CN108893012A - A kind of aqueous derusting priming paint - Google Patents

A kind of aqueous derusting priming paint Download PDF

Info

Publication number
CN108893012A
CN108893012A CN201810792276.6A CN201810792276A CN108893012A CN 108893012 A CN108893012 A CN 108893012A CN 201810792276 A CN201810792276 A CN 201810792276A CN 108893012 A CN108893012 A CN 108893012A
Authority
CN
China
Prior art keywords
parts
agent
water
cellulose
primer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810792276.6A
Other languages
Chinese (zh)
Inventor
毛小文
苏友
喻琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan's Manufacturing Ltd By Share Ltd Lacquer
Original Assignee
Hunan's Manufacturing Ltd By Share Ltd Lacquer
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hunan's Manufacturing Ltd By Share Ltd Lacquer filed Critical Hunan's Manufacturing Ltd By Share Ltd Lacquer
Priority to CN201810792276.6A priority Critical patent/CN108893012A/en
Publication of CN108893012A publication Critical patent/CN108893012A/en
Pending legal-status Critical Current

Abstract

The invention belongs to technical field of environmental protection paint, specially a kind of water-thinned antirust primer, the raw material including following parts by weight:1~5 part of cellulose, 1~5 part of pH adjusting agent, 1~5 part of wetting agent, 2~8 parts of dispersing agent, 15~25 parts of antifreezing agent, 2~8 parts of defoaming agent, 90~110 parts of ferrotitanium powder, 90~110 parts of iron oxide red, 40~60 parts of trbasic zinc phosphate, 1~5 part of rust remover, 20~40 parts of coalescing agent, 1~5 part of preservative, 150~200 parts of water, 450~550 parts of aqueous acrylic emulsion.Water-thinned antirust primer film layer of the present invention is securely fine and close, and adhesive force is extremely strong, and antirust and derusting effect are good, and the substance that containing benezene, formaldehyde etc. are not harmful to the human body, and non-volatility gas generates, and is conducive to promote the use of.

Description

A kind of aqueous derusting priming paint
Technical field
The present invention relates to technical field of environmental protection paint, and in particular to a kind of aqueous derusting priming paint.
Background technique
Priming paint is the first layer of paint system, one or more layers wash coats is brushed before brushing finish paint can not only save Decoration cost is saved, from the point of view of long-range and decorative effect, priming is applied and gets twice the result with half the effort, and the good adhesive force of priming paint makes metope more Cunning is flattened out, finishing coat is enabled to be easier to brush, guarantees the uniform pickup of finishing coat while increasing the richness of finishing coat, to make paint system Optimum efficiency is played, nowadays as the requirement to building coating is higher and higher, the requirement to priming paint is also more and more, not only needs Want wear-and corrosion-resistant moisture-proof, but also need it is environmentally protective, it is harmless to the human body, however most of coating products are currently on the market Reaching various purposes all contains the irritating chemical addition agent in part, can affect to human body.
In addition, metal material surface is easy the invasion by corrosive substances various in atmosphere and causes to get rusty, currently used for Metal rust preventing is various organic solvent oil primers mostly, organic molten due to using although having certain antirust function Agent, and organic solvent is since its is inflammable, toxic, volatile, pollution environment, at the same exist again when transport and construction it is dangerous etc. because Element causes the use of such organic solvent oil primer to be restricted, in addition, priming paint on the market only has single antirust at present Function, the effect not derusted, thus must first remove the rusty scale of metal surface before coating, be such as surface-treated it is bad, will be big The big attachment for influencing film and substrate, causes the phenomenon that falling off.Therefore, the present invention is directed to research and develop a kind of aqueous derusting bottom of environmental protection Paint, preferably to meet industry needs.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of safety and environmental protection, can effectively antirust, derusting, Can be widely used in the new and old metal protections such as house ornamentation, public environment, iron structure, mechanical equipment, municipal maintenance, super expressway and The aqueous derusting priming paint of decoration.
A kind of water-thinned antirust primer, the raw material including following parts by weight:
1~5 part of cellulose
1~5 part of pH adjusting agent
1~5 part of wetting agent
2~8 parts of dispersing agent
15~25 parts of antifreezing agent
2~8 parts of defoaming agent
90~110 parts of ferrotitanium powder
90~110 parts of iron oxide red
40~60 parts of trbasic zinc phosphate
1~5 part of rust remover
20~40 parts of coalescing agent
1~5 part of preservative
150~200 parts of water
450~550 parts of aqueous acrylic emulsion
Preferably, which includes the raw material of following parts by weight:
1~2 part of cellulose
1~2 part of pH adjusting agent
1.5~3 parts of wetting agent
4~5 parts of dispersing agent
18~20 parts of antifreezing agent
4~5 parts of defoaming agent
95~100 parts of ferrotitanium powder
95~100 parts of iron oxide red
45~50 parts of trbasic zinc phosphate
2~3 parts of rust remover
25~30 parts of coalescing agent
2~3 parts of preservative
180~190 parts of water
490~500 parts of aqueous acrylic emulsion
Further, the cellulose is HEC30000 cellulose, HBR30000 cellulose, one in hydroxyethyl cellulose Kind.
Further, the pH adjusting agent is ammonium hydroxide or AMP95 multifunctional assistant.
Further, the wetting agent is wetting agent FN211 or wetting agent PE-100 or wetting agent X-405.
Further, the dispersing agent is sodium salt dispersing agent.
Further, the antifreezing agent is ethylene glycol or propylene glycol.
Further, the defoaming agent includes foamicide and foam inhibitor, and the mass ratio of foamicide and foam inhibitor is 1:1.
Further, the rust remover is rust remover FA60 or rust remover DL-800.
The invention also includes the preparation methods of water-thinned antirust primer, include the following steps:By water, cellulose, pH adjusting agent, Wetting agent, dispersing agent, antifreezing agent, defoaming agent, ferrotitanium powder, iron oxide red, trbasic zinc phosphate, rust remover, coalescing agent, preservative are in order After being added into taper sand mill mixed grinding to the fineness of 40 μ, after adding aqueous acrylic emulsion, stirring evenly, adjust viscosity Obtain product.
The invention also includes the application methods of water-thinned antirust primer comprising following steps:
1) base material treatment:The insecure foreign matters such as the floating rust in metal surface are handled with tools such as water knife, steel brush, powered brush and are done Only, there are oil removal treatment at greasy dirt, the excessively smooth old lacquer painting feather plucking processing of firm attachment;
2) coating:Can direct coating can be mass parts 10~20% to be added before coating if viscosity slightly higher influence construction Water stir evenly to adjust viscosity;Thin brush 1~2 time when coating, coating mode be one in brushing or roller coating or airless spraying Kind;15~20min dry tack free and protective film is formed after coating, subsequent painting work is carried out after 12h.
When in use, execution conditions are water-thinned antirust primer of the present invention:10 DEG C of temperature or more, humidity 85% with Under, rain and snow weather cannot construct, and according to corrosion degree coating 2~3 times, construct interval time 12H or more.Coating 2~3 times, film Layer is uniformly, fine and close, and bright, antirust and derusting effect are more preferable, can reach higher requirement.
Derusting principle of the invention is:Water-thinned antirust primer of the present invention removes rust joint by physical antirust and chemically Conjunction plays a role, and wherein trbasic zinc phosphate is the relatively stable pigment of a kind of chemical property itself, leans on the physical property of itself, quality Hard, particle is subtle, and excellent fillibility improves the consistency of paint film, and with preferred aqueous acrylic emulsion and iron Titanium valve, iron oxide red combine to the greatest extent, form a kind of faintly acid polymer composite, and the iron rust on metal substrates can be made to turn The organoiron compound of black is turned to, and then in one layer of the metal substrates Surface Creation compound by chemical bond and physical bond Film, therefore film layer is securely fine and close, adhesive force is extremely strong, and metal substrates and dielectric separates is made to be no longer influenced by erosion, and original iron rust Or the iron rust born in the process then pass through addition chemically rust remover inhibited or removed.
Beneficial effect:The present invention compared with traditional priming paint, have the advantage that for:
1) water-thinned antirust primer film layer of the present invention is securely fine and close, and adhesive force is extremely strong, and antirust and derusting effect are good.
2) water-thinned antirust primer of the present invention is a kind of unique acidic group formula, can infiltrate into rust rapidly and fully The place of erosion;
3) water-thinned antirust primer of the present invention is the substance that aqueous not containing benezene, formaldehyde etc. are harmful to the human body, and nothing is waved Hair property gas generates, and is conducive to environmental protection;
4) water-thinned antirust primer of the present invention is easy to use, and work efficiency is high, overall cost is low, is suitble to promote the use of.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below Specific embodiment is closed, the present invention is further explained.
Embodiment 1
Water-thinned antirust primer of the invention includes the following raw material:
Cellulose 2g, pH adjusting agent 2g, wetting agent 2g, dispersing agent 5g, antifreezing agent 20g, defoaming agent 5g, ferrotitanium powder 100g, Iron oxide red 100g, trbasic zinc phosphate 50g, rust remover 3g, coalescing agent 30g, preservative 3g, water 190g, aqueous acrylic emulsion 500g.
Wherein cellulose is HEC30000 cellulose, and pH adjusting agent is ammonium hydroxide, and wetting agent is wetting agent FN211, dispersing agent For sodium salt dispersing agent, antifreezing agent is ethylene glycol, and rust remover is rust remover FA60.
Embodiment 2
Cellulose 2g, pH adjusting agent 2g, wetting agent 2g, dispersing agent 5g, antifreezing agent 20g, defoaming agent 5g, ferrotitanium powder 100g, Iron oxide red 100g, trbasic zinc phosphate 50g, rust remover 3g, coalescing agent 30g, preservative 3g, water 190g, aqueous acrylic emulsion 500g.
Wherein cellulose is hydroxyethyl cellulose, and pH adjusting agent is AMP95 multifunctional assistant, and wetting agent is wetting agent X- 405, dispersing agent is sodium salt dispersing agent, and antifreezing agent is propylene glycol, and rust remover is rust remover FA60.
Embodiment 3
Cellulose 1g, pH adjusting agent 1g, wetting agent 1.5g, dispersing agent 4g, antifreezing agent 18g, defoaming agent 4g, ferrotitanium powder 95g, Iron oxide red 95g, trbasic zinc phosphate 45g, rust remover 2g, coalescing agent 25g, preservative 2g, water 180g, aqueous acrylic emulsion 490g.
Wherein cellulose is HEC30000 cellulose, and pH adjusting agent is ammonium hydroxide, and wetting agent is wetting agent FN211, dispersing agent For sodium salt dispersing agent, antifreezing agent is ethylene glycol, and rust remover is rust remover FA60.
Embodiment 4
Cellulose 2g, pH adjusting agent 2g, wetting agent 3g, dispersing agent 5g, antifreezing agent 20g, defoaming agent 5g, ferrotitanium powder 100g, Iron oxide red 100g, trbasic zinc phosphate 50g, rust remover 3g, coalescing agent 30g, preservative 3g, water 190g, aqueous acrylic emulsion 500g.
Wherein cellulose is HEC30000 cellulose, and pH adjusting agent is ammonium hydroxide, and wetting agent is wetting agent FN211, dispersing agent For sodium salt dispersing agent, antifreezing agent is ethylene glycol, and rust remover is rust remover FA60.
Embodiment 5
Cellulose 5g, pH adjusting agent 5g, wetting agent 5g, dispersing agent 6g, antifreezing agent 25g, defoaming agent 8g, ferrotitanium powder 110g, Iron oxide red 110g, trbasic zinc phosphate 60g, rust remover 5g, coalescing agent 40g, preservative 5g, water 200g, aqueous acrylic emulsion 550g.
Wherein cellulose is HBR30000 cellulose, and pH adjusting agent is AMP95 multifunctional assistant, and wetting agent is wetting agent PE-100, dispersing agent are sodium salt dispersing agent, and antifreezing agent is propylene glycol, and rust remover is rust remover DL-800.
Embodiment 6
Cellulose 1g, pH adjusting agent 1g, wetting agent 1g, dispersing agent 2g, antifreezing agent 15g, defoaming agent 2g, ferrotitanium powder 90g, iron Rouge and powder 90g, trbasic zinc phosphate 60g, rust remover 1g, coalescing agent 20g, preservative 1g, water 150g, aqueous acrylic emulsion 450g.
Wherein cellulose is hydroxyethyl cellulose, and pH adjusting agent is AMP95 multifunctional assistant, and wetting agent is wetting agent X- 405, dispersing agent is sodium salt dispersing agent, and antifreezing agent is propylene glycol, and rust remover is rust remover FA60.
The preparation method of water-thinned antirust primer in Examples 1 to 6 is as follows:By water, cellulose, pH adjusting agent, wetting agent, Dispersing agent, antifreezing agent, defoaming agent, ferrotitanium powder, iron oxide red, trbasic zinc phosphate, rust remover, coalescing agent, preservative are added into order After taper sand mill mixed grinding to the fineness of 40 μ, addition aqueous acrylic emulsion is stirred evenly, is obtained after water use regulation viscosity To product.
The application method of water-thinned antirust primer in Examples 1 to 6 includes the following steps:
1) base material treatment:The insecure foreign matters such as the floating rust in metal surface are handled with tools such as water knife, steel brush, powered brush and are done Only, there are oil removal treatment at greasy dirt, the excessively smooth old lacquer painting feather plucking processing of firm attachment;
2) coating:Can direct coating can be mass parts 10~20% to be added before coating if viscosity slightly higher influence construction Water stir evenly to adjust viscosity;Thin brush 1~2 time when coating, base, coating mode is for brushing or roller coating or without gas blowout One of apply;15~20min dry tack free and protective film is formed after coating, subsequent painting work is carried out after 12h.
When in use, execution conditions are water-thinned antirust primer in Examples 1 to 6:10 DEG C of temperature or more, humidity 85% Hereinafter, rain and snow weather cannot construct, according to corrosion degree coating 2~3 times, construct interval time 12H or more.Coating 2~3 times, Even film layer, fine and close, bright, antirust and derusting effect are more preferable, can reach higher requirement.
The inspection result of water-thinned antirust primer in Examples 1 to 6 is as follows:
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (10)

1. a kind of water-thinned antirust primer, which is characterized in that the raw material including following parts by weight:
1~5 part of cellulose
1~5 part of pH adjusting agent
1~5 part of wetting agent
2~8 parts of dispersing agent
15~25 parts of antifreezing agent
2~8 parts of defoaming agent
90~110 parts of ferrotitanium powder
90~110 parts of iron oxide red
40~60 parts of trbasic zinc phosphate
1~5 part of rust remover
20~40 parts of coalescing agent
1~5 part of preservative
150~200 parts of water
450~550 parts of aqueous acrylic emulsion.
2. a kind of water-thinned antirust primer according to claim 1, which is characterized in that the raw material including following parts by weight:
1~2 part of cellulose
1~2 part of pH adjusting agent
1.5~3 parts of wetting agent
4~5 parts of dispersing agent
18~20 parts of antifreezing agent
4~5 parts of defoaming agent
95~100 parts of ferrotitanium powder
95~100 parts of iron oxide red
45~50 parts of trbasic zinc phosphate
2~3 parts of rust remover
25~30 parts of coalescing agent
2~3 parts of preservative
180~190 parts of water
490~500 parts of aqueous acrylic emulsion.
3. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the cellulose is HEC30000 One of cellulose, HBR30000 cellulose, hydroxyethyl cellulose.
4. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the pH adjusting agent be ammonium hydroxide or AMP95 multifunctional assistant.
5. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the wetting agent is wetting agent FN211 or wetting agent PE-100 or wetting agent X-405.
6. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the dispersing agent is sodium salt dispersion Agent.
7. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the antifreezing agent be ethylene glycol or Propylene glycol.
8. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the defoaming agent includes foamicide And foam inhibitor, the mass ratio of foamicide and foam inhibitor are 1:1.
9. a kind of water-thinned antirust primer according to claim 1 or 2, which is characterized in that the rust remover is rust remover FA60 or rust remover DL-800.
10. a kind of application method of water-thinned antirust primer, which is characterized in that be based on waterborne anti-rust bottom of any of claims 1 or 2 Paint, includes the following steps:
1) base material treatment:Handle the insecure foreign matters such as the floating rust in metal surface;
2) primer painting:Can direct coating can be mass parts 10~20% to be added before coating if viscosity slightly higher influence construction Water stir evenly to adjust viscosity;Thin brush 1~2 time when coating, coating mode be one in brushing or roller coating or airless spraying Kind;Primer painting drying time is greater than 12h and carries out subsequent painting work again.
CN201810792276.6A 2018-07-18 2018-07-18 A kind of aqueous derusting priming paint Pending CN108893012A (en)