CN109293893A - 一种耐紫外线高透明的芳杂环聚合物树脂及其制备方法和在纤维或薄膜的应用 - Google Patents

一种耐紫外线高透明的芳杂环聚合物树脂及其制备方法和在纤维或薄膜的应用 Download PDF

Info

Publication number
CN109293893A
CN109293893A CN201811145331.9A CN201811145331A CN109293893A CN 109293893 A CN109293893 A CN 109293893A CN 201811145331 A CN201811145331 A CN 201811145331A CN 109293893 A CN109293893 A CN 109293893A
Authority
CN
China
Prior art keywords
aromatic heterocyclic
polymer resin
heterocyclic polymer
high transparency
resistant high
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811145331.9A
Other languages
English (en)
Inventor
潘鑫
刘文熙
王庭辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811145331.9A priority Critical patent/CN109293893A/zh
Publication of CN109293893A publication Critical patent/CN109293893A/zh
Pending legal-status Critical Current

Abstract

本发明涉及树脂技术领域，具体涉及一种耐紫外线高透明的芳杂环聚合物树脂及其制备方法和在纤维或薄膜的应用，所述耐紫外线高透明的芳杂环聚合物树脂的制备方法为：以偶氮苯‑4,4’‑二甲酸和/或偶氮苯‑3,3’‑二甲酸、含氟对苯二甲酸和/或含氟邻苯二甲酸、硫酸肼为反应原料，在发烟硫酸中进行缩聚反应，得到所述芳杂环聚合物树脂。本发明的芳杂环聚合物树脂具有优异的耐紫外线性能和较高的透明度，还具有良好的尺寸稳定性、耐热性、耐氧化、电绝缘、耐溶剂性、特殊的导电性以及电致发光等性能，综合性能优异。

Description

一种耐紫外线高透明的芳杂环聚合物树脂及其制备方法和在 纤维或薄膜的应用
技术领域
本发明涉及树脂技术领域，具体涉及一种耐紫外线高透明的芳杂环聚合物树脂及其制备方法和在纤维或薄膜的应用。
背景技术
杂环化合物环状有机化合物中，构成环的原子除碳原子外还有其他原子时，这类环状有机化合物叫作杂环化合物，非碳原子称为杂原子。最常见的杂原子是氧和硫，杂环上可以有一个杂原子，也可以有两个或更多个杂原子，杂原子可以是一种原子，也可以是两种不同的原子。和环烷烃一样，杂环也可以分为脂杂环和芳杂环两大类。一般来说，芳杂环的环系都有一定程度的稳定性和芳香性，在一般化学反应中，环不易破裂。部分芳杂环可以聚合成高分子树脂，由于其独特的优良性能而具有广泛的潜在应用价值。
发明内容
为了克服现有技术中存在的缺点和不足，本发明的目的在于提供一种耐紫外线高透明的芳杂环聚合物树脂，该芳杂环聚合物树脂具有优异的耐紫外线性能和较高的透明度，还具有良好的尺寸稳定性、耐热性、耐氧化、电绝缘、耐溶剂性、特殊的导电性以及电致发光等性能，综合性能优异。
本发明的另一个目的在于提供一种耐紫外线高透明的芳杂环聚合物树脂的制备方法，该制备方法步骤简单，操作控制方便，质量稳定，生产效率高，生产成本低，可大规模化工业生产。
本发明的还一个目的在于提供一种耐紫外线高透明的芳杂环聚合物树脂的应用。
本发明的目的通过下述技术方案实现：一种耐紫外线高透明的芳杂环聚合物树脂，所述芳杂环聚合物树脂包括以Am-Bn表示的聚合物链，其中，A和B均为构成聚合物链主链的重复单元，且重复单元A、B以任意顺序排列，m和n均为正整数；
所述重复单元A的结构式为：
所述重复单元B的结构式为：其中，R1、R2、R3和R4为未取代或取代的氟，且R1、R2、R3和R4中至少有一个为取代的氟。
优选的，所述主链中具有无规共聚物构型、交替共聚物构型或嵌段共聚物构型，即，所述芳杂环聚合物树脂的聚合方式可以为无规共聚、交替共聚或嵌段共聚。
优选的，所述芳杂环聚合物树脂采用无机填料进行改性。
优选的，所述无机填料为云母、炭黑、白炭黑、滑石粉、硅灰石、氮化物、碳化物、氧化物、硫酸盐、碳酸盐、硅酸盐、氟硅酸盐和磷酸盐中的至少一种。
优选的，所述氮化物为氮化硅和/或氮化硼；所述碳化物为碳化硅和/或碳化硼；所述氧化物为氧化钙、氧化锌、氧化镁、氧化铁、二氧化硅和二氧化钛中的至少一种。
优选的，所述二氧化硅为纳米二氧化硅，所述二氧化钛为纳米二氧化钛。
优选的，所述硫酸盐为硫酸钙、硫酸镁、硫酸锌、硫酸钡、硫酸铁、硫酸亚铁中的至少一种；所述硅酸盐为硅酸钠、硅酸铝和硅酸镁中的至少一种；所述碳酸盐为碳酸钙、碳酸镁和碳酸锌中的至少一种；所述氟硅酸盐为氟硅酸钠、氟硅酸钾和氟硅酸镁中的至少一种；所述磷酸盐为磷酸钙、磷酸氢钙、磷酸镁和磷酸氢镁中的至少一种。
优选的，所述芳杂环聚合物树脂采用改性剂进行改性，所述改性剂为玻璃微珠、晶须、碳纤维、玻璃纤维、芳纶浆粕、芳纶短纤、硅酮和聚四氟乙烯中的至少一种。
本发明的另一个目的通过下述技术方案实现：一种耐紫外线高透明的芳杂环聚合物树脂的制备方法，以偶氮苯-4,4’-二甲酸和/或偶氮苯-3,3’-二甲酸、含氟对苯二甲酸和/或含氟邻苯二甲酸、硫酸肼为反应原料，在发烟硫酸中进行缩聚反应，得到所述芳杂环聚合物树脂。
具体的，聚合单体(偶氮苯-4,4’-二甲酸和/或偶氮苯-3,3’-二甲酸、含氟对苯二甲酸和/或含氟邻苯二甲酸)、硫酸肼和发烟硫酸的摩尔比为1： (1.01-5.0)：(5-15)，其中发烟硫酸摩尔数以发烟硫酸中SO3摩尔数计。
其中，聚合单体(偶氮苯-4,4’-二甲酸和/或偶氮苯-3,3’-二甲酸)与聚合单体(含氟对苯二甲酸和/或含氟邻苯二甲酸)的摩尔比为(0.01-0.99)： (0.99-0.01)。为了节省成本，优选的，聚合单体(偶氮苯-4,4’-二甲酸和/ 或偶氮苯-3,3’-二甲酸)与聚合单体(含氟对苯二甲酸和/或含氟邻苯二甲酸) 的摩尔比为(0.90-0.99)：(0.10-0.01)。
进一步的，偶氮苯-4,4’-二甲酸和偶氮苯-3,3’-二甲酸的摩尔比为 (0-1)：(1-0)，含氟对苯二甲酸和含氟邻苯二甲酸的摩尔比为(0-1)：(1-0)。
本发明的还一个目的通过下述技术方案实现：一种耐紫外线高透明的芳杂环聚合物树脂的应用，所述芳杂环聚合物树脂应用于纤维或薄膜。
优选的，所述薄膜应用于高温胶带、FPC基材、COF基材、FCCL基材、碳化膜基材、石墨化散热膜基材、高温保护膜、LED灯条、OLED柔性显示基材、导电膜基材、高温绝缘膜或手机盖板。
本发明的有益效果在于：本发明的芳杂环聚合物树脂具有优异的耐紫外线性能和较高的透明度，还具有良好的尺寸稳定性、耐热性、耐氧化、电绝缘、耐溶剂性、特殊的导电性以及电致发光等性能，综合性能优异。
本发明的制备方法步骤简单，操作控制方便，质量稳定，生产效率高，生产成本低，可大规模化工业生产。
本发明的耐紫外线高透明的芳杂环聚合物树脂在纤维或薄膜的应用。
具体实施方式
为了便于本领域技术人员的理解，下面结合实施例对本发明作进一步的说明，实施方式提及的内容并非对本发明的限定。
实施例1
一种耐紫外线高透明的芳杂环聚合物树脂，所述芳杂环聚合物树脂包括以 Am-Bn表示的聚合物链，其中，A和B均为构成聚合物链主链的重复单元，且重复单元A、B以任意顺序排列，m和n均为正整数；
所述重复单元A的结构式为：
所述重复单元B的结构式为：其中，R1、R2、R3和R4为未取代或取代的氟，且R1、R2、R3和R4中至少有一个为取代的氟。
所述芳杂环聚合物树脂采用无机填料进行改性。
所述无机填料为云母、炭黑、白炭黑、滑石粉、硅灰石、氮化物、碳化物和氧化物中的至少一种。
所述氮化物为氮化硅和/或氮化硼；所述碳化物为碳化硅和/或碳化硼；所述氧化物为氧化钙、氧化锌、氧化镁、氧化铁、二氧化硅和二氧化钛中的至少一种。
所述二氧化硅为纳米二氧化硅，所述二氧化钛为纳米二氧化钛。
一种耐紫外线高透明的芳杂环聚合物树脂的制备方法，以偶氮苯-4,4’- 二甲酸、含氟对苯二甲酸、硫酸肼为反应原料，在发烟硫酸中进行缩聚反应，得到所述芳杂环聚合物树脂。聚合单体(偶氮苯-4,4’-二甲酸、含氟对苯二甲酸)、硫酸肼和发烟硫酸的摩尔比为1：(1.01、2.0、3.0、4.0或5.0)：(5、 8、10、12或15)，其中发烟硫酸摩尔数以发烟硫酸中SO3摩尔数计。
其中，聚合单体(偶氮苯-4,4’-二甲酸)与聚合单体(含氟对苯二甲酸) 的摩尔比为(0.01、0.25、0.50、0.75或0.99)：(0.99、0.75、0.50、0.25或 0.01)。
实施例2
一种耐紫外线高透明的芳杂环聚合物树脂，所述芳杂环聚合物树脂包括以 Am-Bn表示的聚合物链，其中，A和B均为构成聚合物链主链的重复单元，且重复单元A、B以任意顺序排列，m和n均为正整数；
所述重复单元A的结构式为：
所述重复单元B的结构式为：其中，R1、R2、R3和R4为未取代或取代的氟，且R1、R2、R3和R4中至少有一个为取代的氟。
所述芳杂环聚合物树脂采用无机填料进行改性。
所述无机填料为硫酸盐、碳酸盐、硅酸盐、氟硅酸盐和磷酸盐中的至少一种。
所述硫酸盐为硫酸钙、硫酸镁、硫酸锌、硫酸钡、硫酸铁、硫酸亚铁中的至少一种；所述硅酸盐为硅酸钠、硅酸铝和硅酸镁中的至少一种；所述碳酸盐为碳酸钙、碳酸镁和碳酸锌中的至少一种；所述氟硅酸盐为氟硅酸钠、氟硅酸钾和氟硅酸镁中的至少一种；所述磷酸盐为磷酸钙、磷酸氢钙、磷酸镁和磷酸氢镁中的至少一种。
一种耐紫外线高透明的芳杂环聚合物树脂的制备方法，以偶氮苯-3,3’- 二甲酸、含氟邻苯二甲酸、硫酸肼为反应原料，在发烟硫酸中进行缩聚反应，得到所述芳杂环聚合物树脂。聚合单体(偶氮苯-3,3’-二甲酸、含氟邻苯二甲酸)、硫酸肼和发烟硫酸的摩尔比为1：(1.01、2.0、3.0、4.0或5.0)：(5、 8、10、12或15)，其中发烟硫酸摩尔数以发烟硫酸中SO3摩尔数计。
其中，聚合单体(偶氮苯-3,3’-二甲酸)与聚合单体(含氟邻苯二甲酸) 的摩尔比为(0.01、0.25、0.50、0.75或0.99)：(0.99、0.75、0.50、0.25或 0.01)。
实施例3
一种耐紫外线高透明的芳杂环聚合物树脂，所述芳杂环聚合物树脂包括以 Am-Bn表示的聚合物链，其中，A和B均为构成聚合物链主链的重复单元，且重复单元A、B以任意顺序排列，m和n均为正整数；
所述重复单元A的结构式为：
所述重复单元B的结构式为：其中， R1、R2、R3和R4为未取代或取代的氟，且R1、R2、R3和R4中至少有一个为取代的氟。
所述芳杂环聚合物树脂采用改性剂进行改性，所述改性剂为玻璃微珠、晶须、碳纤维、玻璃纤维、芳纶浆粕、芳纶短纤、硅酮和聚四氟乙烯中的至少一种。
一种耐紫外线高透明的芳杂环聚合物树脂的制备方法，以偶氮苯-4,4’- 二甲酸和偶氮苯-3,3’-二甲酸、含氟对苯二甲酸和含氟邻苯二甲酸、硫酸肼为反应原料，在发烟硫酸中进行缩聚反应，得到所述芳杂环聚合物树脂。聚合单体(偶氮苯-4,4’-二甲酸和偶氮苯-3,3’-二甲酸、含氟对苯二甲酸和含氟邻苯二甲酸)、硫酸肼和发烟硫酸的摩尔比为1：(1.01、2.0、3.0、4.0或5.0)： (5、8、10、12或15)，其中发烟硫酸摩尔数以发烟硫酸中SO3摩尔数计。
其中，聚合单体(偶氮苯-4,4’-二甲酸和偶氮苯-3,3’-二甲酸)与聚合单体(含氟对苯二甲酸和含氟邻苯二甲酸)的摩尔比为(0.01、0.25、0.50、 0.75或0.99)：(0.99、0.75、0.50、0.25或0.01)。
偶氮苯-4,4’-二甲酸和偶氮苯-3,3’-二甲酸的摩尔比为(0.01、0.25、 0.50、0.75或0.99)：(0.99、0.75、0.50、0.25或0.01)，含氟对苯二甲酸和含氟邻苯二甲酸的摩尔比为(0.01、0.25、0.50、0.75或0.99)：(0.99、0.75、 0.50、0.25或0.01)。
实施例4
一种耐紫外线高透明的芳杂环聚合物树脂的应用，所述芳杂环聚合物树脂应用于纤维。
实施例5
一种耐紫外线高透明的芳杂环聚合物树脂的应用，所述芳杂环聚合物树脂应用于薄膜。
所述薄膜应用于高温胶带、FPC基材、COF基材、FCCL基材、碳化膜基材、石墨化散热膜基材、高温保护膜、LED灯条、OLED柔性显示基材、导电膜基材、高温绝缘膜或手机盖板。
经测试，应用本发明的芳杂环聚合物树脂制得的薄膜紫外光老化试验可以达到1740-1930h，透明度可以达到90.7-94.5％,具有优异的耐紫外线性能和较高的透明度。
上述实施例为本发明较佳的实现方案，除此之外，本发明还可以其它方式实现，在不脱离本发明构思的前提下任何显而易见的替换均在本发明的保护范围之内。

Claims (10)

1.一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述芳杂环聚合物树脂包括以Am-Bn表示的聚合物链，其中，A和B均为构成聚合物链主链的重复单元，且重复单元A、B以任意顺序排列，m和n均为正整数；
所述重复单元A的结构式为：和/或
所述重复单元B的结构式为：和/或其中，R1、R2、R3和R4为未取代或取代的氟，且R1、R2、R3和R4中至少有一个为取代的氟。
2.根据权利要求1所述的一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述芳杂环聚合物树脂采用无机填料进行改性。
3.根据权利要求2所述的一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述无机填料为云母、炭黑、白炭黑、滑石粉、硅灰石、氮化物、碳化物、氧化物、硫酸盐、碳酸盐、硅酸盐、氟硅酸盐和磷酸盐中的至少一种。
4.根据权利要求3所述的一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述氮化物为氮化硅和/或氮化硼；所述碳化物为碳化硅和/或碳化硼；所述氧化物为氧化钙、氧化锌、氧化镁、氧化铁、二氧化硅和二氧化钛中的至少一种。
5.根据权利要求4所述的一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述二氧化硅为纳米二氧化硅，所述二氧化钛为纳米二氧化钛。
6.根据权利要求3所述的一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述硫酸盐为硫酸钙、硫酸镁、硫酸锌、硫酸钡、硫酸铁、硫酸亚铁中的至少一种；所述硅酸盐为硅酸钠、硅酸铝和硅酸镁中的至少一种；所述碳酸盐为碳酸钙、碳酸镁和碳酸锌中的至少一种；所述氟硅酸盐为氟硅酸钠、氟硅酸钾和氟硅酸镁中的至少一种；所述磷酸盐为磷酸钙、磷酸氢钙、磷酸镁和磷酸氢镁中的至少一种。
7.根据权利要求1所述的一种耐紫外线高透明的芳杂环聚合物树脂，其特征在于：所述芳杂环聚合物树脂采用改性剂进行改性，所述改性剂为玻璃微珠、晶须、碳纤维、玻璃纤维、芳纶浆粕、芳纶短纤、硅酮和聚四氟乙烯中的至少一种。
8.如权利要求1-7任一项所述的一种耐紫外线高透明的芳杂环聚合物树脂的制备方法，其特征在于：以偶氮苯-4,4’-二甲酸和/或偶氮苯-3,3’-二甲酸、含氟对苯二甲酸和/或含氟邻苯二甲酸、硫酸肼为反应原料，在发烟硫酸中进行缩聚反应，得到所述芳杂环聚合物树脂。
9.如权利要求1-7任一项所述的一种耐紫外线高透明的芳杂环聚合物树脂的应用，其特征在于：所述芳杂环聚合物树脂应用于纤维或薄膜。
10.根据权利要求9所述的一种耐紫外线高透明的芳杂环聚合物树脂的应用，其特征在于：所述薄膜应用于高温胶带、FPC基材、COF基材、FCCL基材、碳化膜基材、石墨化散热膜基材、高温保护膜、LED灯条、OLED柔性显示基材、导电膜基材、高温绝缘膜或手机盖板。
CN201811145331.9A 2018-09-29 2018-09-29 一种耐紫外线高透明的芳杂环聚合物树脂及其制备方法和在纤维或薄膜的应用 Pending CN109293893A (zh)