CN109294435A - A kind of nontoxic fire-type stainless steel materials paint - Google Patents
A kind of nontoxic fire-type stainless steel materials paint Download PDFInfo
- Publication number
- CN109294435A CN109294435A CN201811012983.5A CN201811012983A CN109294435A CN 109294435 A CN109294435 A CN 109294435A CN 201811012983 A CN201811012983 A CN 201811012983A CN 109294435 A CN109294435 A CN 109294435A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- resin
- silicone resin
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of nontoxic fire-type stainless steel materials paint, it is made of according to parts by weight following raw material: 12~18 parts of kochenite, 14~18 parts of resin, 18~26 parts of epoxy modified silicone resin, 0.1~0.6 part of antimony oxide, 15~24 parts of water soluble resin, 16~22 parts of turpentine oil, 5~15 parts of silicone resin, hydrogenate 12~18 parts of fourth cyanogen glue, 1.3~1.9 parts of hydroxyethyl cellulose, 7~15 parts of tea-seed oil, 3~8 parts of kaolinite, do not float 3.2~4.3 parts of type aluminium powder slurries, 7~12 parts of tung oil, 4~8 parts of clay, 0.3~0.7 part of deionized water, 2.8~3.5 parts of rutile type titanium white, 4~9 parts and 0.3~0.8 part of triethanolamine of adhesive.The features such as fire-retardant paint of the present invention can obstruct fire spreading, and fire protecting performance is good, and small toxicity, anti-corrosion ability is strong, can be attached to body surface for a long time, durable.
Description
Technical field
The present invention relates to stainless steel materials to produce and process correlative technology field, more particularly to a kind of nontoxic fire-type
Stainless steel materials paint.
Background technique
Paint be it is a kind of can securely be covered on body surface, the chemistry for playing protection, decoration, mark and other specific uses is mixed
Close object coating.Paint is viscous oily pigment, inflammable in not dry situation, not soluble in water, is slightly soluble in fat, dissolve in alcohol, aldehyde,
Ether, benzene, alkane are soluble in gasoline, kerosene, diesel oil.
It is all by film forming matter, subsidiary film forming matter and three kinds of auxiliary film forming matter no matter painting kind or form
Base substance composition: film forming matter: also referred to as binder, film forming matter is largely organic high molecular compound such as natural resin
The mixes such as (rosin, lacquer), coating (tung oil, flame retardant, soya-bean oil, fish oil etc.), synthetic resin, by pyroreaction
At the paint (such as: inorganic zinc rich paint) that also organic/inorganic substance combines.It is the main body for constituting paint, decides the performance of paint film.Such as
Fruit does not have film forming matter, and simple pigment and auxiliary material cannot form paint film.
Subsidiary film forming matter: including various pigment, extender pigment, rust resisting pigment.Pigment provides color and covering for paint film
Power, improves the protective value and decorative effect of paint, and the service life of paint can be improved in the pigment of good weatherability.Extender pigment can
It is folded multiple by the accumulation of pigment using the performance of itself " sheet, needle-shaped " structure to increase the thickness of paint film, form fish scale
The paint film of shape improves the service life of paint film, improves waterproofness and rust-proof effect.Rust resisting pigment passes through itself physics and chemistry
Anti-rust action, prevents body surface by atmosphere, chemicals attack, and metal surface is rusted.
Auxiliary film forming matter: including various auxiliary agents, solvent, various auxiliary agents are in the production process of paint, storage process, use
Process and the forming process of paint film play the role of very important.Although the amount used is all seldom, to the performance shadow of paint film
It rings very big.It even can not form paint film such as: not doing, sink to the bottom agglomeration, skinning.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the fire prevention that the one kind proposed is nontoxic
Type stainless steel materials paint.
To achieve the goals above, present invention employs following technical solutions:
A kind of nontoxic fire-type stainless steel materials paint, is made of according to parts by weight following raw material: kochenite 12
~18 parts, 14~18 parts of resin, 18~26 parts of epoxy modified silicone resin, 0.1~0.6 part of antimony oxide, water soluble resin 15~
24 parts, 16~22 parts of turpentine oil, 5~15 parts of silicone resin, hydrogenation 12~18 parts of fourth cyanogen glue, 15~25 parts of zeolite powder, linseed oil
10~18 parts, 1.6~2.3 parts of polyvinyl butyral, 1.5~2.3 parts of butanol, 1.3~1.9 parts of hydroxyethyl cellulose, tea seed
7~15 parts of oil, 3~8 parts of kaolinite, not floating 3.2~4.3 parts of type aluminium powder slurries, 7~12 parts of tung oil, glues 1.7~2.5 parts of copper powder
Native 4~8 parts, 1.4~1.9 parts of aluminium oxide, 0.3~0.7 part of deionized water, 2.8~3.5 parts of rutile type titanium white, adhesive 4
~9 parts and 0.3~0.8 part of triethanolamine.
The nontoxic fire-type stainless steel materials paint of above-mentioned one kind, is made of according to parts by weight following raw material:
12~17 parts of kochenite, 14~17 parts of resin, 18~25 parts of epoxy modified silicone resin, 0.1~0.5 part of antimony oxide, water
15~23 parts of molten resin, 16~21 parts of turpentine oil, 5~14 parts of silicone resin, hydrogenation 12~17 parts of fourth cyanogen glue, zeolite powder 15~24
Part, 10~17 parts of linseed oil, 1.6~2.2 parts of polyvinyl butyral, 1.5~2.2 parts of butanol, hydroxyethyl cellulose 1.3~
1.8 parts, 7~14 parts of tea-seed oil, 1.7~2.4 parts of copper powder, 3~7 parts of kaolinite, not floating 3.2~4.2 parts of type aluminium powder slurries, tung oil
7~11 parts, 4~7 parts of clay, 1.4~1.8 parts of aluminium oxide, 0.3~0.6 part of deionized water, rutile type titanium white 2.8~3.4
Part, 4~8 parts of adhesive and 0.3~0.7 part of triethanolamine.
The nontoxic fire-type stainless steel materials paint of above-mentioned one kind, is made of according to parts by weight following raw material:
13~18 parts of kochenite, 15~18 parts of resin, 19~26 parts of epoxy modified silicone resin, 0.2~0.6 part of antimony oxide, water
16~24 parts of molten resin, 17~22 parts of turpentine oil, 6~15 parts of silicone resin, hydrogenation 13~18 parts of fourth cyanogen glue, zeolite powder 16~25
Part, 11~18 parts of linseed oil, 1.7~2.3 parts of polyvinyl butyral, 1.6~2.3 parts of butanol, hydroxyethyl cellulose 1.4~
1.9 parts, 8~15 parts of tea-seed oil, 1.8~2.5 parts of copper powder, 4~8 parts of kaolinite, not floating 3.3~4.3 parts of type aluminium powder slurries, tung oil
8~12 parts, 5~8 parts of clay, 1.5~1.9 parts of aluminium oxide, 0.4~0.7 part of deionized water, rutile type titanium white 2.9~3.5
Part, 5~9 parts of adhesive and 0.4~0.8 part of triethanolamine.
The nontoxic fire-type stainless steel materials paint of above-mentioned one kind, is made of according to parts by weight following raw material:
15 parts of kochenite, 16 parts of resin, 22 parts of epoxy modified silicone resin, 0.35 part of antimony oxide, 19.5 parts of water soluble resin, turpentine
19 parts of oil, 10 parts of silicone resin, hydrogenation 15 parts of fourth cyanogen glue, 20 parts of zeolite powder, 14 parts of linseed oil, polyvinyl butyral 1.95
Part, does not float type aluminum paste at 1.9 parts of butanol, 1.6 parts of hydroxyethyl cellulose, 11 parts of tea-seed oil, 2.1 parts of copper powder, 5.5 parts of kaolinite
3.75 parts of liquid, 6 parts of clay, 1.65 parts of aluminium oxide, 0.5 part of deionized water, 3.15 parts of rutile type titanium white, glues 9.5 parts of tung oil
6.5 parts and 0.55 part of triethanolamine of mixture.
Compared with prior art, the invention has the benefit that
The nontoxic fire-type stainless steel materials of one kind of the invention have the advantages that fire resistance property is strong with paint, encounter open fire
It is nonflammable later, the security performance of security performance and storage that paint uses is improved there is no any security risk,
And it is suitable for the adverse circumstances such as high temperature, humidity, pH-value be higher, has that formula is simple, low manufacture cost, the scope of application
Extensively, the advantages of being readily produced, convenient for beneficial effects such as popularization and use.
Specific embodiment
Embodiment 1
A kind of nontoxic fire-type stainless steel materials paint, is made of according to parts by weight following raw material: kochenite 12
Part, 14 parts of resin, 18 parts of epoxy modified silicone resin, 0.1 part of antimony oxide, 15 parts of water soluble resin, 16 parts of turpentine oil, silicone tree
5 parts of rouge, hydrogenation 12 parts of fourth cyanogen glue, 15 parts of zeolite powder, 10 parts of linseed oil, 1.6 parts of polyvinyl butyral, 1.5 parts of butanol, hydroxyl second
1.3 portions of base cellulose, 1.7 parts of copper powder, 3 parts of kaolinite, does not float 3.2 parts of type aluminium powder slurries, 7 parts of tung oil, clay 4 at 7 parts of tea-seed oil
Part, 1.4 parts of aluminium oxide, 0.3 part of deionized water, 2.8 parts of rutile type titanium white, 4 parts of adhesive and 0.3 part of triethanolamine.
Embodiment 2
The nontoxic fire-type stainless steel materials paint of above-mentioned one kind, is made of according to parts by weight following raw material: amber
18 parts of resin, 18 parts of resin, 26 parts of epoxy modified silicone resin, 0.6 part of antimony oxide, 24 parts of water soluble resin, 22 parts of turpentine oil,
15 parts of silicone resin, hydrogenation 18 parts of fourth cyanogen glue, 25 parts of zeolite powder, 18 parts of linseed oil, 2.3 parts of polyvinyl butyral, butanol 2.3
Part, does not float 4.3 parts of type aluminium powder slurries, tung oil at 1.9 parts of hydroxyethyl cellulose, 15 parts of tea-seed oil, 2.5 parts of copper powder, 8 parts of kaolinite
12 parts, 8 parts of clay, 1.9 parts of aluminium oxide, 0.7 part of deionized water, 3.5 parts of rutile type titanium white, 9 parts of adhesive and three ethyl alcohol
0.8 part of amine.
Embodiment 3
The nontoxic fire-type stainless steel materials paint of above-mentioned one kind, is made of according to parts by weight following raw material: amber
15 parts of resin, 16 parts of resin, 22 parts of epoxy modified silicone resin, 0.35 part of antimony oxide, 19.5 parts of water soluble resin, turpentine oil 19
Part, 10 parts of silicone resin, hydrogenation 15 parts of fourth cyanogen glue, 20 parts of zeolite powder, 14 parts of linseed oil, 1.95 parts of polyvinyl butyral, fourth
1.9 parts of alcohol, 11 parts of tea-seed oil, 2.1 parts of copper powder, 5.5 parts of kaolinite, does not float type aluminium powder slurries 3.75 at 1.6 parts of hydroxyethyl cellulose
Part, 9.5 parts of tung oil, 6 parts of clay, 1.65 parts of aluminium oxide, 0.5 part of deionized water, 3.15 parts of rutile type titanium white, adhesive
6.5 parts and 0.55 part of triethanolamine.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of nontoxic fire-type stainless steel materials paint, which is characterized in that have following raw material group according to parts by weight
At: 12~18 parts of kochenite, 14~18 parts of resin, 18~26 parts of epoxy modified silicone resin, 0.1~0.6 part of antimony oxide,
15~24 parts of water soluble resin, 16~22 parts of turpentine oil, 5~15 parts of silicone resin, 12~18 parts of fourth cyanogen glue of hydrogenation, zeolite powder 15~
25 parts, 10~18 parts of linseed oil, 1.6~2.3 parts of polyvinyl butyral, 1.5~2.3 parts of butanol, hydroxyethyl cellulose 1.3~
1.9 parts, 7~15 parts of tea-seed oil, 1.7~2.5 parts of copper powder, 3~8 parts of kaolinite, not floating 3.2~4.3 parts of type aluminium powder slurries, tung oil
7~12 parts, 4~8 parts of clay, 1.4~1.9 parts of aluminium oxide, 0.3~0.7 part of deionized water, rutile type titanium white 2.8~3.5
Part, 4~9 parts of adhesive and 0.3~0.8 part of triethanolamine.
2. the nontoxic fire-type stainless steel materials paint of one kind according to claim 1, which is characterized in that according to
Parts by weight are made of following raw material: 12~17 parts of kochenite, 14~17 parts of resin, epoxy modified silicone resin 18~25
Part, 0.1~0.5 part of antimony oxide, 15~23 parts of water soluble resin, 16~21 parts of turpentine oil, 5~14 parts of silicone resin, hydrogenation fourth cyanogen
12~17 parts of glue, 15~24 parts of zeolite powder, 10~17 parts of linseed oil, 1.6~2.2 parts of polyvinyl butyral, butanol 1.5~
2.2 parts, 1.3~1.8 parts of hydroxyethyl cellulose, 7~14 parts of tea-seed oil, 1.7~2.4 parts of copper powder, 3~7 parts of kaolinite, not floating type
3.2~4.2 parts of aluminium powder slurries, 7~11 parts of tung oil, 4~7 parts of clay, 1.4~1.8 parts of aluminium oxide, deionized water 0.3~0.6
Part, 2.8~3.4 parts of rutile type titanium white, 4~8 parts of adhesive and 0.3~0.7 part of triethanolamine.
3. the nontoxic fire-type stainless steel materials paint of one kind according to claim 1, which is characterized in that according to
Parts by weight are made of following raw material: 13~18 parts of kochenite, 15~18 parts of resin, epoxy modified silicone resin 19~26
Part, 0.2~0.6 part of antimony oxide, 16~24 parts of water soluble resin, 17~22 parts of turpentine oil, 6~15 parts of silicone resin, hydrogenation fourth cyanogen
13~18 parts of glue, 16~25 parts of zeolite powder, 11~18 parts of linseed oil, 1.7~2.3 parts of polyvinyl butyral, butanol 1.6~
2.3 parts, 1.4~1.9 parts of hydroxyethyl cellulose, 8~15 parts of tea-seed oil, 1.8~2.5 parts of copper powder, 4~8 parts of kaolinite, not floating type
3.3~4.3 parts of aluminium powder slurries, 8~12 parts of tung oil, 5~8 parts of clay, 1.5~1.9 parts of aluminium oxide, deionized water 0.4~0.7
Part, 2.9~3.5 parts of rutile type titanium white, 5~9 parts of adhesive and 0.4~0.8 part of triethanolamine.
4. the nontoxic fire-type stainless steel materials paint of one kind according to claim 1, which is characterized in that according to
Parts by weight are made of following raw material: 15 parts of kochenite, 16 parts of resin, 22 parts of epoxy modified silicone resin, antimony oxide 0.35
Part, 19.5 parts of water soluble resin, 19 parts of turpentine oil, 10 parts of silicone resin, hydrogenation 15 parts of fourth cyanogen glue, 20 parts of zeolite powder, linseed oil 14
Part, 1.95 parts of polyvinyl butyral, 1.9 parts of butanol, 1.6 parts of hydroxyethyl cellulose, 11 parts of tea-seed oil, 2.1 parts of copper powder, kaolinite
5.5 parts of stone, not floating 3.75 parts of type aluminium powder slurries, 9.5 parts of tung oil, 6 parts of clay, 1.65 parts of aluminium oxide, 0.5 part of deionized water, gold
3.15 parts of red stone-type titanium dioxide, 6.5 parts of adhesive and 0.55 part of triethanolamine.