CN108753065A - A kind of aqueous steel structure paint - Google Patents
A kind of aqueous steel structure paint Download PDFInfo
- Publication number
- CN108753065A CN108753065A CN201810391049.2A CN201810391049A CN108753065A CN 108753065 A CN108753065 A CN 108753065A CN 201810391049 A CN201810391049 A CN 201810391049A CN 108753065 A CN108753065 A CN 108753065A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel structure
- aqueous
- aqueous steel
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed by the invention to belong to water-repellent paint technical field, specially a kind of aqueous steel structure paint, the aqueous steel structure enamel-cover includes following constituent：Water：10-20 parts；Nano aluminium oxide：2-3 parts；Aqueous alkide resin：5-10 parts；Acrylic emulsion：70-90 parts；Dispersant：0.4-0.6 parts；Corrosion inhibiter：0.6-0.8 parts；Coalescents：1-2 parts；Surfactant：0.3-0.5 parts；Rutile type titanium white：15-20 parts；Hydrophobic molecule is modified hydroxy acid sodium salt：0.5-0.7 parts；0.1-0.2 parts of anti-flash rusting agent；Color stuffing：20-30 parts；Fungusproof anti-corrosion agent：0.1-0.3 parts and thickener：0.1-0.2 parts, has shielded effect to visible light, storage stability is excellent, and service life is long, has good stain resistant, alkali resistance and salt fog resistance, its drying property, water resistance and gloss can be optimal, convenient for construction, adhesion property is good, and service life is long, and unharmful substance, it is environmentally protective.
Description
Technical field
The present invention relates to water-repellent paint technical field, specially a kind of aqueous steel structure paint.
Background technology
Outdoor steel structure material includes big machinery, bridge, communal facility etc..Traditional steel structure material is with coating
Solvent based product, volatile organic content are high, manufacture, construct, catch up in, film-forming during, given out into air
Volatile organic matter environmental pollution is serious, and increasingly strict with environmental regulation, coating industry has been increasingly towards without public affairs
Harmful, pollution-free, energy conservation and environmental protection, Gao Xiang economy direction develop.Water paint be a kind of low volatility, energy conservation and environmental protection, efficiently into
Row and the coating variety haveing excellent performance.But water-repellent paint currently on the market still uses the conducts such as organic reagent benzene, toluene mostly
Solvent and some toxic additives are added, and poor waterproof properties, stability is poor, and anti-corrosive properties and slow release are not satisfied by use
It needs.For this purpose, it is proposed that a kind of aqueous steel structure paint.
Invention content
The purpose of the present invention is to provide a kind of aqueous steel structure paints, to solve existing market mentioned above in the background art
On water-repellent paint still use organic reagent benzene, toluene etc. as solvent mostly and some toxic additives, and waterproof be added
Poor performance, stability is poor, and anti-corrosive properties and slow release are not satisfied by the problem of use needs.
To achieve the above object, the present invention provides the following technical solutions：A kind of aqueous steel structure paint, the aqueous steel structure enamel-cover include
Following constituent：
Water：10-20 parts；Nano aluminium oxide：2-3 parts；Aqueous alkide resin：5-10 parts；Acrylic emulsion：70-90 parts；Point
Powder：0.4-0.6 parts；Corrosion inhibiter：0.6-0.8 parts；Coalescents：1-2 parts；Surfactant：0.3-0.5 parts；Rutile-type
Titanium dioxide：15-20 parts；Hydrophobic molecule is modified hydroxy acid sodium salt：0.5-0.7 parts；0.1-0.2 parts of anti-flash rusting agent；Color stuffing：20-30
Part；Fungusproof anti-corrosion agent：0.1-0.3 parts and thickener：0.1-0.2 parts.
Preferably, the corrosion inhibiter is alkali metal sulfamate salt corrosion inhibiter.
Preferably, the coalescents are Lauryl Alcohol ester.
Preferably, the surfactant is dodecyl benzene sulfonate.
Preferably, the color stuffing iron clad is red, trbasic zinc phosphate, aluminium triphosphate, blanc fixe and talcum powder.
Compared with prior art, the beneficial effects of the invention are as follows：A kind of aqueous steel structure paint that the invention proposes, to visible light
Having shielded effect, storage stability is excellent, and service life is long, has good stain resistant, alkali resistance and salt fog resistance,
Its drying property, water resistance and gloss can be optimal, and convenient for construction, adhesion property is good, and service life is long, and without nuisance
Matter, it is environmentally protective.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
The every other embodiment that technical staff is obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution：A kind of aqueous steel structure paint, the aqueous steel structure enamel-cover include following constituent：
Water：10-20 parts；Nano aluminium oxide：2-3 parts；Aqueous alkide resin：5-10 parts；Acrylic emulsion：70-90 parts；Point
Powder：0.4-0.6 parts；Corrosion inhibiter：0.6-0.8 parts, the corrosion inhibiter is alkali metal sulfamate salt corrosion inhibiter；Coalescents：1-2
Part, the coalescents are Lauryl Alcohol ester；Surfactant：0.3-0.5 parts, the surfactant is detergent alkylate sulphur
Hydrochlorate；Rutile type titanium white：15-20 parts；Hydrophobic molecule is modified hydroxy acid sodium salt：0.5-0.7 parts；0.1-0.2 parts of anti-flash rusting agent；
Color stuffing：20-30 parts, the color stuffing iron clad is red, trbasic zinc phosphate, aluminium triphosphate, blanc fixe and talcum powder；Fungus-proof antisepsis
Agent：0.1-0.3 parts and thickener：0.1-0.2 parts.
Embodiment 1
By water：15 parts；Dispersant：0.5 part；Corrosion inhibiter：0.7 part；Surfactant：0.4 part；Acrylic emulsion：80 parts；
Hydrophobic molecule is modified hydroxy acid sodium salt：0.6 part and fungusproof anti-corrosion agent：0.2 part of mixing, stirs evenly, and mixing speed is 700 revs/min
Then nano aluminium oxide is added in clock：2.5 part；Rutile type titanium white：17.5 parts and color stuffing：It 25 parts, stirs evenly, stirs
Rate is 400 revs/min, and mixing time is 22.5 minutes, and after the completion of stirring, grinding, milling time is 65 minutes, is ground to thin
Degree control is at 30 microns hereinafter, being eventually adding aqueous alkide resin：7.5 part；Coalescents：1.5 part；0.15 part of anti-flash rusting agent and
Thickener：0.15 part, stirring at low speed is uniform, filters and packages.
Embodiment 2
By water：10 parts；Dispersant：0.6 part；Corrosion inhibiter：0.6 part；Surfactant：0.3 part；Acrylic emulsion：90 parts；
Hydrophobic molecule is modified hydroxy acid sodium salt：0.5 part and fungusproof anti-corrosion agent：0.3 part of mixing, stirs evenly, and mixing speed is 600 revs/min
Then nano aluminium oxide is added in clock：3 parts；Rutile type titanium white：15 parts and color stuffing：It 30 parts, stirs evenly, stir speed (S.S.)
It it is 300 revs/min, mixing time is 20 minutes, and after the completion of stirring, grinding, milling time is 60 minutes, is ground to fineness control
At 30 microns hereinafter, being eventually adding aqueous alkide resin：5 parts；Coalescents：2 parts；Anti- flash rusting agent 0.1 and thickener：0.2 part,
Stirring at low speed is uniform, filters and packages.
Embodiment 3
By water：20 parts；Dispersant：0.4 part；Corrosion inhibiter：0.8 part；Surfactant：0.5 part；Acrylic emulsion：70 parts；
Hydrophobic molecule is modified hydroxy acid sodium salt：0.7 part and fungusproof anti-corrosion agent：0.1 part of mixing, stirs evenly, and mixing speed is 800 revs/min
Then nano aluminium oxide is added in clock：2 parts；Rutile type titanium white：20 parts and color stuffing：It 20 parts, stirs evenly, stir speed (S.S.)
It it is 500 revs/min, mixing time is 25 minutes, and after the completion of stirring, grinding, milling time is 70 minutes, is ground to fineness control
At 30 microns hereinafter, being eventually adding aqueous alkide resin：10 parts；Coalescents：1 part；0.2 part of anti-flash rusting agent and thickener：0.1
Part, stirring at low speed is uniform, filters and packages.
In summary embodiment, highly preferred embodiment of the present invention are embodiment 1, which has visible light
The effect of shielding, storage stability is excellent, and service life is long, has good stain resistant, alkali resistance and salt fog resistance, does
Dry property, water resistance and gloss can be optimal, and convenient for construction, adhesion property is good, and service life is long, and unharmful substance, green
Colour circle is protected.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of aqueous steel structure paint, it is characterised in that：The aqueous steel structure enamel-cover includes following constituent：
Water：10-20 parts；Nano aluminium oxide：2-3 parts；Aqueous alkide resin：5-10 parts；Acrylic emulsion：70-90 parts；Dispersion
Agent：0.4-0.6 parts；Corrosion inhibiter：0.6-0.8 parts；Coalescents：1-2 parts；Surfactant：0.3-0.5 parts；Rutile type titanium
White powder：15-20 parts；Hydrophobic molecule is modified hydroxy acid sodium salt：0.5-0.7 parts；0.1-0.2 parts of anti-flash rusting agent；Color stuffing：20-30 parts；
Fungusproof anti-corrosion agent：0.1-0.3 parts and thickener：0.1-0.2 parts.
2. a kind of aqueous steel structure paint according to claim 1, it is characterised in that：The corrosion inhibiter is alkali metal sulfamate salt
Corrosion inhibiter.
3. a kind of aqueous steel structure paint according to claim 1, it is characterised in that：The coalescents are Lauryl Alcohol ester.
4. a kind of aqueous steel structure paint according to claim 1, it is characterised in that：The surfactant is detergent alkylate
Sulfonate.
5. a kind of aqueous steel structure paint according to claim 1, it is characterised in that：The color stuffing iron clad is red, trbasic zinc phosphate, three
Poly aluminium phosphate, blanc fixe and talcum powder.