CN109264995A - Iron rust mottled enamels and preparation method thereof - Google Patents
Iron rust mottled enamels and preparation method thereof Download PDFInfo
- Publication number
- CN109264995A CN109264995A CN201811108562.2A CN201811108562A CN109264995A CN 109264995 A CN109264995 A CN 109264995A CN 201811108562 A CN201811108562 A CN 201811108562A CN 109264995 A CN109264995 A CN 109264995A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- component
- iron rust
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of iron rust mottled enamels and preparation method thereof, the component and each component mass parts that glaze used in iron rust mottled enamels contains are as follows: potassium feldspar: 50-70 parts, quartz: 10-12 parts, barium carbonate: 3-4 parts, zinc oxide: 3-5 parts, vanadic anhydride: 1-2 parts, iron oxide red: 5-8 parts, nickel oxide: 0.3-0.6 parts, calcite: 10-20 parts, talcum: 5-8 parts.Glaze paint of the invention has extremely beautiful rust, and intensity is high, and wear-resisting, low cost is applicable in vast household china, and porcelain can allow client more safe to use.
Description
Technical field
The present invention relates to a kind of iron rust mottled enamels and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of iron rust mottled enamels, its glaze are provided
Face has extremely beautiful rust, and intensity is high, wear-resisting, low cost, is applicable in vast household china, porcelain, can allow client
It is more safe to use.
In order to solve the above technical problems, the technical scheme is that a kind of iron rust mottled enamels, glaze used in it contain
Some components and each component mass parts are as follows:
Potassium feldspar: 50-70 parts,
Quartz: 10-12 parts,
Barium carbonate: 3-4 parts,
Zinc oxide: 3-5 parts,
Vanadic anhydride: 1-2 parts,
Iron oxide red: 5-8 parts,
Nickel oxide: 0.3-0.6 parts,
Calcite: 10-20 parts,
Talcum: 5-8 parts.
Contain in the step of preparation method of the iron rust mottled enamels, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 15~18 hours, the glaze after ball milling crossed 325
Mesh, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
After above-mentioned technical proposal, glaze paint of the invention has extremely beautiful rust, and intensity is high, wear-resisting, makes
Valence is low, is applicable in vast household china, and porcelain can allow client more safe to use.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of iron rust mottled enamels, the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 50 parts,
Quartz: 10 parts,
Barium carbonate: 3 parts,
Zinc oxide: 3 parts,
Vanadic anhydride: 1 part,
Iron oxide red: 5 parts,
Nickel oxide: 0.3 part,
Calcite: 10 parts,
Talcum: 5 parts.
Contain in the step of preparation method of the iron rust mottled enamels, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 15 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
Embodiment two
A kind of iron rust mottled enamels, the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 70 parts,
Quartz: 12 parts,
Barium carbonate: 4 parts,
Zinc oxide: 5 parts,
Vanadic anhydride: 2 parts,
Iron oxide red: 8 parts,
Nickel oxide: 0.6 part,
Calcite: 20 parts,
Talcum: 8 parts.
Contain in the step of preparation method of the iron rust mottled enamels, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 18 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
Embodiment three
A kind of iron rust mottled enamels, the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 60 parts,
Quartz: 11 parts,
Barium carbonate: 3 parts,
Zinc oxide: 3 parts,
Vanadic anhydride: 1 part,
Iron oxide red: 6 parts,
Nickel oxide: 0.4 part,
Calcite: 15 parts,
Talcum: 6 parts.
Contain in the step of preparation method of the iron rust mottled enamels, method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 16 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1290 DEG C -1330 DEG C of oxidizing atmospheres
Product.
The iron rust mottled enamels that three above embodiment is prepared, glaze paint have extremely beautiful rust, and intensity is high, resistance to
Mill, low cost are applicable in vast household china, and porcelain can allow client more safe to use.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. a kind of iron rust mottled enamels, it is characterised in that the component and each component mass parts that glaze used in it contains are as follows:
Potassium feldspar: 50-70 parts,
Quartz: 10-12 parts,
Barium carbonate: 3-4 parts,
Zinc oxide: 3-5 parts,
Vanadic anhydride: 1-2 parts,
Iron oxide red: 5-8 parts,
Nickel oxide: 0.3-0.6 parts,
Calcite: 10-20 parts,
Talcum: 5-8 parts.
2. a kind of preparation method of iron rust mottled enamels as described in claim 1, it is characterised in that contain in the step of method:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: press glaze: ball: mass ratio=1:1:1.5 of water, wet ball grinding 15~18 hours, the glaze after ball milling crossed 325 mesh
Sieve, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through firing finished product under 1290 DEG C -1330 DEG C of oxidizing atmospheres.