CN109020216A - Cordierite glaze and preparation method thereof - Google Patents
Cordierite glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109020216A CN109020216A CN201811136871.0A CN201811136871A CN109020216A CN 109020216 A CN109020216 A CN 109020216A CN 201811136871 A CN201811136871 A CN 201811136871A CN 109020216 A CN109020216 A CN 109020216A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- cordierite
- component
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cordierite glaze and preparation method thereof, the component and each component mass parts contained in glaze used in cordierite glaze is as follows: 20-30 parts of cordierite, 20-30 parts of spodumene, 8-12 parts of kaolin, 10-15 parts of calcinated talc powder, 2-4 parts of barium carbonate.2-4 parts of calcium carbonate, 1-2 parts of magnesium carbonate.The present invention adapts to resistance to hot pot, can pass through 300-400 rapid heat cycle performance test.
Description
Technical field
The present invention relates to a kind of cordierite glaze and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of cordierite glaze is provided, it is adapted to
Resistance to hot pot can pass through 300-400 rapid heat cycle performance test.
In order to solve the above technical problems, the technical scheme is that a kind of cordierite glaze, in glaze used in it
The component and each component mass parts contained is as follows:
20-30 parts of cordierite,
20-30 parts of spodumene,
8-12 parts of kaolin,
10-15 parts of calcinated talc powder,
2-4 parts of barium carbonate,
2-4 parts of calcium carbonate,
1-2 parts of magnesium carbonate.
The present invention also provides a kind of preparation method of cordierite glaze, the step of method in contain
S1: it stocks up according to the mass parts of each component and each component；
S2: according to ball: water: mass ratio=1.5:0.7:1 of material wet ball grinding 10~12 hours, then crosses 160 meshes
Net, then it is tuned into the glaze slip that concentration is 40-50 Baume degrees；
S3: green compact glazing enters kiln after dry, burns finished product by 1160-1200 DEG C of kiln temperature.
After above-mentioned technical proposal, cordierite glaze of the invention, glaze paint is semimat glaze colours, it adapts to heat-resisting
Pot, can pass through 300-400 rapid heat cycle performance test.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of cordierite glaze, the component and each component mass parts contained in glaze used in it are as follows:
20 parts of cordierite,
20 parts of spodumene,
8 parts of kaolin,
10 parts of calcinated talc powder,
2 parts of barium carbonate,
2 parts of calcium carbonate,
1 part of magnesium carbonate.
Contain in the step of preparation method of the cordierite glaze, method
S1: it stocks up according to the mass parts of each component and each component；
S2: according to ball: water: mass ratio=1.5:0.7:1 of material wet ball grinding 10 hours, then crosses 160 mesh screens, then
It is tuned into the glaze slip that concentration is 40-50 Baume degrees；
S3: green compact glazing enters kiln after dry, burns finished product by 1160-1200 DEG C of kiln temperature.
Embodiment two
A kind of cordierite glaze, the component and each component mass parts contained in glaze used in it are as follows:
30 parts of cordierite,
30 parts of spodumene,
12 parts of kaolin,
15 parts of calcinated talc powder,
4 parts of barium carbonate,
4 parts of calcium carbonate,
2 parts of magnesium carbonate.
Contain in the step of preparation method of the cordierite glaze, method
S1: it stocks up according to the mass parts of each component and each component；
S2: according to ball: water: mass ratio=1.5:0.7:1 of material wet ball grinding 12 hours, then crosses 160 mesh screens, then
It is tuned into the glaze slip that concentration is 40-50 Baume degrees；
S3: green compact glazing enters kiln after dry, burns finished product by 1160-1200 DEG C of kiln temperature.
Embodiment three
A kind of cordierite glaze, the component and each component mass parts contained in glaze used in it are as follows:
25 parts of cordierite,
25 parts of spodumene,
10 parts of kaolin,
12 parts of calcinated talc powder,
3 parts of barium carbonate,
3 parts of calcium carbonate,
2 parts of magnesium carbonate.
Contain in the step of preparation method of the cordierite glaze, method
S1: it stocks up according to the mass parts of each component and each component；
S2: according to ball: water: mass ratio=1.5:0.7:1 of material wet ball grinding 11 hours, then crosses 160 mesh screens, then
It is tuned into the glaze slip that concentration is 40-50 Baume degrees；
S3: green compact glazing enters kiln after dry, burns finished product by 1160-1200 DEG C of kiln temperature.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. a kind of cordierite glaze, it is characterised in that the component and each component mass parts contained in glaze used in it is as follows:
20-30 parts of cordierite,
20-30 parts of spodumene,
8-12 parts of kaolin,
10-15 parts of calcinated talc powder,
2-4 parts of barium carbonate,
2-4 parts of calcium carbonate,
1-2 parts of magnesium carbonate.
2. a kind of preparation method of cordierite glaze as described in claim 1, it is characterised in that contain in the step of method
S1: it stocks up according to the mass parts of each component and each component；
S2: according to ball: water: mass ratio=1.5:0.7:1 of material wet ball grinding 10~12 hours, then crosses 160 mesh screens, then
It is tuned into the glaze slip that concentration is 40-50 Baume degrees；
S3: green compact glazing enters kiln after dry, burns finished product by 1160-1200 DEG C of kiln temperature.