CN109135027A - 一种耐高温塑料板材 - Google Patents
一种耐高温塑料板材 Download PDFInfo
- Publication number
- CN109135027A CN109135027A CN201811186934.3A CN201811186934A CN109135027A CN 109135027 A CN109135027 A CN 109135027A CN 201811186934 A CN201811186934 A CN 201811186934A CN 109135027 A CN109135027 A CN 109135027A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistance
- polycarbonate
- resistance plastice
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温塑料板材，包括以下重量组分：聚乙烯40‑50份、聚碳酸酯20‑30份、聚苯醚10‑15份、磷化硼3‑6份、蓖麻油酸钙3‑5份、3‑羟基苯甲酸6‑8份、氯化钠1‑3份、滑石粉2‑4份、抗氧化剂0.8‑1.2份、阻燃剂1‑2份。本发明通过上述材料配比，在高温下不易老化，具有较高的硬度及韧性，可以用于制作车饰材料内场合。
Description
技术领域
本发明涉及一种塑料板材，具体涉及一种耐高温塑料板材。
背景技术
塑料具有良好的硬度及韧性，可用于制作各种板材，应用广泛。但是一般的塑料不具有耐高温的性质，比如车内的车饰塑料，在夏天高温暴晒之后，车内座椅或操作台的表面温度甚至达到80摄氏度，在这种情况下，一般的工程塑料很容易老化，甚至在高温下直接融化，造成财产损失。
发明内容
本发明的目的是提供一种耐高温塑料板材，高温下仍然能保持较高的硬度及韧性。
为实现上述目的，本发明采用的一种耐高温塑料板材，其特征在于，包括以下组分：聚乙烯、聚碳酸酯、聚苯醚、磷化硼、蓖麻油酸钙、3-羟基苯甲酸、氯化钠、滑石粉、抗氧化剂、阻燃剂。
进一步的，包括以下重量组分：聚乙烯40-50份、聚碳酸酯20-30份、聚苯醚10-15份、磷化硼3-6份、蓖麻油酸钙3-5份、3-羟基苯甲酸6-8份、氯化钠1-3份、滑石粉2-4份、抗氧化剂0.8-1.2份、阻燃剂1-2份。
进一步的，包括以下重量组分：聚乙烯42-48份、聚碳酸酯22-28份、聚苯醚11-14份、磷化硼4-5份、蓖麻油酸钙3.2-4.8份、3-羟基苯甲酸6.5-7.5份、氯化钠1.5-2.5份、滑石粉2.5-3.5份、抗氧化剂0.9-1.1份、阻燃剂1.2-1.8份。
进一步的，包括以下重量组分：聚乙烯44-46份、聚碳酸酯24-26份、聚苯醚12-13份、磷化硼4.2-4.8份、蓖麻油酸钙3.6-4.4份、3-羟基苯甲酸6.8-7.2份、氯化钠1.8-2.2份、滑石粉2.8-3.2份、抗氧化剂0.9-1.1份、阻燃剂1.4-1.6份。
进一步的，包括以下重量组分：聚乙烯45份、聚碳酸酯25份、聚苯醚12.5份、磷化硼4.5份、蓖麻油酸钙4份、3-羟基苯甲酸7份、氯化钠2份、滑石粉3份、抗氧化剂1份、阻燃剂1.5份。
本发明通过上述材料配比，在高温下不易老化，具有较高的硬度及韧性，可以用于制作车饰材料内场合。
具体实施方式
下面结合实施例对本发明作进一步详细说明。
实施例1：
一种耐高温塑料板材，包括以下重量组分：聚乙烯40份、聚碳酸酯30份、聚苯醚15份、磷化硼3份、蓖麻油酸钙3份、3-羟基苯甲酸8份、氯化钠3份、滑石粉2份、抗氧化剂0.8份、阻燃剂1份。
实施例2：
一种耐高温塑料板材，包括以下重量组分：聚乙烯50份、聚碳酸酯20份、聚苯醚10份、磷化硼6份、蓖麻油酸钙5份、3-羟基苯甲酸6份、氯化钠1份、滑石粉4份、抗氧化剂1.2份、阻燃剂2份。
实施例3：
一种耐高温塑料板材，包括以下重量组分：聚乙烯45份、聚碳酸酯25份、聚苯醚12.5份、磷化硼4.5份、蓖麻油酸钙4份、3-羟基苯甲酸7份、氯化钠2份、滑石粉3份、抗氧化剂1份、阻燃剂1.5份。
Claims (5)
1.一种耐高温塑料板材，其特征在于，包括以下组分：聚乙烯、聚碳酸酯、聚苯醚、磷化硼、蓖麻油酸钙、3-羟基苯甲酸、氯化钠、滑石粉、抗氧化剂、阻燃剂。
2.根据权利要求1所述的一种耐高温塑料板材，其特征在于，包括以下重量组分：聚乙烯40-50份、聚碳酸酯20-30份、聚苯醚10-15份、磷化硼3-6份、蓖麻油酸钙3-5份、3-羟基苯甲酸6-8份、氯化钠1-3份、滑石粉2-4份、抗氧化剂0.8-1.2份、阻燃剂1-2份。
3.根据权利要求2所述的一种耐高温塑料板材，其特征在于，包括以下重量组分：聚乙烯42-48份、聚碳酸酯22-28份、聚苯醚11-14份、磷化硼4-5份、蓖麻油酸钙3.2-4.8份、3-羟基苯甲酸6.5-7.5份、氯化钠1.5-2.5份、滑石粉2.5-3.5份、抗氧化剂0.9-1.1份、阻燃剂1.2-1.8份。
4.根据权利要求3所述的一种耐高温塑料板材，其特征在于，包括以下重量组分：聚乙烯44-46份、聚碳酸酯24-26份、聚苯醚12-13份、磷化硼4.2-4.8份、蓖麻油酸钙3.6-4.4份、3-羟基苯甲酸6.8-7.2份、氯化钠1.8-2.2份、滑石粉2.8-3.2份、抗氧化剂0.9-1.1份、阻燃剂1.4-1.6份。
5.根据权利要求4所述的一种耐高温塑料板材，其特征在于，包括以下重量组分：聚乙烯45份、聚碳酸酯25份、聚苯醚12.5份、磷化硼4.5份、蓖麻油酸钙4份、3-羟基苯甲酸7份、氯化钠2份、滑石粉3份、抗氧化剂1份、阻燃剂1.5份。