CN106283329A - A kind of antistatic flame-retardant textile and production method thereof - Google Patents
A kind of antistatic flame-retardant textile and production method thereof Download PDFInfo
- Publication number
- CN106283329A CN106283329A CN201610649165.0A CN201610649165A CN106283329A CN 106283329 A CN106283329 A CN 106283329A CN 201610649165 A CN201610649165 A CN 201610649165A CN 106283329 A CN106283329 A CN 106283329A
- Authority
- CN
- China
- Prior art keywords
- mixed yarn
- yarn
- strand
- retardant textile
- antistatic flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to textile production technical field, be specifically related to a kind of antistatic flame-retardant textile and production method thereof.This fabric is the twills being made up of warp thread and weft yarn, wherein: warp thread is made up of with conductive yam the strand of mixed yarn × 2, and mixed yarn is the blending of FRC, aramid fiber and acrylic fiber, and conductive yam is the doubling of polyester filament and polyester derivative electrical filament；Weft yarn is the strand of mixed yarn × 2, and mixed yarn is the blending of FRC, aramid fiber and acrylic fiber.Its production method includes step: 1) warping process；2) sizing operation；3) denting；4) weaving process.The interval of antistatic flame-retardant textile fabric two warp thread provided by the present invention is reasonable, and fabric is soft, good permeability, antistatic are good, strength is high, has preferable snugness of fit.
Description
Technical field
The invention belongs to textile production technical field, be specifically related to a kind of antistatic flame-retardant textile and production method thereof.
Background technology
Along with expanding economy, textile application field constantly expands, and the especially utilization on technical textile is outstanding
It is prominent, brings many facilities to the productive life of people, but meanwhile, also bring some puzzlements and even endanger,
Such as textile is in wearing process, and produced electrostatic easily makes accumulation, causes dust to adhere to, and higher voltage is easily formed
Electric shock, even it may happen that blast under inflammable, explosive environments.The fire incident thus caused in turn results in showing of massive losses
As the most too numerous to enumerate.Therefore, how to give that textile is the most functional important realistic meaning.
Summary of the invention
For solving the deficiencies in the prior art, the invention provides a kind of antistatic flame-retardant textile and production method thereof.
A kind of antistatic flame-retardant textile, for the twills being made up of warp thread and weft yarn, wherein:
Described warp thread is made up of with conductive yam the strand of mixed yarn × 2, and described mixed yarn is FRC, aramid fiber fibre
The blending of peacekeeping acrylic fiber, described conductive yam is the doubling of polyester filament and polyester derivative electrical filament.
Concrete, in warp thread, the strand of mixed yarn × 2 arranges according to the ratio of 55～65:1 with conductive yam, it is preferred that mixed
The strand of spinning × 2 arranges according to the ratio of 60:1 with conductive yam.
Concrete, in warp thread, mixed yarn be ratio be 40～50:20～30:25～35 FRC, aramid fiber fine
The blending of peacekeeping acrylic fiber, it is preferred that mixed yarn be ratio be the FRC of 45:25:30, aramid fiber and acrylon
The blending of fiber.
Described weft yarn is the strand of mixed yarn × 2, and described mixed yarn is FRC, aramid fiber and acrylic fiber
Blending.
Concrete, in weft yarn, mixed yarn be ratio be 40～50:20～30:25～35 FRC, aramid fiber fine
The blending of peacekeeping acrylic fiber, it is preferred that mixed yarn be ratio be the FRC of 45:25:30, aramid fiber and acrylon
The blending of fiber.
Concrete, the count of mixed yarn in described warp thread and the mixed yarn in described weft yarn be respectively 19.5～
20.0tex.Preferably, the mixed yarn in described warp thread is 19.7tex with the count of the mixed yarn in described weft yarn.
Concrete, the end count of antistatic flame-retardant textile is 250～255/10cm, filling density 195～200/10cm, fabric width
160～170cm, it is preferred that the end count of antistatic flame-retardant textile is 252/10cm, 197/10cm of filling density, fabric width 165cm.
Preferred: polyester filament model is DTY75D；Polyester derivative electrical filament model is that 18D ash is led；In warp thread, mixed yarn × 2
Strand 4200, conductive yam 70；Two warp thread be spaced apart 2.4cm.
Present invention also offers the production method of a kind of antistatic flame-retardant textile, comprise the following steps:
1) warping process
Strand and conductive yam to mixed yarn × 2 carry out warping respectively, and warping speed controls at 400～500 ms/min,
The weight of conductive yam tension pulley is 1.8～2.2 times of the strand tension pulley weight of mixed yarn × 2.
2) sizing operation
Strand and conductive yam to mixed yarn × 2 carry out sizing respectively, and sizing speed is 40～45 meters/min.
Concrete,
Step 2) in the slurry that uses include each raw material of following weight portion: the phosphate ester starch of 35.0～40.0 parts, 4.5
～the liquid propene of 5.5 parts, the smooth agent of 9.0～11.0 parts, the bisnaphthol of 0.9～1.1 part, slurry solid content is 4.2 ±
1%.
Phosphate ester starch, from prior art, can obtain, such as: Wuhan Dong Mei company produces by the way of purchase
JF-962 series of products.
Liquid propene, from prior art, can obtain, such as: the DH-that Wuhan Dong Mei company produces by the way of purchase
930 series of products.
Smooth agent, from prior art, can obtain, such as: the series that Wuhan Dong Mei company produces by the way of purchase
DH-68 product.
Preferably, step 2) in the slurry that uses include each raw material of following weight portion: the phosphate ester starch of 37.5 parts, 5
The liquid propene of part, the smooth agent of 10 parts, the bisnaphthol of 1 part, slurry solid content is 4.2 ± 1%.
Preferably, single stock tank sizing is used.
3) denting
Menopause tablet, heald, reed is sequentially passed through, when passing, in strict accordance with two kinds of warps according to the requirement of looming draft design
The arrangement ratio of yarn penetrates.
4) weaving process
It is interleaved obtaining fabric by the strand of the strand/conductive yam of warp thread mixed yarn × 2 Yu weft yarn mixed yarn × 2.
Preferably, step 4) in: loom speed is 500r/min, and warp tension is 1850 ± 50N, and heald level time is
300°。
Concrete, step 4) in: being 2 before and after back rest position, height is 75, is-1, highly before and after warp stop frame position
It is that page 0,1～4 heald frame height is respectively 130mm, 123mm, 123mm, 123mm, 128mm, 18mm benchmark ZA203-190 and is
114mm, page 1～6 heald frame opening amount big blade a value is respectively 110mm, 70mm, 65mm, 60mm, 50mm, 40mm, pickwheel
32T/4。
The production method mixed yarn of antistatic flame-retardant textile provided by the present invention does a kind of through yarn material, utilizes terylene
Long filament does another kind of through yarn material, and both coordinate certain arrangement ratio, uses the formula of size of rational allocation, repeatedly optimizes technique
Method, according to 2/1 twill left to right design organization, air-jet loom can complete high-quality production.Provided by the present invention anti-
The interval of electrostatic flame-retardant textile fabric two warp thread is reasonable, and fabric is soft, good permeability, antistatic are good, strength is high, has relatively
Good snugness of fit.
Detailed description of the invention
Principle and feature to the present invention are described below, and example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1
1) warping process
Strand and conductive yam to mixed yarn × 2 carry out warping respectively, and warping speed controls at 450 ms/min, conductive yam
The weight of tension pulley is 2 times of the strand tension pulley weight of mixed yarn × 2.
2) sizing operation
Strand and conductive yam to mixed yarn × 2 carry out sizing respectively, and sizing speed is 42.5 meters/min.
The slurry used includes each raw material of following weight portion: the phosphate ester starch of 37.5 parts, the liquid propene of 5 parts, 10
The smooth agent of part, the bisnaphthol of 1 part, slurry solid content is 4.2 ± 1%, uses single stock tank sizing.
3) denting
Menopause tablet, heald, reed is sequentially passed through, when passing, in strict accordance with two kinds of warps according to the requirement of looming draft design
The arrangement ratio of yarn penetrates.
4) weaving process
It is interleaved obtaining fabric by the strand of the strand/conductive yam of warp thread mixed yarn × 2 Yu weft yarn mixed yarn × 2.
Loom speed is 500r/min, and warp tension is 1850 ± 50N, and heald level time is 300 °.Before and after back rest position
Being 2, height is 75, be-1 before and after warp stop frame position, be highly page 0,1～4 heald frame height be respectively 130mm, 123mm,
123mm, 123mm, 128mm, 18mm benchmark ZA203-190 is 114mm, and page 1～6 heald frame opening amount big blade a value is respectively
110mm, 70mm, 65mm, 60mm, 50mm, 40mm, pickwheel 32T/4.
Embodiment 2
1) warping process
Strand and conductive yam to mixed yarn × 2 carry out warping respectively, and warping speed controls at 400 ms/min, conductive yam
The weight of tension pulley is 2.2 times of the strand tension pulley weight of mixed yarn × 2.
2) sizing operation
Strand and conductive yam to mixed yarn × 2 carry out sizing respectively, and sizing speed is 45 meters/min.
The slurry used includes each raw material of following weight portion: the phosphate ester starch of 35.00 parts, the liquid propene of 5.5 parts,
The smooth agent of 9.0 parts, the bisnaphthol of 1.1 parts, slurry solid content is 4.2 ± 1%, uses single stock tank sizing.
3) denting
Menopause tablet, heald, reed is sequentially passed through, when passing, in strict accordance with two kinds of warps according to the requirement of looming draft design
The arrangement ratio of yarn penetrates.
4) weaving process
It is interleaved obtaining fabric by the strand of the strand/conductive yam of warp thread mixed yarn × 2 Yu weft yarn mixed yarn × 2.
Loom speed is 500r/min, and warp tension is 1850 ± 50N, and heald level time is 300 °.Before and after back rest position
Being 2, height is 75, be-1 before and after warp stop frame position, be highly page 0,1～4 heald frame height be respectively 130mm, 123mm,
123mm, 123mm, 128mm, 18mm benchmark ZA203-190 is 114mm, and page 1～6 heald frame opening amount big blade a value is respectively
110mm, 70mm, 65mm, 60mm, 50mm, 40mm, pickwheel 32T/4.
Embodiment 3
1) warping process
Strand and conductive yam to mixed yarn × 2 carry out warping respectively, and warping speed controls at 500 ms/min, conductive yam
The weight of tension pulley is 2.2 times of the strand tension pulley weight of mixed yarn × 2.
2) sizing operation
Strand and conductive yam to mixed yarn × 2 carry out sizing respectively, and sizing speed is 40 meters/min.
The slurry used includes each raw material of following weight portion: the phosphate ester starch of 40.0 parts, the liquid propene of 4.5 parts,
The smooth agent of 11.0 parts, the bisnaphthol of 0.9 part, slurry solid content is 4.2 ± 1%, uses single stock tank sizing.
3) denting
Menopause tablet, heald, reed is sequentially passed through, when passing, in strict accordance with two kinds of warps according to the requirement of looming draft design
The arrangement ratio of yarn penetrates.
4) weaving process
It is interleaved obtaining fabric by the strand of the strand/conductive yam of warp thread mixed yarn × 2 Yu weft yarn mixed yarn × 2.
Loom speed is 500r/min, and warp tension is 1850 ± 50N, and heald level time is 300 °.Before and after back rest position
Being 2, height is 75, be-1 before and after warp stop frame position, be highly page 0,1～4 heald frame height be respectively 130mm, 123mm,
123mm, 123mm, 128mm, 18mm benchmark ZA203-190 is 114mm, and page 1～6 heald frame opening amount big blade a value is respectively
110mm, 70mm, 65mm, 60mm, 50mm, 40mm, pickwheel 32T/4.
The foregoing is only the better embodiment of the present invention, not in order to limit the present invention, all spirit in the present invention
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (10)
1. an antistatic flame-retardant textile, it is characterised in that: for the twills being made up of warp thread and weft yarn, wherein:
Described warp thread is made up of with conductive yam the strand of mixed yarn × 2, described mixed yarn be FRC, aramid fiber and
The blending of acrylic fiber, described conductive yam is the doubling of polyester filament and polyester derivative electrical filament；
Described weft yarn is the strand of mixed yarn × 2, and described mixed yarn is the mixed of FRC, aramid fiber and acrylic fiber
Spin.
Antistatic flame-retardant textile the most according to claim 1, it is characterised in that in described warp thread: the strand of mixed yarn × 2
Arrange according to the ratio of 55～65:1 with conductive yam；Mixed yarn be ratio be 40～50:20～30:25～35 anti-flaming viscose fine
Dimension, aramid fiber and the blending of acrylic fiber.
Antistatic flame-retardant textile the most according to claim 1, it is characterised in that in described weft yarn: mixed yarn is that ratio is
The blending of FRC, aramid fiber and the acrylic fiber of 40～50:20～30:25～35.
Antistatic flame-retardant textile the most according to claim 1, it is characterised in that the mixed yarn in described warp thread and described latitude
The count of the mixed yarn in yarn is respectively 19.5～20.0tex.
Antistatic flame-retardant textile the most according to claim 1, it is characterised in that: end count is 250～255/10cm, filling density
195～200/10cm, fabric width 160～170cm.
6. the production method of an antistatic flame-retardant textile, it is characterised in that comprise the following steps:
1) warping process
Strand and conductive yam to mixed yarn × 2 carry out warping respectively, and warping speed controls at 400～500 ms/min, conduction
The weight of yarn tension dish is 1.8～2.2 times of the strand tension pulley weight of mixed yarn × 2；
2) sizing operation
Strand and conductive yam to mixed yarn × 2 carry out sizing respectively, and sizing speed is 40～45 meters/min；
3) denting；
4) weaving process
It is interleaved obtaining fabric by the strand of the strand/conductive yam of warp thread mixed yarn × 2 Yu weft yarn mixed yarn × 2.
The production method of antistatic flame-retardant textile the most according to claim 6, it is characterised in that step 2) the middle slurry used
Material includes each raw material of following weight portion: the phosphate ester starch of 35.0～40.0 parts, the liquid propene of 4.5～5.5 parts, 9.0～
The smooth agent of 11.0 parts, the bisnaphthol of 0.9～1.1 part, slurry solid content is 4.2 ± 1%.
The production method of antistatic flame-retardant textile the most according to claim 6, it is characterised in that step 2) in: use single
Stock tank sizing.
The production method of antistatic flame-retardant textile the most according to claim 6, it is characterised in that step 4) in: loom speed
Degree is 500r/min, and warp tension is 1850 ± 50N, and heald level time is 300 °.
The production method of antistatic flame-retardant textile the most according to claim 6, it is characterised in that step 4) in: back rest position
Being 2 before and after putting, height is 75, be-1 before and after warp stop frame position, be highly page 0,1～4 heald frame height be respectively 130mm,
123mm, 123mm, 123mm, 128mm, 18mm benchmark ZA203-190 is 114mm, page 1～6 heald frame opening amount big blade a value point
Not Wei 110mm, 70mm, 65mm, 60mm, 50mm, 40mm, pickwheel 32T/4.