CN108950865A - A kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant - Google Patents
A kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant Download PDFInfo
- Publication number
- CN108950865A CN108950865A CN201810861424.5A CN201810861424A CN108950865A CN 108950865 A CN108950865 A CN 108950865A CN 201810861424 A CN201810861424 A CN 201810861424A CN 108950865 A CN108950865 A CN 108950865A
- Authority
- CN
- China
- Prior art keywords
- water
- fabric
- superfine fibre
- chrysanthemum valve
- oil repellant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation methods that dirty anti-mite fabric is refused with water and oil repellant, belong to functional fabric technical field.A kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant of the present invention, this refuses dirty anti-mite fabric by forming dispersion tiling by high-pressure water-jet using chrysanthemum valve superfine fibre with water and oil repellant, reach high density compact structure, to achieve the effect that isolation is anti-mite；Then product is refused dirty function additive with water and oil repellant by weaving to impregnate, so that fabric has the function of that water and oil repellant refuses dirt.This method simple process is convenient for assembly line operate in large scale, easy control of process conditions in production process, and production cost is low；A process for preparing the functional fibres come, can also have good functionality by repeatedly washing, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation methods that dirty anti-mite fabric is refused with water and oil repellant, belong to functional fabric technology
Field.
Background technique
Currently, as textile technology and life taste, the raising of quality, the garment material of simple function cannot expire
Sufficient people's lives demand.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The development of dimension is the technological innovation of traditional textile industry, and the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.In addition to functional fibre refers to the physical mechanical property possessed by the general fiber, also have
The tencel of certain specific function.Such as: fiber has the function of health care (antibacterial, mite killing, physical therapy and eliminate the unusual smell)
；Safeguard function (radiation protection, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
It treats and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function possessed by fiber is not secured enough, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture and popularization and use of functional fibre.
The purpose of the present invention is to provide a kind of preparation methods that dirty anti-mite fabric is refused with water and oil repellant, this, which has, refuses
Water refuses oil and refuses dirty anti-mite fabric by forming dispersion tiling by high-pressure water-jet using chrysanthemum valve superfine fibre, and it is tight to reach high density
Real structure, to achieve the effect that isolation is anti-mite；Then product dirty function additive is refused with water and oil repellant by weaving to impregnate,
So that fabric has the function of that water and oil repellant refuses dirt.This method simple process is convenient for assembly line operate in large scale, in production process
Easy control of process conditions, production cost are low；A process for preparing the functional fibres come, can also have by repeatedly washing
Good functionality, is worth of widely use.
Summary of the invention
The technical solution adopted by the present invention to solve the technical problems is: a kind of to refuse dirty anti-mite fabric with water and oil repellant
Preparation method, the steps include:
(1), chrysanthemum valve superfine fibre is subjected to mixing combing；
(2), the chrysanthemum valve superfine fibre vertical and horizontal successively lapping for combing step (1), so that every square metre of chrysanthemum valve is ultra-fine
The weight of fiber is at 60-110 grams；
(3), chrysanthemum valve superfine fibre is dispersed by high-pressure water-jet, the pressure of water is 1 megapascal, high-pressure water-jet in high-pressure water-jet
Chrysanthemum valve superfine fibre is dispersed and forms high density structures；
(4), the chrysanthemum valve superfine fibre fabric after step (3) spun lacing is rolled 3-5 times with roller, so that chrysanthemum valve superfine fibre face
The weight ratio of material and water is 5:0.1-1；
(5), the processed chrysanthemum valve superfine fibre fabric of step (4) is entered in circulation solution case by conveyer belt, recycles solution
Weaving is 3-5:105 with the weight ratio that water and oil repellant refuses dirty function additive and water in case, and the temperature for recycling solution in solution case is
50-115 degrees Celsius, soaking time of the chrysanthemum valve superfine fibre fabric in circulation solution case is 1-3 minutes；
(6), the chrysanthemum valve superfine fibre functional fabric after arranging step (5) is rolled 3-5 times with roller, so that chrysanthemum valve superfine fibre
The weight ratio of functional fabric and water is 5:0.1-1；
(7), the chrysanthemum valve superfine fibre functional fabric that step (6) prepares is put into steam drying box and is baked, bake temperature
Degree is 80-110 degrees Celsius, and baking time is 5-10 minutes；
(8), bake after chrysanthemum valve superfine fibre functional fabric carried out shaping according to required breadth size, trimming, be packaged envelope
Dress is prepared into and refuses dirty anti-mite fabric with water and oil repellant.
Chrysanthemum valve superfine fibre is according to weight ratio by the terylene of 60%-80% and the brocade of 20%-40% in the preferred step (1)
Synthetic fibre composition.
A kind of preparation method that dirty anti-mite fabric is refused with water and oil repellant of the purpose of the present invention, there is water and oil repellant to refuse for this
Dirty anti-mite fabric disperses tiling by being formed using chrysanthemum valve superfine fibre by high-pressure water-jet, reaches high density compact structure,
To achieve the effect that isolation is anti-mite；Then product is refused dirty function additive with water and oil repellant by weaving to impregnate, so that face
Material has the function of that water and oil repellant refuses dirt.This method simple process is convenient for assembly line operate in large scale, technique item in production process
Part is easy to control, and production cost is low；A process for preparing the functional fibres come, can also have good by repeatedly washing
Functionality is worth of widely use.
Specific embodiment
Specific embodiment one: a kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant the steps include:
(1), chrysanthemum valve superfine fibre is subjected to mixing combing；
(2), the chrysanthemum valve superfine fibre vertical and horizontal successively lapping for combing step (1), so that every square metre of chrysanthemum valve is ultra-fine
The weight of fiber is at 60 grams；
(3), chrysanthemum valve superfine fibre is dispersed by high-pressure water-jet, the pressure of water is 1 megapascal, high-pressure water-jet in high-pressure water-jet
Chrysanthemum valve superfine fibre is dispersed and forms high density structures；
(4), the chrysanthemum valve superfine fibre fabric after step (3) spun lacing is rolled 3 times with roller, so that chrysanthemum valve superfine fibre fabric
Weight ratio with water is 5:0.1；
(5), the processed chrysanthemum valve superfine fibre fabric of step (4) is entered in circulation solution case by conveyer belt, recycles solution
Weaving is 3:105 with the weight ratio that water and oil repellant refuses dirty function additive and water in case, and the temperature for recycling solution in solution case is 50
Degree Celsius, soaking time of the chrysanthemum valve superfine fibre fabric in circulation solution case is 1 minute；
(6), the chrysanthemum valve superfine fibre functional fabric after arranging step (5) is rolled 3 times with roller, so that chrysanthemum valve superfine fibre function
The weight ratio of energy fabric and water is 5:0.1；
(7), the chrysanthemum valve superfine fibre functional fabric that step (6) prepares is put into steam drying box and is baked, bake temperature
Degree is 80 degrees Celsius, and baking time is 5 minutes；
(8), bake after chrysanthemum valve superfine fibre functional fabric carried out shaping according to required breadth size, trimming, be packaged envelope
Dress is prepared into and refuses dirty anti-mite fabric with water and oil repellant.
Chrysanthemum valve superfine fibre is made of according to weight ratio 60% terylene and 40% polyamide fibre in the step (1).
Specific embodiment two: a kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant the steps include:
(1), chrysanthemum valve superfine fibre is subjected to mixing combing；
(2), the chrysanthemum valve superfine fibre vertical and horizontal successively lapping for combing step (1), so that every square metre of chrysanthemum valve is ultra-fine
The weight of fiber is at 80 grams；
(3), chrysanthemum valve superfine fibre is dispersed by high-pressure water-jet, the pressure of water is 1 megapascal, high-pressure water-jet in high-pressure water-jet
Chrysanthemum valve superfine fibre is dispersed and forms high density structures；
(4), the chrysanthemum valve superfine fibre fabric after step (3) spun lacing is rolled 4 times with roller, so that chrysanthemum valve superfine fibre fabric
Weight ratio with water is 5:0.6；
(5), the processed chrysanthemum valve superfine fibre fabric of step (4) is entered in circulation solution case by conveyer belt, recycles solution
Weaving is 4:105 with the weight ratio that water and oil repellant refuses dirty function additive and water in case, and the temperature for recycling solution in solution case is 85
Degree Celsius, soaking time of the chrysanthemum valve superfine fibre fabric in circulation solution case is 2 minutes；
(6), the chrysanthemum valve superfine fibre functional fabric after arranging step (5) is rolled 4 times with roller, so that chrysanthemum valve superfine fibre function
The weight ratio of energy fabric and water is 5:0.7；
(7), the chrysanthemum valve superfine fibre functional fabric that step (6) prepares is put into steam drying box and is baked, bake temperature
Degree is 90 degrees Celsius, and baking time is 8 minutes；
(8), bake after chrysanthemum valve superfine fibre functional fabric carried out shaping according to required breadth size, trimming, be packaged envelope
Dress is prepared into and refuses dirty anti-mite fabric with water and oil repellant.
Chrysanthemum valve superfine fibre is made of according to weight ratio 70% terylene and 30% polyamide fibre in the step (1).
Specific embodiment three: a kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant the steps include:
(1), chrysanthemum valve superfine fibre is subjected to mixing combing；
(2), the chrysanthemum valve superfine fibre vertical and horizontal successively lapping for combing step (1), so that every square metre of chrysanthemum valve is ultra-fine
The weight of fiber is at 110 grams；
(3), chrysanthemum valve superfine fibre is dispersed by high-pressure water-jet, the pressure of water is 1 megapascal, high-pressure water-jet in high-pressure water-jet
Chrysanthemum valve superfine fibre is dispersed and forms high density structures；
(4), the chrysanthemum valve superfine fibre fabric after step (3) spun lacing is rolled 5 times with roller, so that chrysanthemum valve superfine fibre fabric
Weight ratio with water is 5:1；
(5), the processed chrysanthemum valve superfine fibre fabric of step (4) is entered in circulation solution case by conveyer belt, recycles solution
Weaving is 1:21 with the weight ratio that water and oil repellant refuses dirty function additive and water in case, and the temperature for recycling solution in solution case is 115
Degree Celsius, soaking time of the chrysanthemum valve superfine fibre fabric in circulation solution case is 3 minutes；
(6), the chrysanthemum valve superfine fibre functional fabric after arranging step (5) is rolled 5 times with roller, so that chrysanthemum valve superfine fibre function
The weight ratio of energy fabric and water is 5:1；
(7), the chrysanthemum valve superfine fibre functional fabric that step (6) prepares is put into steam drying box and is baked, bake temperature
Degree is 110 degrees Celsius, and baking time is 10 minutes；
(8), bake after chrysanthemum valve superfine fibre functional fabric carried out shaping according to required breadth size, trimming, be packaged envelope
Dress is prepared into and refuses dirty anti-mite fabric with water and oil repellant.
The chrysanthemum valve superfine fibre is made of according to weight ratio 80% terylene and 20% polyamide fibre.
The purpose of the present invention is to provide a kind of preparation methods that dirty anti-mite fabric is refused with water and oil repellant, this, which has, refuses
Water refuses oil and refuses dirty anti-mite fabric by forming dispersion tiling by high-pressure water-jet using chrysanthemum valve superfine fibre, and it is tight to reach high density
Real structure, to achieve the effect that isolation is anti-mite；Then product dirty function additive is refused with water and oil repellant by weaving to impregnate,
So that fabric has the function of that water and oil repellant refuses dirt.This method simple process is convenient for assembly line operate in large scale, in production process
Easy control of process conditions, production cost are low；A process for preparing the functional fibres come, can also have by repeatedly washing
Good functionality, is worth of widely use.
Obviously, the above embodiments are merely examples for clarifying the description, and does not limit the embodiments.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of variation or
It changes.There is no necessity and possibility to exhaust all the enbodiments.And it is extended from this it is obvious variation or
It changes still within the protection scope of the invention.
Claims (2)
1. a kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant, it is characterised in that the steps include:
(1), chrysanthemum valve superfine fibre is subjected to mixing combing；
(2), the chrysanthemum valve superfine fibre vertical and horizontal successively lapping for combing step (1), so that every square metre of chrysanthemum valve is ultra-fine
The weight of fiber is at 60-110 grams；
(3), chrysanthemum valve superfine fibre is dispersed by high-pressure water-jet, the pressure of water is 1 megapascal, high-pressure water-jet in high-pressure water-jet
Chrysanthemum valve superfine fibre is dispersed and forms high density structures；
(4), the chrysanthemum valve superfine fibre fabric after step (3) spun lacing is rolled 3-5 times with roller, so that chrysanthemum valve superfine fibre face
The weight ratio of material and water is 5:0.1-1；
(5), the processed chrysanthemum valve superfine fibre fabric of step (4) is entered in circulation solution case by conveyer belt, recycles solution
Weaving is 3-5:105 with the weight ratio that water and oil repellant refuses dirty function additive and water in case, and the temperature for recycling solution in solution case is
50-115 degrees Celsius, soaking time of the chrysanthemum valve superfine fibre fabric in circulation solution case is 1-3 minutes；
(6), the chrysanthemum valve superfine fibre functional fabric after arranging step (5) is rolled 3-5 times with roller, so that chrysanthemum valve superfine fibre
The weight ratio of functional fabric and water is 5:0.1-1；
(7), the chrysanthemum valve superfine fibre functional fabric that step (6) prepares is put into steam drying box and is baked, bake temperature
Degree is 80-110 degrees Celsius, and baking time is 5-10 minutes；
(8), bake after chrysanthemum valve superfine fibre functional fabric carried out shaping according to required breadth size, trimming, be packaged envelope
Dress is prepared into and refuses dirty anti-mite fabric with water and oil repellant.
2. a kind of preparation method for refusing dirty anti-mite fabric with water and oil repellant according to claim 1, which is characterized in that
Chrysanthemum valve superfine fibre is made of according to weight ratio the terylene of 60%-80% and the polyamide fibre of 20%-40% in the step (1).