CN108998855A - 一种引诱型渔网线的制备方法 - Google Patents
一种引诱型渔网线的制备方法 Download PDFInfo
- Publication number
- CN108998855A CN108998855A CN201810704667.8A CN201810704667A CN108998855A CN 108998855 A CN108998855 A CN 108998855A CN 201810704667 A CN201810704667 A CN 201810704667A CN 108998855 A CN108998855 A CN 108998855A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- luring
- fishing lines
- type fishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种引诱型渔网线的制备方法，包括如下组分：乙烯‑醋酸乙烯酯共聚物10～30份、高分子量聚乙烯90～100份、白油10～15份、环保颜料1～3份、增塑剂10～15份、滑石粉1～5份、丁香油1～5份、食用明胶5～10份、甜菜渣1～5份、陈皮1～5份、香椿叶粉1～5份、大蒜素1～5份、芫荽1～5份、玉米蛋白粉5～10份、水解蛋白1～2份、芦荟凝胶3～5份、玉米肽1～3份、微晶纤维素2～4份、二羟基丙酮2～4份、诱食剂1～3份、乳木果油0.5～1份、透明质酸0.5～1份、茶多酚0.5～1份、亚麻籽胶1～2份、珠光剂2～4份、大豆卵磷脂0.5～1份，作为主要原料，添加丝胶肽、窖泥等辅助诱鱼成分，利用鱼类的取食和光趋特性，制成多种引诱型渔网，提高捕鱼效率。
Description
技术领域
本发明属于渔具领域，具体涉及一种引诱型渔网线的制备方法。
背景技术
随着捕捞渔业的日益发展，人们逐渐利用鱼类的进食和光趋特性，利用渔灯和诱饵辅助捕捞作业，来提高捕获量。目前渔民大多使用土法制作饵料，比如用蚯蚓、面粉虫等活体诱饵，但是活体诱饵不仅针对的鱼类范围较窄，也且比较难采集，而无法长期存储；另一些则用粮食结合酒精等辅料搅拌作为诱饵，价格低廉，但是在大中型湖泊中钓鱼，由于水深，水域广阔，单纯的诱食剂由于亲水性太强，缺少载体，在水中浸泡后会很快被水流冲散，因此诱鱼效果不好，浪费饵料且效率不高。使用渔灯，利用鱼类的光趋特性，辅助捕捞，效率不高。光的扩散性不强，只集中在很小的范围内，且浪费电能。
发明内容
本发明的目的是针对现有的问题，提供了一种引诱型渔网线的制备方法。
本发明通过以下技术方案实现：
一种引诱型渔网线，由以下重量份的原料制成：乙烯-醋酸乙烯脂共聚物10～30份、高分子量聚乙烯90～100份、白油10～15份、环保颜料1～3份、增塑剂10～15份、滑石粉1～5份、丁香油1～5份、食用明胶5～10份、甜菜渣1～5份、陈皮1～5份、香椿叶粉1～5份、大蒜素1～5份、芫荽1～5份玉米蛋白粉5～10份、水解蛋白1～2份、芦荟凝胶3～5份、玉米肽1～3份、微晶纤维素2～4份、二羟基丙酮2～4份、诱食剂1～3份、乳木果油0.5～1份、透明质酸0.5～1份、茶多酚0.5～1份、亚麻籽胶1～2份、珠光剂2～4份、大豆卵磷脂0.5～1份。
一种引诱型渔网线的制备方法，包括以下步骤：(1)分别将乙烯-醋酸乙烯脂共聚物、高分子量聚乙烯、白油、环保颜料、增塑剂、滑石粉、丁香油、食用明胶、甜菜渣、陈皮、香椿叶粉、大蒜素、芫荽、玉米蛋白粉、水解蛋白、芦荟凝胶、玉米肽、微晶纤维素、二羟基丙酮、诱食剂、乳木果油、透明质酸、茶多酚、亚麻籽胶、珠光剂、大豆卵磷脂加入到混合机搅拌均匀，静置30min至相平衡；(2)将混合物在密炼机中共混10～15min，温度为160℃，共混物熔体骤冷至室温并粉碎成粒状，得颗粒料；(3)将颗粒料投入挤出机中，物料在料筒中受到温度和剪切力的作用被熔融，并由螺杆推向机头，熔融的物料经机头的喷丝板喷出成丝，经冷却水槽冷却，再经热牵伸、定型热处理、卷取，再以单丝为基本单元，采用常规渔网线的制造工艺编捻，即得。
进一步的，第(1)步中所述的诱食剂是由以下重量份数的组分构成:窖泥5～10份、1～3份、高梁粉10～15份、草莓酒0.5～1份、富硒酵母0.5～1份、大豆分离蛋白1～2份、丁香粉5～10份、细辛粉1～2份、豆粕1～2份、甲壳素1～2份、小茴香粉0.5～1份、山药多糖0.5～1份、紫蕊草粉1～2份、甘氨酸三甲内酯0.5～1份、茶树精油0.5～1份。
进一步的，第(1)步中所述的珠光剂是由以下重量份数的组分构成：所述的珠光剂是由以下重量份数的组分构成：香豆素11份、淀粉黄原酸酯5份、亚硫酸镁5份、乙酸戊酯9份、大豆卵磷脂3份、醋酸纤维素9份、正己醇5份。
进一步的，第(3)步中所述的挤出温度为：第一段，180～190℃；第二段，190～200℃；第三段，200～210℃；末段，210～215℃。
进一步的，第(3)中所述的热牵伸，第一牵伸辊压力为0.7～0.95bar、第二牵伸辊压力为2.65～3.5bar，然后在85～95℃下进行烘干，然后使用卷绕辊进行卷绕，第一卷绕辊转速为3000m/min，第二卷绕辊转速为3500m/min，第三卷绕辊转速为3700m/min，进行进一步牵伸。
本发明的有益效果：
本发明提供的一种引诱型渔网线的制备过程中，在配方中加入玉米蛋白粉、食用明胶、芦荟凝胶作为主料，使得产品具有很好的降解性，使用过程安全可靠，不会对环境造成污染；同时改变了诱食剂的配方，增加丁香油、甘氨酸三甲内酯等成分，气味好，易于吸引鱼类，便于捕捞，且成本不高。
本发明相比现有技术具有以下优点：
本发明所述的引诱型渔网线可以用于编捻渔网，无论是淡水还是海水都能适用。它既能起渔网捕捞作用又能诱鱼，并能集中诱鱼，提高上鱼速度，诱鱼功能的使用时间长。以玉米蛋白粉、食用明胶及芦荟凝胶作为主要原料，以丁香油、二羟基丙酮作为增塑剂，添加丝胶肽、甘氨酸三甲内酯、等诱鱼成分，根据鱼类品种的取食特性，制成利用鱼的取食和光趋特性的渔网线，对鱼的味觉感官诱惑力大，无需添加额外的易分散的诱食剂，可循环使用。
具体实施方式
下面用具体实施例说明本发明，但并不是对本发明的限制。
实施例1
一种引诱型渔网线，由以下重量份的原料制成：乙烯-醋酸乙烯脂共聚物15份、高分子量聚乙烯100份、白油10份、环保颜料1份、增塑剂10份、滑石粉3份、丁香油5份、食用明胶5份、甜菜渣3份、陈皮3份、香椿叶粉3份、大蒜素3份、芫荽3份、玉米蛋白粉5份、水解蛋白1份、芦荟凝胶3份、玉米肽2份、微晶纤维素2份、二羟基丙酮3份、诱食剂3份、乳木果油1份、透明质酸1份、茶多酚1份、亚麻籽胶1份、珠光剂3份、大豆卵磷脂0.5份。
一种引诱型渔网线的制备方法，包括以下步骤：(1)分别将乙烯-醋酸乙烯脂共聚物、高分子量聚乙烯、白油、环保颜料、增塑剂、滑石粉、丁香油、食用明胶、甜菜渣、陈皮、香椿叶粉、大蒜素、芫荽、玉米蛋白粉、水解蛋白、芦荟凝胶、玉米肽、微晶纤维素、二羟基丙酮、诱食剂、乳木果油、透明质酸、茶多酚、亚麻籽胶、珠光剂、大豆卵磷脂加入到混合机搅拌均匀，静置30min至相平衡；(2)将混合物在密炼机中共混15min，温度为160℃，共混物熔体骤冷至室温并粉碎成粒状，得颗粒料；(3)将颗粒料投入挤出机中，物料在料筒中受到温度和剪切力的作用被熔融，并由螺杆推向机头，熔融的物料经机头的喷丝板喷出成丝，经冷却水槽冷却，再经热牵伸、定型热处理、卷取，再以单丝为基本单元，采用常规渔网线的制造工艺编捻，即得。
进一步的，第(1)步中所述的诱食剂是由以下重量份数的组分构成:窖泥5份、高梁粉10份、草莓酒1份、富硒酵母1份、大豆分离蛋白2份、丁香粉5份、细辛粉2份、豆粕2份、甲壳素2份、小茴香粉1份、山药多糖1份、紫蕊草粉2份、甘氨酸三甲内酯0.5份、茶树精油1份。
进一步的，第(1)步中所述的珠光剂是由以下重量份数的组分构成：所述的珠光剂是由以下重量份数的组分构成：香豆素11份、淀粉黄原酸酯5份、亚硫酸镁5份、乙酸戊酯9份、大豆卵磷脂3份、醋酸纤维素9份、正己醇5份。
进一步的，第(3)步中所述的挤出温度为：第一段，180～190℃；第二段，190～200℃；第三段，200～210℃；末段，210～215℃。
进一步的，第(3)中所述的热牵伸，第一牵伸辊压力为0.8bar、第二牵伸辊压力为3.0bar，然后在90℃下进行烘干，然后使用卷绕辊进行卷绕，第一卷绕辊转速为3000m/min，第二卷绕辊转速为3500m/min，第三卷绕辊转速为3700m/min，进行进一步牵伸。
实施例2
一种引诱型渔网线，由以下重量份的原料制成：乙烯-醋酸乙烯脂共聚物10份、高分子量聚乙烯100份、白油10份、环保颜料1份、增塑剂10份、滑石粉3份、丁香油5份、食用明胶5份、甜菜渣3份、陈皮3份、香椿叶粉3份、大蒜素3份、芫荽3份、玉米蛋白粉5份、水解蛋白1份、芦荟凝胶3份、玉米肽2份、微晶纤维素2份、二羟基丙酮3份、诱食剂3份、乳木果油1份、透明质酸1份、茶多酚1份、亚麻籽胶1份、珠光剂3份、大豆卵磷脂0.5份。
一种引诱型渔网线的制备方法，包括以下步骤：(1)分别将乙烯-醋酸乙烯脂共聚物、高分子量聚乙烯、白油、环保颜料、增塑剂、滑石粉、丁香油、食用明胶、甜菜渣、陈皮、香椿叶粉、大蒜素、芫荽、玉米蛋白粉、水解蛋白、芦荟凝胶、玉米肽、微晶纤维素、二羟基丙酮、诱食剂、乳木果油、透明质酸、茶多酚、亚麻籽胶、珠光剂、大豆卵磷脂加入到混合机搅拌均匀，静置30min至相平衡；(2)将混合物在密炼机中共混15min，温度为160℃，共混物熔体骤冷至室温并粉碎成粒状，得颗粒料；(3)将颗粒料投入挤出机中，物料在料筒中受到温度和剪切力的作用被熔融，并由螺杆推向机头，熔融的物料经机头的喷丝板喷出成丝，经冷却水槽冷却，再经热牵伸、定型热处理、卷取，再以单丝为基本单元，采用常规渔网线的制造工艺编捻，即得。
进一步的，第(1)步中所述的诱食剂是由以下重量份数的组分构成:丝胶肽4份、窖泥10份、高梁粉15份、草莓酒1份、富硒酵母1份、大豆分离蛋白2份、丁香粉10份、细辛粉2份、豆粕2份、甲壳素2份、小茴香粉1份、山药多糖1份、紫蕊草粉1份、甘氨酸三甲内酯0.5份、茶树精油1份。
进一步的，第(1)步中所述的珠光剂是由以下重量份数的组分构成：所述的珠光剂是由以下重量份数的组分构成：香豆素11份、淀粉黄原酸酯5份、亚硫酸镁5份、乙酸戊酯9份、大豆卵磷脂3份、醋酸纤维素9份、正己醇5份。
进一步的，第(3)步中所述的挤出温度为：第一段，180～190℃；第二段，190～200℃；第三段，200～210℃；末段，210～215℃。
进一步的，第(3)中所述的热牵伸，第一牵伸辊压力为0.8bar、第二牵伸辊压力为3.0bar，然后在90℃下进行烘干，然后使用卷绕辊进行卷绕，第一卷绕辊转速为3000m/min，第二卷绕辊转速为3500m/min，第三卷绕辊转速为3700m/min，进行进一步牵伸。
对比例1
本对比例与实施例2相比，在原料称取步骤中，省去诱食剂成分，除此外的方法步骤均相同。
对比例2
本对比例与实施例2相比，在原料称取步骤中，省去珠光剂成分，除此外的方法步骤均相同。
表1各实施例和对比例所制备渔网线的力学性能
注：上表1中所述的断裂强度和结节强度均是通过英国INSTRON～4466型强力试验机测得，测试时控制温度条件为20±2℃，相对湿度控制为50±5%，控制拉伸的速度为300mm/min，长度为600mm。鱼诱引率采用，进入静态投放渔网的各种种类鱼的数目占该水域鱼类总数目的百分比计算可得。
由上表1可以看出，本发明处理工艺制得的渔网线对鱼类引诱性能得到了有效的改善，同时其断裂伸长率、断裂强度、结节强度控制较好，与原性能相差无几。鱼类更易入网，效果明显。
本发明中所描述的具体实施例仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
尽管对本发明已作出了详细的说明并引证了一些具体实施例,但是对本领域熟练技术人员来说,只要不离开木发明的精神和范围可作各种变化或修正是显然的。
Claims (6)
1.一种引诱型渔网线的制备方法，其特征在于，由下列重量份数的原料制成：
乙烯-醋酸乙烯脂共聚物10～30份、高分子量聚乙烯90～100份、白油10～15份、环保颜料1～3份、增塑剂10～15份、滑石粉1～5份、丁香油1～5份、食用明胶5～10份、甜菜渣1～5份、陈皮1～5份、香椿叶粉1～5份、大蒜素1～5份、芫荽1～5份、玉米蛋白粉5～10份、水解蛋白1～2份、芦荟凝胶35份、玉米肽1～3份、微晶纤维素2～4份、二羟基丙酮2～4份、诱食剂1～3份、乳木果油0.5～1份、透明质酸0.5～1份、茶多酚0.5～1份、亚麻籽胶1～2份、珠光剂2～4份、大豆卵磷脂0.5～1份。
2.根据权利要求1所述的一种引诱型渔网线的制备方法，其特征在于，所述的诱食剂是由以下重量份数的组分构成:窖泥5～10份、1～3份、高梁粉10～15份、草莓酒0.5～1份、富硒酵母0.5～1份、大豆分离蛋白1～2份、丁香粉5～10份、细辛粉1～2份、豆粕1～2份、甲壳素1～2份、小茴香粉0.5～1份、山药多糖0.5～1份、紫蕊草粉1～2份、甘氨酸三甲内酯0.5～1份、茶树精油0.5～1份。
3.根据权利要求1所述的一种引诱型渔网线的制备方法，其特征在于，所述的珠光剂是由以下重量份数的组分构成：香豆素11份、淀粉黄原酸酯5份、亚硫酸镁5份、乙酸戊酯9份、大豆卵磷脂3份、醋酸纤维素9份、正己醇5份。
4.根据权利要求1所述的一种引诱型渔网线的制备方法，其特征在于，包括以下步骤：(1)分别将乙烯-醋酸乙烯脂共聚物、高分子量聚乙烯、白油、环保颜料、增塑剂、滑石粉、丁香油、食用明胶、甜菜渣、陈皮、香椿叶粉、大蒜素、芫荽、玉米蛋白粉、水解蛋白、芦荟凝胶、玉米肽、微晶纤维素、二羟基丙酮、诱食剂、乳木果油、透明质酸、茶多酚、滑石粉、亚麻籽胶、珠光剂、大豆卵磷脂加入到混合机搅拌均匀，静置30min至相平衡，将混合物在密炼机中共混10～15min，温度为170℃，共混物熔体骤冷至室温并粉碎成粒状，得颗粒料；(4)将颗粒料投入挤出机中，物料在料筒中受到温度和剪切力的作用被熔融，并由螺杆推向机头，熔融的物料经机头的喷丝板喷出成丝，经冷却水槽冷却，再经热牵伸、定型热处理、卷取，再以单丝为基本单元，采用常规渔网线的制造工艺编捻，即得。
5.根据权利要求2所述的一种引诱型渔网线的制备方法，其特征在于：所述步骤(4)中挤出温度为：第一段，180～190℃；第二段，190～200℃；第三段，200～210℃；末段，210～215℃。
6.根据权利要求2所述的一种引诱型渔网线的制备方法，其特征在于：所述步骤(4)中热牵伸，第一牵伸辊压力为0.7～0.95bar、第二牵伸辊压力为2.65～3.5bar，然后在85～95℃下进行烘干，然后使用卷绕辊进行卷绕，第一卷绕辊转速为3000m/min，第二卷绕辊转速为3500m/min，第三卷绕辊转速为3700m/min，进行进一步牵伸。