CN109097052A - A kind of natural medical stone agricultural soil heavy metal deactivator and preparation method thereof - Google Patents
A kind of natural medical stone agricultural soil heavy metal deactivator and preparation method thereof Download PDFInfo
- Publication number
- CN109097052A CN109097052A CN201811010395.8A CN201811010395A CN109097052A CN 109097052 A CN109097052 A CN 109097052A CN 201811010395 A CN201811010395 A CN 201811010395A CN 109097052 A CN109097052 A CN 109097052A
- Authority
- CN
- China
- Prior art keywords
- parts
- medical stone
- heavy metal
- raw material
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of natural medical stone agricultural soil heavy metal deactivators and preparation method thereof, matal deactivator includes the raw material of following parts by weight: 20~40 parts of clay mineral, 25~35 parts of quick lime, 20~30 parts of medical stone, 10~30 parts of natural phosphate fertilizer, 5~10 parts of oyster shell and 2~6 parts of red mud, preparation method includes the following steps, S1, the preparation of raw material;S2, the calcination processing of raw material;S3, the pulverization process of raw material;S4, the mixing of raw material.Matal deactivator of the present invention can be passivated and repair various heavy, especially lead and cadmium, while the quality of the yield soil of crops is greatly improved, and be more advantageous to the growth of crop, and standby simple process, easy to operate, at low cost, suitable for mass production.
Description
Technical field
The present invention relates to matal deactivator technical fields more particularly to a kind of natural medical stone agricultural soil heavy metal to be passivated
Agent and preparation method thereof.
Background technique
As Chinese Industrialization, Development of China's Urbanization quickly propel, heavy metal pollution of soil becomes increasingly conspicuous, chemical industry, mining, smelting
Industrial " three Waste "s, urban transportation, atmospheric sedimentation, feces of livestock and poultry, municipal sludge, the agriculture chemicals such as refining etc. become primary pollution source.
Since agricultural land soil is by heavy metal pollution, the agricultural product heavy metal pollution problem produced on contaminated farmland becomes increasingly conspicuous.In
State's heavy metal content in soil has been more than that soil background, especially Cd and Pb are seriously polluted.
Traditional research method is that the chemical substances such as white lime, calcium silicates are added into soil, by the way that these substances are added,
The series reactions such as precipitating, absorption, ion exchange, humification and redox can occur with heavy metal element, significantly reduce
Its biological effectiveness and transportable property, hence it is evident that slow down toxic action of the heavy metal pollution to plant growth, plant pair is greatly decreased
The absorption and accumulation of heavy metal, still, these substances are inorganic substances mostly, influence soil physical chemistry property and fertility, right
Microorganism growing environment causes different degrees of influence, also influence repair after the completion of soil using degree, it is also possible to produce
Raw secondary pollution, we have devised a kind of natural medical stone agricultural soil heavy metal deactivator and preparation method thereof and come thus
Solve problem above.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of natural medical stone agricultural proposed
Soil heavy metal passivant and preparation method thereof.
To achieve the goals above, present invention employs following technical solutions:
A kind of natural medical stone agricultural soil heavy metal deactivator, the raw material including following parts by weight: clay mineral 20~
40 parts, 25~35 parts of quick lime, 20~30 parts of medical stone, 10~30 parts of natural phosphate fertilizer, 5~10 parts of oyster shell and red mud 2~6
Part.
Preferably, the raw material including following parts by weight: 35 parts of clay mineral, 30 parts of quick lime, 27 parts of medical stone, phosphate fertilizer 25
Part, 8 parts of oyster shell and 5 parts of red mud.
Preferably, the natural phosphate fertilizer is one of guano, beast bone meal, fishbone dust.
Preferably, the clay mineral is the mixture of sepiolite, zeolite and diatomite, sepiolite, zeolite and diatomite
Ratio be 1.8:1.5:1.
A kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, includes the following steps,
S1, the preparation of raw material: according to the ratio of each component weigh the clay mineral of corresponding weight, quick lime, medical stone,
Phosphate fertilizer, oyster shell and red mud;
S2, the calcination processing of raw material: to the oyster shell in S1 with 650~800 DEG C of progress calcination processings, until incinerate,
Obtain calcining powder;
The pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added to pulverizer by S3
In, it is pulverized and mixed, crushing 20~after forty minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to and stir in S2
It mixes after being stirred 30~50 minutes in device, obtains matal deactivator.
Preferably, it when weighing red mud in the S1, needs first to dry red mud.
Preferably, in the S1 clay mineral, quick lime, medical stone and oyster shell before weighing, need through over cleaning and
It is dried.
Preferably, the S2 lime stone and clay mineral smash it through 80-160 mesh.
Preferably, broken 100~200 meshes excessively afterwards of medical stone in the S2.
Preferably, lime stone, medical stone and clay mineral are successively added in pulverizer in the S3, between the time of addition
It is divided into 3~5 minutes.
Compared with prior art, the beneficial effects of the present invention are:
1, medical stone fertilizing ability with higher, the effect for improving soil texture, improving soil water-reataining fertilizer-keeping ability, can
Keep hardened soil loose, good moisture, ventilation, temperature condition is created for plant root growth development, to have
Conducive to the trans-utilization of nutrient in soil, keep crops cauline leaf in great numbers, improve plant photosynthesis, guarantees supporting for tuber initiation stage
Divide and need, be conducive to stem tuber and expand, increases big or middle fruit rate, improve the soil of the yield and quality of crops, be more advantageous to work
The growth of object;
2, sepiolite and natural phosphate fertilizer while, apply, and can improve soil pH value by sepiolite, utilize phosphatic suction
The effects of being accompanied by and generating mineral precipitation, the residue for promoting Cd, Pb in contaminated soil low to activity from the high exchange state of activity
State conversion, to significantly reduce the biological effectiveness and transfer ability of Cd, Pb;
3, calcined oyster shell and red mud have preferable fixed effect, passivation ability to Cd in contaminated soil and Pb
By force;
4, farming can be also greatly improved while being passivated and repairing various heavy in matal deactivator of the invention
The production yields of object;
5, the preparation process of matal deactivator is simple, easy to operate, at low cost, suitable for mass production.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.
Embodiment one
A kind of natural medical stone agricultural soil heavy metal deactivator, the raw material including following parts by weight: 20 parts of clay mineral,
25 parts of quick lime, 20 parts of medical stone, 10 parts of natural phosphate fertilizer, 5 parts of oyster shell and 2 parts of red mud.
A kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, includes the following steps,
S1, the preparation of raw material: according to the ratio of each component weigh the clay mineral of corresponding weight, quick lime, medical stone,
Phosphate fertilizer, oyster shell and red mud;
The calcination processing of raw material: S2 to the oyster shell in S1 with 650 DEG C of progress calcination processings, until incinerating, is forged
Burn powder;
The pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added to pulverizer by S3
In, it is pulverized and mixed, crushes after twenty minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to and stir in S2
It mixes after being stirred 30 minutes in device, obtains matal deactivator.
Embodiment two
A kind of natural medical stone agricultural soil heavy metal deactivator, the raw material including following parts by weight: 25 parts of clay mineral,
27 parts of quick lime, 22 parts of medical stone, 15 parts of natural phosphate fertilizer, 6 parts of oyster shell and 3 parts of red mud.
A kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, includes the following steps,
S1, the preparation of raw material: according to the ratio of each component weigh the clay mineral of corresponding weight, quick lime, medical stone,
Phosphate fertilizer, oyster shell and red mud;
The calcination processing of raw material: S2 to the oyster shell in S1 with 680 DEG C of progress calcination processings, until incinerating, is forged
Burn powder;
The pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added to pulverizer by S3
In, it is pulverized and mixed, after crushing 25 minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to and stir in S2
It mixes after being stirred 35 minutes in device, obtains matal deactivator.
Embodiment three
A kind of natural medical stone agricultural soil heavy metal deactivator, the raw material including following parts by weight: 30 parts of clay mineral,
27 parts of quick lime, 24 parts of medical stone, 20 parts of natural phosphate fertilizer, 7 parts of oyster shell and 4 parts of red mud.
A kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, includes the following steps,
S1, the preparation of raw material: according to the ratio of each component weigh the clay mineral of corresponding weight, quick lime, medical stone,
Phosphate fertilizer, oyster shell and red mud;
The calcination processing of raw material: S2 to the oyster shell in S1 with 700 DEG C of progress calcination processings, until incinerating, is forged
Burn powder;
The pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added to pulverizer by S3
In, it is pulverized and mixed, after crushing 30 minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to and stir in S2
It mixes and is stirred in device after forty minutes, obtain matal deactivator.
Example IV
A kind of natural medical stone agricultural soil heavy metal deactivator, the raw material including following parts by weight: 35 parts of clay mineral,
30 parts of quick lime, 27 parts of medical stone, 25 parts of phosphate fertilizer, 8 parts of oyster shell and 5 parts of red mud.
A kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, includes the following steps,
S1, the preparation of raw material: according to the ratio of each component weigh the clay mineral of corresponding weight, quick lime, medical stone,
Phosphate fertilizer, oyster shell and red mud;
The calcination processing of raw material: S2 to the oyster shell in S1 with 750 DEG C of progress calcination processings, until incinerating, is forged
Burn powder;
The pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added to pulverizer by S3
In, it is pulverized and mixed, after crushing 35 minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to and stir in S2
It mixes after being stirred 45 minutes in device, obtains matal deactivator.
Embodiment five
A kind of natural medical stone agricultural soil heavy metal deactivator, the raw material including following parts by weight: 40 parts of clay mineral,
35 parts of quick lime, 30 parts of medical stone, 30 parts of natural phosphate fertilizer, 10 parts of oyster shell and 6 parts of red mud.
A kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, includes the following steps,
S1, the preparation of raw material: according to the ratio of each component weigh the clay mineral of corresponding weight, quick lime, medical stone,
Phosphate fertilizer, oyster shell and red mud;
The calcination processing of raw material: S2 to the oyster shell in S1 with 800 DEG C of progress calcination processings, until incinerating, is forged
Burn powder;
The pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added to pulverizer by S3
In, it is pulverized and mixed, crushes after forty minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to and stir in S2
It mixes after being stirred 50 minutes in device, obtains matal deactivator.
One, two, three, four, No. five passivator can be made respectively by above-mentioned five groups of embodiments, take the soil of the weight such as six portionings
Earth, and the content of lead therein and cadmium is measured and is recorded, dissipate upper one to No. five in five groups of experiment soil respectively thereto
Matal deactivator, and be sufficiently mixed with soil, and the amount of application of matal deactivator is the 0.8- for testing soil gross mass
3.5%, then the vegetables in six groups of test soil in kind with kind, pour the water of equivalent, after vegetable ripeness, in soil
The content of lead and cadmium is measured, and harvested vegetable, is weighed, obtains following table:
It can be obtained by upper table, using the soil of matal deactivator of the present invention, the content of lead and cadmium in the soil after passivation
It is greatly lowered, while passing through analytical calculation it is found that the effect of No. four matal deactivators is optimal, i.e., in five groups of embodiments, in fact
The matal deactivator effect that the formula and method for applying example four are prepared is best, while having used the soil of matal deactivator of the invention
Earth is more advantageous to the growth of crop.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of natural medical stone agricultural soil heavy metal deactivator, which is characterized in that the raw material including following parts by weight: clay
20~40 parts of mineral, 25~35 parts of quick lime, 20~30 parts of medical stone, 10~30 parts of natural phosphate fertilizer, 5~10 parts of oyster shell and red
2~6 parts of mud.
2. a kind of natural medical stone agricultural soil heavy metal deactivator according to claim 1, which is characterized in that including with
The raw material of lower parts by weight: 35 parts of clay mineral, 30 parts of quick lime, 27 parts of medical stone, 25 parts of phosphate fertilizer, 8 parts of oyster shell and red mud 5
Part.
3. a kind of natural medical stone agricultural soil heavy metal deactivator according to claim 1, which is characterized in that the day
Right phosphate fertilizer is one of guano, beast bone meal, fishbone dust.
4. a kind of natural medical stone agricultural soil heavy metal deactivator according to claim 1, which is characterized in that described glutinous
Native mineral are the mixture of sepiolite, zeolite and diatomite, and the ratio of sepiolite, zeolite and diatomite is 1.8:1.5:1.
5. a kind of preparation method of natural medical stone agricultural soil heavy metal deactivator, which is characterized in that include the following steps,
The preparation of raw material: S1 weighs clay mineral, quick lime, medical stone, the phosphorus of corresponding weight according to the ratio of each component
Fertilizer, oyster shell and red mud;
The calcination processing of raw material: S2 to the oyster shell in S1 with 650~800 DEG C of progress calcination processings, until incinerating, is obtained
Calcine powder;
S3, the pulverization process of raw material: lime stone weighed in S1, medical stone, sepiolite and zeolite are added in pulverizer, into
Row is pulverized and mixed, and crushing 20~after forty minutes, pulverulent mixture is obtained after sieving;
The mixing of raw material: S4 will calcine powder, pulverulent mixture, the phosphate fertilizer in S1 and red mud in S3 are added to blender in S2
In be stirred 30~50 minutes after, obtain matal deactivator.
6. a kind of preparation method of natural medical stone agricultural soil heavy metal deactivator according to claim 5, feature
It is, when weighing red mud in the S1, needs first to dry red mud.
7. a kind of preparation method of natural medical stone agricultural soil heavy metal deactivator according to claim 5, feature
It is, clay mineral, quick lime, medical stone and oyster shell need before weighing by washing and drying treatment in the S1.
8. a kind of preparation method of natural medical stone agricultural soil heavy metal deactivator according to claim 5, feature
It is, the S2 lime stone and clay mineral smash it through 80-160 mesh.
9. a kind of preparation method of natural medical stone agricultural soil heavy metal deactivator according to claim 5, feature
It is, crosses 100~200 meshes after the medical stone in the S2 is broken.
10. a kind of preparation method of natural medical stone agricultural soil heavy metal deactivator according to claim 5, feature
It is, lime stone, medical stone and clay mineral are successively added in pulverizer in the S3, and the time interval of addition is 3~5 points
Clock.