CN109133749A - 一种生态型柔性木屑路面材料 - Google Patents

一种生态型柔性木屑路面材料 Download PDF

Info

Publication number
CN109133749A
CN109133749A CN201811149593.2A CN201811149593A CN109133749A CN 109133749 A CN109133749 A CN 109133749A CN 201811149593 A CN201811149593 A CN 201811149593A CN 109133749 A CN109133749 A CN 109133749A
Authority
CN
China
Prior art keywords
weight
parts
ground surface
surface material
sawdust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811149593.2A
Other languages
English (en)
Inventor
祁文洋
赵建新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Municipal Engineering Design Insitute Group Co Ltd
Original Assignee
Shanghai Municipal Engineering Design Insitute Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Municipal Engineering Design Insitute Group Co Ltd filed Critical Shanghai Municipal Engineering Design Insitute Group Co Ltd
Priority to CN201811149593.2A priority Critical patent/CN109133749A/zh
Publication of CN109133749A publication Critical patent/CN109133749A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种生态型柔性木屑路面材料，其特征在于以总量100重量份计，所述路面材料由以下重量份的组分构成：木屑15~25重量份、玄武岩30~40重量份、水4~8重量份、水泥5~10重量份、石灰0.5~1重量份、乳化沥青20~30重量份、颜料4~8重量份。本发明生态型柔性木屑路面材料具有透水性、抗滑性、柔软性高的优点；此外，木屑路面材料具有良好的施工和易性及耐久性，适用于城市住宅区、公园等人行步道铺装。

Description

一种生态型柔性木屑路面材料
技术领域
本发明涉及道路工程技术领域，公开了一种生态型柔性木屑路面材料。
背景技术
目前我国城市住宅区、公园、景区以及绿道的人行步道在铺装时主要考虑了两个生态要素：景观色彩、抗滑，由此而产生的铺装材料包括：彩色环氧碎石、彩色沥青混凝土、彩色水泥混凝土等。在这些铺装材料中，是以石料作为骨料，如果用于人行步道，其舒适性不足。此外，上述彩色铺装方案，虽然可做成透水，但不能直接铺筑与土基之上，仍需要铺筑下承层，使得路表硬化，对生态环境的影响较大。
随着我国经济的不断发展，对良好生态环境的要求越来越高。需要一种可用于住宅区、公园、景区人行步道以及城市绿道人行步道的专用生态型铺装材料，使铺装材料与绿化景观等相协调，同时提高步行的安全性和舒适性。
发明内容
本发明的目的是提供一种生态型柔性木屑路面材料，以解决城市住宅区、公园等人行步道铺装的舒适性不足问题，同时降低铺装对生态环境的影响。
本发明解决上述技术问题的技术方案如下：一种生态型柔性木屑路面材料，其特征在于以总量100重量份计，所述路面材料由以下重量份的组分构成：木屑15～25重量份、玄武岩30～40重量份、水4～8重量份、水泥5～10重量份、石灰0.5～1重量份、乳化沥青20～30重量份、颜料4～8重量份。
优选的，所述玄武岩为1.18mm单一粒径颗粒。
优选的，所述颜料为氧化铁红或氧化铁绿。
优选的，所述乳化沥青技术性能满足以下要求
25℃恩格拉粘度为2～10s，1.18mm筛上余量≤0.1％，与矿料的粘附性，裹覆面积≥2/3，蒸发残留量≥50％，蒸发残留物性质满足25℃针入度为5～30，软化点>55℃。
本发明的有益效果是：具有透水性、抗滑性、柔软性高的优点；此外，木屑路面材料具有良好的常温施工和易性以及耐久性，适用于城市住宅区、公园、景区以及绿道的人行步道铺装。
具体实施方式
在此记载的实施例为本发明的特定具体实施方式，用于说明本发明的构思，为示例性的，并非对本发明实施方式及范围的限定。除了在此记载的实施例以外，本领域技术人员还能够基于本申请专利要求书和说明书所公开内容采用显而易见的其它技术方案，这些技术方案包括采用对在此记载的实施例做出任何显而易见的替换和修改的技术方案。
一种生态型柔性木屑路面材料，其特征在于以总量100重量份计，所述路面材料由以下重量份的组分构成：木屑15～25重量份、玄武岩30～40重量份、水4～8重量份、水泥5～10重量份、石灰0.5～1重量份、乳化沥青20～30重量份、颜料4～8重量份。
优选的，所述玄武岩为1.18mm单一粒径颗粒。
优选的，所述颜料为氧化铁红或氧化铁绿。
优选的，所述乳化沥青技术性能满足表1要求。
表1乳化沥青技术要求
以下实施例所用的部分原料来源如下：木屑、颜料、石灰均由阿里巴巴上购买；玄武岩为浙江嵊州石料场生产的玄武岩碎石料；水泥为上海佐仁建材有限公司的海螺牌42.5号硅酸盐水泥；乳化沥青为日本日沥公司生产的改性乳化沥青。
实施例1
本实施例生态型柔性木屑路面材料由以下组分构成：木屑27.5千克、玄武岩54.3千克、水10千克、水泥11千克、石灰1千克、乳化沥青34.6千克、氧化铁红10千克。
实施例2
本实施例生态型柔性木屑路面材料由以下组分构成：木屑26.7千克、玄武岩46.7千克、水8千克、水泥9.3千克、石灰1千克、乳化沥青33千克，氧化铁绿8千克。
上述实施例生态型柔性木屑路面材料采用以下工艺制备：首先将称量好的木屑和玄武岩加入JW750平口搅拌机进行拌和，拌和时间为5min；然后依次加入乳化沥青、水进行拌，拌和时间为1.5min；最后依次加入水泥、石灰和颜料进行拌和，拌和时间为2min，制得生态型柔性木屑路面材料。
试验例1
利用实施例1、实施例2所得的生态型柔性木屑路面材料分别制备马歇尔试件，观察试件色泽与均匀性，之后进行20℃的肯塔堡飞散试验。试验结果见表2。
表2试验结果
样品编号 色泽 均匀性 飞散损失/％
实施例1 红褐色 良好 9
实施例2 棕绿色 良好 11
通过上述数据可以得知，本发明生态型柔性木屑路面材料具有良好的景观色彩、均匀性以及耐久性。
试验例2
利用实施例1、实施例2所得的生态型柔性木屑路面材料分别制备车辙试件，依次进行缓冲性试验、渗水性试验以及抗滑性测试，其中弹性试验方法为：将高尔夫弹性球从1m高度自由下落，经路面反弹后上升的高度(m)；由于渗水较快，渗水性试验采用渗水400ml的时间(s)为指标。试验结果见表3。
表3试验结果
样品编号 反弹高度/m 渗水时间/s BPN/％
实施例1 0.15 4 55
实施例2 0.22 6 52
通过上述数据可以得知，本发明生态型柔性木屑路面材料具有良好的柔韧性、渗水性以及抗滑性。
上述披露的各项技术特征并不限于已披露的与其他特征的组合，本领域技术人员还可根据发明之目的进行各技术特征之间的其它组合，以实现本发明之目的为准。

Claims (4)

1.一种生态型柔性木屑路面材料，其特征在于以总量100重量份计，所述路面材料由以下重量份的组分构成：木屑15~25重量份、玄武岩30~40重量份、水4~8重量份、水泥5~10重量份、石灰0.5~1重量份、乳化沥青20~30重量份、颜料4~8重量份。
2.根据权利要求1所述的生态型柔性木屑路面材料，其特征在于，所述的玄武岩为1.18mm单一粒径颗粒。
3.根据权利要求1所述的生态型柔性木屑路面材料，其特征在于，所述的颜料为氧化铁红或氧化铁绿。
4.根据权利要求1所述的生态型柔性木屑路面材料，其特征在于，所述的乳化沥青为阳离子乳化沥青，其25℃恩格拉粘度为2~10，蒸发残留物25℃针入度为5~30。
CN201811149593.2A 2018-09-29 2018-09-29 一种生态型柔性木屑路面材料 Pending CN109133749A (zh)