CN109276749A - 抗沾粘敷料及其制造方法 - Google Patents
抗沾粘敷料及其制造方法 Download PDFInfo
- Publication number
- CN109276749A CN109276749A CN201710594012.5A CN201710594012A CN109276749A CN 109276749 A CN109276749 A CN 109276749A CN 201710594012 A CN201710594012 A CN 201710594012A CN 109276749 A CN109276749 A CN 109276749A
- Authority
- CN
- China
- Prior art keywords
- foaming
- polyurethane film
- aqueous
- foaming layer
- sublevel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗沾粘敷料及其制造方法，抗沾粘敷料中包含水性发泡层及形成于其上的聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上。其中，混合硬化剂六亚甲基二异氰酸酯、聚乙二醇、聚丙二醇、2,2‑二羟甲基丙酸、乙二胺与1,4‑丁二醇混合形成主剂，在加入1,4‑丁二醇时加入功能性添加剂，制成预聚物；再利用机械发泡机台将预聚物打成机械发泡体，涂布在离心纸上制成水性发泡层。
Description
技术领域
本发明涉及一种抗沾粘敷料，具体涉及一种利用机械发泡机台制备的抗沾粘敷料及其制造方法。
背景技术
众所周知，在传统高吸收泡棉敷料及其制造方法法中，传统技术不使用水性聚氨酯，也未添加功能性添加剂，另就添加方式而言，传统工艺采用的是物理混合。这些导致了传统高吸收泡棉敷料保湿效果差，不具有抗菌功能，因此急需加以改善。此外，传统技术使用的是无纺布，且聚氨酯膜上并未涂上点状胶。
发明内容
本发明是为了解决上述传统泡棉敷料保湿效果差，不具有抗菌功能，以及伤口组织液不容易被吸收的问题，目的在于提供一种抗沾粘敷料及其制造方法。
本发明提供的一种抗沾粘敷料，其特征在于，包括：水性发泡层，底部用于贴附在皮肤的伤口上；以及聚氨酯膜，形成于水性发泡层上，且聚氨酯膜的上方涂有若干点状胶；
其中，水性发泡层是由机械发泡机台将预聚物打成机械发泡体，涂布在离心纸上制成的，
预聚物包括：主剂和0.05～0.35mol％的功能性添加剂，
主剂包括：水性发泡层包括2.0～2.2mol％的硬化剂六亚甲基二异氰酸酯、0.2～0.4mol％的聚乙二醇、0.6～0.8mol％的聚丙二醇、0.4～0.6mol％的2,2-二羟甲基丙酸、0.1～0.3mol％的乙二胺、与0.1～0.3mol％的1,4-丁二醇，
功能性添加剂在加入1,4-丁二醇时加入。
本发明提供的抗沾粘敷料，还可以具有这样的特征：
其中，在1.0mol％的预聚物中，含有0.1mol％的功能性添加剂。
本发明提供的抗沾粘敷料，还可以具有这样的特征：
其中，功能性添加剂为玻尿酸、胶原蛋白、甲壳素及海藻酸钠中任意一至多种。
本发明提供的抗沾粘敷料，还可以具有这样的特征：
其中，水性发泡层包括孔径大小范围为100～1000μm的第一发泡次层及孔径大小小于100μm的第二发泡次层，第一发泡次层与聚氨酯膜粘接，第二发泡次层贴附在伤口上。
本发明提供的抗沾粘敷料，还可以具有这样的特征：
其中，聚氨酯膜的厚度范围是0.01～0.04mm，聚氨酯膜水气穿透率大于每日3000克/平方公尺。
本发明提供的抗沾粘敷料，还可以具有这样的特征：
其中，点状胶是感压胶或热熔胶。
本发明提供的一种抗沾粘敷料的制造方法，其特征在于，将2.0～2.2mol％的硬化剂六亚甲基二异氰酸酯、0.2～0.4mol％的聚乙二醇、0.6～0.8mol％的聚丙二醇、0.4～0.6mol％的2,2-二羟甲基丙酸、0.1～0.3mol％的乙二胺、与0.1～0.3mol％的1,4-丁二醇，混合形成主剂，在加入1,4-丁二醇(1,4-butanediol)时加入0.05～0.35mol％的功能性添加剂，制成预聚物；
利用机械发泡机台将预聚物打成机械发泡体，涂布在离心纸上制成水性发泡层；
在水性发泡层上形成聚氨酯膜，在该聚氨酯膜上涂有若干点状胶，且水性发泡层的底部用于贴附在皮肤的伤口上；
本发明提供的抗沾粘敷料的制造方法，还可以具有这样的特征：
其中，在1.0mol％预聚物中，含有0.1mol％的功能性添加剂。
本发明提供的抗沾粘敷料的制造方法，还可以具有这样的特征：
其中，功能性添加剂为玻尿酸(hyaluronic acid)、胶原蛋白(collagen)、甲壳素(chitin/chitosan)及海藻酸钠(sodium alginate)中任意一至多种。
本发明提供的抗沾粘敷料的制造方法，还可以具有这样的特征：
其中，水性发泡层包括孔径大小范围为100～1000μm的第一发泡次层及孔径大小小于100μm的第二发泡次层，第一发泡次层与聚氨酯膜粘接，第二发泡次层贴附在伤口上。
发明的作用与效果
根据本发明所涉及的抗沾粘敷料及其制造方法，由于使用了采用化学交联方式加入的功能性添加剂，同时使用水性发泡层和聚氨酯膜来代替传统的无纺布，使得本发明具有如下优点：
1.功能性添加剂中提到的玻尿酸(hyaluronic acid)与胶原蛋白(collagen)是对于伤口具有保湿的功能，而甲壳素是对于伤口具有抑菌的功能，这使得本发明涉及的抗沾粘敷料具有非常优良的保湿性。
2.主剂中含有的PEG及发泡组合物中的PEG2000与PPG2000具有吸水性，使得本发明涉及的抗沾粘敷料具有非常优良的吸水性。
3.六亚甲基二异氰酸酯与PEG及PPG还有玻尿酸会与胶原蛋白内的-OH基反应，且六亚甲基二异氰酸酯也会与甲壳素-NH2发生化学交联。这些化学交联会使发泡过的发泡体附在聚氨酯膜上，与传统物理混合效果相比效果更佳。
4.传统的载体使用无纺布，而本发明使用了聚氨酯膜，聚氨酯膜具有阻隔外部细菌感染，防水，抗菌的功能。另本发明中使用了点涂的点状胶，虽然点状胶具有不透气性，但点状胶仅以点状分布在聚氨酯膜上，故可保持聚氨酯膜具有的透气性。
附图说明
图1是本发明的抗沾粘敷料的截面示意图；
图2是本发明的抗沾粘敷料的上视图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，以下实施例结合附图对本发明提供的抗沾粘敷料及其制造方法的组成、工作原理以及有益效果作具体阐述。
图1是本发明的抗沾粘敷料的截面示意图；
图2是本发明的抗沾粘敷料的上视图。
如图1、2所示，本实施例中的抗沾粘敷料中包括：水性发泡层(aqueous foamlayer)10上形成有聚氨酯膜(polyurethane film)20，水性发泡层10下是贴附上皮肤31的伤口30上，
水性发泡层10是由2.0～2.2mol％的硬化剂六亚甲基二异氰酸酯(hexamethylenediisocyanate，HDI)与0.2～0.4mol％的聚乙二醇(polyethylene glycol，PEG，Mn2000)与0.6～0.8mol％的聚丙二醇(polypropylene glycol，PPG，Mn2000)与0.4～0.6mol％的2,2-二羟甲基丙酸(2,2-Bis(hydroxymethyl)propionic acid)与0.1～0.3mol％的乙二胺(ethylenediamine)与0.1～0.3mol％的1,4-丁二醇(1,4-butanediol)混合形成的主剂，再在加入1,4-丁二醇时加入0.05～0.35mol％功能性添加剂，制成水性预聚物；最后利用机械发泡机台打成机械发泡体，涂布在离心纸上制成。
此外，聚氨酯膜20上涂有若干点状胶。
为了使水性发泡层10能保湿保水气且达到不沾粘伤口效果，水性发泡层10含有孔径大小范围为100～1000μm的第一发泡次层101及孔径大小小于100μm的第二发泡次层102，第一发泡次层101与聚氨酯膜20粘接，第二发泡次层102贴附在伤口30上。水性发泡层10的基材厚度范围是0.5-1.5mm。
为了使水性发泡层10能保湿保水气，功能性添加剂是可选择地加入于水性发泡层10内，功能性添加剂为玻尿酸、胶原蛋白、甲壳素(chitin/chitosan)及海藻酸钠(sodiumalginate)的任意一至多种。玻尿酸与胶原蛋白是对于伤口具有保湿的功能，聚乙二醇与聚丙二醇是对于伤口具有吸水的功能，而甲壳素是对于伤口具有抑菌的功能。
聚氨酯膜20的厚度范围为0.01～0.04mm，以0.025mm为优选。聚氨酯膜20的水气穿透率MVTR要大于3000g/m2.day。聚氨酯膜的功能是阻隔外部细菌感染，防水，抗菌且当做载体。
下结合实施例A-G来详细说明本实施例中的抗沾粘敷料及其制造方法的使用方法和工作原理。
实施例A
制备水性发泡层，由2.0mol％硬化剂六亚甲基二异氰酸酯与0.2mol％聚乙二醇PEG2000(polyethylene glycol，PEG，Mn2000)与0.8mol％聚丙二醇PPG2000(polypropylene glycol，PPG，Mn2000)与0.4mol％2,2-二羟甲基丙酸与0.1mol％乙二胺(ethylenediamine)与0.3mol％1,4-丁二醇混合形成主剂，且不加入功能性添加剂，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
实施例B
制备水性发泡层，由2.0mol％的硬化剂六亚甲基二异氰酸酯与0.3mol％的聚乙二醇PEG2000(polyethylene glycol，PEG，Mn2000)与0.7mol％的聚丙二醇PPG2000(polypropylene glycol，PPG，Mn2000)与0.4mol％的2,2-二羟甲基丙酸与0.1mol％的乙二胺与0.3mol％1,4-丁二醇混合形成主剂，且不加入功能性添加剂，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
实施例C
制备水性发泡层，先由2.0mol％硬化剂六亚甲基二异氰酸酯与0.4mol％聚乙二醇PEG2000与0.6mol％的聚丙二醇PPG2000与0.4mol％的2,2-二羟甲基丙酸与0.1mol％的乙二胺与0.3mol％的1,4-丁二醇混合形成主剂，且不加入功能性添加剂，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
实施例D
水性发泡层上形成有聚氨酯膜，水性发泡层下是贴附上皮肤之的伤口上；制备水性发泡层，由2.0mol％硬化剂六亚甲基二异氰酸酯与0.2mol％聚乙二醇PEG2000与0.8mol％聚丙二醇PPG2000与0.4mol％2,2-二羟甲基丙酸与0.1mol％乙二胺与0.3mol％1,4-丁二醇混合形成主剂，且不加入功能性添加剂，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
实施例E
水性发泡层上形成有聚氨酯膜，水性发泡层下是贴附上皮肤的伤口上；制备水性发泡层，由2.0mol％硬化剂六亚甲基二异氰酸酯与0.2mol％聚乙二醇PEG2000与0.8mol％聚丙二醇PPG2000与0.4mol％2,2-二羟甲基丙酸与0.1mol％乙二胺与0.3mol％1,4-丁二醇混合形成主剂，在加入1,4-丁二醇时加入0.1mol％功能性添加剂玻尿酸，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
实施例F
水性发泡层上形成有聚氨酯膜，水性发泡层下是贴附上皮肤的伤口上；制备水性发泡层，由2.0mol％硬化剂六亚甲基二异氰酸酯与0.2mol％聚乙二醇PEG2000与0.8mol％聚丙二醇PPG2000与0.4mol％2,2-二羟甲基丙酸与0.1mol％乙二胺(ethylenediamine)与0.3mol％1,4-丁二醇混合形成主剂，在加入1,4-丁二醇时加入0.2mol％功能性添加剂玻尿酸，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
实施例G
水性发泡层上形成有聚氨酯膜，水性发泡层下是贴附上皮肤的伤口上；制备水性发泡层，由2.0mol％硬化剂六亚甲基二异氰酸酯与0.2mol％聚乙二醇PEG2000与0.8mol％聚丙二醇与0.4mol％2,2-二羟甲基丙酸与0.1mol％乙二胺与0.3mol％1,4-丁二醇混合形成主剂，在加入1,4-丁二醇时加入0.3mol％功能性添加剂玻尿酸，制成预聚物；再利用机械发泡机台打成机械发泡体，涂布在离心纸上制成水性发泡层；水性发泡层上形成有聚氨酯膜，水性发泡层的底部用于贴附在皮肤的伤口上；聚氨酯膜上涂有若干点状胶。
根据上述实施例A-G中制备的水性发泡层的性质如下表：
| 实例 | 吸水率(g/g) | 强度(MPa) | 延展性(％) |
| A | 2 | 10 | 250 |
| B | 2.5 | 8 | 220 |
| C | 3 | 6 | 200 |
| D | 3 | 10 | 230 |
| E | 4 | 10 | 210 |
| F | 5 | 10 | 200 |
| G | N/A | N/A | N/A |
在表中，延展性(％)通过伸长率(elogation)来表示。
实施例的作用与效果
根据本发明所涉及的抗沾粘敷料及其制造方法，由于使用了采用化学交联方式加入的功能性添加剂，同时使用水性发泡层和聚氨酯膜来代替传统的无纺布，使得本发明具有如下优点：
(1)本发明加入功能性添加剂，功能性添加剂是选自玻尿酸、胶原蛋白、海藻酸钠及甲壳素，传统技术并未添加功能性添加剂。
(2)就添加方式而言，传统上是物理混合的方式，本发明的添加方式是采用化学交联的方法。
(3)本发明的抗沾粘敷料的优点是具有非常优良的保湿与吸水效果，吸水效果是来自于主剂的PEG及发泡组合物中的PEG2000与PPG2000。玻尿酸与胶原蛋白是对于伤口具有保湿的功能，而甲壳素是对于伤口具有抑菌的功能，而依据抗沾粘敷料所预计设计的目的，玻尿酸、胶原蛋白、海藻酸钠及甲壳素中可任意选一者或任意选二者或任意选三者。
(4)传统的载体是用无纺布，本发明是使用聚氨酯膜，该聚氨酯膜上点涂了点状胶，虽然点状胶具有不透气性，但点状胶以点状分布在聚氨酯膜上可保持聚氨酯膜具有的透气性。
以上实施例仅为表达了本发明的优选具体实施方式，但并不能因此而理解为对本发明权利要求的限制。应当指出的是，对于本技术领域中的一般技术人员而言，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。
Claims (10)
1.一种抗沾粘敷料，其特征在于，包括：
水性发泡层，底部用于贴附在皮肤的伤口上；以及
聚氨酯膜，形成于所述水性发泡层上，且所述聚氨酯膜的上方涂有若干点状胶，
其中，水性发泡层是由机械发泡机台将预聚物打成机械发泡体，涂布在离心纸上制成的，
所述预聚物包括：主剂和0.05～0.35mol％的功能性添加剂，
所述主剂包括：2.0～2.2mol％的硬化剂六亚甲基二异氰酸酯、0.2～0.4mol％的聚乙二醇、0.6～0.8mol％的聚丙二醇、0.4～0.6mol％的2,2-二羟甲基丙酸、0.1～0.3mol％的乙二胺与0.1～0.3mol％的1,4-丁二醇，
所述功能性添加剂在加入1,4-丁二醇时加入。
2.根据权利要求1所述的抗沾粘敷料，其特征在于：
其中，在1.0mol％的所述预聚物中，含有0.1mol％的所述功能性添加剂。
3.根据权利要求1所述的抗沾粘敷料，其特征在于：
其中，所述功能性添加剂为玻尿酸、胶原蛋白、甲壳素及海藻酸钠中任意一至多种。
4.根据权利要求1所述的抗沾粘敷料，其特征在于：
其中，所述水性发泡层包括孔径大小范围为100～1000μm的第一发泡次层及孔径大小小于100μm的第二发泡次层，
所述第一发泡次层与所述聚氨酯膜粘接，所述第二发泡次层贴附在伤口上。
5.根据权利要求1所述的抗沾粘敷料，其特征在于：
其中，所述聚氨酯膜的厚度范围是0.01～0.04mm，所述聚氨酯膜的水气穿透率大于每日3000克/平方公尺。
6.根据权利要求1所述的抗沾粘敷料，其特征在于：
其中，所述点状胶是感压胶或热熔胶。
7.一种抗沾粘敷料的制造方法，其特征在于，包括：
将2.0～2.2mol％的硬化剂六亚甲基二异氰酸酯、0.2～0.4mol％的聚乙二醇、0.6～0.8mol％的聚丙二醇、0.4～0.6mol％的2,2-二羟甲基丙酸、0.1～0.3mol％的乙二胺与0.1～0.3mol％的1,4-丁二醇，混合形成主剂，且在加入1,4-丁二醇时加入0.05～0.35mol％的功能性添加剂，制成预聚物，
利用机械发泡机台将所述预聚物打成机械发泡体，涂布在离心纸上制成所述水性发泡层，
在所述水性发泡层上形成所述聚氨酯膜，所述聚氨酯膜上涂有若干所述点状胶，
所述水性发泡层的底部用于贴附在皮肤的伤口上。
8.根据权利要求7所述抗沾粘敷料的制造方法，其特征在于：
其中，在1.0mol％的所述预聚物中，含有0.1mol％的所述功能性添加剂。
9.根据权利要求7所述抗沾粘敷料的制造方法，其特征在于：
其中，所述功能性添加剂为玻尿酸、胶原蛋白、甲壳素及海藻酸钠中任意一至多种。
10.根据权利要求7所述抗沾粘伤口的制造方法，其特征在于：
其中，所述水性发泡层包括孔径大小范围为100～1000μm的第一发泡次层及孔径大小小于100μm的第二发泡次层，
所述第一发泡次层与所述聚氨酯膜粘接，所述第二发泡次层贴附在伤口上。