CN109180113A - A kind of composite water-proof paint and its application method of quick-dry type - Google Patents
A kind of composite water-proof paint and its application method of quick-dry type Download PDFInfo
- Publication number
- CN109180113A CN109180113A CN201810927802.5A CN201810927802A CN109180113A CN 109180113 A CN109180113 A CN 109180113A CN 201810927802 A CN201810927802 A CN 201810927802A CN 109180113 A CN109180113 A CN 109180113A
- Authority
- CN
- China
- Prior art keywords
- parts
- proof paint
- composite water
- water
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite water-proof paints of quick-dry type, including powder and liquid material, powder includes portland cement, 100 mesh quartz sands, 200 mesh quartz sands, micro-crystal powder, organosilicon hydrophobic powder, hydroxypropyl methyl cellulose ether, water-reducing agent, latex powder, bentonite, defoaming agent, starch ether；Liquid material includes styrene-acrylic emulsion, acrylate and vinyl acetate emulsion, ash concrete or white cement, low-alkalinity sulphoaluminate cement, titanium dioxide, coarse whiting, talcum powder, emulsifier, defoaming agent, coalescing agent, multifunctional assistant AMP-95, water, polyacrylamide；The ratio of powder and liquid material is 1:1.The invention also discloses the application methods of above-mentioned composite water-proof paint.The film of composite water-proof paint of the invention has excellent waterproof performance, weather resistance；Coating rate of drying is fast, can play the role of long-term waterproof.The application method of composite water-proof paint of the invention can be improved construction efficiency, shorten the construction period, reduce construction cost.
Description
Technical field
The present invention relates to a kind of water-repellent paint more particularly to the composite water-proof paints and its application method of a kind of quick-dry type.
Background technique
The leakage problems of building are generally existing, and buildings waterproof becomes question of common concern in architectural engineering, especially
After modern architecture tends to high stratification, assembling, the requirement to waterproofing work is higher.And water-repellent paint is often made in waterproofing work
One of primary roofing material.Water-repellent paint, which is applied to the cured rear waterproofing membrane formed of the coating in base, to be had centainly
Intensity, preferable extensibility, crack resistance, impermeability and weatherability, while having good thermal adaptability are easy to operate,
For ease of maintenaince with maintenance.But water-repellent paint in the prior art in order to reach reliable waterproof performance, need to base into
The multiple smearing of row, the coating smeared every time need drying at least 24 hours, just can be carried out subsequent construction, due to doing for coating
The dry time is up to 24 hours, greatly reduces construction efficiency, seriously affects the construction period of architectural engineering, increase and be constructed into
This, also affect building moves in the time limit.It is badly in need of being not only able to achieve rapid draing currently on the market, but also excellent waterproof effect can be reached
Water-repellent paint.
Summary of the invention
For overcome the deficiencies in the prior art, one of the objects of the present invention is to provide a kind of paintings of the composite water-proof of quick-dry type
Material, film has excellent waterproof performance, weather resistance, and adhesive property is good, has to the deformation of base's retractility relatively strong
Adaptability, coating rate of drying is fast, also have anti acid alkali performance, long-term waterproof can be played the role of.
The second object of the present invention is to provide the application method of the composite water-proof paint of one of the object of the invention, this method
Used in composite water-proof paint rate of drying it is fast, can be improved construction efficiency, shorten the construction period, reduce construction cost.
An object of the present invention adopts the following technical scheme that realization:
A kind of composite water-proof paint of quick-dry type, including powder and liquid material, which is characterized in that
The powder includes the component of following parts by weight: 400-500 parts of portland cement, 100 mesh quartz sand 250-
350 parts, 100-200 parts of 200 mesh quartz sand, 40-120 parts of micro-crystal powder, 0.1-2 parts of organosilicon hydrophobic powder, hydroxypropyl methyl fiber
Plain ether 0.1-1 parts, 1-3 parts of water-reducing agent, 20-30 parts of latex powder, 0.1-0.3 parts of bentonite, 1-3 parts of defoaming agent, starch ether 0.1-
0.3 part；
The liquid material includes the component of following parts by weight: 40-50 parts of styrene-acrylic emulsion, 10-20 parts of acrylate and vinyl acetate emulsion, buck
Mud or 20-30 parts of white cement, 2-4 parts of low-alkalinity sulphoaluminate cement, 6-10 parts of titanium dioxide, 6-10 parts of coarse whiting, talcum powder 1-3
Part, 2-3 parts of emulsifier, 1-1.5 parts of defoaming agent, 6-8 parts of coalescing agent, 5-10 parts of multifunctional assistant AMP-95, water 10-14
Part, 2-4 parts of polyacrylamide；
The powder and the mass ratio of the liquid material are 1:1.
Further, the powder includes the component of following parts by weight: 450 parts of portland cement, 100 mesh quartz sands
300 parts, 140 parts of 200 mesh quartz sand, 80 parts of micro-crystal powder, 1 part of organosilicon hydrophobic powder, 0.3 part of hydroxypropyl methyl cellulose ether, subtract
2 parts of aqua, 25 parts of latex powder, 0.2 part of bentonite, 2 parts of defoaming agent, 0.1 part of starch ether；
The liquid material includes the component of following parts by weight: 45 parts of styrene-acrylic emulsion, 15 parts of acrylate and vinyl acetate emulsion, ash concrete or plain boiled water
25 parts of mud, 3 parts of low-alkalinity sulphoaluminate cement, 8 parts of titanium dioxide, 8 parts of coarse whiting, 2 parts of talcum powder, 2.5 parts of emulsifier, defoaming agent
1.2 parts, 7 parts of coalescing agent, 6 parts of multifunctional assistant AMP-95,12 parts of water, 3 parts of polyacrylamide；
The powder and the mass ratio of the liquid material are 1:1.
The second object of the present invention adopts the following technical scheme that realization:
The application method of the composite water-proof paint of the quick-dry type of one of the object of the invention, which is characterized in that including following step
It is rapid:
The step of mixing: weighing the powder and liquid material of formula ratio, is uniformly mixed, obtains composite water-proof paint；
The step of brushing: water is added in composite water-proof paint, is brushed after mixing evenly；
The step of blade coating: composite water-proof paint drying to be brushed and then the secondary powder for weighing formula ratio and liquid material are mixed
It closes uniformly, obtains composite water-proof paint, water is added in composite water-proof paint, is scratched after mixing evenly.
Further, further include the steps that maintenance: after the completion of the step of the blade coating, to the composite water-proof paint of blade coating into
At least 24 hours maintenance works of row.
Further, in the step of brushing, the water of 22-23ml is added in every 1 kilogram of composite water-proof paint；It applies
Brush with a thickness of 1mm.
Further, in the step of blade coating, the water of 21-22ml is added in every 1 kilogram of composite water-proof paint；It scrapes
Apply with a thickness of 1-2mm.
Further, after the step of brushing completes, it is spaced the step of carrying out the blade coating again 3-6 hours；?
After the step of brushing completes, when blushing occurs in the composite water-proof paint of brushing, the composite water-proof of brushing is applied
Material carries out sprinkling maintenance.
Further, after by the brushing the step of and the step of the blade coating, the overall thickness of composite water-proof paint is
2-4mm。
Further, the maintenance work in the step of maintenance are as follows: when whitening now occurs in the composite water-proof paint of blade coating
As when, sprinkled water to composite water-proof paint, wet straw screen or mat covering or plastic film covering.
Compared with prior art, the beneficial effects of the present invention are:
1. the powder in the present invention is uniformly mixed by the quartz sand and various active chemistries of white, whiteness is high,
Be adapted to deploy many colors, moreover, because the calcium oxide and alkali that do not dissociate, will not accumulation of salt in the surface soil weathering, there is excellent guarantor
Color, corrosion resistance and wearability.
2. the drying time of water-repellent paint of the invention is 3-6 hours, and the drying time of water-repellent paint on the market is
At least 12 hours, therefore, the rate of drying of composite water-proof paint of the invention was fast, can be improved construction efficiency, shortened construction work
Phase.
3. each component co-action in powder and liquid material of the invention, by adjusting the weight ratio between each component,
So that composite water-proof paint has excellent waterproof performance, weather resistance；Adhesive property is good, to the deformation of base's retractility have compared with
Strong adaptability.
Specific embodiment
In the following, being described further in conjunction with specific embodiment to the present invention, it should be noted that is do not collided
Under the premise of, new embodiment can be formed between various embodiments described below or between each technical characteristic in any combination.It is adopted
Equipment and raw material etc. are commercially available or commonly used in the art.Method in following embodiments, such as nothing are especially said
It is bright, it is the conventional method of this field.
A kind of composite water-proof paint of quick-dry type, including powder and liquid material；
Powder includes the component of following parts by weight: 400-500 parts of portland cement, 250-350 parts of 100 mesh quartz sand,
200 100-200 parts of mesh quartz sands, 40-120 parts of micro-crystal powder, 0.1-2 parts of organosilicon hydrophobic powder, hydroxypropyl methyl cellulose ether
0.1-1 parts, 1-3 parts of water-reducing agent, 20-30 parts of latex powder, 0.1-0.3 parts of bentonite, 1-3 parts of defoaming agent, starch ether 0.1-0.3
Part；
Liquid material includes the component of following parts by weight: 40-50 parts of styrene-acrylic emulsion, 10-20 parts of acrylate and vinyl acetate emulsion, ash concrete or white
20-30 parts of cement, 2-4 parts of low-alkalinity sulphoaluminate cement, 6-10 parts of titanium dioxide, 6-10 parts of coarse whiting, 1-3 parts of talcum powder, emulsification
2-3 parts of agent, 1-1.5 parts of defoaming agent, 6-8 parts of coalescing agent, 5-10 parts of multifunctional assistant AMP-95,10-14 parts of water, polypropylene
2-4 parts of amide；
Powder and the mass ratio of liquid material are 1:1.
Portland cement selects portland cement 42.5R；
Micro-crystal powder can select the micro-crystal powder of the auspicious Co., Ltd that makes the science and technology prosperous of Tongji University's crystallite, Beijing moral；
Organosilicon hydrophobic powder can select Akzo Nobel Seal 80, Tao Shi organosilicon hydrophobic powder；
Water-reducing agent can select the polycarboxylate water-reducer of a watt gram SE-47, the Dow Chemical Company；
Latex powder selects watt gram rubber powder 4115；
Emulsifier is Tao Shi surfactant ECOSURF AS-801；
Defoaming agent selects TaiWan, China Central Asia NXZ defoaming agent；
Multifunctional assistant AMP-95 selects Dow multifunctional assistant AMP-95.
As further embodiment, powder includes the component of following parts by weight: 450 parts of portland cement, 100
300 parts of mesh quartz sand, 140 parts of 200 mesh quartz sand, 80 parts of micro-crystal powder, 1 part of organosilicon hydrophobic powder, hydroxypropyl methyl cellulose ether
0.3 part, 2 parts of water-reducing agent, 25 parts of latex powder, 0.2 part of bentonite, 2 parts of defoaming agent, 0.1 part of starch ether；
Liquid material includes the component of following parts by weight: 45 parts of styrene-acrylic emulsion, 15 parts of acrylate and vinyl acetate emulsion, ash concrete or white cement 25
Part, 3 parts of low-alkalinity sulphoaluminate cement, 8 parts of titanium dioxide, 8 parts of coarse whiting, 2 parts of talcum powder, 2.5 parts of emulsifier, defoaming agent 1.2
Part, 7 parts of coalescing agent, 6 parts of multifunctional assistant AMP-95,12 parts of water, 3 parts of polyacrylamide；
Powder and the mass ratio of liquid material are 1:1.
The application method of the composite water-proof paint of the quick-dry type of one of the object of the invention, the following steps are included:
The step of mixing: weighing the powder and liquid material of formula ratio, is uniformly mixed, obtains composite water-proof paint；
The step of brushing: water is added in composite water-proof paint, is brushed after mixing evenly；
When brushing inner corner trim, need to do 45 degree of slope, while grid cloth can be added to reach humidification；When brushing ground
When, it needs to do toward metope at least 30 centimetres high；
The step of blade coating: composite water-proof paint drying to be brushed and then the secondary powder for weighing formula ratio and liquid material are mixed
It closes uniformly, obtains composite water-proof paint, water is added in composite water-proof paint, is scratched after mixing evenly.When blade coating ground
When, it needs to do toward metope at least 30 centimetres high；
In the construction process, composite water-proof paint cannot be trampled, prevents composite water-proof paint drying too fast.Apply surface layer protection
The subsequent construction such as mortar, tiling can carry out as early as possible after blade coating step completes 48h, and ceramic tile need to use polymer modification porcelain
Brick glue is bonded.
As further embodiment, further include the steps that maintenance: after the completion of the step of blade coating, to the compound anti-of blade coating
Water paint carries out at least 24 hours maintenance works.
As further embodiment, the step of brushing in, 22-23ml is added in every 1 kilogram of composite water-proof paint
Water；Brush with a thickness of 1mm.
As further embodiment, the step of blade coating in, 21-22ml is added in every 1 kilogram of composite water-proof paint
Water；Blade coating with a thickness of 1-2mm.
As further embodiment, after the step of brushing is completed, it is spaced the 3-6 hours steps scratched again
Suddenly；After the step of brushing is completed, when blushing occurs in the composite water-proof paint of brushing, the composite water-proof of brushing is applied
Material carries out sprinkling maintenance.
As further embodiment, after the step of the step of brushing is with blade coating, the total thickness of composite water-proof paint
Degree is 2-4mm.
As further embodiment, the step of maintenance in maintenance work are as follows: when the composite water-proof paint of blade coating goes out
It when existing blushing, is sprinkled water to composite water-proof paint, the covering of wet straw screen or mat or plastic film cover.
Embodiment 1-3:
A kind of composite water-proof paint of quick-dry type, including powder and liquid material, the proportion according to the form below 1 weighs raw material respectively,
Powder and the mass ratio of liquid material are 1:1, and according to following application method carry out using.
Powder includes following component: portland cement, 100 mesh quartz sands, 200 mesh quartz sands, micro-crystal powder, organosilicon hydrophobic
Powder, hydroxypropyl methyl cellulose ether, water-reducing agent, latex powder, bentonite, defoaming agent, starch ether；
Liquid material includes following component: styrene-acrylic emulsion, acrylate and vinyl acetate emulsion, ash concrete or white cement, low-alkalinity sulphoaluminate cement,
Titanium dioxide, coarse whiting, talcum powder, emulsifier, defoaming agent, coalescing agent, multifunctional assistant AMP-95, water, polyacrylamide；
Table 1: embodiment 1-3 raw material proportioning table
The application method of above-mentioned composite water-proof paint, the following steps are included:
The step of mixing: weighing the powder and liquid material of formula ratio, is uniformly mixed, obtains composite water-proof paint；
The step of brushing: water is added in composite water-proof paint, is added 23ml's in every 1 kilogram of composite water-proof paint
Water；Brushed after mixing evenly, brushing with a thickness of 2mm；After the completion of brushing, when the composite water-proof paint of brushing whitens
When phenomenon, sprinkling maintenance is carried out to the composite water-proof paint of brushing.
The step of blade coating: after the step of brushing is completed, it is spaced the step of being scratched again 4 hours；It weighs and matches again
The powder and liquid material just measured be uniformly mixed, obtain composite water-proof paint, be added water in composite water-proof paint, and every 1 kilogram is answered
Close the water that 22ml is added in water-repellent paint；Scratched after mixing evenly, blade coating with a thickness of 2mm；
The step of maintenance: after the completion of the step of blade coating, 24 hours maintenance works are carried out to the composite water-proof paint of blade coating；
When blushing occurs in the composite water-proof paint of blade coating, sprinkled water to composite water-proof paint, wet straw screen or mat covers or plastics
Film covering.
Verify embodiment:
By following tests come the beneficial effect of the composite water-proof paint for the quick-dry type that the present invention is further explained.
1, according to the standard of GB/T 9755-2014 " exterior wall coating material of synthetic resin emulsion " (finishing coat) to composite water-proof paint
It is tested, the temperature for testing environment is 22-24 DEG C, and relative humidity 50-55%, test result is shown in Table 2.
2, composite water-proof paint is tested according to the standard of JC/T 2090-2001 " polymer cement waterproof slurry ",
The temperature for testing environment is 22-24 DEG C, and relative humidity 50-55%, test result is shown in Table 3.
3, composite water-proof paint is tested according to the standard of JG/T 210-2007 " building inside and outside wall priming paint ", is surveyed
The temperature in test ring border is 22-24 DEG C, and relative humidity 50-55%, test result is shown in Table 4.
4, the test of time embodiment 1-3 and commercially available two kinds of coating is dried.Under identical test environment,
The japanning for brushing 1 square metre on cement floor with coating respectively tests the surface drying time of paint film and does solid work the time.Surface drying time is
The time of surface layer film forming；Doing solid work the time is the time for being completely formed solid paint film.Surface drying time is tested with fingers-touch method；Do solid work the time
With pressure cotton pellet method test.
Fingers-touch method: touching surface of the paint film with finger, such as feel that some are tacky, but be sticked to finger without paint, that is, thinks that surface is dry
It is dry；
Pressure cotton pellet method: putting a rayon balls in surface of the paint film, in gently placing drying test device on cotton balls again, simultaneously
Stopwatch is started, through 30s, drying test device and cotton balls are taken away, places 5min, observation trace and loss of gloss of the paint film without cotton balls are existing
As can gently be brushed off with cotton balls, think paint film actual drying, test result is shown in Table 5 if there are 1-2 root staples on paint film.
Table 2: according to the standard of GB/T 9755-2014 " exterior wall coating material of synthetic resin emulsion " (finishing coat) to multiple
Water-repellent paint is closed to be tested:
Table 3: composite water-proof paint is surveyed according to the standard of JC/T 2090-2001 " polymer cement waterproof slurry "
Examination:
Table 4: composite water-proof paint is tested according to the standard of JG/T 210-2007 " building inside and outside wall priming paint ":
From table 2-4 as can be seen, composite water-proof paint of the invention meets GB/T 9755-2014 " outside synthetic resin emulsion
Wall coating " (finishing coat), " building inside and outside wall is used by JC/T 2090-2001 " polymer cement waterproof slurry " and JG/T 210-2007
Priming paint " standard.
Table 5
| Test item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Commercial coating 1 | Commercial coating 2 |
| Surface drying time | 2 | 2 | 1 | 19 | 24 |
| Do solid work the time | 5 | 6 | 4 | 24 | 48 |
As can be seen from Table 5, the surface drying time of the paint film of the composite water-proof paint of embodiment 1-3 and time Jun compare city is done solid work
The coating sold is short, it is seen then that composite water-proof paint of the invention can realize drying within the shorter time.
The above embodiment is only the preferred embodiment of the present invention, and the scope of protection of the present invention is not limited thereto,
The variation and replacement for any unsubstantiality that those skilled in the art is done on the basis of the present invention belong to institute of the present invention
Claimed range.
Claims (9)
1. a kind of composite water-proof paint of quick-dry type, including powder and liquid material, which is characterized in that
The powder includes the component of following parts by weight: 400-500 parts of portland cement, 250-350 parts of 100 mesh quartz sand,
200 100-200 parts of mesh quartz sands, 40-120 parts of micro-crystal powder, 0.1-2 parts of organosilicon hydrophobic powder, hydroxypropyl methyl cellulose ether
0.1-1 parts, 1-3 parts of water-reducing agent, 20-30 parts of latex powder, 0.1-0.3 parts of bentonite, 1-3 parts of defoaming agent, starch ether 0.1-0.3
Part；
The liquid material includes the component of following parts by weight: 40-50 parts of styrene-acrylic emulsion, 10-20 parts of acrylate and vinyl acetate emulsion, ash concrete or white
20-30 parts of cement, 2-4 parts of low-alkalinity sulphoaluminate cement, 6-10 parts of titanium dioxide, 6-10 parts of coarse whiting, 1-3 parts of talcum powder, emulsification
2-3 parts of agent, 1-1.5 parts of defoaming agent, 6-8 parts of coalescing agent, 5-10 parts of multifunctional assistant AMP-95,10-14 parts of water, polypropylene
2-4 parts of amide；
The powder and the mass ratio of the liquid material are 1:1.
2. the composite water-proof paint of quick-dry type according to claim 1, which is characterized in that
The powder includes the component of following parts by weight: 450 parts of portland cement, 300 parts of 100 mesh quartz sand, 200 mesh quartz
140 parts of sand, 80 parts of micro-crystal powder, 1 part of organosilicon hydrophobic powder, 0.3 part of hydroxypropyl methyl cellulose ether, 2 parts of water-reducing agent, latex powder 25
Part, 0.2 part of bentonite, 2 parts of defoaming agent, 0.1 part of starch ether；
The liquid material includes the component of following parts by weight: 45 parts of styrene-acrylic emulsion, 15 parts of acrylate and vinyl acetate emulsion, ash concrete or white cement 25
Part, 3 parts of low-alkalinity sulphoaluminate cement, 8 parts of titanium dioxide, 8 parts of coarse whiting, 2 parts of talcum powder, 2.5 parts of emulsifier, 1.2 parts of defoaming agent,
7 parts of coalescing agent, 6 parts of multifunctional assistant AMP-95,12 parts of water, 3 parts of polyacrylamide；
The powder and the mass ratio of the liquid material are 1:1.
3. the application method of the composite water-proof paint of quick-dry type of any of claims 1 or 2, which is characterized in that including following step
It is rapid:
The step of mixing: weighing the powder and liquid material of formula ratio, is uniformly mixed, obtains composite water-proof paint；
The step of brushing: water is added in composite water-proof paint, is brushed after mixing evenly；
The step of blade coating: composite water-proof paint drying to be brushed and then the secondary powder for weighing formula ratio and liquid material, mixing are equal
It is even, composite water-proof paint is obtained, water is added in composite water-proof paint, is scratched after mixing evenly.
4. the application method of the composite water-proof paint of quick-dry type according to claim 3, which is characterized in that
Further include the steps that maintenance: after the completion of the step of the blade coating, the composite water-proof paint of blade coating being carried out at least 24 hours
Maintenance work.
5. the application method of the composite water-proof paint of quick-dry type according to claim 3, which is characterized in that the brushing
In step, the water of 22-23ml is added in every 1 kilogram of composite water-proof paint；Brush with a thickness of 1mm.
6. the application method of the composite water-proof paint of quick-dry type according to claim 3, which is characterized in that the blade coating
In step, the water of 21-22ml is added in every 1 kilogram of composite water-proof paint；Blade coating with a thickness of 1-2mm.
7. the application method of the composite water-proof paint of quick-dry type according to claim 3, which is characterized in that in the brushing
The step of complete after, the step of interval carries out the blade coating in 3-6 hours again；After the step of brushing completes, work as painting
When blushing occurs in the composite water-proof paint of brush, sprinkling maintenance is carried out to the composite water-proof paint of brushing.
8. the application method of the composite water-proof paint of quick-dry type according to claim 3, which is characterized in that pass through the painting
After the step of the step of brush and the blade coating, the overall thickness of composite water-proof paint is 2-4mm.
9. the application method of the composite water-proof paint of quick-dry type according to claim 4, which is characterized in that the maintenance
The step of in maintenance work are as follows: when blushing occurs in the composite water-proof paint of blade coating, composite water-proof paint is spilt
Water, the covering of wet straw screen or mat or plastic film covering.