CN109135896A - A kind of dehydration-type antirust agent, Preparation method and use - Google Patents
A kind of dehydration-type antirust agent, Preparation method and use Download PDFInfo
- Publication number
- CN109135896A CN109135896A CN201811175466.XA CN201811175466A CN109135896A CN 109135896 A CN109135896 A CN 109135896A CN 201811175466 A CN201811175466 A CN 201811175466A CN 109135896 A CN109135896 A CN 109135896A
- Authority
- CN
- China
- Prior art keywords
- dehydration
- antirust agent
- agent
- minutes
- type antirust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of dehydration-type antirust agent, including the following each component of weight proportion: 52-78 parts of base oil；20-40 parts of antirust agent；2-8 parts of dehydrating agent；Film forming agent: 1-5 parts；0.1-1 parts of antioxidant.The preparation method of dehydration-type antirust agent of the present invention is opened stirring, is stirred 10 minutes the following steps are included: step 1, base oil is added in reaction vessel；Antirust agent, film forming agent are added in reaction vessel by step 2, are stirred 5-20 minutes；Dehydrating agent is added in reaction vessel step 3, stirs 5-20 minutes；Step 4, finally by antioxidant be added reaction vessel in, after the above substance all adds, at 70-80 DEG C, react 100-150 minutes, obtain final products dehydration-type antirust agent.Dehydration-type antirust agent of the present invention can once complete metal material, part, the dehydration of component, antirust；No pollution to the environment has no toxic and side effect to human body.
Description
Technical field
The present invention relates to dehydration antirust technology more particularly to a kind of dehydration-type antirust agent, Preparation method and use.
Background technique
Dehydration-type antirust oil belongs to field of metal surface treatment technology, and composition generally by base oil, prevent by water-removal additive
Rust additive and film forming agent are formed by combining.Currently, dehydration-type antirust oil can not have both the advantages of dehydration and antirust, and easily to ring
Border pollutes, and is also easy to produce toxic side effect to human body.
Summary of the invention
It is an object of the present invention to the advantages of dehydration and antirust can not be had both for current dehydration-type antirust oil, and it is easily right
The problem of environment pollutes, and is also easy to produce toxic side effect to human body proposes a kind of dehydration-type antirust agent, can once complete metal material
Material, part, the dehydration of component, antirust；No pollution to the environment has no toxic and side effect to human body.
To achieve the above object, the technical solution adopted by the present invention is that: a kind of dehydration-type antirust agent, including weight proportion is such as
Under each component:
Further, dehydration-type antirust agent, including the following each component of weight proportion:
Further, the base oil be one of machinery oil, transformer oil, hydraulic oil, kerosene and industrial naptha or
A variety of mixing.
Further, the antirust agent is petroleum sulfonate, lanolin, stearic acid, paraffin, zinc naphthenate and oily triethylenetetraminehexaacetic acid
One of hydramine or a variety of mixing.
Further, the dehydrating agent be one of ethyl alcohol, n-octyl alcohol, isopropanol, petroleum ether, butyl or
A variety of mixing.
Further, the antioxidant is diphenylamines, Butylated Hydroxytoluene, hydroquinone, one in thiophosphoric acid zinc
Kind or a variety of mixing.
The film forming agent is one of pitch, vaseline, phenolic resin, terpene resin, polyisobutylene resin or a variety of
Mixing.
Another object of the present invention also discloses a kind of preparation method of dehydration-type antirust agent, comprising the following steps:
Base oil is added to the container by step 1, opens stirring, is stirred 5-20 minutes；
Antirust agent, film forming agent are added in reaction vessel step 2, stir 5-20 minutes；
Dehydrating agent is added in reaction vessel step 3, stirs 5-20 minutes, preferably 10 minutes；
Step 4, finally by antioxidant be added reaction vessel in, after the above substance all adds, at 70-80 DEG C, instead
It answers 100-150 minutes (preferably 120 minutes), obtains final products.
Another object of the present invention also discloses a kind of above-mentioned dehydration-type antirust agent in metal material, part, component
Short, mid-term dehydration antirust field application.
Further, for the various mechanical, equipment of industrial production enterprise processing, manufacture, maintenance process metal material
Material, the short of components, mid-term dehydration, antirust treatment.
Further, automobile, motorcycle, locomotive, refrigeration air-conditioner, compressor, diesel engine, gasoline engine, electronics, electricity are used for
The processing of the metal parts such as device, household electrical appliances, manufacturing enterprise's ferrous metal and nonferrous materials, part, the dehydration of component, antirust
Processing.
The workpiece that need to be dehydrated and derust is handled using dehydration-type antirust agent of the present invention, comprising the following steps:
1. immersing the metal works after cleaning in the dehydration oil groove equipped with this product, such as workpiece shapes complexity, need to tremble up and down
It moves several times.Single workpiece can take off water for 2~3 minutes, need 3~5 minutes if filling workpiece with hanging basket, notice that workpiece can only
Suspention, cannot be sunken to slot bottom；
2. the periodically ponding that discharge oil groove bottom is taken off；
3. dehydrated oil trench bottom is taper, discharging valve is divided into, so that the moisture content of removing is deposited on bottom, is in due course discharged water
Out.Live metal net should be set away from dehydrated oil trench bottom certain altitude or porous every disk, with guarantee workpiece not with bottom
Water layer contact；
4. implementing naturally dry, air-dried or baking process to workpiece by antirust requirement and process stipulation；
5. the part after dehydration, antirust treatment is placed in appropriate place by regulation, and real by the manufacturing technique requirent of part
Apply subsequent handling.
Using dehydration-type antirust agent of the present invention to needing antirust, but the workpiece for being not required to dehydration is handled, comprising the following steps:
1. the method for taking spray, leaching, painting directly carries out antirust treatment with this product；
2. implementing naturally dry, air-dried or baking process to workpiece by antirust requirement and process stipulation；
3. the part after antirust treatment is placed in appropriate place by regulation, and subsequent by the implementation of the manufacturing technique requirent of part
Process.
Dehydration-type rust inhibitor formulation of the present invention is scientific and reasonable, has the advantage that compared with prior art
1) dehydration-type antirust agent of the present invention has excellent rust-proof effect, is able to satisfy metal material, part, component
It is required between short, mid-term process with inventory's antirust；
2) dehydration-type antirust agent dehydration of the present invention is fast, general only to need eliminate workpiece surface moisture film within 2~5 minutes, and
Make oily mutually infiltration workpiece surface；
3) dehydration-type antirust agent good antirust property of the present invention, the antirust for meeting many export enterprise products require (sea fortune
Defeated 1-3 months, in the case where outer Packing Sound, components can not generate corrosion.Including the product being electroplated)；
4) dehydration-type antirust agent rust-proof life of the present invention because of environment epidemic disaster, it is different due to corrode the difference of sexual element, usually may be used
Up to 1-2；
5) dehydration-type antirust agent of the present invention can be used in normal temperature environment, energy saving, improve effect, easy to use, operation
Person can work in the environment of safety and comfort；
In short, dehydration-type antirust oil of the present invention has several big advantages: dewatering speed is fast compared with existing similar-type products,
Water layer can be replaced separation and taken off, realized fast by the remaining moisture film of workpiece surface, the middle a few minutes for being immersed in dewatering rust preventive oil
The effect of speed dehydration；Good antirust property, this dewatering rust preventive oil can be used as rust prevention during manufacture, also can be used as and seal antirust up for safekeeping, antirust
Phase is long, and the rust-proof life of 1-2 can be realized according to actual condition.As dehydration-type antirust oil, fast dewatering is taken into account and has prevented for a long time
The advantages of rust, is used widely in many industries.
Specific embodiment
The present invention is further described with reference to embodiments:
Embodiment 1
Present embodiment discloses a kind of dehydration-type antirust agent, including the following each component of weight proportion:
The base oil is the mixing of machinery oil and transformer oil that mass ratio is 1:1, and the antirust agent is that mass ratio is
Mixing in the zinc naphthenate and triethanolamine oleate of 1:1.5, the film forming agent are paraffin, and the dehydrating agent is petroleum ether, institute
State the mixing that antioxidant is diphenylamines, Butylated Hydroxytoluene, hydroquinone that mass ratio is 2:3:2.
The preparation method of the present embodiment dehydration-type antirust agent, comprising the following steps:
Base oil is added in reaction vessel step 1, opens stirring, stirs 10 minutes；
Step 2 sequentially adds antirust agent, film forming agent in reaction vessel, stirs 10 minutes；
Dehydrating agent is added in reaction vessel step 3, stirs 10 minutes；
Step 4, finally by antioxidant be added reaction vessel in, after the above substance all adds, at 70-80 DEG C, instead
It answers 120 minutes, obtains final products dehydration-type antirust agent.
Physicochemical property through detecting the present embodiment dehydration-type antirust agent is as follows:
Appearance: brown liquid
Density: 0.857g/cm3
Dehydration property (45# steel): qualified
Salt spray test (35 ± 1 DEG C, 5%NaCl, 72h): 0 grade
Damp heat test (49 ± 1 DEG C, RH > 95%, 360h): 0 grade
Corrosion test (55 ± 1 DEG C, steel, zinc, brass, aluminium, 168h): qualified
Embodiment 2
Present embodiment discloses a kind of dehydration-type antirust agent, including the following each component of weight proportion:
The base oil is the kerosene that mass ratio is 1:1 and industrial naptha mixing, and the antirust agent is that mass ratio is 1:1:3
Paraffin, the mixing in zinc naphthenate and triethanolamine oleate, the dehydrating agent is that mass ratio is 1:1 isopropanol, petroleum ether
Mixing, the antioxidant are diphenylamines；The film forming agent is that mass ratio is the mixed of 2:1 phenolic resin and polyisobutylene resin
It closes.
The preparation method of dehydration-type antirust agent described in the present embodiment, comprising the following steps:
Base oil is added in reaction vessel step 1, opens stirring, stirs 20 minutes；
Step 2 sequentially adds antirust agent, film forming agent in reaction vessel, stirs 20 minutes；
Dehydrating agent is added in reaction vessel step 3, stirs 20 minutes；
Step 4, finally by antioxidant be added reaction vessel in, after the above substance all adds, at 70-80 DEG C, instead
It answers 120 minutes, obtains final products dehydration-type antirust agent.
Physicochemical property through detecting the present embodiment dehydration-type antirust agent is as follows:
Appearance: brown liquid
Density: 0.850g/cm3
Dehydration property (45# steel): qualified
Salt spray test (35 ± 1 DEG C, 5%NaCl, 72h): 0 grade
Damp heat test (49 ± 1 DEG C, RH > 95%, 360h): 0 grade
Corrosion test (55 ± 1 DEG C, steel, zinc, brass, aluminium, 168h): qualified
Finally, it should be noted that the above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations；To the greatest extent
Pipe present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that: its according to
So be possible to modify the technical solutions described in the foregoing embodiments, or to some or all of the technical features into
Row equivalent replacement；And these are modified or replaceed, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (8)
1. a kind of dehydration-type antirust agent, which is characterized in that including the following each component of weight proportion:
2. dehydration-type antirust agent according to claim 1, which is characterized in that the base oil is machinery oil, transformer oil, liquid
One of pressure oil, kerosene and industrial naptha or a variety of mixing.
3. dehydration-type antirust agent according to claim 1, which is characterized in that the antirust agent be petroleum sulfonate, lanolin,
One of stearic acid, paraffin, zinc naphthenate and triethanolamine oleate or a variety of mixing.
4. dehydration-type antirust agent according to claim 1, which is characterized in that the dehydrating agent is ethyl alcohol, n-octyl alcohol, isopropyl
One of alcohol, petroleum ether, butyl or a variety of mixing.
5. dehydration-type antirust agent according to claim 1, which is characterized in that the antioxidant is diphenylamines, tert-butyl pair
One of cresols, hydroquinone, thiophosphoric acid zinc or a variety of mixing.
6. dehydration-type antirust agent according to claim 1, which is characterized in that the film forming agent is pitch, vaseline, phenolic aldehyde tree
One of rouge, terpene resin, polyisobutylene resin or a variety of mixing.
7. a kind of preparation method of dehydration-type antirust agent described in claim 1-6 any one, which is characterized in that including following step
It is rapid:
Base oil is added to the container by step 1, opens stirring, is stirred 5-20 minutes；
Antirust agent, film forming agent are added in reaction vessel step 2, stir 5-20 minutes；
Dehydrating agent is added in reaction vessel step 3, stirs 5-20 minutes；
Step 4, finally by antioxidant be added reaction vessel in, after the above substance all adds, at 70-80 DEG C, reaction
100-150 minutes, obtain final products dehydration-type antirust agent.
8. dehydration-type antirust agent described in a kind of claim 1-6 any one is in short, the mid-term of metal material, part, component
It is dehydrated the application in antirust field.