CN106637176A - Water-based brass antioxidant containing bamboo vinegar and preparation method thereof - Google Patents
Water-based brass antioxidant containing bamboo vinegar and preparation method thereof Download PDFInfo
- Publication number
- CN106637176A CN106637176A CN201611157509.2A CN201611157509A CN106637176A CN 106637176 A CN106637176 A CN 106637176A CN 201611157509 A CN201611157509 A CN 201611157509A CN 106637176 A CN106637176 A CN 106637176A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- bamboo vinegar
- phytic acid
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based brass antioxidant containing bamboo vinegar. The antioxidant per liter is prepared from the following raw materials of, by weight, 10-12 parts of 50wt.% phytic acid, 20-22 parts of 30wt.% hydrogen peroxide, 13-15 parts of bamboo vinegar, 10-12 parts of polyethylene glycol, 4-6 parts of lanthanum nitrate, 3-5 parts of corn starch, 2-4 parts of alumina sol, 3-4 parts of urotropine, 0.1-0.2 part of natural lemon essential oil, 1.2-1.4 parts of sodium dodecyl benzene sulfonate, 2.1-2.4 parts of methyl triethoxysilane and an appropriate amount of deionized water. According to the water-based brass antioxidant containing bamboo vinegar and a preparation method thereof, the phytic acid and the hydrogen peroxide serve as main components, after being modified through a silane coupling agent, the phytic acid is compatible with the corn starch modified through bamboo vinegar and other components, and the prepared antioxidant can directly dissolve in water; operation is easy and convenient, and special devices are not needed; and when the surface of brass is coated with a product, adhesive force is good, the product is not prone to falling off, the antiseptic time is long, and the oxidation-resisting and color-protecting capacity is high.
Description
Technical field
The present invention relates to metal oxidation resistance technical field, more particularly to a kind of water base brass antioxidant of addition bamboo vinegar
And preparation method thereof.
Background technology
The alloy that brass is made up of copper and zinc, both with excellent conduction, thermal conductivity and easily processed into type excellent
Point, and with enough mechanical strengths, hardness and chemical resistance, be commonly used for manufacturing valve, water pipe, air-conditioning internal-external machine company
Adapter and radiator etc..But run into acidity, alkaline corrosion medium or be still susceptible in higher temperatures and high humidity environment oxygen
Change corrosion and change colour, have a strong impact on outward appearance and use value while also bringing bad impact to secondary operation.It is domestic at present
The outer handling process to copper and its anti-oxidant discoloration of alloy surface mainly has:It is inorganic passivation technique for filming, organic inhibition technology, dilute
Native addition method, self-assembling technique and resinous coat technology etc., wherein most economical, easy method is passivated in brass surfaces
Process.Most ripe method is that using bichromate Passivation Treatment, but the method is in process of production and the sexavalence that remains in waste liquid
Chromium is noxious material, and many countries have prohibitted the use of bichromate Passivation Treatment, therefore, document《Brass surfaces richness phytic acid is blunt
Change technical study》Have for brass surfaces antirust with the passivating solution that phytic acid, hydrogen peroxide, polyethylene glycol etc. are prepared as primary raw material
Important realistic meaning.
Process is passivated to cold rolling HAl72-2.5-1 brass strips using passivating solution in document, is as a result shown, rich phytic acid
The optimum process condition of passivating film is:Passivation temperature scope is 35~40 DEG C, and pH value is 2.5, and passivation time is 60s;SEM microcosmic
Pattern shows that film surface is smooth, compact structure;Zero-G test result shows can be to alloy material using rich phytic acid Passivation Treatment
Play a very good protection;Show that the sample ratio processed using rich phytic acid adopts bichromate through the saline fog method test of 12h
The sample of process has in more preferable anti-tarnishing ability and rich phytic acid passivating solution without chromium, and pollution of chromium will not be produced in waste liquid.
But the phytic acid film in document, under the heavier environment of humidity, because damp moisture resistance is not good, storage time is short, coating
When brass surfaces carry out secondary operation, resistance to elevated temperatures is limited, in welding process, it is impossible to keep for a long time and multiple
High temperature impact;Secondly in document also there is short anti oxidation time, environmentally friendly bad adaptability, single function, heat surely in obtained passivator
The problems such as qualitative difference, weatherability difference and sun-proof ultraviolet radiation preventing difference, thus limit the lifting of overall performance and apply model
Enclose, it is necessary to improve existing production technology and formula, prepare the brass table with the function such as anti-corrosion, anti-oxidant, wear-resisting, sun-proof
Face process antioxidant.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of water base brass antioxygen of addition bamboo vinegar
Agent and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of water base brass antioxidant of addition bamboo vinegar, every liter of antioxidant is prepared by the raw materials in:
50wt.% phytic acid 10-12,30wt.% hydrogen peroxide 20-22, bamboo vinegar 13-15, polyethylene glycol 10-12, lanthanum nitrate 4-6, corn form sediment
Powder 3-5, Alumina gel 2-4, methenamine 3-4, natural lemon essential oil 0.1-0.2, neopelex 1.2-1.4, methyl
Triethoxysilane 2.1-2.4, appropriate deionized water.
A kind of preparation method of the water base brass antioxidant of described addition bamboo vinegar, comprises the following steps:
(1)Cornstarch is mixed in deionized water the suspension for being configured to that mass percent concentration is 5-10%, 40- is put into
In 60 DEG C of water-baths, Alumina gel ultrasonic wave dispersion grinding 6-12 hours are added, add bamboo vinegar ultrasound wave irradiation reaction 2-8 hours, it is cold
But to room temperature, filtration washing to neutrality, dry modified corn starch;
(2)MTES and deionized water are pressed into 1:3 mass ratio is stirred at room temperature after mixing and is warming up to 80-
100 DEG C, methenamine ultrasonic disperse 5-7 hours are added, be cooled to 45-55 DEG C of addition reaction of phytic acid 1-2 hour, obtain modified plant
Acid;
(3)By step(1)Obtained modified corn starch grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Temperature to 70-80 DEG C adds natural lemon essential oil reaction 4-6 hours, cooling;
(4)By step(3)Material is put in reactor, adds neopelex and other residual components to stir and evenly mix,
1L is added water to, is stirred 20-60 minutes in 40-50 DEG C, discharging.
It is an advantage of the invention that:The present invention with phytic acid, hydrogen peroxide as main component, due to there is 24 oxygen originals in phytate molecule
Son, 12 hydroxyls and 6 are phosphate-based, and these atoms or group can form complex compound with metallic atom and metal ion, will plant
Acid carry out it is silane coupler modified after, on the one hand can be anti-by hydrogen bond or dehydration between unreacted phosphorus hydroxyl in passivating process
Should, connection forms spatial networks phytic acid (salt) passivating film of high crosslink density, on the other hand can with silane hydrolyzate after generate-
Si-OH- reactions generate-P-O-Si- keys, can generate stable chelate with metal, are attached to one layer of metal surface formation colourless
Homogeneous, the non-microcracked protective film of transparent, surfacing, thickness densification effectively prevents corrosive medium from penetrating into metal surface,
So as to slow down corrosion of metal, it is added to cornstarch Jing bamboo vinegars are modified in raw material, improves its glutinous in water
Degree, then compatibility other antioxidants obtained in effective auxiliary agent can be directly dissolved in water, it is easy to operate, special installation is not necessary to, will produce
It is strong that product are coated in good difficult for drop-off, the anti-corrosion time length of brass surfaces adhesive force, anti-oxidant Anti- tarnishing ability.
Specific embodiment
A kind of water base brass antioxidant of addition bamboo vinegar, every liter of antioxidant is prepared by the raw materials in:
50wt.% phytic acid 10,30wt.% hydrogen peroxide 20, bamboo vinegar 13, polyethylene glycol 10, lanthanum nitrate 4, cornstarch 3, Alumina gel 2, crow
Lip river tropine 3, natural lemon essential oil 0.1, neopelex 1.2, MTES 2.1, appropriate deionized water.
A kind of preparation method of the water base brass antioxidant of described addition bamboo vinegar, comprises the following steps:
(1)Cornstarch is mixed in deionized water the suspension for being configured to that mass percent concentration is 5-10%, 40- is put into
In 60 DEG C of water-baths, Alumina gel ultrasonic wave dispersion grinding 6-12 hours are added, add bamboo vinegar ultrasound wave irradiation reaction 2-8 hours, it is cold
But to room temperature, filtration washing to neutrality, dry modified corn starch;
(2)MTES and deionized water are pressed into 1:3 mass ratio is stirred at room temperature after mixing and is warming up to 80-
100 DEG C, methenamine ultrasonic disperse 5-7 hours are added, be cooled to 45-55 DEG C of addition reaction of phytic acid 1-2 hour, obtain modified plant
Acid;
(3)By step(1)Obtained modified corn starch grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Temperature to 70-80 DEG C adds natural lemon essential oil reaction 4-6 hours, cooling;
(4)By step(3)Material is put in reactor, adds neopelex and other residual components to stir and evenly mix,
1L is added water to, is stirred 20-60 minutes in 40-50 DEG C, discharging.
Obtained copper antioxidant of the invention has following technical parameter:
(1)Resistance to neutral salt spray corrosion test:Through the brass of antioxidant of the present invention process, its anti-tarnishing ability is significantly improved, 8h
Afterwards sample remains to keep the primary colors of alloy not have Staining, and after 12h, specimen surface remains to keep the primary colors of alloy, only on a small quantity
Staining;
(2)The corrosion resistant time of the sample drop of resistance to nitric acid reaches most when sample is put into into Passivation Treatment in product of the present invention 60 seconds
Big value 13 seconds.
Claims (2)
1. it is a kind of addition bamboo vinegar water base brass antioxidant, it is characterised in that every liter of antioxidant is by following weight portion
Raw material is made:50wt.% phytic acid 10-12,30wt.% hydrogen peroxide 20-22, bamboo vinegar 13-15, polyethylene glycol 10-12, lanthanum nitrate 4-
6th, cornstarch 3-5, Alumina gel 2-4, methenamine 3-4, natural lemon essential oil 0.1-0.2, neopelex 1.2-
1.4th, MTES 2.1-2.4, appropriate deionized water.
2. the preparation method of the water base brass antioxidant of a kind of addition bamboo vinegar according to claim 1, its feature exists
In comprising the following steps:
(1)Cornstarch is mixed in deionized water the suspension for being configured to that mass percent concentration is 5-10%, 40- is put into
In 60 DEG C of water-baths, Alumina gel ultrasonic wave dispersion grinding 6-12 hours are added, add bamboo vinegar ultrasound wave irradiation reaction 2-8 hours, it is cold
But to room temperature, filtration washing to neutrality, dry modified corn starch;
(2)MTES and deionized water are pressed into 1:3 mass ratio is stirred at room temperature after mixing and is warming up to 80-
100 DEG C, methenamine ultrasonic disperse 5-7 hours are added, be cooled to 45-55 DEG C of addition reaction of phytic acid 1-2 hour, obtain modified plant
Acid;
(3)By step(1)Obtained modified corn starch grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Temperature to 70-80 DEG C adds natural lemon essential oil reaction 4-6 hours, cooling;
(4)By step(3)Material is put in reactor, adds neopelex and other residual components to stir and evenly mix,
1L is added water to, is stirred 20-60 minutes in 40-50 DEG C, discharging.