CN108929599A - 一种具有超高耐晒度的环保水性色浆 - Google Patents
一种具有超高耐晒度的环保水性色浆 Download PDFInfo
- Publication number
- CN108929599A CN108929599A CN201810929592.3A CN201810929592A CN108929599A CN 108929599 A CN108929599 A CN 108929599A CN 201810929592 A CN201810929592 A CN 201810929592A CN 108929599 A CN108929599 A CN 108929599A
- Authority
- CN
- China
- Prior art keywords
- parts
- sun
- superelevation
- mill base
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种具有超高耐晒度的环保水性色浆,按照质量份计:包括40‑50份水性聚酯改性丙烯酸树脂、5‑6份甲醚化氨基树脂、13‑16份色粉、20‑25溶剂、0.1‑0.2份pH值调节剂、0.1‑0.2份消泡剂、20‑50份稀释剂、0.1‑0.2份分散剂、0.1‑0.2份防沉剂、0.1‑0.2份引发剂经混合搅拌制成的。针对普通色浆耐擦性不行,耐晒度不够,易变色等问题,该发明可以使色浆耐晒等级达到4级以上,且耐擦性高。
Description
技术领域
本发明涉及一种具有超高耐晒度的环保水性色浆。
背景技术
目前国内外的色浆耐晒等级多数在1-2级,放置一段时间极易变色,越来越不符合新增的工艺质量要求,而这一趋势在未来几年随着行业的发展要求也越来越高。因此现特需研究一种具有超高耐晒度的环保水性色浆用以满足市场需求。
发明内容
本发明提出一种具有超高耐晒度的环保水性色浆,针对上述普通色浆耐擦性不行,耐晒度不够,易变色等问题,该发明可以使色浆耐晒等级达到4级以上,且耐擦性高。
本发明的技术方案是这样实现的:
一种具有超高耐晒度的环保水性色浆,按照质量份计:包括40-50份水性聚酯改性丙烯酸树脂、5-6份甲醚化氨基树脂、13-16份色粉、20-25溶剂、0.1-0.2份pH值调节剂、0.1-0.2份消泡剂、20-50份稀释剂、0.1-0.2份分散剂、0.1-0.2份防沉剂、0.1-0.2份引发剂经混合搅拌制成的。
优选地,所述的色粉直径在0.1um-0.3um
优选地,所述的溶剂为无水乙醇、乙二醇单丁醚中的至少一种。
优选地,所述的pH值调节剂为三甲胺、N,N-二甲基乙醇胺、乙基甲基乙醇胺、二甲基乙醇胺和二甲基苯胺中的至少一种。
优选地,所述的消泡剂为乳化硅油与高碳醇脂肪酸酯按照质量比为1:1的混合物。
优选地,所述的稀释剂为去离子纯水。
优选地,所述的分散剂为聚丙烯酸胺盐。
优选地,所述的防沉剂为气相二氧化硅。
优选地,所述的引发剂为过氧化苯甲酰。
本发明产生的有益效果为:本发明可以使我司色浆耐晒度等级达到4级,基本不会出现变色情况,而且耐擦性较强,进一步满足了市场需求,提高了我司技术水平。
具体实施方式
下面将结合本发明实施例对本发明的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
一种具有超高耐晒度的环保水性色浆,按照质量份计:包括40-50份水性聚酯改性丙烯酸树脂、5-6份甲醚化氨基树脂、13-16份色粉、20-25溶剂、0.1-0.2份pH值调节剂、0.1-0.2份消泡剂、20-50份稀释剂、0.1-0.2份分散剂、0.1-0.2份防沉剂、0.1-0.2份引发剂经混合搅拌制成的。
优选地,所述的色粉直径在0.1um-0.3um
优选地,所述的溶剂为无水乙醇、乙二醇单丁醚中的至少一种。
优选地,所述的pH值调节剂为三甲胺、N,N-二甲基乙醇胺、乙基甲基乙醇胺、二甲基乙醇胺和二甲基苯胺中的至少一种。
优选地,所述的消泡剂为乳化硅油与高碳醇脂肪酸酯按照质量比为1:1的混合物。
优选地,所述的稀释剂为去离子纯水。
优选地,所述的分散剂为聚丙烯酸胺盐。
优选地,所述的防沉剂为气相二氧化硅。
优选地,所述的引发剂为过氧化苯甲酰。
本发明中,甲醚化氨基树脂加入水性聚酯改性丙烯酸溶液(DSM帝斯曼的NeoRadP-56水性乳液)反应后,可以固定色浆颜色,长时间不变色,耐晒度大幅度提高。同时甲醚化氨基树脂与分高碳醇脂肪酸等醇酸发生交联反应提高产品的硬度、柔韧度和户外耐候性,其树脂中的羟甲基和烷氧基与水性聚酯改性丙烯酸的羟基反应获得三维网状结构,提高产品的稳定性、柔度和耐冲击性能,而且甲醇醚化树脂比其他如丁醇醚化树脂水溶性更高,因此可以提高原料的水溶性。
引发剂采用过氧化苯甲酰,避免现有常用的过硫酸盐等,基于过硫酸盐等常用引发剂分解产生的离子对涂膜的防锈能力产生影响,我们采用过氧化苯甲酰一方面减少了涂料中残留例子对防锈性能的危害,另一方面它的自由基对主链的夺氢能力较强,接枝倾向较大,效率高。
中和剂的选用,我们避免一般常见的氨水等中和剂,采用三甲胺、N,N-二甲基乙醇胺、乙基甲基乙醇胺、二甲基乙醇胺和二甲基苯胺等以及他们的混合物,避免常规的中和剂会产生多余的电解质离子,对涂料的防锈性能产生不良因素。
本发明中同时还通过乙醇和乙二醇单丁醚作为助溶剂,一方面醚类助溶剂具有良好的溶解特征和优异的助溶能力,使得树脂和水形成均一、透明的溶液体系;另一方面,添加一定量的乙二醇单丁醚后,可以防雾、防皱,提高漆膜的光泽性、流动性,改善现有喷涂色浆后容易产生爆泡现象的问题。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (9)
1.一种具有超高耐晒度的环保水性色浆,其特征在于,按照质量份计:包括40-50份水性聚酯改性丙烯酸树脂、5-6份甲醚化氨基树脂、13-16份色粉、20-25溶剂、0.1-0.2份pH值调节剂、0.1-0.2份消泡剂、20-50份稀释剂、0.1-0.2份分散剂、0.1-0.2份防沉剂、0.1-0.2份引发剂经混合搅拌制成的。
2.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的色粉直径在0.1um-0.3um。
3.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的溶剂为无水乙醇、乙二醇单丁醚中的至少一种。
4.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的pH值调节剂为三甲胺、N,N-二甲基乙醇胺、乙基甲基乙醇胺、二甲基乙醇胺和二甲基苯胺中的至少一种。
5.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的消泡剂为乳化硅油与高碳醇脂肪酸酯按照质量比为1:1的混合物。
6.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的稀释剂为去离子纯水。
7.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的分散剂为聚丙烯酸胺盐。
8.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的防沉剂为气相二氧化硅。
9.如权利要求1所述的一种具有超高耐晒度的环保水性色浆,其特征在于,所述的引发剂为过氧化苯甲酰。