CN108977988A - Sunscreen fabric and preparation method thereof - Google Patents
Sunscreen fabric and preparation method thereof Download PDFInfo
- Publication number
- CN108977988A CN108977988A CN201810981184.2A CN201810981184A CN108977988A CN 108977988 A CN108977988 A CN 108977988A CN 201810981184 A CN201810981184 A CN 201810981184A CN 108977988 A CN108977988 A CN 108977988A
- Authority
- CN
- China
- Prior art keywords
- sun
- fiber
- parts
- proof
- weft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application discloses a kind of sunscreen fabric, the sunscreen fabric is interweaved by warp and weft, and the warp is sun-proof fiber blend yarn, and the weft is polyester fiber mixed yarn；The raw material of the sun-proof fiber blend yarn includes: 40~50 parts of polyvinyl alcohol, washs 35~45 parts of nitrile composite fibre, 20~30 parts of flaxen fiber, 10~15 parts of titanium dioxide, 8~12 parts of ceramic powder by weight；The raw material of the polyester fiber mixed yarn includes: super 60~70 parts of imitative cotton polyester fiber, 20~30 parts of viscose rayon by weight.Sunscreen fabric of the invention, warp are sun-proof fiber blend yarn, and weft is polyester fiber mixed yarn.Due to having the functional fiber of a variety of extra fine quality numbers, it is provided simultaneously with ultraviolet reflection agent, can effectively realize sun-screening function, so that fabric itself integrates sun-proof, comfort.
Description
Technical field
The application belongs to fabric processing technique field, more particularly to a kind of sunscreen fabric and preparation method thereof.
Background technique
With the improvement of the quality of life, requirement of the people to dress-goods is also higher and higher, weather caused by greenhouse effects
Continuous anomalous variation so that being projected by atmosphere, the ultraviolet light in the sunlight on ground is more more and more intense, be people life
Work brings inconvenience.For the people for being engaged in outdoor activities, excessive exposure in the sun, not only results in colour of skin change
It is black, while can also cause the skin problems such as color spot, freckle, What is more can cause the potential risk of cutaneum carcinoma.
Have many sun-proof clothes appearance for having and resisting ultraviolet light function at present, but the quality good and the bad of such product is not
Together or sun-proof result is bad or gas permeability is bad causes clothing sultry, is not suitable for the problems such as wearing for a long time.
Therefore, a kind of sunscreen fabric is needed, sun-proof and comfortable demand can be solved simultaneously.
Summary of the invention
The purpose of the present invention is to provide sunscreen fabrics and preparation method thereof, with overcome the deficiencies in the prior art.
To achieve the above object, the invention provides the following technical scheme:
The embodiment of the present application discloses a kind of sunscreen fabric, and the sunscreen fabric is interweaved by warp and weft,
The warp is sun-proof fiber blend yarn, and the weft is polyester fiber mixed yarn；
The raw material of the sun-proof fiber blend yarn includes: by weight
The raw material of the polyester fiber mixed yarn includes: by weight
Super 60~70 parts of imitative cotton polyester fiber
20~30 parts of viscose rayon.
Preferably, the diameter of the warp is 36~45 μm, and the fiber number of the warp is 155-160dtex.
Preferably, the diameter of the weft is 32~41.6 μm, and the fiber number of the weft is 147-155dtex.
The embodiment of the present application also discloses a kind of preparation method of sunscreen fabric, comprising the following steps:
(1) sun-proof fiber blend yarn is prepared:
By polyvinyl alcohol ultrasonic disperse in water, the first spinning solution is obtained；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min is stirred at 85~98 DEG C, is cooled down later
Obtain the second spinning solution；
By spinning machine by the second spinning solution spinning, sun-proof fiber is made；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral；
(2) polyester fiber mixed yarn is prepared:
Make super imitative cotton polyester fiber and viscose rayon that twisting be handed over to obtain polyester fiber mixed yarn in the shape of a spiral；
(3) sun-proof fiber blend yarn and polyester fiber mixed yarn are mutually perpendicular to interweave and sunscreen fabric is made.
Preferably, by weight, the polyvinyl alcohol is 40~50 parts, and the titanium dioxide is 10~15 parts, the pottery
Porcelain powder is 8~12 parts, and the nitrile composite fibre of washing is 35~45 parts, and the flaxen fiber is 20~30 parts, the super imitative cotton polyester
Fiber is 60~70 parts, and the viscose rayon is 20~30 parts.
Preferably, the step (1) specifically includes:
By polyvinyl alcohol ultrasonic disperse in deionized water, 15~40min of strong stirring at 65~90 DEG C obtains first
Spinning solution, later 10~30min of cooling and standings；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min of strong stirring at 85~98 DEG C, later
20~40min of cooling and standings obtains the second spinning solution；
Second spinning solution is delivered to spinning machine, 40~120min of vacuum defoamation, with nitrogen to the second spinning solution into
Row pressurization, squeezes out strand through spinning head, carries out stretching later and washing process is prevented in 45~60 DEG C of dry 20~30min
Shine fiber；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral.
Preferably, the step (3) specifically includes:
Using sun-proof fiber blend yarn as warp, polyester fiber mixed yarn is as weft, the dosage of the warp and weft
Ratio is 2:1, and sunscreen fabric is made in every two warps intertexture vertical with the weft.
It preferably, further include that dyeing processing is carried out to the sunscreen fabric.
Compared with the prior art, the advantages of the present invention are as follows:
Sunscreen fabric of the invention, warp are sun-proof fiber blend yarn, and weft is polyester fiber mixed yarn.It is more due to having
The functional fiber of kind extra fine quality number, is provided simultaneously with ultraviolet reflection agent, can effectively realize sun-screening function, so that fabric sheet
Body integrates sun-proof, comfort.
Specific embodiment
In one embodiment of the application, provide a kind of sunscreen fabric, the sunscreen fabric be interweaved by warp and weft and
At the warp is sun-proof fiber blend yarn, and the weft is polyester fiber mixed yarn；
The raw material of the sun-proof fiber blend yarn includes: by weight
The raw material of the polyester fiber mixed yarn includes: by weight
Super 60~70 parts of imitative cotton polyester fiber
20~30 parts of viscose rayon.
Wherein, the diameter of the warp is 36~45 μm, and the fiber number of the warp is 155-160dtex.
Wherein, the diameter of the weft is 32~41.6 μm, and the fiber number of the weft is 147-155dtex.
The embodiment of the present application also discloses a kind of preparation method of sunscreen fabric, comprising the following steps:
(1) sun-proof fiber blend yarn is prepared:
By polyvinyl alcohol ultrasonic disperse in water, the first spinning solution is obtained；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min is stirred at 85~98 DEG C, is cooled down later
Obtain the second spinning solution；
By spinning machine by the second spinning solution spinning, sun-proof fiber is made；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral；
(2) polyester fiber mixed yarn is prepared:
Make super imitative cotton polyester fiber and viscose rayon that twisting be handed over to obtain polyester fiber mixed yarn in the shape of a spiral；
(3) sun-proof fiber blend yarn and polyester fiber mixed yarn are mutually perpendicular to interweave and sunscreen fabric is made.
Wherein, by weight, the polyvinyl alcohol is 40~50 parts, and the titanium dioxide is 10~15 parts, the ceramics
Powder is 8~12 parts, and the nitrile composite fibre of washing is 35~45 parts, and the flaxen fiber is 20~30 parts, and the super imitative cotton polyester is fine
Dimension is 60~70 parts, and the viscose rayon is 20~30 parts.
Further, the step (1) specifically includes:
By polyvinyl alcohol ultrasonic disperse in deionized water, 15~40min of strong stirring at 65~90 DEG C obtains first
Spinning solution, later 10~30min of cooling and standings；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min of strong stirring at 85~98 DEG C, later
20~40min of cooling and standings obtains the second spinning solution；
Second spinning solution is delivered to spinning machine, 40~120min of vacuum defoamation, with nitrogen to the second spinning solution into
Row pressurization, squeezes out strand through spinning head, carries out stretching later and washing process is prevented in 45~60 DEG C of dry 20~30min
Shine fiber；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral.
Further, the step (3) specifically includes:
Using sun-proof fiber blend yarn as warp, polyester fiber mixed yarn is as weft, the dosage of the warp and weft
Ratio is 2:1, and sunscreen fabric is made in every two warps intertexture vertical with the weft.
It further, further include that dyeing processing is carried out to the sunscreen fabric.
Wherein, titanium dioxide and ceramic powder can be used as ultraviolet reflection agent, effectively reflection ultraviolet light, to make in the present invention
Sunscreen fabric have good sun-proof result.
To make the object, technical solutions and advantages of the present invention clearer, below to a specific embodiment of the invention into
Row is described in detail.Embodiments of the present invention are only exemplary, and the present invention is not limited to these embodiments.
Embodiment 1
The sunscreen fabric that the embodiment of the present invention 1 provides, is interweaved by warp and weft, and the warp is sun-proof fibre
Mixed yarn is tieed up, the weft is polyester fiber mixed yarn；
The raw material of the sun-proof fiber blend yarn includes: by weight
The raw material of the polyester fiber mixed yarn includes: by weight
Super 70 parts of imitative cotton polyester fiber
20 parts of viscose rayon.
Wherein, the diameter of the warp is 36 μm, and the fiber number of the warp is 155dtex.
Wherein, the diameter of the weft is 32 μm, and the fiber number of the weft is 155dtex.
The preparation method of sunscreen fabric, comprising the following steps:
(1) sun-proof fiber blend yarn is prepared:
By polyvinyl alcohol ultrasonic disperse in deionized water, 15~40min of strong stirring at 65~90 DEG C obtains first
Spinning solution, later 10~30min of cooling and standings；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min of strong stirring at 85~98 DEG C, later
20~40min of cooling and standings obtains the second spinning solution；
Second spinning solution is delivered to spinning machine, 40~120min of vacuum defoamation, with nitrogen to the second spinning solution into
Row pressurization, squeezes out strand through spinning head, carries out stretching later and washing process is prevented in 45~60 DEG C of dry 20~30min
Shine fiber；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral；
(2) polyester fiber mixed yarn is prepared:
Make super imitative cotton polyester fiber and viscose rayon that twisting be handed over to obtain polyester fiber mixed yarn in the shape of a spiral；
(3) using sun-proof fiber blend yarn as warp, polyester fiber mixed yarn is as weft, the use of the warp and weft
Amount ratio is 2:1, and every two warps are vertical with the weft to interweave sunscreen fabric is made.
Later, dyeing processing is carried out to the sunscreen fabric.
Embodiment 2
The sunscreen fabric that the embodiment of the present invention 2 provides, is interweaved by warp and weft, and the warp is sun-proof fibre
Mixed yarn is tieed up, the weft is polyester fiber mixed yarn；
The raw material of the sun-proof fiber blend yarn includes: by weight
The raw material of the polyester fiber mixed yarn includes: by weight
Super 60 parts of imitative cotton polyester fiber
30 parts of viscose rayon.
Wherein, the diameter of the warp is 45 μm, and the fiber number of the warp is 160dtex.
Wherein, the diameter of the weft is 41.6 μm, and the fiber number of the weft is 147dtex.
The preparation method of sunscreen fabric, comprising the following steps:
(1) sun-proof fiber blend yarn is prepared:
By polyvinyl alcohol ultrasonic disperse in deionized water, 15~40min of strong stirring at 65~90 DEG C obtains first
Spinning solution, later 10~30min of cooling and standings；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min of strong stirring at 85~98 DEG C, later
20~40min of cooling and standings obtains the second spinning solution；
Second spinning solution is delivered to spinning machine, 40~120min of vacuum defoamation, with nitrogen to the second spinning solution into
Row pressurization, squeezes out strand through spinning head, carries out stretching later and washing process is prevented in 45~60 DEG C of dry 20~30min
Shine fiber；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral；
(2) polyester fiber mixed yarn is prepared:
Make super imitative cotton polyester fiber and viscose rayon that twisting be handed over to obtain polyester fiber mixed yarn in the shape of a spiral；
(3) using sun-proof fiber blend yarn as warp, polyester fiber mixed yarn is as weft, the use of the warp and weft
Amount ratio is 2:1, and every two warps are vertical with the weft to interweave sunscreen fabric is made.
Later, dyeing processing is carried out to the sunscreen fabric.
Embodiment 3
The sunscreen fabric that the embodiment of the present invention 3 provides, is interweaved by warp and weft, and the warp is sun-proof fibre
Mixed yarn is tieed up, the weft is polyester fiber mixed yarn；
The raw material of the sun-proof fiber blend yarn includes: by weight
The raw material of the polyester fiber mixed yarn includes: by weight
Super 65 parts of imitative cotton polyester fiber
25 parts of viscose rayon.
Wherein, the diameter of the warp is 40 μm, and the fiber number of the warp is 157dtex.
Wherein, the diameter of the weft is 38 μm, and the fiber number of the weft is 150dtex.
The preparation method of sunscreen fabric in the present embodiment, with embodiment 1.
Comparative example 1
Choose common fabric on the market.
The performance test of SPF is carried out to the fabric of Examples 1 to 3 and comparative example 1, as a result such as table 1.
| UVA/% | UVB/% | UPF | |
| Embodiment 1 | 1.61 | 1.43 | 55.23 |
| Embodiment 2 | 1.71 | 1.41 | 52.13 |
| Embodiment 3 | 1.68 | 1.42 | 54.19 |
| Comparative example 1 | 10.19 | 12.23 | 7.41 |
Table 1.
As it can be seen that the sunscreen fabric in Examples 1 to 3, compared to the fabric of comparative example 1, sun-proof better performances.
Sunscreen fabric of the invention, warp are sun-proof fiber blend yarn, and the weft is polyester fiber mixed yarn.Due to tool
The functional fiber of standby a variety of extra fine quality numbers, is provided simultaneously with ultraviolet reflection agent, can effectively realize sun-screening function, so that face
Material integrates sun-proof, comfort in itself.
Finally, it is to be noted that, the terms "include", "comprise" or its any other variant be intended to it is non-exclusive
Property include so that include a series of elements process, method, article or equipment not only include those elements, but also
Further include other elements that are not explicitly listed, or further include for this process, method, article or equipment it is intrinsic
Element.
Claims (8)
1. a kind of sunscreen fabric, it is characterised in that: the sunscreen fabric is interweaved by warp and weft, and the warp is
Sun-proof fiber blend yarn, the weft are polyester fiber mixed yarn；
The raw material of the sun-proof fiber blend yarn includes: by weight
The raw material of the polyester fiber mixed yarn includes: by weight
Super 60~70 parts of imitative cotton polyester fiber
20~30 parts of viscose rayon.
2. sunscreen fabric according to claim 1, which is characterized in that the diameter of the warp is 36~45 μm, the warp
The fiber number of line is 155-160dtex.
3. sunscreen fabric according to claim 1, which is characterized in that the diameter of the weft is 32~41.6 μm, described
The fiber number of weft is 147-155dtex.
4. a kind of preparation method of sunscreen fabric, which comprises the following steps:
(1) sun-proof fiber blend yarn is prepared:
By polyvinyl alcohol ultrasonic disperse in water, the first spinning solution is obtained；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min is stirred at 85~98 DEG C, it is cooling later to obtain
Second spinning solution；
By spinning machine by the second spinning solution spinning, sun-proof fiber is made；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral；
(2) polyester fiber mixed yarn is prepared:
Make super imitative cotton polyester fiber and viscose rayon that twisting be handed over to obtain polyester fiber mixed yarn in the shape of a spiral；
(3) sun-proof fiber blend yarn and polyester fiber mixed yarn are mutually perpendicular to interweave and sunscreen fabric is made.
5. the preparation method according to claim 4, which is characterized in that by weight, the polyvinyl alcohol is 40~50
Part, the titanium dioxide is 10~15 parts, and the ceramic powder is 8~12 parts, and the nitrile composite fibre of washing is 35~45 parts, the fiber crops
Fiber is 20~30 parts, and the super imitative cotton polyester fiber is 60~70 parts, and the viscose rayon is 20~30 parts.
6. the preparation method according to claim 4, which is characterized in that the step (1) specifically includes:
By polyvinyl alcohol ultrasonic disperse in deionized water, 15~40min of strong stirring at 65~90 DEG C obtains the first spinning
Solution, later 10~30min of cooling and standings；
Titanium dioxide and ceramic powder are added in the first spinning solution, 20~50min of strong stirring, cools down later at 85~98 DEG C
20~40min is stood, the second spinning solution is obtained；
Second spinning solution is delivered to spinning machine, 40~120min of vacuum defoamation adds the second spinning solution with nitrogen
Pressure, squeezes out strand through spinning head, carries out stretching and washing process later in 45~60 DEG C of dry 20~30min and obtains sun-proof fibre
Dimension；
Make sun-proof fiber, wash nitrile composite fibre and flaxen fiber twisting is handed over to obtain sun-proof fiber blend yarn in the shape of a spiral.
7. the preparation method according to claim 4, which is characterized in that the step (3) specifically includes:
Using sun-proof fiber blend yarn as warp, polyester fiber mixed yarn is as weft, the usage ratio of the warp and weft
For 2:1, sunscreen fabric is made in every two warps intertexture vertical with the weft.
8. the preparation method according to claim 4, which is characterized in that further include being carried out at dyeing to the sunscreen fabric
Reason.