CN109369016A - A kind of month white glaze and preparation method thereof - Google Patents
A kind of month white glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109369016A CN109369016A CN201811522836.2A CN201811522836A CN109369016A CN 109369016 A CN109369016 A CN 109369016A CN 201811522836 A CN201811522836 A CN 201811522836A CN 109369016 A CN109369016 A CN 109369016A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- calcite
- quartz
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of month white glaze and preparation method thereof, and the moon white glaze is made from the following raw materials in parts by weight: 50 parts of melilite, 20 parts, 10 parts of calcite, 12 parts of Copper Ores, 10 parts of talcum powder, 0.5 part of tin oxide of quartz；The present invention is different from traditional formula and preparation method is different, with melilite for main raw material, quartz, calcite, Copper Ores, talcum powder and tin oxide are added, is needed during enamel frit makeing by a crucible for smelting, glaze good fluidity after melting, good luster.
Description
Technical field
The invention belongs to porcelain technical fields, and in particular to a kind of month white glaze and preparation method thereof.
Background technique
Pottery is one of five big kiln porcelain of China's Song Dynasty, the treasure in Chinese tradition technology in producing porcelain, with unique transmutation
Art and be renown far and wide in generation, be the exclusive national treasure porcelain in Henan Province Xuchang Yuzhou City town mind Hou.Pottery is originally color or heavy with glaze thickness
In glaze bottom or outstanding glaze or floating glaze table, the thick muddy work of glaze, glaze layer opalescence jade-like stone profit, work of being administrations with multiplied departments are intended to drip, and three-dimensional sense is extremely strong.Pottery
Be mind with transmutation, natural transmutation is that the essence place of pottery art and pottery are rely the four seas of becoming famous, porcelain woods of making a name it is rare it
Place.With a kind of glaze is applied in firing, then " it is of the same colour to enter kiln, kiln discharge ten thousand is color " in multicoloured once firing.Ever-changing transmutation
Effect, forms the infinite mystery of colors changing hue, it is dark blue, green in red inner purple, purple in reside it is white, white in general red, multicolored imbibition, phase
It reflects and blazes, and have the title of " pottery without right, transmutation is unparalleled ".
Chun glaze is one layer of decorative layer on pottery surface, is the principal element for determining pottery glaze colours and generating, utilizes natural mine
Raw material or the certain industrial chemicals of addition cooperate according to a certain percentage, melt under high temperature reducing atmospheres effect and are covered on green body
Surface increases the beauty of pottery natural trend with dicoration abundant rich in jade-like stone profit gloss and colorful vitreum layer
Sense makes pottery have certain artistic value and enjoying value.
Moon white glaze its glaze color ratio celeste glaze in chun glaze is thin, pure white clear like as moonlight, and enamel is bright and clean moist.Tradition
Using Yuzhou ore such as feldspar, quartz, calcite as primary raw material when firing, glaze colours is easy sootiness, goes out glaze eye, yield rate
It is low.
Summary of the invention
To solve the above-mentioned problems, the present invention provides a kind of month white glaze and preparation method thereof.
The technical solution adopted by the present invention are as follows:
A kind of month white glaze, it is made from the following raw materials in parts by weight: 50 parts of melilite, 20 parts of quartz, and 10 parts of calcite,
12 parts of Copper Ores, 10 parts of talcum powder, 0.5 part of tin oxide.
A kind of preparation method of moon white glaze as described above, comprising the following steps:
(1) melilite, quartz, calcite, the Copper Ores for weighing above-mentioned parts by weight are put into ball milling and crush, and are sieved after mixing
As mix powder；
(2) mix powder is placed in crucible and carries out melting, be smelted into the molten matter of fluidised form and be placed on quenching in sink, keep fluidised form molten
Matter splits into fritter；
(3) it fluidised form is melted into the fritter that matter is split into is placed in ball milling together with talcum powder, tin oxide and smash it through 200 mesh again
Sieve, what is finally obtained is the glaze of moon white glaze.
Melilite belongs to silicate mineral salt, and it is the master of glaze that internal content, which is potassium element, sodium element and calcium constituent etc.,
Ingredient is wanted, the formation mainly for glaze plays an important role.Numerous mineral reserve are distributed in Yuzhou.
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of prevention and treatment glaze paint and heap
Product, dosage cannot be excessive, otherwise will lead to glaze paint crystallization devitrification, temperature is caused to narrow, and variation is very few, and glaze paint is caused to be smoked.
Quartz is metamorphic rock, and content is silica, and the main glossiness for increasing glaze cannot be excessive, can not be lacked,
Otherwise it will cause glaze paint variation color to reduce.
Copper Ores are most important Copper Ores mineral, generally by Cu, tri- kinds of element compositions of Fe, S, theory composition (%) Cu
34.56, Fe 30.52, S 34.92, theoretical chemistry formula are CuFeS2。
Talcum powder is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion system
Number, promotes the formation of glaze-body interface, and increase opaque.
The beneficial effects of the present invention are: the present invention is different from traditional formula and preparation method is different, based on melilite
The raw material wanted is added quartz, calcite, Copper Ores, talcum powder and tin oxide, is needed during enamel frit makeing by a crucible
Melting, the glaze good fluidity after melting, good luster.
Specific embodiment
A kind of month white glaze, it is made from the following raw materials in parts by weight: 50 parts of melilite, 20 parts of quartz, and calcite 10
Part, 12 parts of Copper Ores, 10 parts of talcum powder, 0.5 part of tin oxide.
A kind of preparation method of moon white glaze as described above, comprising the following steps:
(1) melilite, quartz, calcite, the Copper Ores for weighing above-mentioned parts by weight are put into ball milling and crush, and are sieved after mixing
As mix powder；
(2) mix powder is placed in crucible and carries out melting, be smelted into the molten matter of fluidised form and be placed on quenching in sink, keep fluidised form molten
Matter splits into fritter；
(3) it fluidised form is melted into the fritter that matter is split into is placed in ball milling together with talcum powder, tin oxide and smash it through 200 mesh again
Sieve, what is finally obtained is the glaze of moon white glaze.
Embodiment 1
A kind of month white glaze, it is made from the following raw materials in parts by weight: 50 parts of melilite, 20 parts of quartz, and 10 parts of calcite,
12 parts of Copper Ores, 10 parts of talcum powder, 0.5 part of tin oxide.
A kind of preparation method of moon white glaze as described above, comprising the following steps:
(1) potassium feldspar, quartz, calcite, the Copper Ores for weighing above-mentioned parts by weight are put into ball milling and crush, and are sieved after mixing
As mix powder；
(2) mix powder is placed in crucible and carries out melting, crucible is generally located on the flue between kiln and chimney, under furnace
A supplement dye chamber separately is set, when flue gas shortage of heat or kiln stop burning, i.e., available aftercombustion room roasting, crucible has on bottom
One aperture is blocked with admant English bead, until mix powder be melt into fluidised form melt matter when, bead is floated, melt matter i.e. flow under
Quenching in the sink of face makes molten matter split into crisp and transparent fritter；
(3) fritter that molten matter is split into is placed in ball milling together with talcum powder, zinc oxide and smashes it through 140 meshes again, most
What is obtained afterwards is glaze.
Claims (2)
1. a kind of month white glaze, it is characterised in that: it is made from the following raw materials in parts by weight: 50 parts of melilite, 20 parts of quartz,
10 parts of calcite, 12 parts of Copper Ores, 10 parts of talcum powder, 0.5 part of tin oxide.
2. a kind of preparation method of moon white glaze as described in claim 1, it is characterised in that: the following steps are included:
(1) melilite, quartz, calcite, the Copper Ores for weighing above-mentioned parts by weight are put into ball milling and crush, and are sieved after mixing
As mix powder；
(2) mix powder is placed in crucible and carries out melting, be smelted into the molten matter of fluidised form and be placed on quenching in sink, keep fluidised form molten
Matter splits into fritter；
(3) it fluidised form is melted into the fritter that matter is split into is placed in ball milling together with talcum powder, tin oxide and smash it through 200 mesh again
Sieve, what is finally obtained is the glaze of moon white glaze.