CN109135466A - A kind of aqueous derusting finishing coat - Google Patents
A kind of aqueous derusting finishing coat Download PDFInfo
- Publication number
- CN109135466A CN109135466A CN201810791525.XA CN201810791525A CN109135466A CN 109135466 A CN109135466 A CN 109135466A CN 201810791525 A CN201810791525 A CN 201810791525A CN 109135466 A CN109135466 A CN 109135466A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- rust
- finishing coat
- waterborne anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of environmental protection paint, specially a kind of waterborne anti-rust finishing coat, the raw material including following parts by weight: 1~5 part of cellulose, 1~5 part of pH adjusting agent, 1~5 part of wetting agent, 2~8 parts of dispersing agent, 15~25 parts of antifreezing agent, 1~5 part of defoaming agent, 90~110 parts of barium sulfate, 90~110 parts of ferrotitanium powder, 90~110 parts of iron oxide red, 20~50 parts of trbasic zinc phosphate, 2~5 parts of rust remover, 10~30 parts of coalescing agent, 1~5 part of preservative, 150~200 parts of water, 400~500 parts of aqueous acrylic emulsion.Waterborne anti-rust topcoat paint film layer of the present invention is securely fine and close, and adhesive force is extremely strong, and antirust and derusting effect are good, and the substance that containing benezene, formaldehyde etc. are not harmful to the human body, and non-volatility gas generates, and is conducive to promote the use of.
Description
Technical field
The present invention relates to technical field of environmental protection paint, and in particular to a kind of aqueous derusting finishing coat.
Background technique
Finishing coat is the final coating of coating, has decoration and defencive function, is one finally smeared in construction wall finishing
Layer, the overall effect showed after finishing is embodied by this layer.Therefore there is higher requirement to material therefor,
Not only there are good coloration and brightness, more require good anti-pollution, ageing-resistant, moisture-proof, mildew resistance is good, will also be whether there is or not
Fire hazard, easy for construction, dried coating film are fast, protect the features such as light protects good color, good permeability, but also need it is environmentally protective, it is right
Human body and environment nonhazardous, however most of coating products in order to reach various purposes all contain part irritation currently on the market
Chemical addition agent, can affect to human body.
In addition, metal material surface is easy the invasion by corrosive substances various in atmosphere and causes to get rusty, currently used for
Metal rust preventing is various organic solvent oiliness finishing coats mostly, organic molten due to using although having certain antirust function
Agent, and organic solvent is since its is inflammable, toxic, volatile, pollution environment, at the same exist again when transport and construction it is dangerous etc. because
Element causes the use of such organic solvent oiliness finishing coat to be restricted, in addition, finishing coat on the market only has single antirust at present
Function, the effect not derusted, thus must first remove the rusty scale of metal surface before coating, be such as surface-treated it is bad, will be big
The big attachment for influencing film and substrate, is caused the phenomenon that falling off, and cannot remove in time if generating iron rust in use
It goes, so that service life and usage experience are influenced, therefore, the present invention is directed to research and develop a kind of aqueous derusting finishing coat of environmental protection, with more
Meet industry needs well.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of safety and environmental protection, can effectively antirust, derusting,
Can be widely used in the new and old metal protections such as house ornamentation, public environment, iron structure, mechanical equipment, municipal maintenance, super expressway and
The aqueous derusting finishing coat of decoration.
A kind of waterborne anti-rust finishing coat, the raw material including following parts by weight:
1~5 part of cellulose
1~5 part of pH adjusting agent
1~5 part of wetting agent
2~8 parts of dispersing agent
15~25 parts of antifreezing agent
1~5 part of defoaming agent
90~110 parts of barium sulfate
90~110 parts of ferrotitanium powder
90~110 parts of iron oxide red
20~50 parts of trbasic zinc phosphate
2~6 parts of rust remover
10~30 parts of coalescing agent
1~5 part of preservative
150~200 parts of water
400~500 parts of aqueous acrylic emulsion.
It is further preferred that the waterborne anti-rust finishing coat includes the raw material of following parts by weight:
1~2 part of cellulose
1~2 part of pH adjusting agent
2~3 parts of wetting agent
4~5 parts of dispersing agent
18~20 parts of antifreezing agent
2~3 parts of defoaming agent
95~100 parts of barium sulfate
95~100 parts of ferrotitanium powder
95~100 parts of iron oxide red
35~45 parts of trbasic zinc phosphate
3~4 parts of rust remover
20~25 parts of coalescing agent
2~3 parts of preservative
180~190 parts of water
420~450 parts of aqueous acrylic emulsion.
In the present invention, the cellulose is HEC30000 cellulose, HBR30000 cellulose, one in hydroxyethyl cellulose
Kind.
In the present invention, the pH adjusting agent is ammonium hydroxide or AMP95 multifunctional assistant.
In the present invention, the wetting agent is wetting agent FN211 or wetting agent PE-100 or wetting agent X-405.
In the present invention, the dispersing agent is sodium salt dispersing agent.
In the present invention, the antifreezing agent is ethylene glycol or propylene glycol.
In the present invention, the defoaming agent includes foamicide NXZ and foam inhibitor A10, and the mass ratio of foamicide and foam inhibitor is
1:1。
In the present invention, the rust remover is rust remover FA60 or rust remover DL-800.
The invention also includes the preparation method of waterborne anti-rust finishing coat, include the following steps: by water, cellulose, pH adjusting agent,
Wetting agent, dispersing agent, antifreezing agent, defoaming agent, ferrotitanium powder, iron oxide red, trbasic zinc phosphate, rust remover, coalescing agent, preservative are in order
After being added into taper sand mill mixed grinding to the fineness of 40 μ, after adding aqueous acrylic emulsion, stirring evenly, adjust viscosity
Obtain product.
The invention also includes the application methods of waterborne anti-rust finishing coat comprising following steps:
1) base material treatment: the insecure foreign matters such as the floating rust in metal surface are handled with tools such as water knife, steel brush, powered brush and are done
Only, there is oil removal treatment at greasy dirt, apply priming after the excessively smooth old lacquer painting feather plucking processing of firm attachment, it is 3~5 hours dry
It is spare；
2) coating: can direct coating can be mass parts 10~20% to be added before coating if viscosity slightly higher influence construction
Water stir evenly to adjust viscosity；Thin brush 1~2 time when coating, base, coating mode is for brushing or roller coating or without gas blowout
One of apply；15~20min dry tack free and protective film is formed after coating, subsequent painting work is carried out after 12h.
Waterborne anti-rust finishing coat of the present invention when in use, execution conditions are as follows: 10 DEG C of temperature or more, humidity 85% with
Under, rain and snow weather cannot construct, and according to corrosion degree coating 2~3 times, construct interval time 12h or more.Coating 2~3 times, film
Layer is uniformly, fine and close, and bright, antirust and derusting effect are more preferable.
Derusting principle of the invention are as follows: waterborne anti-rust finishing coat of the present invention removes rust joint by physical antirust and chemically
Conjunction plays a role, and wherein trbasic zinc phosphate is the relatively stable pigment of a kind of chemical property itself, leans on the physical property of itself, quality
Hard, particle is subtle, and excellent fillibility improves the consistency of paint film, and with preferred aqueous acrylic emulsion and sulphur
Sour barium, ferrotitanium powder, iron oxide red combine to the greatest extent, form a kind of faintly acid polymer composite, can make on metal substrates
Rust transformation be black organoiron compound, and then in one layer of metal substrates Surface Creation by chemical bond and physical bond
Complexes membrane, therefore film layer is securely fine and close, adhesive force is extremely strong, and so that metal substrates and dielectric separates is no longer influenced by erosion, and it is original
Iron rust or the iron rust that bears in the process then pass through addition chemically rust remover inhibited or removed.
The utility model has the advantages that the present invention has the advantage that compared with traditional finishing coat are as follows:
1) waterborne anti-rust topcoat paint film layer of the present invention is securely fine and close, and adhesive force is extremely strong, and antirust and derusting effect are good, and
Better effect is used in combination in the priming paint that derusts；
2) waterborne anti-rust finishing coat of the present invention is a kind of unique acidic group formula, can infiltrate into rust rapidly and fully
The place of erosion；
3) waterborne anti-rust finishing coat of the present invention is the substance that aqueous not containing benezene, formaldehyde etc. are harmful to the human body, and nothing is waved
Hair property gas generates, and is conducive to environmental protection；
4) waterborne anti-rust finishing coat of the present invention is easy to use, and work efficiency is high, overall cost is low, is suitble to promote the use of.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
Waterborne anti-rust finishing coat of the invention includes the following raw material:
Cellulose 2g, pH adjusting agent 1.5g, wetting agent 3g, dispersing agent 5g, antifreezing agent 20g, defoaming agent 3g, barium sulfate
100g, ferrotitanium powder 100g, iron oxide red 100g, trbasic zinc phosphate 50g, antirust agent 3.5g, coalescing agent 25g, preservative 3g, water 190g,
Aqueous acrylic emulsion 420g.
Wherein cellulose is HEC30000 cellulose, and pH adjusting agent is ammonium hydroxide, and wetting agent is wetting agent FN211, dispersing agent
For sodium salt dispersing agent, antifreezing agent is ethylene glycol, and rust remover is rust remover FA60.
Embodiment 2
Cellulose 2g, pH adjusting agent 1.5g, wetting agent 3g, dispersing agent 5g, antifreezing agent 20g, defoaming agent 3g, barium sulfate
100g, ferrotitanium powder 100g, iron oxide red 100g, trbasic zinc phosphate 50g, antirust agent 3.5g, coalescing agent 25g, preservative 3g, water 190g,
Aqueous acrylic emulsion 420g.
Wherein cellulose is hydroxyethyl cellulose, and pH adjusting agent is AMP95 multifunctional assistant, and wetting agent is wetting agent X-
405, dispersing agent is sodium salt dispersing agent, and antifreezing agent is propylene glycol, and rust remover is rust remover FA60.
Embodiment 3
Cellulose 1g, pH adjusting agent 1g, wetting agent 2g, dispersing agent 4g, antifreezing agent 18g, defoaming agent 2g, barium sulfate 95g, iron
Titanium valve 95g, iron oxide red 95g, trbasic zinc phosphate 35g, rust remover 3g, coalescing agent 20g, preservative 2g, water 180g, aqueous acrylamide yogurt
Liquid 420g.
Wherein cellulose is HEC30000 cellulose, and pH adjusting agent is ammonium hydroxide, and wetting agent is wetting agent FN211, dispersing agent
For sodium salt dispersing agent, antifreezing agent is ethylene glycol, and rust remover is rust remover FA60.
Embodiment 4
Cellulose 2g, pH adjusting agent 2g, wetting agent 3g, dispersing agent 5g, antifreezing agent 20g, defoaming agent 3g, barium sulfate 100g,
Ferrotitanium powder 100g, iron oxide red 100g, trbasic zinc phosphate 45g, rust remover 4g, coalescing agent 25g, preservative 3g, water 190g, aqueous acrylamide
Yogurt liquid 450g.
Wherein cellulose is HEC30000 cellulose, and pH adjusting agent is ammonium hydroxide, and wetting agent is wetting agent FN211, dispersing agent
For sodium salt dispersing agent, antifreezing agent is ethylene glycol, and rust remover is rust remover FA60.
Embodiment 5
Cellulose 5g, pH adjusting agent 5g, wetting agent 5g, dispersing agent 8g, antifreezing agent 25g, defoaming agent 5g, barium sulfate 110g,
Ferrotitanium powder 110g, iron oxide red 110g, trbasic zinc phosphate 50g, rust remover 6g, coalescing agent 30g, preservative 5g, water 200g, aqueous acrylamide
Yogurt liquid 500g.
Wherein cellulose is HBR30000 cellulose, and pH adjusting agent is AMP95 multifunctional assistant, and wetting agent is wetting agent
PE-100, dispersing agent are sodium salt dispersing agent, and antifreezing agent is propylene glycol, and rust remover is rust remover DL-800.
Embodiment 6
Cellulose 1g, pH adjusting agent 1g, wetting agent 1g, dispersing agent 2g, antifreezing agent 15g, defoaming agent 1g, barium sulfate 90g, iron
Titanium valve 90g, iron oxide red 90g, trbasic zinc phosphate 20g, rust remover 2g, coalescing agent 10g, preservative 1g, water 150g, aqueous acrylamide yogurt
Liquid 400g.
Wherein cellulose is hydroxyethyl cellulose, and pH adjusting agent is AMP95 multifunctional assistant, and wetting agent is wetting agent X-
405, dispersing agent is sodium salt dispersing agent, and antifreezing agent is propylene glycol, and rust remover is rust remover FA60.
Waterborne anti-rust finishing coat in Examples 1 to 6 the preparation method is as follows: by water, cellulose, pH adjusting agent, wetting agent,
Dispersing agent, antifreezing agent, defoaming agent, ferrotitanium powder, iron oxide red, trbasic zinc phosphate, rust remover, coalescing agent, preservative are added into order
After taper sand mill mixed grinding to the fineness of 40 μ, addition aqueous acrylic emulsion is stirred evenly, is obtained after water use regulation viscosity
To product.
The application method of waterborne anti-rust finishing coat in Examples 1 to 6 includes the following steps:
1) base material treatment: the insecure foreign matters such as the floating rust in metal surface are handled with tools such as water knife, steel brush, powered brush and are done
Only, there are oil removal treatment at greasy dirt, the excessively smooth old lacquer painting feather plucking processing of firm attachment；
2) coating: can direct coating can be mass parts 10~20% to be added before coating if viscosity slightly higher influence construction
Water stir evenly to adjust viscosity；Thin brush 1~2 time when coating, coating mode be one in brushing or roller coating or airless spraying
Kind；15~20min dry tack free and protective film is formed after coating, subsequent painting work is carried out after 12h.
Waterborne anti-rust finishing coat of the present invention when in use, execution conditions are as follows: 10 DEG C of temperature or more, humidity 85% with
Under, rain and snow weather cannot construct, and according to corrosion degree coating 2~3 times, construct interval time 12h or more.
Waterborne anti-rust finishing coat of the invention the preparation method is as follows: by water, cellulose, pH adjusting agent, wetting agent, dispersion
Agent, antifreezing agent, defoaming agent, ferrotitanium powder, iron oxide red, trbasic zinc phosphate, rust remover, coalescing agent, preservative are added into taper in order
After sand mill mixed grinding to the fineness of 40 μ, addition aqueous acrylic emulsion, stir evenly, adjust viscosity after obtain product.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (10)
1. a kind of waterborne anti-rust finishing coat, which is characterized in that the raw material including following parts by weight:
1~5 part of cellulose
1~5 part of pH adjusting agent
1~5 part of wetting agent
2~8 parts of dispersing agent
15~25 parts of antifreezing agent
1~5 part of defoaming agent
90~110 parts of barium sulfate
90~110 parts of ferrotitanium powder
90~110 parts of iron oxide red
20~50 parts of trbasic zinc phosphate
2~6 parts of rust remover
10~30 parts of coalescing agent
1~5 part of preservative
150~200 parts of water
400~500 parts of aqueous acrylic emulsion.
2. a kind of waterborne anti-rust finishing coat according to claim 1, which is characterized in that the raw material including following parts by weight:
1~2 part of cellulose
1~2 part of pH adjusting agent
2~3 parts of wetting agent
4~5 parts of dispersing agent
18~20 parts of antifreezing agent
2~3 parts of defoaming agent
95~100 parts of barium sulfate
95~100 parts of ferrotitanium powder
95~100 parts of iron oxide red
35~45 parts of trbasic zinc phosphate
3~4 parts of rust remover
20~25 parts of coalescing agent
2~3 parts of preservative
180~190 parts of water
420~450 parts of aqueous acrylic emulsion.
3. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the cellulose is HEC30000
One of cellulose, HBR30000 cellulose, hydroxyethyl cellulose.
4. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the pH adjusting agent be ammonium hydroxide or
AMP95 multifunctional assistant.
5. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the wetting agent is wetting agent
FN211 or wetting agent PE-100 or wetting agent X-405.
6. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the dispersing agent is sodium salt dispersion
Agent.
7. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the antifreezing agent be ethylene glycol or
Propylene glycol.
8. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the defoaming agent includes foamicide
The mass ratio of NXZ and foam inhibitor A10, foamicide and foam inhibitor is 1:1.
9. a kind of waterborne anti-rust finishing coat according to claim 1 or 2, which is characterized in that the rust remover is rust remover
FA60 or rust remover DL-800.
10. a kind of application method of waterborne anti-rust finishing coat, which is characterized in that be based on waterborne anti-rust face of any of claims 1 or 2
Paint, includes the following steps:
1) base material treatment: the insecure foreign matter such as floating rust in processing metal surface simultaneously paints priming paint；
2) finishing coat coating: the water that mass parts 10~20% are added before coating is stirred evenly to adjust viscosity；Thin brush 1~2 when coating
Time, coating mode is brushing or roller coating or airless spraying, and thin brush time interval is greater than 12h.