said lining is flooded, adopting heating rate then is that 20 ℃/s and temperature are that 160 ℃ PULSE HEATING mode is to the processing that formalizes of said lining;
Said finishing agent is the ethanolic solution of Bamboo vinegar solution content 35%;
Said post-finishing agent is the aqueous solution of Bamboo vinegar solution content 85%; Also contain Poloxamer in the said post-finishing agent, said Poloxamer is that general formula is HO (C
2H
4O)
a-(C
3H
6O) b-(C
2H
4O)
aThe auxiliary agent of H, a is 79 in the present embodiment, and b is 28, and the mean molecule quantity of this auxiliary agent is 7680～9510, and the content of said auxiliary agent is 1.5%;
Said dried is that heating-up temperature is 120 ℃ a heat drying;
When weaving lining, the high-count yarn that warp adopts bifilar bamboo fibre to form through twisting, parallel adopt the bifilar compact spinning line that bright and beautiful fiber forms through twisting of washing.
Through the lining that said method makes, its ultimate strength>=300N; Washing shrinkage≤3%.The radial density of said lining is 170 pieces/inch, 85 pieces/inch of latitudinal densities.Said lining is a jacquard fabrics, and said jacquard fabrics is through will propose the lining with patterning that forms on said lining surface as the bamboo fibre yarn of warp from said lining interior section.
It is to carry out by GB/T 3923.1 that ultimate strength of the present invention is measured.Washing shrinkage according to the invention such as nothing specialize and all refer to permanent washing shrinkage, and permanent washing shrinkage is meant the shrinkage that fabric is measured when repeatedly washing is no longer shunk afterwards.
Claims (8)
1. the bamboo fibre and the manufacturing approach of washing bright and beautiful fiber interweaving lining may further comprise the steps:
1. weave lining, adopt finishing agent that said lining is carried out impregnation process, carry out dried then;
2. after the dried, said lining is cooled to room temperature;
3. adopt post-finishing agent that said lining is flooded, adopt heating rate to surpass 10 ℃/s and temperature then and be no more than 160 ℃ PULSE HEATING mode the processing that formalizes of said lining;
Said finishing agent is not less than 30% ethanolic solution for Bamboo vinegar solution content;
Said post-finishing agent is not less than 70% the aqueous solution for Bamboo vinegar solution content;
Said dried is that heating-up temperature is 78～120 ℃ a heat drying;
When weaving lining, the yarn that warp adopts one or multiply bamboo fibre to form through twisting, parallel adopt one or multiply to wash bright and beautiful fiber and form yarn through twisting.
2. bamboo fibre according to claim 1 and the manufacturing approach of washing bright and beautiful fiber interweaving lining is characterized in that, step also comprises the lining modification procedure: adopt Cryogenic air atmosphere plasma that said lining is carried out modification 2. and 3..
3. bamboo fibre according to claim 1 and the manufacturing approach of washing bright and beautiful fiber interweaving lining is characterized in that: after said face weave is accomplished, carry out preshrunk earlier and carry out 1. described dipping of step and dried then.
4. bamboo fibre according to claim 1 and the manufacturing approach of washing bright and beautiful fiber interweaving lining is characterized in that: when weaving said lining, adopt satin weave technology that warp is hidden in said lining inside, make parallel float on said lining surface.
5. a kind of bamboo fibre according to claim 1 and the manufacturing approach of washing bright and beautiful fiber interweaving lining, it is characterized in that: said post-finishing agent comprises that Bamboo vinegar solution and general formula are HO (C
2H
4O)
a-(C
3H
6O) b-(C
2H
4O)
aThe auxiliary agent of H, the content of said auxiliary agent is not less than 0.1%.
6. the lining that is made by above-mentioned arbitrary claim is characterized in that: the radial density of said lining is 170～175 pieces/inch, 80～85 pieces/inch of latitudinal densities; Lining ultimate strength>=240N; Washing shrinkage≤5%.
7. lining according to claim 6; It is characterized in that: said lining is a jacquard fabrics; Said jacquard fabrics is through will propose the lining with patterning that forms on said lining surface as the bamboo fibre yarn of warp from said lining interior section.
8. lining according to claim 6 is characterized in that: said lining is the satin weave lining, and said satin weave is five piece three and flies satin or five piece two and fly satin.