CN109161229A - A kind of Environmental Protective Water-paint - Google Patents
A kind of Environmental Protective Water-paint Download PDFInfo
- Publication number
- CN109161229A CN109161229A CN201810645188.3A CN201810645188A CN109161229A CN 109161229 A CN109161229 A CN 109161229A CN 201810645188 A CN201810645188 A CN 201810645188A CN 109161229 A CN109161229 A CN 109161229A
- Authority
- CN
- China
- Prior art keywords
- coating
- parts
- purified cotton
- cornstarch
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of Environmental Protective Water-paint is related to technical field of environmental protection paint, and the coating includes following component in parts by weight: white marble powder 25-35, bentonite 15-25, purified cotton 25-35, cornstarch 7-12, methylcellulose 8-15, nano zine oxide 3-8；The purified cotton is crushed to 60-80 mesh；The cornstarch is handled by gelatinization；The white marble powder is crushed to 65-180 mesh.
Description
Technical field
The present invention relates to technical field of environmental protection paint, specifically a kind of Environmental Protective Water-paint.
Background technique
Formaldehyde is the common additive of coating, colourless, there is the gas of intense stimulus type smell, for carcinogenic and cause anomaly
Matter, for own health, in finishing especially selection coating when, to select environmental protection coating material as far as possible, but environmental protection coating material, especially
It is water paint, poor air permeability, and existing environmental protection coating material color is single, and mostly pure color, is unable to satisfy colour mixture requirement, such as
Fruit uses wallpaper, and the resin on metope glue and wallpaper surface all contains a certain amount of harmful substance under normal conditions, so being badly in need of one
The new wall decorative paint of kind, to meet the various demands of people.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of Environmental Protective Water-paints, and having solved existing coating can not be adjusted
Room temperature, the single problem of color.
A kind of technical solution of present invention solution technical problem are as follows: Environmental Protective Water-paint, it is characterised in that: the coating is pressed
Parts by weight include following component: white marble powder 25-35, bentonite 15-25, purified cotton 25-35, cornstarch 7-12, methyl
Cellulose 8-15, nano zine oxide 3-8；The purified cotton is crushed to 60-80 mesh；The cornstarch is handled by gelatinization；Institute
It states white marble powder and is crushed to 65-180 mesh.
The coating further includes the colored purified cotton of clothes, and the clothes are 3-8 with colored purified cotton parts by weight, described
Colored purified cotton is crushed to 80-100 mesh.
The white marble powder is crushed to 80-100 mesh.
The preparation method for coating is as follows: being first sufficiently mixed cornstarch and methylcellulose for use；It is first that the Chinese is white
Beautiful powder, bentonite, purified cotton are put into blender and stirred 5 to 15 minutes, are put into the cornstarch and Methyl cellulose mixed later
Element stirs 1 to 5 minute, is put into the colored purified cotton of clothes, stirs 1 to 5 minute, is finally putting into nano zine oxide stirring 1 to 5
Minute can package encapsulation.
The coating application method is as follows: the sailor that 5-7kg is added in 1kg coating is dynamic or blender is stirred until homogeneous, institute
The temperature for stating water is greater than 20 DEG C, less than 30 DEG C；After stirring, mixture is uniformly draped over one's shoulders and scrapes or be sprayed on wall.
The coating further includes deionized water, parts by weight 20-40；Pure-acrylic emulsion, parts by weight 9-15；Coating is used
Dispersing agent, dispersant weight number are 1-2；Coating coalescing agent, coating are 3-5 with coalescing agent parts by weight；Coating is used
Defoaming agent, coating are 1-3 with defoaming agent parts by weight；Coating fungicide, coating are 1-3 with fungicide parts by weight.
The preparation method for coating is as follows: being put into dispersion machine after enough water is done deionization processing, sequentially adds later
White marble powder, bentonite, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating are used
Defoaming agent, methylcellulose, cornstarch, clothes use colored purified cotton, add the stage in material, dispersing speed is maintained at
300-500 turns, and every kind of material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with revolving speed 800-1500's
Revolving speed continues stirring 5 minutes, closes dispersion machine later, canning sealing, can opening when use, form of construction work and standard aqueous
Coating is similar.
Coating is Kathon CG with fungicide.
Benefit effect of the invention is: white marble powder not only the alternative titanium dioxide being usually used in coating and white marble powder from
Body dimensionally stable, environmental protection, the graceful beauty of the product effect constructed, shelf-life are longer.So white marble powder is applied as environmental protection
The main material of material has more utility value.Cornstarch is good adhesive agent after gelatinization, and not only tackness is strong, and there are no appoint
What is polluted, and is suitable for smearing after being combined with water, and be able to maintain stronger adhesive force after capable of drying.
The addition of purified cotton can allow pull resistance, crack resistance and the heat insulating effect of dope layer to be all greatly improved,
Whether arid area or humid area.Purified cotton is also equipped with the effect for adjusting indoor humidity simultaneously, when indoor humidity is larger
When purified cotton can adsorb a certain amount of steam, when room temperature is dry, the steam being adsorbed in purified cotton can diffuse to room again
It is interior, play the role of equilibrium humidity, nano zine oxide can play antibacterial, disinfection, anti-ultraviolet.
Clothes are effective identical as purified cotton with colored purified cotton institute, while additional color can also be provided for coating, especially
It is the various colors of light color, this enriches the choice of indoor colour.
This coating is divided into siccative and wet feed, and siccative is easy to store, and scene plus water are needed when use.Without adding when wet feed uses
Water, can opening are i.e. smearable.
Pre-gelatinized cornstarch mainly uses roller manufacture processing.
Specific embodiment
The present invention will be further described with reference to embodiments.
Embodiment 1.
The coating includes following component in parts by weight: 35 parts of white marble powder, 25 parts of bentonite, 35 parts of purified cotton, jade
12 parts of rice starch, 15 parts of methylcellulose, 8 parts of nano zine oxide, clothes use colored 8 parts of purified cotton；The purified cotton powder, clothes
80 mesh are broken to colored purified cotton；The cornstarch is handled by pre-gelatinized；The white marble powder is crushed to 180 mesh.
The preparation method for coating is as follows: being first sufficiently mixed cornstarch and methylcellulose uniformly stand-by；First will
White marble powder, bentonite, purified cotton are put into blender and stirred 5 to 15 minutes, are put into the cornstarch and methyl mixed later
Cellulose stirs 1 to 5 minute, is put into the colored purified cotton of clothes, stirs 1 to 5 minute, is finally putting into nano zine oxide stirring 1
It can package encapsulation to 5 minutes.
The coating application method is as follows: the sailor that 7kg is added in 1kg coating is dynamic or blender is stirred until homogeneous exquisiteness,
The temperature of the water is greater than 20 DEG C, less than 30 DEG C；After stirring, mixture uniformly is smeared to drape over one's shoulders and is scraped in wall.
Embodiment 2.
The coating includes following component in parts by weight: 25 parts of white marble powder, 15 parts of bentonite, 25 parts of purified cotton, jade
7 parts of rice starch, 8 parts of methylcellulose, 3 parts of nano zine oxide, colored 3 parts of purified cotton；The purified cotton powder, the colored essence of clothes
Cotton processed is broken to 80 mesh；The cornstarch is handled by pre-gelatinized；The white marble powder is crushed to 65 mesh.
The preparation method for coating is as follows: being first sufficiently mixed cornstarch and methylcellulose；Again by white marble powder, swollen
Profit soil, purified cotton are put into blender and stirred 5 to 15 minutes, are put into the cornstarch and methylcellulose mixed, stirring 1 later
To 5 minutes, it is put into the colored purified cotton of clothes, is stirred 1 to 5 minute, nano zine oxide is finally putting into and stirs 1 to 5 minute
Package encapsulation.
The coating application method is as follows: the sailor that 6kg is added in 1kg coating is dynamic or blender is stirred until homogeneous exquisiteness,
The temperature of the water is greater than 20 DEG C, less than 30 DEG C；After stirring, mixture uniformly is smeared to drape over one's shoulders and is scraped in wall.
Embodiment 3.
The coating includes following component in parts by weight: 30 parts of white marble powder, 20 parts of bentonite, 30 parts of purified cotton, jade
9 parts of rice starch, 11 parts of methylcellulose, 6 parts of nano zine oxide, colored 5 parts of purified cotton；The purified cotton, the colored essence of clothes
Cotton processed is crushed to 75 mesh；The cornstarch is handled by pre-gelatinized；The white marble powder is crushed to 80 mesh.
The preparation method for coating is as follows: being first sufficiently mixed cornstarch and methylcellulose uniformly stand-by；First will
White marble powder, bentonite, purified cotton are put into blender and stirred 5 to 15 minutes, are put into the cornstarch and methyl mixed later
Cellulose stirs 1 to 5 minute, is put into the colored purified cotton of clothes, stirs 1 to 5 minute, is finally putting into nano zine oxide stirring 1
It can package encapsulation to 5 minutes.
The coating application method is as follows: the sailor that 6kg is added in 1kg coating is dynamic or blender is stirred until homogeneous exquisiteness,
The temperature of the water is greater than 20 DEG C, less than 30 DEG C；After stirring, mixture uniformly is smeared to drape over one's shoulders and is scraped in wall.
Embodiment 4.
The coating includes following component in parts by weight: 30 parts of white marble powder, 20 parts of bentonite, 30 parts of purified cotton, jade
9 parts of rice starch, 11 parts of methylcellulose, 6 parts of nano zine oxide, colored 5 parts of purified cotton；The purified cotton, the colored essence of clothes
Cotton processed is crushed to 75 mesh；The cornstarch is handled by pre-gelatinized；The white marble powder is crushed to 100 mesh.
The preparation method for coating is as follows: being first sufficiently mixed cornstarch and methylcellulose uniformly stand-by；First will
White marble powder, bentonite, purified cotton are put into blender and stirred 5 to 15 minutes, are put into the cornstarch and methyl mixed later
Cellulose stirs 1 to 5 minute, is put into the colored purified cotton of clothes, stirs 1 to 5 minute, is finally putting into nano zine oxide stirring 1
It can package encapsulation to 5 minutes.
The coating application method is as follows: the sailor that 6kg is added in 1kg coating is dynamic or blender is stirred until homogeneous exquisiteness,
The temperature of the water is greater than 20 DEG C, less than 30 DEG C；After stirring, mixture uniformly is smeared to drape over one's shoulders and is scraped in wall.
Embodiment 5.
The coating includes following component in parts by weight: 30 parts of white marble powder, 20 parts of bentonite, 30 parts of purified cotton, jade
9 parts of rice starch, 11 parts of methylcellulose, 6 parts of nano zine oxide, clothes use colored 5 parts of purified cotton；The purified cotton, clothes are used
Colored purified cotton is crushed to 75 mesh；The cornstarch is handled by gelatinization；The white marble powder is crushed to 90 mesh.
The preparation method for coating is as follows: being first sufficiently mixed cornstarch and methylcellulose uniformly stand-by；First will
White marble powder, bentonite, purified cotton are put into blender and stirred 5 to 15 minutes, are put into the cornstarch and methyl mixed later
Cellulose stirs 1 to 5 minute, is put into the colored purified cotton of clothes, stirs 1 to 5 minute, is finally putting into nano zine oxide stirring 1
It can package encapsulation to 5 minutes.
The coating application method is as follows: the sailor that 6kg is added in 1kg coating is dynamic or blender is stirred until homogeneous exquisiteness,
The temperature of the water is greater than 20 DEG C, less than 30 DEG C；After stirring, mixture uniformly is smeared to drape over one's shoulders and is scraped in wall.
Embodiment 6.
The coating includes following component in parts by weight: 35 parts of white marble powder, 25 parts of bentonite, 35 parts of purified cotton, jade
12 parts of rice starch, 15 parts of methylcellulose, 8 parts of nano zine oxide, clothes use colored 8 parts of purified cotton, 40 parts of deionized water, pure C
15 parts of lotion, 2 parts of dispersing agent of coating, 5 parts of coating coalescing agent, 3 parts of coating defoaming agent, 3 parts of coating fungicide.Institute
It states purified cotton powder, clothes and is broken to 80 mesh with colored purified cotton；The cornstarch is handled by pre-gelatinized；The white marble powder powder
It is broken to 180 mesh.
The preparation method for coating is as follows: deionized water being put into dispersion machine, sequentially adds white marble powder, swelling later
Soil, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating defoaming agent, methyl are fine
It ties up element, cornstarch, clothes and uses colored purified cotton, added the stage in material, dispersing speed is maintained at 300-500 and turns, and every kind
Material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with the revolving speed of revolving speed 800-1500, continues stirring 5
Minute, close dispersion machine later, canning sealing, can opening when use, form of construction work is similar with standard aqueous coating.
Coating is Kathon CG with fungicide.
Embodiment 7.
The coating includes following component in parts by weight: 25 parts of white marble powder, 15 parts of bentonite, 25 parts of purified cotton, jade
7 parts of rice starch, 8 parts of methylcellulose, 3 parts of nano zine oxide, colored 3 parts of purified cotton, 20 parts of deionized water, pure-acrylic emulsion 9-
Part, 1 part of dispersing agent of coating, 3 parts of coating coalescing agent, 1 part of coating defoaming agent, 1 part of coating fungicide；The purification
Cotton powder, clothes are broken to 80 mesh with colored purified cotton；The cornstarch is handled by gelatinization；The white marble powder is broken to 120 mesh.
The preparation method for coating is as follows: deionized water being put into dispersion machine, sequentially adds white marble powder, swelling later
Soil, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating defoaming agent, methyl are fine
It ties up element, cornstarch, clothes and uses colored purified cotton, added the stage in material, dispersing speed is maintained at 300-500 and turns, and every kind
Material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with the revolving speed of revolving speed 800-1500, continues to stir
Dispersion 5 minutes, closes dispersion machine later, canning sealing, can opening when use, and form of construction work is similar with standard aqueous coating.
Coating is Kathon CG with fungicide.
Embodiment 8.
The coating includes following component in parts by weight: 30 parts of white marble powder, 20 parts of bentonite, 30 parts of purified cotton, jade
9 parts of rice starch, 11 parts of methylcellulose, 6 parts of nano zine oxide, clothes use colored 5 parts of purified cotton, 30 parts of deionized water, pure C
12 parts of lotion, 1.5 parts of dispersing agent of coating, 4 parts of coating coalescing agent, 2 parts of coating defoaming agent, 2 parts of coating fungicide；
The purified cotton, clothes are crushed to 75 mesh with colored purified cotton；The cornstarch is handled by gelatinization；The white marble powder powder
It is broken to 90 mesh.
The preparation method for coating is as follows: deionized water being put into dispersion machine, sequentially adds white marble powder, swelling later
Soil, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating defoaming agent, methyl are fine
It ties up element, cornstarch, clothes and uses colored purified cotton, added the stage in material, dispersing speed is maintained at 300-500 and turns, and every kind
Material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with the revolving speed of revolving speed 800-1500, continues to stir
Dispersion 5 minutes, closes dispersion machine later, canning sealing, can opening when use, and form of construction work is similar with standard aqueous coating.
Coating is Kathon CG with fungicide.
Embodiment 9.
The coating includes following component in parts by weight: 35 parts of white marble powder, 25 parts of bentonite, 35 parts of purified cotton, jade
12 parts of rice starch, 15 parts of methylcellulose, 8 parts of nano zine oxide, clothes use colored 8 parts of purified cotton, 40 parts of deionized water, pure C
15 parts of lotion, 2 parts of dispersing agent of coating, 5 parts of coating coalescing agent, 3 parts of coating defoaming agent, 3 parts of coating fungicide.Institute
It states purified cotton powder, clothes and is broken to 80 mesh with colored purified cotton；The cornstarch is handled by pre-gelatinized；The white marble powder powder
It is broken to 130 mesh.
The preparation method for coating is as follows: being put into dispersion machine after enough water is done deionization processing, sequentially adds later
White marble powder, bentonite, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating are used
Defoaming agent, methylcellulose, cornstarch, clothes use colored purified cotton, add the stage in material, dispersing speed is maintained at
300-500 turns, and every kind of material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with revolving speed 800-1500's
Revolving speed continues to be dispersed with stirring 5 minutes, closes dispersion machine later, canning sealing, and can opening when use smears mode and routine
Water paint is similar.
Coating is Kathon CG with fungicide.
Embodiment 10.
The coating includes following component in parts by weight: 25 parts of white marble powder, 15 parts of bentonite, 25 parts of purified cotton, jade
7 parts of rice starch, 8 parts of methylcellulose, 3 parts of nano zine oxide, colored 3 parts of purified cotton, 20 parts of deionized water, pure-acrylic emulsion 9-
Part, 1 part of dispersing agent of coating, 3 parts of coating coalescing agent, 1 part of coating defoaming agent, 1 part of coating fungicide；The purification
Cotton powder, clothes are broken to 80 mesh with colored purified cotton；The cornstarch is handled by pre-gelatinized；The white marble powder is crushed to
160 mesh.
The preparation method for coating is as follows: deionized water being put into dispersion machine, sequentially adds white marble powder, swelling later
Soil, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating defoaming agent, methyl are fine
It ties up element, cornstarch, clothes and uses colored purified cotton, added the stage in material, dispersing speed is maintained at 300-500 and turns, and every kind
Material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with the revolving speed of revolving speed 800-1500, continues to stir
Dispersion 5 minutes, closes dispersion machine later, canning sealing, can opening when use, and form of construction work is similar with standard aqueous coating.
Coating is Kathon CG with fungicide.
Embodiment 11.
The coating includes following component in parts by weight: 30 parts of white marble powder, 20 parts of bentonite, 30 parts of purified cotton, jade
9 parts of rice starch, 11 parts of methylcellulose, 6 parts of nano zine oxide, clothes use colored 5 parts of purified cotton, 30 parts of deionized water, pure C
12 parts of lotion, 1.5 parts of dispersing agent of coating, 4 parts of coating coalescing agent, 2 parts of coating defoaming agent, 2 parts of coating fungicide；
The purified cotton, clothes are crushed to 90 mesh with colored purified cotton；The cornstarch is handled by gelatinization；The white marble powder powder
It is broken to 100 mesh.
The preparation method for coating is as follows: being put into dispersion machine after enough water is done deionization processing, sequentially adds later
White marble powder, bentonite, purified cotton, nano zine oxide, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating are used
Defoaming agent, methylcellulose, cornstarch, clothes use colored purified cotton, add the stage in material, dispersing speed is maintained at
300-500 turns, and every kind of material addition interval is greater than 5 minutes, after material adds, keeps dispersion machine with revolving speed 800-1500's
Revolving speed continues to be dispersed with stirring 5 minutes, closes dispersion machine later, canning sealing, can opening when use, form of construction work and routine
Water paint is similar.
Coating is Kathon CG with fungicide.
Claims (8)
1. a kind of Environmental Protective Water-paint, it is characterised in that: the coating includes following component in parts by weight: white marble powder 25-
35, bentonite 15-25, purified cotton 25-35, cornstarch 7-12, methylcellulose 8-15, nano zine oxide 3-8；The purification
Cotton is crushed to 60-80 mesh；The cornstarch is handled by gelatinization；The white marble powder is crushed to 65-180 mesh.
2. a kind of Environmental Protective Water-paint according to claim 1, it is characterised in that: the coating further includes clothes colour
Purified cotton, the clothes are 3-8 with colored purified cotton parts by weight, and the colour purified cotton is crushed to 80-100 mesh.
3. a kind of Environmental Protective Water-paint according to claim 2, it is characterised in that: the white marble powder is crushed to 80-100
Mesh.
4. a kind of Environmental Protective Water-paint according to claim 3, it is characterised in that: the preparation method for coating is as follows: first
Cornstarch and methylcellulose are sufficiently mixed for use；White marble powder, bentonite, purified cotton are put into blender and stirred first
5 to 15 minutes, it is put into the cornstarch and methylcellulose mixed later, stirs 1 to 5 minute, is put into the colored essence of clothes
Cotton processed stirs 1 to 5 minute, and being finally putting into nano zine oxide stirring 1 to 5 minute can package encapsulation.
5. a kind of Environmental Protective Water-paint according to claim 4, it is characterised in that: the coating application method is as follows: will
The sailor that 5-7kg is added in 1kg coating moves or blender is stirred until homogeneous, and the temperature of the water is greater than 20 DEG C, less than 30 DEG C；Stirring
After, mixture is uniformly draped over one's shoulders and scrapes or be sprayed on wall.
6. a kind of Environmental Protective Water-paint according to claim 3, it is characterised in that: the coating further includes deionized water,
Parts by weight are 20-40；Pure-acrylic emulsion, parts by weight 9-15；Coating dispersing agent, dispersant weight number are 1-2；Coating
With coalescing agent, coating is 3-5 with coalescing agent parts by weight；Coating defoaming agent, coating are 1- with defoaming agent parts by weight
3；Coating fungicide, coating are 1-3 with fungicide parts by weight.
7. a kind of Environmental Protective Water-paint according to claim 6, it is characterised in that: the preparation method for coating is as follows: will
Enough water is put into dispersion machine after doing deionization processing, sequentially adds white marble powder, bentonite, purified cotton, nano oxidized later
Zinc, pure-acrylic emulsion, coating dispersing agent, coating coalescing agent, coating defoaming agent, methylcellulose, cornstarch, clothes
It with colored purified cotton, is added the stage in material, dispersing speed is maintained at 300-500 and turns, and every kind of material addition interval is greater than 5 points
Clock after material adds, keeps dispersion machine with the revolving speed of revolving speed 800-1500, continues stirring 5 minutes, close dispersion later
Machine, canning sealing, can opening when use, form of construction work are similar with standard aqueous coating.
8. a kind of Environmental Protective Water-paint according to claim 7, it is characterised in that: the coating is Kathon CG with fungicide.