CN109370300A - A kind of touch display screen ink - Google Patents
A kind of touch display screen ink Download PDFInfo
- Publication number
- CN109370300A CN109370300A CN201811289836.2A CN201811289836A CN109370300A CN 109370300 A CN109370300 A CN 109370300A CN 201811289836 A CN201811289836 A CN 201811289836A CN 109370300 A CN109370300 A CN 109370300A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- display screen
- touch display
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of touch display screen ink, including polyester modification methyl phenyl silicone resin, titanium dioxide, active carbon powder, pigment, ultra-fine barium sulfate, nano silica, glass powder, hexa methoxy melamine resin and auxiliary agent, the auxiliary agent includes A187 silane coupling agent, advection agent, defoaming agent, diluent and disinfection sanitizer.The present invention has extraordinary acidproof and high temperature resistance, and the function of peculiar smell can be effectively played using active carbon powder, the solid rear smell generated of later period ink is reduced, and by increasing fungicedal powder, increase the bactericidal effect of later period touch screen, keeps panel clean and tidy.
Description
Technical field
The present invention relates to Printing ink producing field, in particular to a kind of touch display screen ink.
Background technique
Touch screen cover-plate glass is widely used in high-end smartphones, plate as a kind of high-intensitive, damage resistant glass
The fields such as computer, flat panel TV and industrial business touch screen.OGS is one of touch screen industry future thrust.Integration touching
Control (OneGlassSolution, OGS) technology refers to the technology that ITO conductive film and sensor are directly formed on protection glass,
One block of glass plays a dual role of protecting glass and touch sensor simultaneously.Glass after OGS technical treatment is after cutting
Obtain OGS touch screen.There are the more traditional G/G touch technology of OGS technology many advantages e.g. can save a piece of glass substrate, make
Make that one of bonding process can be saved in program, to advantageously reduce production cost, improve product yield.And obtain
OGS touch screen has the characteristics that light, thin, translucency is good.But glass is easy to produce slight crack in cut place, in turn after cutting
OGS touch screen product machinery compressive resistance is caused to decline.It is generally necessary to overcome the above problem by subsequent secondary hardening process.
Current touch screen ink can have dense strong sharp aroma after smearing, need a very long time
It can dissipate, and touch screen ink is after solid, it is acidproof, heat-resisting ability is poor, a large amount of bacterium is had using surface long afterwards
Adherency needs external fungicide to be sterilized, very inconvenient.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of touch display screen ink, can quick adsorption fall ink sheet
The sharp aroma of body, while will not influence the normal printing of ink, it will not influence the color of ink, and have and sterilize well,
High temperature resistant and acid resistance.
The present invention is achieved through the following technical solutions: a kind of touch display screen ink, including polyester modification methyl
Phenyl polysiloxane, titanium dioxide, active carbon powder, pigment, ultra-fine barium sulfate, nano silica, glass powder, hexa methoxy trimerization
Melamine resin and auxiliary agent.
As a preferred technical solution, the auxiliary agent include A187 silane coupling agent, advection agent, defoaming agent, diluent with
And disinfection sanitizer.
Each ingredient specific gravity is respectively as follows: 50-70 parts of polyester modification methyl phenyl silicone resin, titanium as a preferred technical solution,
20-30 parts of white powder, 5-12 parts of active carbon powder, 6-15 parts of pigment, 1-4 parts of ultra-fine barium sulfate, 3-8 parts of nano silica, glass
2-6 parts of glass powder, 2-7 parts of hexa methoxy melamine resin and auxiliary agent.
The specific gravity of each auxiliary agent is respectively as follows: 1-2 parts of A187 silane coupling agent, advection agent 0.3- as a preferred technical solution,
0.8 part, 0.1-0.4 parts of defoaming agent, 3-9 parts of diluent and 1-3 parts of disinfection sanitizer.
The active carbon powder is superfines as a preferred technical solution, is added by multiple tracks dispersion and fining technique
Enter to inside and stir evenly, the active carbon powder after refinement is the fine particle of black.
The levelling agent is polyether modified siloxane as a preferred technical solution, and the defoaming agent is modified poly- silicon oxygen
Alkane, the diluent are ethyl alcohol or water, and the disinfection sanitizer is herbal mediciment.
The disinfection sanitizer is Chinese medicine wormwood as a preferred technical solution, which is ground into
It after powdered, is finally putting into entire ink, then is stirred for being mixed into ink.
The auxiliary agent further includes acid proofing agent as a preferred technical solution,.
The acid proofing agent is nano aluminium oxide as a preferred technical solution,.
The beneficial effects of the present invention are: the present invention has extraordinary acidproof and high temperature resistance, and utilize active carbon
Powder can effectively play the function of peculiar smell, reduce the solid rear smell generated of later period ink, and by increasing fungicedal powder,
Increase the bactericidal effect of later period touch screen, keeps panel clean and tidy.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
Any feature disclosed in this specification unless specifically stated can be equivalent or with similar purpose by other
Alternative features are replaced.That is, unless specifically stated, each feature is an example in a series of equivalent or similar characteristics
?.
The present invention has removes odor function well, and has extraordinary heat-resisting ability and acidproof effect,
Later period spray it is solid after there is very long service life, lower mask body introduces main component of the invention, specifically includes polyester
Modifying methylphenyl silicone resin, titanium dioxide, active carbon powder, pigment, ultra-fine barium sulfate, nano silica, glass powder, pregnancy
Oxygroup melamine resin and auxiliary agent.
In the present embodiment, auxiliary agent includes A187 silane coupling agent, advection agent, defoaming agent, diluent and disinfection sanitizer,
Each ingredient specific gravity be respectively as follows: 50 parts of polyester modification methyl phenyl silicone resin, 20 parts of titanium dioxide, 5 parts of active carbon powder, 6 parts of pigment,
1 part of ultra-fine barium sulfate, 3 parts of nano silica, 2 parts of glass powder, 2 parts of hexa methoxy melamine resin and auxiliary agent.
The specific gravity of each auxiliary agent is respectively as follows: 1 part of A187 silane coupling agent, 0.3 part of advection agent, 0.1 part of defoaming agent, diluent 3
Part and 1 part of disinfection sanitizer.
Alternatively, auxiliary agent includes A187 silane coupling agent, advection agent, defoaming agent, diluent and disinfection sanitizer, each ingredient
Specific gravity is respectively as follows: 70 parts of polyester modification methyl phenyl silicone resin, 30 parts of titanium dioxide, 12 parts of active carbon powder, 15 parts of pigment, ultra-fine
4 parts of barium sulfate, 8 parts of nano silica, 6 parts of glass powder, 7 parts of hexa methoxy melamine resin and auxiliary agent, each auxiliary agent
Specific gravity is respectively as follows: 2 parts of A187 silane coupling agent, 0.8 part of advection agent, 0.4 part of defoaming agent, 9 parts of diluent and disinfection sanitizer 3
Part.
In the present embodiment, active carbon powder is superfines, is added to inside and stirs by multiple tracks dispersion and fining technique
It mixes uniformly, the active carbon powder after refinement is the fine particle of black.Active carbon powder after above-mentioned complete refinement is added to
It after in entire ink, is adequately stirred, which can be placed on last progress, and the purpose is to make the ink surface layer after smearing
There is one layer of subtle adsorption layer, the sharp aroma and external sharp aroma that absorption generates itself.
Wherein, levelling agent is polyether modified siloxane, the defoaming agent be modified polyorganosiloxane, diluent be ethyl alcohol or
Water, the disinfection sanitizer are herbal mediciment, and disinfection sanitizer is Chinese medicine wormwood, which is carried out being ground into powder
It after shape, is finally putting into entire ink, then is stirred for being mixed into ink.When facilitating finishing operations, a sterilization is realized
Purpose.
In the present embodiment, auxiliary agent further includes acid proofing agent, and acid proofing agent is nano aluminium oxide, or using other acid proofing agents
It can be with herein its purpose is to increase the acid resistance in ink later period, the ingredient of specific acid proofing agent is not repeated specifically.
The beneficial effects of the present invention are:
1, the present invention has extraordinary acidproof and high temperature resistance, and can be effectively played using active carbon powder
The function of peculiar smell reduces the solid rear smell generated of later period ink；
2 and by increase fungicedal powder, increase later period touch screen bactericidal effect, keep panel it is clean and tidy, use process is more
What is added is healthy and safe.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
The change or replacement expected without creative work, should be covered by the protection scope of the present invention.Therefore, of the invention
Protection scope should be determined by the scope of protection defined in the claims.
Claims (9)
1. a kind of touch display screen ink, it is characterised in that: including polyester modification methyl phenyl silicone resin, titanium dioxide, active carbon
Powder, pigment, ultra-fine barium sulfate, nano silica, glass powder, hexa methoxy melamine resin and auxiliary agent.
2. touch display screen ink as described in claim 1, it is characterised in that: the auxiliary agent include A187 silane coupling agent,
Advection agent, defoaming agent, diluent and disinfection sanitizer.
3. touch display screen ink as described in claim 1, it is characterised in that: each ingredient specific gravity is respectively as follows: polyester modification first
50-70 parts of base phenyl polysiloxane, 20-30 parts of titanium dioxide, 5-12 parts of active carbon powder, 6-15 parts of pigment, ultra-fine barium sulfate 1-4
Part, 3-8 parts of nano silica, 2-6 parts of glass powder, 2-7 parts of hexa methoxy melamine resin and auxiliary agent.
4. touch display screen ink as claimed in claim 2, it is characterised in that: the specific gravity of each auxiliary agent is respectively as follows: A187 silane
1-2 parts of coupling agent, 0.3-0.8 parts of advection agent, 0.1-0.4 parts of defoaming agent, 3-9 parts of diluent and 1-3 parts of disinfection sanitizer.
5. touch display screen ink as described in claim 1, it is characterised in that: the active carbon powder is superfines,
It is added to inside and stirs evenly by multiple tracks dispersion and fining technique, the active carbon powder after refinement is the fine particle of black.
6. touch display screen ink as claimed in claim 2, it is characterised in that: the levelling agent is polyether modified siloxane,
The defoaming agent is modified polyorganosiloxane, and the diluent is ethyl alcohol or water, and the disinfection sanitizer is herbal mediciment.
7. touch display screen ink as claimed in claim 6, it is characterised in that: the disinfection sanitizer is Chinese medicine wormwood, should
It after Chinese medicine wormwood is pulverized into powder, is finally putting into entire ink, then is stirred for being mixed into ink.
8. touch display screen ink as claimed in claim 2, it is characterised in that: the auxiliary agent further includes acid proofing agent.
9. touch display screen ink as claimed in claim 8, it is characterised in that: the acid proofing agent is nano aluminium oxide.