CN109098001A - A kind of anhydrous fibrillation treatment method of Lyocell fibers - Google Patents
A kind of anhydrous fibrillation treatment method of Lyocell fibers Download PDFInfo
- Publication number
- CN109098001A CN109098001A CN201810750998.5A CN201810750998A CN109098001A CN 109098001 A CN109098001 A CN 109098001A CN 201810750998 A CN201810750998 A CN 201810750998A CN 109098001 A CN109098001 A CN 109098001A
- Authority
- CN
- China
- Prior art keywords
- lyocell fibers
- anhydrous
- fibrillation
- fabric
- treatment method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of anhydrous fibrillation treatment method of Lyocell fibers, includes the following steps: (1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees that the pick-up of Lyocell fibers fabric is 85-95%；(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind control is in 35-40pa/m, the beating time is 45-55min, it divides Lyocell fibers sharply and generates extremely fine and closely woven villus, assign fabric ultimate attainment softness simultaneously, it is fluffy, the sliding feel experience of silk, it efficiently solves the problems, such as to generate a large amount of waste water in traditional Lyocell fibers fibrillation process and COD is higher, also the consumption of chemical agent Water Energy is reduced, achievees the purpose that efficient, high speed, environmental protection.
Description
Technical field
The invention belongs to textile fabric production fields, and in particular to a kind of anhydrous fibrillation processing side of Lyocell fibers
Method.
Background technique
Lyocell fibers belong to a kind of regenerated celulose fibre of high wet modulus, have comfort possessed by cotton fiber,
Sucting wet air permeability, and there is preferable Peng's lubricant nature, make fabric that there is pendency sense, plentiful feel, smooth sense and light as silk
No matter pool sense all has fabulous toughness in the state of dry or wet, and strength is higher under hygrometric state.Tencel fiber is using day
Right renewable timber is raw material, and fiber obtained from manufacturing through green processing, in the whole process, water and amine oxide solvent are almost
It is completely retracted, any pollution is not caused to environment, therefore there is very high use value in the production of environmentally protective fabric,
There are many deficiencies for the technique to the processing of Lyocell fibers fibrillation domestic at present, and traditional fibrillation process can generate largely
Waste water, COD is higher, the later period need to carry out waste water it is certain come out, fibrillation processing troublesome in poeration and traditional is easy to produce
It is raw because scratch forms the phenomenon more than Shared-with cloth, be further improved.
Summary of the invention
The purpose of the present invention is overcoming the prior art, the Lyocell fibers that a kind of blowdown is small, process is short are provided
Anhydrous fibrillation treatment method.
The present invention adopts the following technical scheme:
1, the anhydrous fibrillation treatment method of a kind of Lyocell fibers, characterized by the following steps:
(1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees rolling for Lyocell fibers fabric
Remaining rate is 85-95%；
(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind-force control
For system in 35-40pa/m, the beating time is 45-55min.
Further, the treatment fluid includes the hydrophilic softening agent of the leavening agent of 4-6g/L, 7-9g/L.
Further, the leavening agent is cation fatty acid derivative species or high ammonia value organic silicon.
Further, the hydrophilic softening agent is the epoxy co-modified silicone oil of polyethers.
Further, further include step (3) airflow dyeing: anhydrous fibrillation will be carried out treated Lyocell fibers fabric
Airflow dyeing is carried out, secondary beating is carried out to Lyocell fibers fabric using the wind-force that air-flow generates.
Further, in the step (3), the wind-force that air-flow generates is 9-13pa/m.
Further, the anhydrous fibrillation processing carries out in soft machine, Lyocell fibers fabric in soft machine into
When row processing, the quantity of every pipe is no more than 300m.
Further, the pre-treatment carries out in stenter, and the treatment fluid is placed in the groove of stenter, lyocell
Fiber fabric is completed the pick-up of 85-95% by padding machine after groove suction.
By the above-mentioned description of this invention it is found that compared with prior art, the beneficial effects of the present invention are: the present invention passes through
Lyocell fibers are handled in treatment fluid first, make pick-up 85-95%, wind-force is then controlled and Lyocell fibers is clapped
It beats, divides Lyocell fibers sharply and generate extremely fine and closely woven villus, while assigning fabric ultimate attainment softness, it is fluffy, what silk was slided
Feel experience, efficiently solves the problems, such as to generate a large amount of waste water in traditional Lyocell fibers fibrillation process and COD is higher, also subtract
Few chemical agent Water Energy consumption, achievees the purpose that efficient, high speed, environmental protection；By the process control of anhydrous fibrillation in 45-
Within 50min, avoids Lyocell fibers and form phenomenon more than defective cloth because of scratch；Anhydrous fibrillation treated lyocell is fine
Dimension carries out airflow dyeing, generates powerful wind-force using air-flow and carries out secondary beating to Lyocell fibers, generates after being atomized superfine
The waste wool generated by Lyocell fibers division that microparticle water mist adheres to fabric surface is effectively removed, so that reaching makes to knit
Object surface is more fine and smooth, and neatly, silk is sliding, not the characteristics of hair loss.
Specific embodiment
Below by way of specific embodiment, the invention will be further described.
A kind of anhydrous fibrillation treatment method of Lyocell fibers, includes the following steps:
(1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees rolling for Lyocell fibers fabric
Remaining rate is 85-95%；
(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind-force control
For system in 35-40pa/m, the beating time is 45-55min；
(3) it dyes: will carry out anhydrous fibrillation treated that Lyocell fibers carry out airflow dyeing, air-flow is utilized to generate
Wind-force carries out secondary beating to Lyocell fibers, specifically, the wind-force that air-flow generates is 9-13pa/m.
Specifically, pre-treatment carries out in stenter, which is placed in groove, and Lyocell fibers fabric is inhaled through groove
The pick-up of 85-95% is completed after material by padding machine, then carries out anhydrous fibrillation processing under micro- damp state.
Treatment fluid includes the hydrophilic softening agent of the leavening agent of 4-6g/L, 7-9g/L, specifically, leavening agent is cation fat
Acid derivative class or high ammonia value organic silicon, hydrophilic softening agent are the epoxy co-modified silicone oil of polyethers, and further, leavening agent is south
The leavening agent NJ-05 of capital Qixia Mountain printing and dyeing assistant factory production, hydrophilic softening agent are that Industrial Co., Ltd's production is learned in rainbow beautification in Jiangxi
Hydrophilic softening agent HY-303.
Anhydrous fibrillation processing carries out in soft machine, and Sai Er fiber fabric carries out anhydrous fibrillation processing in soft machine
When, it is necessary to assure the quantity of every pipe is no more than 300m, specifically, soft machine is the open width air of PENTEK company of Italy production
Soft machine-EnAIRgy.
Embodiment 1
A kind of anhydrous fibrillation treatment method of Lyocell fibers, includes the following steps:
(1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees rolling for Lyocell fibers fabric
Remaining rate is 85%；
(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind-force control
For system in 40pa/m, the beating time is 45min；
(3) it dyes: will carry out anhydrous fibrillation treated that Lyocell fibers carry out airflow dyeing, air-flow is utilized to generate
Wind-force carries out secondary beating to Lyocell fibers, specifically, the wind-force that air-flow generates is 13pa/m.
Specifically, pre-treatment carries out in stenter, which is placed in groove, and Lyocell fibers fabric is inhaled through groove
By the pick-up of padding machine completion 85% after material, anhydrous fibrillation processing then is carried out under micro- damp state.
Treatment fluid includes the hydrophilic softening agent of the leavening agent of 4g/L, 9g/L, specifically, leavening agent spreads out for cation fatty acid
Biological species or high ammonia value organic silicon, hydrophilic softening agent are the epoxy co-modified silicone oil of polyethers, and further, leavening agent is dwelt for Nanjing
The leavening agent NJ-05 of Xia Shan printing and dyeing assistant factory production, hydrophilic softening agent are the parent that Industrial Co., Ltd's production is learned in rainbow beautification in Jiangxi
Water softening agent HY-303.
Anhydrous fibrillation processing carries out in soft machine, and Sai Er fiber fabric carries out anhydrous fibrillation processing in soft machine
When, it is necessary to assure the quantity of every pipe is no more than 300m, specifically, soft machine is the open width air of PENTEK company of Italy production
Soft machine-EnAIRgy.
Embodiment 2
A kind of anhydrous fibrillation treatment method of Lyocell fibers, includes the following steps:
(1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees rolling for Lyocell fibers fabric
Remaining rate is 95%；
(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind-force control
For system in 35pa/m, the beating time is 55min；
(3) it dyes: will carry out anhydrous fibrillation treated that Lyocell fibers carry out airflow dyeing, air-flow is utilized to generate
Wind-force carries out secondary beating to Lyocell fibers, specifically, the wind-force that air-flow generates is 9pa/m.
Specifically, pre-treatment carries out in stenter, which is placed in groove, and Lyocell fibers fabric is inhaled through groove
By the pick-up of padding machine completion 95% after material, anhydrous fibrillation processing then is carried out under micro- damp state.
Treatment fluid includes the hydrophilic softening agent of the leavening agent of 6g/L, 7g/L, specifically, leavening agent spreads out for cation fatty acid
Biological species or high ammonia value organic silicon, hydrophilic softening agent are the epoxy co-modified silicone oil of polyethers, and further, leavening agent is dwelt for Nanjing
The leavening agent NJ-05 of Xia Shan printing and dyeing assistant factory production, hydrophilic softening agent are the parent that Industrial Co., Ltd's production is learned in rainbow beautification in Jiangxi
Water softening agent HY-303.
Anhydrous fibrillation processing carries out in soft machine, and Sai Er fiber fabric carries out anhydrous fibrillation processing in soft machine
When, it is necessary to assure the quantity of every pipe is no more than 300m, specifically, soft machine is the open width air of PENTEK company of Italy production
Soft machine-EnAIRgy.
Embodiment 3
A kind of anhydrous fibrillation treatment method of Lyocell fibers, includes the following steps:
(1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees rolling for Lyocell fibers fabric
Remaining rate is 90%；
(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind-force control
For system in 37pa/m, the beating time is 50min；
(3) it dyes: will carry out anhydrous fibrillation treated that Lyocell fibers carry out airflow dyeing, air-flow is utilized to generate
Wind-force carries out secondary beating to Lyocell fibers, specifically, the wind-force that air-flow generates is 11pa/m.
Specifically, pre-treatment carries out in stenter, which is placed in groove, and Lyocell fibers fabric is inhaled through groove
By the pick-up of padding machine completion 90% after material, anhydrous fibrillation processing then is carried out under micro- damp state.
Treatment fluid includes the hydrophilic softening agent of the leavening agent of 5g/L, 8g/L, specifically, leavening agent spreads out for cation fatty acid
Biological species or high ammonia value organic silicon, hydrophilic softening agent are the epoxy co-modified silicone oil of polyethers, and further, leavening agent is dwelt for Nanjing
The leavening agent NJ-05 of Xia Shan printing and dyeing assistant factory production, hydrophilic softening agent are the parent that Industrial Co., Ltd's production is learned in rainbow beautification in Jiangxi
Water softening agent HY-303.
Anhydrous fibrillation processing carries out in soft machine, and Sai Er fiber fabric carries out anhydrous fibrillation processing in soft machine
When, it is necessary to assure the quantity of every pipe is no more than 300m, specifically, soft machine is the open width air of PENTEK company of Italy production
Soft machine-EnAIRgy.
Lyocell fibers made from above three embodiments are tested, following performance parameter is obtained:
Each performance parameter table of 1 Lyocell fibers of table
By above table it is found that the technique is first handled Lyocell fibers in treatment fluid, make pick-up 85-95%,
Then it controls wind-force to pat Lyocell fibers, divides Lyocell fibers sharply and generate extremely fine and closely woven villus, together
When assign fabric ultimate attainment softness, fluffy, the sliding feel experience of silk passes through the lyocell of fibrillation process for producing with the prior art
Fiber, i.e. comparative example are compared, and indices can all reach, and are carried out at anhydrous fibrillation using this technique to Lyocell fibers
Reason, efficiently solves the problems, such as to generate a large amount of waste water in traditional Lyocell fibers fibrillation process and COD is higher, also reduces chemistry
The consumption of medicament Water Energy achievees the purpose that efficient, high speed, environmental protection.
The foregoing is only a preferred embodiment of the present invention, therefore cannot be limited the scope of implementation of the present invention with this, i.e.,
According to equivalent changes and modifications made by scope of the present invention patent and description, it should still belong to what the invention patent covered
In range.
Claims (8)
1. a kind of anhydrous fibrillation treatment method of Lyocell fibers, characterized by the following steps:
(1) pre-treatment: Lyocell fibers fabric being placed in treatment fluid and is handled, and guarantees the pick-up of Lyocell fibers fabric
For 85-95%；
(2) it anhydrous fibrillation processing: is patted with the Lyocell fibers fabric that wind-force obtains step (1), wind control exists
35-40pa/m, beating time are 45-55min.
2. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 1, it is characterised in that: the place
Reason liquid includes the hydrophilic softening agent of the leavening agent of 4-6g/L, 7-9g/L.
3. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 2, it is characterised in that: described fluffy
Loose agent is cation fatty acid derivative species or high ammonia value organic silicon.
4. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 2, it is characterised in that: the parent
Water softening agent is the epoxy co-modified silicone oil of polyethers.
5. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 1 or 2 or 3 or 4, feature exist
In: further include step (3) airflow dyeing: will carry out anhydrous fibrillation treated that Lyocell fibers fabric carries out airflow dyeing,
Secondary beating is carried out to Lyocell fibers fabric using the wind-force that air-flow generates.
6. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 5, it is characterised in that: the step
Suddenly in (3), the wind-force that air-flow generates is 9-13pa/m.
7. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 1 or 2 or 3 or 4, feature exist
In: the anhydrous fibrillation processing carries out in soft machine, when Lyocell fibers fabric is handled in soft machine, every pipe
Quantity is no more than 300m.
8. a kind of anhydrous fibrillation treatment method of Lyocell fibers according to claim 1 or 2 or 3 or 4, feature exist
In: the pre-treatment carries out in stenter, and the treatment fluid is placed in the groove of stenter, and Lyocell fibers fabric is in groove
After suction, the pick-up of 85-95% is completed by padding machine.