CN108913952A - 一种高温合金及其制备方法 - Google Patents
一种高温合金及其制备方法 Download PDFInfo
- Publication number
- CN108913952A CN108913952A CN201810840227.5A CN201810840227A CN108913952A CN 108913952 A CN108913952 A CN 108913952A CN 201810840227 A CN201810840227 A CN 201810840227A CN 108913952 A CN108913952 A CN 108913952A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- alloy
- casting
- preparation
- temperature alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (6)