CN109090765A - 一种防臭鞋底及其制备方法 - Google Patents
一种防臭鞋底及其制备方法 Download PDFInfo
- Publication number
- CN109090765A CN109090765A CN201811275211.0A CN201811275211A CN109090765A CN 109090765 A CN109090765 A CN 109090765A CN 201811275211 A CN201811275211 A CN 201811275211A CN 109090765 A CN109090765 A CN 109090765A
- Authority
- CN
- China
- Prior art keywords
- layer
- parts
- linear fiber
- reverse side
- fiber layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种防臭鞋底，其特征在于：按照重量份数，包括EVA鞋底，所述EVA鞋底上设置有正面线型纤维层，弹性纤维层以及反面线型纤维层组成，在正面线型纤维层和反面线型纤维层涂有一层纳米氧化铜涂层，所述正面线型纤维层，弹性纤维层以及反面线型纤维层的截面均设置为沟槽状，所述正面线圈结构层，弹性纤维层以及反面线型纤维层均包括如下组分，甲壳素纤维10‑20份、风化壳淋积型稀土矿5‑10份、乙基香草醛类化合物12‑20份、酰基苯胺类化合物12‑20份、亲水柔软助剂2‑5份，本发明具有抑制脚臭且抗菌的优点。
Description
技术领域
本发明涉及鞋底技术领域，具体涉及一种防臭鞋底及其制备方法。
背景技术
鞋底材料的种类很多，一般分为天然类鞋底材料和合成类鞋底材料两种。天然类鞋底材料包括天然底革、竹、木材等，合成类鞋底材料包括橡胶、PU材料、PVC合成树脂等。
人们在行走时，脚上的汗腺会分泌出分泌物，这些分泌物在细菌、霉菌分解下会产生异味，而在剧烈运动后，大量的出汗后尤为明显，人们想到经常换鞋垫来改善，短期内效果还可以，但是长时间还是会复发，所以这只是治标不治本的办法，因此需要从鞋底进行改进。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种防臭鞋底，其具有抑制脚臭、抗菌且吸湿快干的优点。
为实现上述目的，本发明提供了如下技术方案：一种防臭鞋底，其特征在于：按照重量份数，包括EVA鞋底，所述EVA鞋底上设置有正面线型纤维层，弹性纤维层以及反面线型纤维层组成，其中弹性纤维层处于中间，各层通过粘结剂固定，在正面线型纤维层和反面线型纤维层涂有一层纳米氧化铜涂层，所述正面线型纤维层，弹性纤维层以及反面线型纤维层的截面均设置为沟槽状，所述正面线圈结构层，弹性纤维层以及反面线型纤维层均包括如下组分，甲壳素纤维10-20份、风化壳淋积型稀土矿5-10份、乙基香草醛类化合物12-20份、酰基苯胺类化合物12-20份、亲水柔软助剂2-5份；所述正面线圈结构层，弹性纤维层以及反面线型纤维层镶嵌有玻璃-银离子抗菌剂10-20份，所述玻璃-银离子抗菌剂为载体选为玻璃的银离子抗菌剂，所述玻璃：银离子抗菌剂=3:1。
通过采用上述技术方案，甲壳素对大肠杆菌、金黄色葡萄球菌、白色念珠菌具有优异的抑菌效果。风化壳淋积型稀土矿能与织物中的氧、氮等配位离子形成螯合物，使乙基香草醛类化合物和酰基苯胺类化合物牢固地与织物结合；并且乙基香草醛类化合物和酰基苯胺类化合物之间以稀土离子为联结点，产生协同抑菌作用。沟槽状的设置有利于正面线型纤维层，弹性纤维层以及反面线型纤维层具有吸湿快干的效果。玻璃-银离子抗菌剂可增强正面线圈结构层，弹性纤维层以及反面线型纤维层的强度。
本发明进一步设置为：所述风化壳淋积型稀土矿向江西购买，且3mm﹤粒径﹤5mm。
通过采用上述技术方案，采用上述的风化壳淋积型稀土矿效果最佳。
本发明的另一个目的为提供一种防臭鞋底的制备方法，包括如下步骤：按照重量份数称取相应的组分，
步骤1：在EVA鞋底上铺设正面线型纤维层，弹性纤维层以及反面线型纤维层，其中正面线型纤维层，弹性纤维层以及反面线型纤维层之间通过粘结剂固定；
步骤2：将玻璃-银离子抗菌剂和步骤1得到的成品加入抗菌处理罐中，升温至62℃，加压到0.2MPa，保持压力不变，持续120min；
步骤3：解除压力，将甲壳素纤维、风化壳淋积型稀土矿、乙基香草醛类化合物、酰基苯胺类化合物、亲水柔软助剂加入抗菌处理罐中，升温至62℃，加压到0.4MPa，保持压力不变，持续120min，然后降压至0.3MPa保持60min；
步骤4：将步骤3得到的成品取出并烘干，即可得到防臭鞋底。
通过采用上述技术方案，可以实现工业化生产，提高生产效率。
综上所述，本发明具有以下有益效果：
1、本发明的防臭鞋底能够作用于整个鞋底而不仅仅在于防臭鞋底与脚底接触的部分，具有全面性，利用本发明利用各组分的协同作用，具有优异的吸湿快干和防臭抑菌性能；
2、利用加压工艺使得玻璃-银离子抗菌剂得以扩散，使得银离子分布更加均匀，并且增加了银离子与防臭鞋底之间的附着力，增强抗菌防臭的持久性；
3、本发明采用的制备方法可以实现工业化生产，提高整体的生产效率。
附图说明
图1为实施例1的结构示意图。
具体实施方式
参照附图对本发明做进一步说明。
实施例1：一种防臭鞋底，如图1所示，按照重量份数，包括EVA鞋底，所述EVA鞋底上设置有正面线型纤维层，弹性纤维层以及反面线型纤维层组成，其中弹性纤维层处于中间，各层通过粘结剂固定，在正面线型纤维层和反面线型纤维层涂有一层纳米氧化铜涂层，所述正面线型纤维层，弹性纤维层以及反面线型纤维层的截面均设置为沟槽状，
所述正面线圈结构层，弹性纤维层以及反面线型纤维层均包括如下组分，甲壳素纤维10份、风化壳淋积型稀土矿5份、乙基香草醛类化合物12份、酰基苯胺类化合物12份、亲水柔软助剂2份；
所述正面线圈结构层，弹性纤维层以及反面线型纤维层镶嵌有玻璃-银离子抗菌剂10份，所述玻璃-银离子抗菌剂为载体选为玻璃的银离子抗菌剂，所述玻璃：银离子抗菌剂=3:1。
所述风化壳淋积型稀土矿向江西购买，且3mm﹤粒径﹤5mm。
一种防臭鞋底的制备方法，包括如下步骤：按照重量份数称取相应的组分，
步骤1：在EVA鞋底上铺设正面线型纤维层，弹性纤维层以及反面线型纤维层，其中正面线型纤维层，弹性纤维层以及反面线型纤维层之间通过粘结剂固定；
步骤2：将玻璃-银离子抗菌剂和步骤1得到的成品加入抗菌处理罐中，升温至62℃，加压到0.2MPa，保持压力不变，持续120min；
步骤3：解除压力，将甲壳素纤维、风化壳淋积型稀土矿、乙基香草醛类化合物、酰基苯胺类化合物、亲水柔软助剂加入抗菌处理罐中，升温至62℃，加压到0.4MPa，保持压力不变，持续120min，然后降压至0.3MPa保持60min；
步骤4：将步骤3得到的成品取出并烘干，即可得到防臭鞋底。
实施例2：一种防臭鞋底，：按照重量份数，包括EVA鞋底，所述EVA鞋底上设置有正面线型纤维层，弹性纤维层以及反面线型纤维层组成，其中弹性纤维层处于中间，各层通过粘结剂固定，在正面线型纤维层和反面线型纤维层涂有一层纳米氧化铜涂层，所述正面线型纤维层，弹性纤维层以及反面线型纤维层的截面均设置为沟槽状，
所述正面线圈结构层，弹性纤维层以及反面线型纤维层均包括如下组分，甲壳素纤维15份、风化壳淋积型稀土矿7份、乙基香草醛类化合物16份、酰基苯胺类化合物16份、亲水柔软助剂3.5份；
所述正面线圈结构层，弹性纤维层以及反面线型纤维层镶嵌有玻璃-银离子抗菌剂15份，所述玻璃-银离子抗菌剂为载体选为玻璃的银离子抗菌剂，所述玻璃：银离子抗菌剂=3:1。
所述风化壳淋积型稀土矿向江西购买，且3mm﹤粒径﹤5mm。
一种防臭鞋底的制备方法，包括如下步骤：按照重量份数称取相应的组分，
步骤1：在EVA鞋底上铺设正面线型纤维层，弹性纤维层以及反面线型纤维层，其中正面线型纤维层，弹性纤维层以及反面线型纤维层之间通过粘结剂固定；
步骤2：将玻璃-银离子抗菌剂和步骤1得到的成品加入抗菌处理罐中，升温至62℃，加压到0.2MPa，保持压力不变，持续120min；
步骤3：解除压力，将甲壳素纤维、风化壳淋积型稀土矿、乙基香草醛类化合物、酰基苯胺类化合物、亲水柔软助剂加入抗菌处理罐中，升温至62℃，加压到0.4MPa，保持压力不变，持续120min，然后降压至0.3MPa保持60min；
步骤4：将步骤3得到的成品取出并烘干，即可得到防臭鞋底。
实施例3：一种防臭鞋底，：按照重量份数，包括EVA鞋底，所述EVA鞋底上设置有正面线型纤维层，弹性纤维层以及反面线型纤维层组成，其中弹性纤维层处于中间，各层通过粘结剂固定，在正面线型纤维层和反面线型纤维层涂有一层纳米氧化铜涂层，所述正面线型纤维层，弹性纤维层以及反面线型纤维层的截面均设置为沟槽状，
所述正面线圈结构层，弹性纤维层以及反面线型纤维层均包括如下组分，甲壳素纤维20份、风化壳淋积型稀土矿10份、乙基香草醛类化合物20份、酰基苯胺类化合物20份、亲水柔软助剂5份；
所述正面线圈结构层，弹性纤维层以及反面线型纤维层镶嵌有玻璃-银离子抗菌剂20份，所述玻璃-银离子抗菌剂为载体选为玻璃的银离子抗菌剂，所述玻璃：银离子抗菌剂=3:1。
所述风化壳淋积型稀土矿向江西购买，且3mm﹤粒径﹤5mm。
一种防臭鞋底的制备方法，包括如下步骤：按照重量份数称取相应的组分，
步骤1：在EVA鞋底上铺设正面线型纤维层，弹性纤维层以及反面线型纤维层，其中正面线型纤维层，弹性纤维层以及反面线型纤维层之间通过粘结剂固定；
步骤2：将玻璃-银离子抗菌剂和步骤1得到的成品加入抗菌处理罐中，升温至62℃，加压到0.2MPa，保持压力不变，持续120min；
步骤3：解除压力，将甲壳素纤维、风化壳淋积型稀土矿、乙基香草醛类化合物、酰基苯胺类化合物、亲水柔软助剂加入抗菌处理罐中，升温至62℃，加压到0.4MPa，保持压力不变，持续120min，然后降压至0.3MPa保持60min；
步骤4：将步骤3得到的成品取出并烘干，即可得到防臭鞋底。
表1为实施例1-3的抗菌性能测试结果
以上所述仅为本发明的较佳实施例，并不用于限制本发明，凡在本发明的设计构思之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (3)
1.一种防臭鞋底，其特征在于：按照重量份数，包括EVA鞋底，所述EVA鞋底上设置有正面线型纤维层，弹性纤维层以及反面线型纤维层组成，其中弹性纤维层处于中间，各层通过粘结剂固定，在正面线型纤维层和反面线型纤维层涂有一层纳米氧化铜涂层，所述正面线型纤维层，弹性纤维层以及反面线型纤维层的截面均设置为沟槽状，所述正面线圈结构层，弹性纤维层以及反面线型纤维层均包括如下组分，甲壳素纤维10-20份、风化壳淋积型稀土矿5-10份、乙基香草醛类化合物12-20份、酰基苯胺类化合物12-20份、亲水柔软助剂2-5份；所述正面线圈结构层，弹性纤维层以及反面线型纤维层镶嵌有玻璃-银离子抗菌剂10-20份，所述玻璃-银离子抗菌剂为载体选为玻璃的银离子抗菌剂，所述玻璃：银离子抗菌剂=3:1。
2.根据权利要求1所述的一种防臭鞋底，其特征在于：所述风化壳淋积型稀土矿向江西购买，且3mm﹤粒径﹤5mm。
3.如根据权利要求1-2所述的一种防臭鞋底的制备方法，其特征在于：包括如下步骤：按照重量份数称取相应的组分，
步骤1：在EVA鞋底上铺设正面线型纤维层，弹性纤维层以及反面线型纤维层，其中正面线型纤维层，弹性纤维层以及反面线型纤维层之间通过粘结剂固定；
步骤2：将玻璃-银离子抗菌剂和步骤1得到的成品加入抗菌处理罐中，升温至62℃，加压到0.2MPa，保持压力不变，持续120min；
步骤3：解除压力，将甲壳素纤维、风化壳淋积型稀土矿、乙基香草醛类化合物、酰基苯胺类化合物、亲水柔软助剂加入抗菌处理罐中，升温至62℃，加压到0.4MPa，保持压力不变，持续120min，然后降压至0.3MPa保持60min；
步骤4：将步骤3得到的成品取出并烘干，即可得到防臭鞋底。