CN109338566A - A kind of web process - Google Patents
A kind of web process Download PDFInfo
- Publication number
- CN109338566A CN109338566A CN201811436396.9A CN201811436396A CN109338566A CN 109338566 A CN109338566 A CN 109338566A CN 201811436396 A CN201811436396 A CN 201811436396A CN 109338566 A CN109338566 A CN 109338566A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- weft yarn
- warp thread
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of web process comprising step 1: yarn soaks, and learns from else's experience yarn and weft yarn is immersed in clear water;Step 2: yarn transmission, by step 1 warp thread and weft yarn be placed in transmission rack, transmission rack can be used for transmitting warp thread and weft yarn;Step 3: yarn drying is arranged in transmission rack and dries up section, and when warp thread and weft yarn pass through the drying section, warp thread and weft yarn are dried up along the vertical direction in state, drying fan is hung from above vertically positioned at the warp thread and weft yarn for drying up section;Step 4: fabric forming, by step 3 warp thread and weft yarn interweave jointly and form fabric.In above-mentioned fabric treatment process, using such as carrying out blowing straight processing from the basic composition yarn of fabric, it is formed by the smooth height of fabric fabric.
Description
Technical field
The present invention relates to the technical fields of fabric production, more particularly, to a kind of web process.
Background technique
The requirement that people wear flatness for clothing at present is higher and higher, and the flatness of clothing can be by various conditions
It is influenced.
Common clothing clothes processing flow can refer to one kind of Chinese invention patent application CN104983089A for needle
The processing method of woven garment, procedure of processing include spinning, braiding, perching, cutting, sew, blow hair, ironing, drying etc., process
In step, in order to guarantee that the relatively important step of later period flatness is ironing, ironing itself is to inside clothing fabric
Effect is straightened in yarn generation.
Although later period ironing can also be played the role of pressing clothing, if not can guarantee the straightness of fabric itself, no
It only will affect clothing straightness made of the later period, and the generation of measuring of fabric when making clothing can be bothered.
Fabric producer is during producing fabric, in order to guarantee the straightness of fabric, also only simply by pure physics
The mode being straightened, evens up fabric by force, and the fabric flatness produced has to be optimized.
Summary of the invention
The object of the present invention is to provide a kind of web process, the fabric flatness produced can be effectively promoted.
Foregoing invention purpose of the invention has the technical scheme that
A kind of web process, step 1: yarn soaks, and learns from else's experience yarn and weft yarn is immersed in clear water;
Step 2: yarn transmission, by step 1 warp thread and weft yarn be placed in transmission rack, transmission rack can be used for transmitting warp
Yarn and weft yarn;
Step 3: yarn drying, the setting drying section in transmission rack, when warp thread and weft yarn pass through the drying section, warp thread
The warp thread and weft yarn for being located at drying section are dried up along the vertical direction in state, drying fan is hung from above vertically with weft yarn;
Step 4: fabric forming, by step 3 warp thread and weft yarn interweave jointly and form fabric.
By using above-mentioned technical proposal, if certain bending occurs in yarn interior before production, yarn is immersed in clear water
In, after hanging state from above vertically, using gravity, yarn is integrally in hang state from above vertically, and drying fan is along vertical side
It is dried up to the part yarn, the yarn of bending state can also be dried, blow directly, and then will blow the yarn under straight state
Line is used for the braiding of fabric, and it is higher to be formed by fabric fabric flatness;In above-mentioned fabric treatment process, from the basic structure of fabric
It carries out blowing straight processing at yarn, is formed by the smooth height of fabric fabric.
Preferably, conductive yam is additionally provided in the fabric, the conductive yam is handed over jointly with the warp thread, the weft yarn three
It knits to form the fabric.
By using above-mentioned technical proposal, when being fabricated to clothing using the fabric, if generating electrostatic, the electrostatic when wearing
Electrical conduction can be carried out by conductive yam, certain anti-static electrification can be played.
Preferably, the conductive yam is carbon nanotube polyester electric conduction fiber.
By using above-mentioned technical proposal, carbon nanotube polyester electric conduction fiber is the conductive fiber of conductive relative good, is adopted
The conductive yam made of this material, anti-static effect is more preferably.
Preferably, step 5: the fabric of formation is immersed in concentrated alkali solution by the contracting of fabric alkali.
By using above-mentioned technical proposal, fabric is immersed in concentrated alkali solution, the density and bullet of fabric can be effectively increased
Property, and the intensity of fabric can be improved and improve gloss, reduce the washing shrinkage of fabric.
Preferably, step 6: fabric bleaching makees bleaching agent using sodium hypochlorite or hydrogen peroxide or sodium chlorite, to fabric
Carry out bleaching.
By using above-mentioned technical proposal, bleaching agent is made using sodium hypochlorite or hydrogen peroxide or sodium chlorite etc., it can be to base
Cloth carries out blanching effect, and fabric entirety whitening effect is preferable.
Preferably, step 7: fabric is soft, and softening agent is added and carries out supple-settlement.
By using above-mentioned technical proposal, softening agent meeting energy fabric generates emollescence, when fabric is used for later period clothing system
When making, it can be more easier to carry out cutting moulding to fabric, and wearing comfort is higher.
Preferably, step 8: fabric drying carries out drying and processing to the fabric in step 7.
By using above-mentioned technical proposal, heating, drying can be carried out to fabric outer surface, fabric outer surface as concentrated base it is molten
The non-dry liquids such as liquid, bleaching agent, softening agent originally can be dried sufficiently, be convenient for fabric subsequent use.
Preferably, step 9: scalding hair edge sealing, using heating member fitting fabric cloth along progress blanching edge sealing.
By using above-mentioned technical proposal, since traditional fabric selvedge can generate flash, in transport or production process,
Flash is easy to be extracted, and causes the part fabric to generate plucking and scraps, is carried out using heating member to fabric selvedge in step 9
It heats and scalds hair, flash caused by fabric selvedge can be removed, and fabric selvedge can be made to form melting edge sealing, can be greatly reduced
Scrappage when later period fabric produces.
Preferably, step 10: dust-removing hangs the fabric in transmitting step eight from above vertically, and blower is blown towards fabric surface
Wind dedusting.
By using above-mentioned technical proposal, to fabric, the dust being infected on fabric can be direct by blower for the wind of blower
It blows off, reaches dust removing effects.
Preferably, the wind that drying fan is blown out in step 3 is hot wind.
By using above-mentioned technical proposal, using hot wind, warp thread and weft yarn with clear water can be dried up directly, warp thread and
Weft yarn smoothes out with the fingers straight better effect.
In conclusion advantageous effects of the invention are as follows: soaked using yarn, yarn transmission, yarn drying, fabric at
Shape, the contracting of fabric alkali, fabric bleaching, fabric is soft, fabric drying, scalds hair edge sealing, dust-removing, and the fabric produced has flat
Whole degree is high, is not easy the few feature of plucking, remaining dust amount.
Detailed description of the invention
Fig. 1 is embodiment processing step flow diagram.
Specific embodiment
Below in conjunction with attached drawing, invention is further described in detail.
Referring to Fig.1, it is a kind of web process disclosed by the invention, production stage is:
Step 1: yarn soaks, and clean water is poured into cylinder, has warp thread and weft yarn cylinder to be immersed in clear water coiling
In, guarantee that warp thread and weft yarn surface are uniformly soaked by clear water, and yarn bobbin is in vertical display.
Step 2: yarn transmission, by step 1 warp thread and weft yarn be placed in transmission rack, the end of a thread of warp thread and weft yarn
It can be transmitted by a drive roll and pull or be directly connected with fabric forming device;
Step 3: yarn drying, the setting drying section in transmission rack, when warp thread and weft yarn pass through the drying section, warp thread
The warp thread and weft yarn for being located at drying section are dried up along the vertical direction in state, drying fan is hung from above vertically with weft yarn;In the step
Drying fan warm wind blower can be used, the wind which is blown out is hot wind, and hot wind can generate warp thread and weft yarn straight
Connecing desiccation, warp thread and weft yarn can also be blown directly by self weight.
Step 4: fabric shapes, and conductive yam is added in warp thread, weft yarn, and conductive yam selects carbon nanotube polyester electric conduction fiber,
Warp thread, weft yarn, conductive yam are interweaved jointly and form fabric.
Step 5: the fabric of formation is immersed in concentrated alkali solution by the contracting of fabric alkali.Alkali contracting is cotton fabrics in relaxed state
Under, with the technique of concentrated alkali solution processing.The purpose of alkali contracting is primarily to increase fabric
Density and elasticity, and the intensity of fabric can be improved and improve gloss, reduce the washing shrinkage of fabric.
Step 6: fabric bleaching is made bleaching agent using sodium hypochlorite or hydrogen peroxide or sodium chlorite, is bleached to fabric
Processing.Wherein, sodium hypochlorite bleaching effect is general, and easy damaged fiber, and has large effect, but its cost to environment
Low, equipment is simple, therefore is still widely used in cotton fabrics bleaching.Hydrogen peroxide bleaching effect is good, small to fibre damage, has
Certain impurity elimination ability, it is applicable not only to cotton, and other fibers can be made to obtain good bleaching effect, therefore particularly suitable
In the bleaching of cotton and the fine blended fabric of conjunction.Only bleaching effect is good on sodium chlorite, and small to fibre damage, its impurity elimination ability
By force, it is a kind of ideal bleaching agent to fiber wide adaptability.It therefore, is most preferably hydrogen peroxide in the present embodiment as bleaching agent.
Step 7: fabric is soft, and softening agent is added and carries out supple-settlement.Wherein, softening agent also selects softening agent 101, soft
Soft dose of HC etc., and then effective emollescence is carried out to fabric.
Step 8: fabric drying carries out drying and processing to the fabric in step 7, during processing, in step 7
It is by the way of vertically drying that fabric, which is preferably also, i.e. the whole vertical hang-up of fabric, dryer heats fabric outer surface,
By the undried liquid drying in fabric outer surface.
Step 9: scalding hair edge sealing, using heating member fitting fabric cloth along progress blanching edge sealing.Plane is in level where fabric
State, the quantity of heating member are two, and two heating members are located on two relative sides of fabric, the temperature foot of heating member
Enough horizontal transport can be constantly carried out along boiling hot hair operation, fabric is carried out to fabric cloth, fabric needs are tightened up, and keep the tight of cloth cover
Taut, heating member can be with fabric cloth along being contacted, and fabric cloth is scalded along upper flash meeting heated object, and flash can directly be scalded
Fall, fabric cloth edge can also obtain edge sealing.
Step 10: dust-removing after blower being similarly disposed at heating member, hangs the base in transmitting step eight from above vertically
Cloth, for blower towards fabric surface, the wind that blower is blown out is preferably cold wind, on the one hand, the wind energy that blower is blown out will be outside fabric
The dust on surface is blown down, and on the other hand, the cold wind of blower blowout can radiate in time to the edge sealing on fabric cloth edge, in turn
Guarantee the Forming Quality of later period fabric.
The embodiment of present embodiment is presently preferred embodiments of the present invention, not limits protection model of the invention according to this
Enclose, therefore: the equivalence changes that all structures under this invention, shape, principle are done, should all be covered by protection scope of the present invention it
It is interior.
Claims (10)
1. a kind of web process, production stage are:
Step 1: yarn soaks, and learns from else's experience yarn and weft yarn is immersed in clear water;
Step 2: yarn transmission, by step 1 warp thread and weft yarn be placed in transmission rack, transmission rack can be used for transmitting warp
Yarn and weft yarn;
Step 3: yarn drying, the setting drying section in transmission rack, when warp thread and weft yarn pass through the drying section, warp thread
The warp thread and weft yarn for being located at drying section are dried up along the vertical direction in state, drying fan is hung from above vertically with weft yarn;
Step 4: fabric forming, by step 3 warp thread and weft yarn interweave jointly and form fabric.
2. a kind of web process according to claim 1, production stage are: it is additionally provided with conductive yam in the fabric,
The conductive yam and the warp thread, the weft yarn three interweave jointly and form the fabric.
3. a kind of web process according to claim 2, production stage are: the conductive yam is carbon nanotube polyester
Conductive fiber.
4. a kind of web process according to claim 1, production stage are:
Step 5: the fabric of formation is immersed in concentrated alkali solution by the contracting of fabric alkali.
5. a kind of web process according to claim 4, production stage are: step 6: fabric bleaching, using secondary chlorine
Sour sodium or hydrogen peroxide or sodium chlorite make bleaching agent, carry out bleaching to fabric.
6. a kind of web process according to claim 5, production stage are: step 7: fabric is soft, is added soft
Agent carries out supple-settlement.
7. a kind of web process according to claim 6, production stage are: step 8: fabric drying, to step 7
In fabric carry out drying and processing.
8. a kind of web process according to claim 7, production stage are: step 9: hair edge sealing is scalded, using heating
Part is bonded fabric cloth along progress blanching edge sealing.
9. a kind of web process according to claim 8, production stage are: step 10: dust-removing is hung from above vertically
Fabric in transmitting step eight, blower is towards fabric surface dust-removing.
10. a kind of web process according to claim 1, production stage are: drying fan is blown in step 3
Wind out is hot wind.