CN106756923A - A kind of water base brass antioxidant of uvioresistant for adding BTA and preparation method thereof - Google Patents
A kind of water base brass antioxidant of uvioresistant for adding BTA and preparation method thereof Download PDFInfo
- Publication number
- CN106756923A CN106756923A CN201611157494.XA CN201611157494A CN106756923A CN 106756923 A CN106756923 A CN 106756923A CN 201611157494 A CN201611157494 A CN 201611157494A CN 106756923 A CN106756923 A CN 106756923A
- Authority
- CN
- China
- Prior art keywords
- bta
- antioxidant
- phytic acid
- water
- stone powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water base brass antioxidant of uvioresistant for adding BTA, every liter of antioxidant is made from the following raw materials in parts by weight:50wt.% phytic acid 14 16, 30wt.% hydrogen peroxide 27 29, polyethylene glycol 12 15, triethanolamine 46, aluminium dihydrogen phosphate 35, medical stone powder 24, BTA 1.8 1.9, Tissuemat E 23, ginger juice 8 10, ethyl triethoxysilane 2.5 2.7, appropriate deionized water, the present invention is with phytic acid, hydrogen peroxide is main component, by phytic acid carry out it is silane coupler modified after, compatibility is through the modified medical stone powder of BTA and other compositions again, obtained antioxidant can be directly dissolved in water, it is easy to operate, it is not necessary to special installation, product is coated in brass surfaces adhesive force good, it is long with the good antirust coat of the surface binding energy of the copper more continuous densification anti-corrosion time, ultra-violet radiation resisting Anti- tarnishing ability is excellent.
Description
Technical field
The present invention relates to metal oxidation resistance technical field, more particularly to a kind of water base Huang of uvioresistant for adding BTA
Copper antioxidant and preparation method thereof.
Background technology
The alloy that brass is made up of copper and zinc, both with excellent conductive, thermal conductivity and easily processed into type excellent
Point, and with enough mechanical strengths, hardness and chemical resistance, be commonly used for manufacture valve, water pipe, air-conditioning internal-external machine and connect
Adapter and radiator etc..But run into acid, alkaline corrosion medium or in higher temperatures and high humidity environment be still susceptible to oxygen
Change corrosion and change colour, have a strong impact on outward appearance and use value while also bringing bad influence to secondary operation.It is domestic at present
The outer handling process to copper and its anti-oxidant discoloration of alloy surface mainly has:It is inorganic passivation technique for filming, organic inhibition technology, dilute
Native addition method, self-assembling technique and resinous coat technology etc., wherein most economical, easy method is passivated in brass surfaces
Treatment.Most ripe method is to use bichromate Passivation Treatment, but the sexavalence that the method is remained in process of production and in waste liquid
Chromium is noxious material, and many countries have prohibitted the use of bichromate Passivation Treatment, therefore, document《Brass surfaces richness phytic acid is blunt
Change technical study》With phytic acid, hydrogen peroxide, polyethylene glycol etc. for passivating solution prepared by primary raw material has for brass surfaces antirust
Important realistic meaning.
Treatment is passivated to cold rolling HAl72-2.5-1 brass strips using passivating solution in document, is as a result shown, rich phytic acid
The optimum process condition of passivating film is:Passivation temperature scope is 35~40 DEG C, and pH value is 2.5, and passivation time is 60s;SEM is microcosmic
Pattern shows that film surface is smooth, compact structure;Zero-G test result shows can be to alloy material using rich phytic acid Passivation Treatment
Play a very good protection;Bichromate is used using the sample ratio that rich phytic acid is processed by the saline fog method experiment display of 12h
The sample for the treatment of is free of chromium in having more preferable anti-tarnishing ability and rich phytic acid passivating solution, and pollution of chromium will not be produced in waste liquid.
But the phytic acid film in document, under the heavier environment of humidity, because damp moisture resistance is not good, storage time is short, coating
When brass surfaces carry out secondary operation, resistance to elevated temperatures is limited, in welding process, it is impossible to keep for a long time and multiple
High temperature impact;Secondly in document also there is short anti oxidation time, environmentally friendly bad adaptability, unitary function, heat surely in obtained passivator
The problems such as qualitative difference, weatherability difference and sun-proof ultraviolet radiation preventing difference, thus limit the lifting of overall performance and apply model
Enclose, it is necessary to improve existing production technology and formula, prepare the brass table with the function such as anti-corrosion, anti-oxidant, wear-resisting, sun-proof
Face treatment antioxidant.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of uvioresistant water of addition BTA
Base brass antioxidant and preparation method thereof.
The present invention is achieved by the following technical solutions:
It is a kind of add BTA the water base brass antioxidant of uvioresistant, every liter of antioxidant by following weight portion raw material
It is made:50wt.% phytic acid 14-16,30wt.% hydrogen peroxide 27-29, polyethylene glycol 12-15, triethanolamine 4-6, aluminium dihydrogen phosphate 3-
5th, medical stone powder 2-4, BTA 1.8-1.9, Tissuemat E 2-3, ginger juice 8-10, ethyl triethoxysilane 2.5-2.7,
Appropriate deionized water.
A kind of preparation method of the water base brass antioxidant of uvioresistant of described addition BTA, including following step
Suddenly:
(1)Medical stone powder is mixed the suspension for being configured to that mass percent concentration is 5-10% in deionized water, 40- is put into
In 60 DEG C of water-baths, add BTA ultrasonic disperse to grind 6-12 hours, add ginger juice ultrasound wave irradiation to react 2-8 hours, it is cold
But to room temperature, filtration washing to neutrality, the dry medical stone powder that must be modified;
(2)Ethyl triethoxysilane and deionized water are pressed 1:3 mass ratio is warming up to 80- after mixing is stirred at room temperature
100 DEG C, add triethanolamine ultrasonic disperse 5-7 hours, be cooled to 45-55 DEG C and add reaction of phytic acid 1-2 hours, obtain modified plant
Acid;
(3)By step(1)Obtained modified medical stone powder grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Temperature to 70-80 DEG C of addition Tissuemat E grinds 4-6 hours, cooling;
(4)By step(3)Material is put into reactor, adds 30wt.% hydrogen peroxide and other residual components to stir and evenly mix, and is added water
To 1L, stirred 20-60 minutes in 40-50 DEG C, discharging.
It is an advantage of the invention that:The present invention with phytic acid, hydrogen peroxide as main component, due to there is 24 oxygen originals in phytate molecule
Son, 12 hydroxyls and 6 are phosphate-based, and these atoms or group can form complex compound with metallic atom and metal ion, will plant
Acid carry out it is silane coupler modified after, on the one hand can be anti-by hydrogen bond or dehydration between unreacted phosphorus hydroxyl in passivating process
Should, connection forms spatial networks phytic acid (salt) passivating film of high crosslink density, on the other hand can with silane hydrolyzate after generate-
Si-OH- reaction generation-P-O-Si- keys, can be attached to one layer of metal surface formation colourless with the chelate of metal generation stabilization
Homogeneous, the non-microcracked protective film of transparent, surfacing, thickness densification effectively prevents corrosive medium from penetrating into metal surface,
So as to slow down corrosion of metal, medical stone powder is added in raw material through BTA is modified, improves it in water
Viscosity, then compatibility other antioxidants obtained in effective auxiliary agent can be directly dissolved in water, easy to operate, be not necessary to special installation, will
It is good that product is coated in brass surfaces adhesive force, long, anti-with the good antirust coat of the surface binding energy of the copper more continuous densification anti-corrosion time
Ultraviolet radiation Anti- tarnishing ability is excellent.
Specific embodiment
A kind of water base brass antioxidant of uvioresistant for adding BTA, every liter of antioxidant is by following weight portion
Raw material is made:50wt.% phytic acid 14,30wt.% hydrogen peroxide 27, polyethylene glycol 12, triethanolamine 4, aluminium dihydrogen phosphate 3, medical stone
Powder 2, BTA 1.8, Tissuemat E 2, ginger juice 8, ethyl triethoxysilane 2.5, appropriate deionized water.
A kind of preparation method of the water base brass antioxidant of uvioresistant of described addition BTA, including following step
Suddenly:
(1)Medical stone powder is mixed the suspension for being configured to that mass percent concentration is 5-10% in deionized water, 40- is put into
In 60 DEG C of water-baths, add BTA ultrasonic disperse to grind 6-12 hours, add ginger juice ultrasound wave irradiation to react 2-8 hours, it is cold
But to room temperature, filtration washing to neutrality, the dry medical stone powder that must be modified;
(2)Ethyl triethoxysilane and deionized water are pressed 1:3 mass ratio is warming up to 80- after mixing is stirred at room temperature
100 DEG C, add triethanolamine ultrasonic disperse 5-7 hours, be cooled to 45-55 DEG C and add reaction of phytic acid 1-2 hours, obtain modified plant
Acid;
(3)By step(1)Obtained modified medical stone powder grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Temperature to 70-80 DEG C of addition Tissuemat E grinds 4-6 hours, cooling;
(4)By step(3)Material is put into reactor, adds 30wt.% hydrogen peroxide and other residual components to stir and evenly mix, and is added water
To 1L, stirred 20-60 minutes in 40-50 DEG C, discharging.
There is following technical parameter using copper antioxidant obtained in the present invention:
(1)Resistance to neutral salt spray corrosion test:By the brass of antioxidant of the present invention treatment, its anti-tarnishing ability is significantly improved, and 8
After h sample remain to keep alloy primary colors there is no Staining, after 12 h, specimen surface remain to keep alloy primary colors, it is only few
The Staining of amount;
(2)The corrosion resistant time of the sample drop of resistance to nitric acid reaches most when sample is put into Passivation Treatment in product of the present invention 60 seconds
Big value 13 seconds.
Claims (2)
1. it is a kind of add BTA the water base brass antioxidant of uvioresistant, it is characterised in that every liter of antioxidant is under
The raw material of row weight portion is made:50wt.% phytic acid 14-16,30wt.% hydrogen peroxide 27-29, polyethylene glycol 12-15, triethanolamine 4-
6th, aluminium dihydrogen phosphate 3-5, medical stone powder 2-4, BTA 1.8-1.9, Tissuemat E 2-3, ginger juice 8-10, the ethoxy of ethyl three
Base silane 2.5-2.7, appropriate deionized water.
2. it is according to claim 1 it is a kind of add BTA the water base brass antioxidant of uvioresistant making side
Method, it is characterised in that comprise the following steps:
(1)Medical stone powder is mixed the suspension for being configured to that mass percent concentration is 5-10% in deionized water, 40- is put into
In 60 DEG C of water-baths, add BTA ultrasonic disperse to grind 6-12 hours, add ginger juice ultrasound wave irradiation to react 2-8 hours, it is cold
But to room temperature, filtration washing to neutrality, the dry medical stone powder that must be modified;
(2)Ethyl triethoxysilane and deionized water are pressed 1:3 mass ratio is warming up to 80- after mixing is stirred at room temperature
100 DEG C, add triethanolamine ultrasonic disperse 5-7 hours, be cooled to 45-55 DEG C and add reaction of phytic acid 1-2 hours, obtain modified plant
Acid;
(3)By step(1)Obtained modified medical stone powder grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Temperature to 70-80 DEG C of addition Tissuemat E grinds 4-6 hours, cooling;
(4)By step(3)Material is put into reactor, adds 30wt.% hydrogen peroxide and other residual components to stir and evenly mix, and is added water
To 1L, stirred 20-60 minutes in 40-50 DEG C, discharging.