CN109082158A - A kind of touch screen high temperature ink and preparation method thereof - Google Patents
A kind of touch screen high temperature ink and preparation method thereof Download PDFInfo
- Publication number
- CN109082158A CN109082158A CN201811289852.1A CN201811289852A CN109082158A CN 109082158 A CN109082158 A CN 109082158A CN 201811289852 A CN201811289852 A CN 201811289852A CN 109082158 A CN109082158 A CN 109082158A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- auxiliary agent
- high temperature
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of touch screen high temperature inks and preparation method thereof, including polyester modification methyl phenyl silicone resin, titanium dioxide, water-absorbing resin, pigment, ultra-fine barium sulfate, nano silica, glass powder, hexa methoxy melamine resin and auxiliary agent, the auxiliary agent includes A187 silane coupling agent, advection agent, defoaming agent and disinfection sanitizer.Ink of the invention can adsorb certain steam and fragrance during the preparation process, have certain fragrance after later period printing, while can be used as diluent after absorbing steam, without additionally adding diluent, and have extraordinary high temperature resistant and acid resistance.
Description
Technical field
The present invention relates to Printing ink producing field, in particular to a kind of touch screen high temperature ink and preparation method thereof.
Background technique
Touch screen cover-plate glass is widely used in high-end smartphones, plate as a kind of high-intensitive, damage resistant glass
The fields such as computer, flat panel TV and industrial business touch screen.OGS is one of touch screen industry future thrust.Integration touching
Control (OneGlassSolution, OGS) technology refers to the technology that ITO conductive film and sensor are directly formed on protection glass,
One block of glass plays a dual role of protecting glass and touch sensor simultaneously.Glass after OGS technical treatment is after cutting
Obtain OGS touch screen.There are the more traditional G/G touch technology of OGS technology many advantages e.g. can save a piece of glass substrate, make
Make that one of bonding process can be saved in program, to advantageously reduce production cost, improve product yield.And obtain
OGS touch screen has the characteristics that light, thin, translucency is good.But glass is easy to produce slight crack in cut place, in turn after cutting
OGS touch screen product machinery compressive resistance is caused to decline.It is generally necessary to overcome the above problem by subsequent secondary hardening process.
There can be many sharp aromas after current ink use, be affected to external environment, and product is resistance to
Acid, heat-resisting ability are poor.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of touch screen high temperature ink and preparation method thereof, Neng Gou
Certain steam and fragrance are adsorbed in preparation process, there is certain fragrance after later period printing, while absorbing can after steam
As diluent, without additionally adding diluent, and there is extraordinary high temperature resistant and acid resistance, can effectively solve the problem that existing
Deficiency in technology.
The present invention is achieved through the following technical solutions: a kind of touch screen high temperature ink, including polyester modification first
Base phenyl polysiloxane, titanium dioxide, water-absorbing resin, pigment, ultra-fine barium sulfate, nano silica, glass powder, hexa methoxy trimerization
Melamine resin and auxiliary agent, the auxiliary agent include A187 silane coupling agent, advection agent, defoaming agent and disinfection sanitizer.
Each ingredient specific gravity is respectively as follows: 50-70 parts of polyester modification methyl phenyl silicone resin, titanium as a preferred technical solution,
20-30 parts of white powder, 7-12 parts of water-absorbing resin, 6-15 parts of pigment, 1-4 parts of ultra-fine barium sulfate, 3-8 parts of nano silica, glass
2-6 parts of powder, 2-7 parts of hexa methoxy melamine resin and auxiliary agent.
The specific gravity of each auxiliary agent is respectively as follows: 1-2 parts of A187 silane coupling agent, advection agent 0.3- as a preferred technical solution,
0.8 part, 0.1-0.4 parts of defoaming agent and 1-3 parts of disinfection sanitizer.
The auxiliary agent further includes acid proofing agent as a preferred technical solution,.
The acid proofing agent is nano aluminium oxide as a preferred technical solution,.
A kind of preparation method of touch screen high temperature ink, specifically includes following steps:
Step 1: taking polyester modification methyl phenyl silicone resin, titanium dioxide, water-absorbing resin, pigment, ultra-fine barium sulfate, nanometer
The material of said components is stirred and is uniformly mixed by silica, glass powder, hexa methoxy melamine resin, is obtained
Solution one;
Step 2: auxiliary agent is added in solution one obtained above, auxiliary agent includes 1-2 parts of A187 silane coupling agent, advection agent
0.3-0.8 parts, 0.1-0.4 parts of defoaming agent and 1-3 parts of disinfection sanitizer continue to stir, obtain solution two after auxiliary agent is added;
Step 3: solution two is placed in a closed housing, casing interior is passed through hot gas source, and in hot gas source
Fragrance is added, a component is fumigated, absorbs fragrance and steam using water-absorbing resin, the water-absorbing resin shape after absorbing steam
At diluent, fumigate 20 minutes;
Step 4: can be taken off after the completion of stifling, it is put into crushing container, utilizes the crushing vane powder in crushing container
It is broken, all components are all ground into powder and are stirred again uniformly;
Step 5: dispersing 30-40min at 1500-1800rpm using dispersion machine, ground, is added using three-roller
Defoaming agent, levelling agent, are uniformly mixing to obtain host agent, and HMMM resin is added in host agent, in 500rpm
Lower dispersion 20min.
The diluent is water as a preferred technical solution,.
The beneficial effects of the present invention are: ink of the invention, can adsorb certain steam and perfume (or spice) during the preparation process
Taste has certain fragrance after later period printing, while can be used as diluent after absorbing steam, without additionally adding diluent, and
With extraordinary high temperature resistant and acid resistance.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
Any feature disclosed in this specification unless specifically stated can be equivalent or with similar purpose by other
Alternative features are replaced.That is, unless specifically stated, each feature is an example in a series of equivalent or similar characteristics
?.
Embodiment one
Ink in the present embodiment includes polyester modification methyl phenyl silicone resin, titanium dioxide, water-absorbing resin, pigment, ultra-fine
Barium sulfate, nano silica, glass powder, hexa methoxy melamine resin and auxiliary agent, the auxiliary agent include A187 silane
Coupling agent, advection agent, defoaming agent and disinfection sanitizer.
Wherein, each ingredient specific gravity is respectively as follows: 50 parts of polyester modification methyl phenyl silicone resin, 20 parts of titanium dioxide, water-absorbing resin 7
Part, 6 parts of pigment, 1 part of ultra-fine barium sulfate, 3 parts of nano silica, 2 parts of glass powder, 2 parts of hexa methoxy melamine resin with
And auxiliary agent, the specific gravity of each auxiliary agent are respectively as follows: 1 part of A187 silane coupling agent, 0.3 part of advection agent, 0.1 part of defoaming agent and sterilization and disappear
1 part of toxic agent, auxiliary agent further includes acid proofing agent, and in the present embodiment, acid proofing agent is nano aluminium oxide.
Embodiment two
Ink in the present embodiment includes polyester modification methyl phenyl silicone resin, titanium dioxide, water-absorbing resin, pigment, ultra-fine
Barium sulfate, nano silica, glass powder, hexa methoxy melamine resin and auxiliary agent, the auxiliary agent include A187 silane
Coupling agent, advection agent, defoaming agent and disinfection sanitizer.
Wherein, each ingredient specific gravity is respectively as follows: 70 parts of polyester modification methyl phenyl silicone resin, 30 parts of titanium dioxide, water-absorbing resin
12 parts, 15 parts of pigment, 4 parts of ultra-fine barium sulfate, 8 parts of nano silica, 6 parts of glass powder, 7 parts of hexa methoxy melamine resin
And auxiliary agent, the specific gravity of each auxiliary agent are respectively as follows: 2 parts of A187 silane coupling agent, 0.8 part of advection agent, 0.4 part of defoaming agent and sterilization
3 parts of disinfectant, auxiliary agent further includes acid proofing agent, and in the present embodiment, acid proofing agent is nano aluminium oxide.
The preparation method of above-described embodiment one and two is all the same, the specific steps are as follows:
(1) polyester modification methyl phenyl silicone resin, titanium dioxide, water-absorbing resin, pigment, ultra-fine barium sulfate, nano-silica are taken
The material of said components is stirred and is uniformly mixed by SiClx, glass powder, hexa methoxy melamine resin, obtains solution
One;
(2) auxiliary agent is added in solution one obtained above, auxiliary agent includes 1-2 parts of A187 silane coupling agent, advection agent 0.3-
0.8 part, 0.1-0.4 parts of defoaming agent and 1-3 parts of disinfection sanitizer continue to stir, obtain solution two after auxiliary agent is added;
(3) solution two is placed in a closed housing, casing interior is passed through hot gas source, and adds in hot gas source
Enter fragrance, a component is fumigated, absorbs fragrance and steam using water-absorbing resin, the water-absorbing resin after absorbing steam is formed
Diluent is fumigated 20 minutes;
(4) it can be taken off, be put into crushing container after the completion of fumigating, crushed using the crushing vane in crushing container, it will
All components are all ground into powder and are stirred again uniformly;
(5) disperse 30-40min at 1500-1800rpm using dispersion machine, ground using three-roller, addition disappears
Infusion, levelling agent, are uniformly mixing to obtain host agent, HMMM resin are added in host agent, at 500 rpm
Disperse 20min.
The beneficial effects of the present invention are: ink of the invention, can adsorb certain steam and perfume (or spice) during the preparation process
Taste has certain fragrance after later period printing, while can be used as diluent after absorbing steam, without additionally adding diluent, and
With extraordinary high temperature resistant and acid resistance.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
The change or replacement expected without creative work, should be covered by the protection scope of the present invention.Therefore, of the invention
Protection scope should be determined by the scope of protection defined in the claims.
Claims (7)
1. a kind of touch screen high temperature ink and preparation method thereof, it is characterised in that: including polyester modification methyl phenyl silicone resin,
Titanium dioxide, water-absorbing resin, pigment, ultra-fine barium sulfate, nano silica, glass powder, hexa methoxy melamine resin and
Auxiliary agent, the auxiliary agent include A187 silane coupling agent, advection agent, defoaming agent and disinfection sanitizer.
2. touch screen high temperature ink as described in claim 1, it is characterised in that: each ingredient specific gravity is respectively as follows: polyester modification
50-70 parts of methyl phenyl silicone resin, 20-30 parts of titanium dioxide, 7-12 parts of water-absorbing resin, 6-15 parts of pigment, ultra-fine barium sulfate 1-4
Part, 3-8 parts of nano silica, 2-6 parts of glass powder, 2-7 parts of hexa methoxy melamine resin and auxiliary agent.
3. touch screen high temperature ink as described in claim 1, it is characterised in that: the specific gravity of each auxiliary agent is respectively as follows: A187 silicon
1-2 parts of alkane coupling agent, 0.3-0.8 parts of advection agent, 0.1-0.4 parts of defoaming agent and 1-3 parts of disinfection sanitizer.
4. touch display screen ink as described in claim 1, it is characterised in that: the auxiliary agent further includes acid proofing agent.
5. touch display screen ink as claimed in claim 4, it is characterised in that: the acid proofing agent is nano aluminium oxide.
6. a kind of preparation method of touch screen high temperature ink, which is characterized in that specifically include following steps:
Step 1: taking polyester modification methyl phenyl silicone resin, titanium dioxide, water-absorbing resin, pigment, ultra-fine barium sulfate, nano-silica
The material of said components is stirred and is uniformly mixed by SiClx, glass powder, hexa methoxy melamine resin, obtains solution
One;
Step 2: auxiliary agent is added in solution one obtained above, auxiliary agent includes 1-2 parts of A187 silane coupling agent, advection agent 0.3-
0.8 part, 0.1-0.4 parts of defoaming agent and 1-3 parts of disinfection sanitizer continue to stir, obtain solution two after auxiliary agent is added;
Step 3: solution two is placed in a closed housing, casing interior is passed through hot gas source, and is added in hot gas source
Fragrance fumigates a component, absorbs fragrance and steam using water-absorbing resin, the water-absorbing resin after absorbing steam forms dilute
Agent is released, is fumigated 20 minutes;
Step 4: can be taken off after the completion of stifling, it is put into crushing container, is crushed using the crushing vane in crushing container, it will
All components are all ground into powder and are stirred again uniformly;
Step 5: dispersing 30-40min at 1500-1800rpm using dispersion machine, ground using three-roller, defoaming is added
Agent, levelling agent, are uniformly mixing to obtain host agent, and HMMM resin is added in host agent, divides at 500 rpm
Dissipate 20min.
7. the preparation method of touch screen high temperature ink as claimed in claim 5, it is characterised in that: the diluent is water.