CN108892984A - A kind of green environmental friendly coatings of highly effective flame-retardant - Google Patents
A kind of green environmental friendly coatings of highly effective flame-retardant Download PDFInfo
- Publication number
- CN108892984A CN108892984A CN201810568619.0A CN201810568619A CN108892984A CN 108892984 A CN108892984 A CN 108892984A CN 201810568619 A CN201810568619 A CN 201810568619A CN 108892984 A CN108892984 A CN 108892984A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- agent
- highly effective
- environmental friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to chemical technology field, in particular a kind of green environmental friendly coatings of highly effective flame-retardant include the following steps:S1；It conscientiously checks and quite produces required each equipment, be allowed in intact clean state, operator wears safety protective tools S2；Fire-resistant composition is configured according to the component ratio of required coating；S3；Sand mill or ball mill grinding dispersion fire prevention raw material are carried out to required material；S4；Add mixed solvent, stirring configuration fireproof coating；S5；Molding coating is repeatedly examined；S6；Packaging is sealed to molding coating, sticks ingredient, application method, production time and effective time and points for attention.The present invention is non-toxic and tasteless, green safe by this coating of the configuration of corresponding proportion and there is good elasticity, flexibility, water resistance and the high heat-insulating, fire-preventing coating quality of waterproofness, stability to stablize, using effect is good, while with excellent flameproof effect, it is provided simultaneously with heat insulating function.
Description
Technical field
The present invention relates to technical field more particularly to a kind of green environmental friendly coatings of highly effective flame-retardant.
Background technique
Chinese coating industry the real estate of fast growth, automobile, ship, etc. downstream industries promotion under, to be higher than
The speed of GDP5%-10% increases, and becomes the second big country of world's coating material production and consumption, generally China's coating industry in 2008
Macroeconomic running quality improves a lot, and constantly to large enterprises, brand enterprise is concentrated in market, industry profitability and anti-risk
Ability enhancing, is presented benign development situation on the whole.Environmental protection coating material be it is a kind of can securely be covered on body surface, rise protection, dress
The chemical mixture coating of decorations, mark and other specific uses.Paint is because of the moisture-proof defencive function of its anti-corrosion and decoration function
Can, and by the favor of finishing person, but organic solvents, the harm to the human body such as addition benzene are larger mostly for existing paint, and it also can be to ring
Border affects, and resistance to oxidation is not strong, and fire retardant performance is poor, and wear-resistance and oil-resistance ability is poor, as people are to environmental protection
Consciousness is more and more stronger, this just needs a kind of reliable performance, to the environment protection oil paint of human body and environmental nonpollution.Heat-insulated high resistant fire prevention,
The coating of water-proof environmental protection is particularly important.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of green of the highly effective flame-retardant proposed
Environmental protection coating material.
To achieve the goals above, present invention employs following technical solutions：
A kind of green environmental friendly coatings of highly effective flame-retardant, include the following steps:
S1；It conscientiously checks and quite produces required each equipment, be allowed in intact clean state, operator
Wear safety protective tools
S2；Fire-resistant composition is configured according to the component ratio of required coating；
S3；Sand mill or ball mill grinding dispersion fire prevention raw material are carried out to required material；
S4；Add mixed solvent, stirring configuration fireproof coating；
S5；Molding coating is repeatedly examined；
S6；Packaging is sealed to molding coating, sticks ingredient, application method, production time and effective time
And points for attention.
Preferably, the component ratio of the coating configures modified acroleic acid 20-40 parts, 2-5 parts of bentonite, wollastonite 15-
25 parts, 10-18 parts of polyvinyl alcohol, 15-25 parts of light calcium carbonate powder, 3-8 parts of activating agent, 2-7 parts of toughener, 3-8 parts of hydrophobing agent, film forming help
1-3 parts of agent, 70-110 parts of china clay, 30-45 parts of titanium dioxide, 3-10 parts of perlite particle, 4-6 parts of sepiolite, water-base epoxy tree
Rouge, 20-30 parts, 11-16 parts of waterglass, 11-15 parts of potassium hydroxide, 4-9 parts of sodium metasilicate, 3-8 parts of zinc chloride.
Preferably, described to pass through china clay, titanium dioxide, perlite particle, sepiolite with the requisite quality got ready respectively
Ball mill is ground, and milling time will control fineness in 100um or less in 60min or more.
Preferably, the mixed solvent includes：Elastic emulsion, fungicide, film forming solvent, thickener, disappears at pigment dispersing agent
Infusion and PH debug agent, and weight part ratio is as follows：Elastic emulsion：Pigment dispersing agent：Fungicide：Film forming solvent：Thickener：Defoaming
Agent and：Debug agent=35：7：2：4：2.2：3：0.3.
Preferably, the ingredient of the required coating and high china clay, titanium dioxide, perlite particle, sepiolite are according to number
Proportion is added to high-speed mixer stirring 30min or more, while adding water in thinning vessel, sequentially add under the low speed by
Aqueous epoxy resins, waterglass, potassium hydroxide, sodium metasilicate, zinc chloride raw material according to number proportion mention after stirring 15-20min
High wheel speed, with 1-2 hours formation products of high-speed stirred.
Compared with prior art, the invention proposes a kind of green environmental friendly coatings of highly effective flame-retardant, have below beneficial to effect
Fruit：
1, there is excellent environmental-protecting performance by proportion coating, it is non-toxic and tasteless, it is green safe；And there is good bullet
Property, flexibility, water resistance and waterproofness, the coating there is no volatile organic solvent and free formaldehyde, safety and environmental protection, without nocuousness
Substance will not damage human health；Ageing resistance is strong, not easily to fall off, and stability is high.
2, to be stablized by proportion heat-insulating, fire-preventing coating quality, using effect is good, while with excellent flameproof effect,
It is provided simultaneously with heat insulating function.
In the present invention, it is not directed to part in the device and is the same as those in the prior art or can be realized by using the prior art,
The present invention has excellent environmental-protecting performance by proportion coating, non-toxic and tasteless, green safe；And have good elastic, soft
Toughness, water resistance and waterproofness, the coating do not have volatile organic solvent and free formaldehyde, and safety and environmental protection is free of harmful substance,
Human health will not be damaged；Ageing resistance is strong, not easily to fall off, and stability is high；By matching heat-insulating, fire-preventing coating quality
Stablize, using effect is good, while with excellent flameproof effect, is provided simultaneously with heat insulating function.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
A kind of green environmental friendly coatings of highly effective flame-retardant, include the following steps:
S1；It conscientiously checks and quite produces required each equipment, be allowed in intact clean state, operator
Wear safety protective tools
S2；Fire-resistant composition is configured according to the component ratio of required coating；
S3；Sand mill or ball mill grinding dispersion fire prevention raw material are carried out to required material；
S4；Add mixed solvent, stirring configuration fireproof coating；
S5；Molding coating is repeatedly examined；
S6；Packaging is sealed to molding coating, sticks ingredient, application method, production time and effective time
And points for attention.
The component ratio of the coating configures modified acroleic acid 20-40 parts, 2-5 parts of bentonite, 15-25 parts of wollastonite, gathers
10-18 parts of vinyl alcohol, 15-25 parts of light calcium carbonate powder, 3-8 parts of activating agent, 2-7 parts of toughener, 3-8 parts of hydrophobing agent, coalescing agent 1-3
Part, 70-110 parts of china clay, 30-45 parts of titanium dioxide, 3-10 parts of perlite particle, 4-6 parts of sepiolite, aqueous epoxy resins, 20-
30 parts, 11-16 parts of waterglass, 11-15 parts of potassium hydroxide, 4-9 parts of sodium metasilicate, 3-8 parts of zinc chloride.
The china clay by with the requisite quality got ready, titanium dioxide, perlite particle, sepiolite respectively through ball mill into
Row grinding, milling time will control fineness in 100um or less in 60min or more.
The mixed solvent includes：Elastic emulsion, pigment dispersing agent, fungicide, film forming solvent, thickener, defoaming agent and
PH debugs agent, and weight part ratio is as follows：Elastic emulsion：Pigment dispersing agent：Fungicide：Film forming solvent：Thickener：Defoaming agent and：
Debug agent=35：7：2：4：2.2：3：0.3.
The ingredient and high china clay, titanium dioxide, perlite particle, sepiolite of coating needed for described are matched according to number, are added
Enter to high-speed mixer and stir 30min or more, while adding water in thinning vessel, sequentially adds match according to number under the low speed
Aqueous epoxy resins, waterglass, potassium hydroxide, sodium metasilicate, the zinc chloride raw material of ratio after stirring 15-20min, improve impeller and turn
Speed, with 1-2 hours formation products of high-speed stirred.
Specific embodiment 1；
According to weight, the component of the fireproof coating includes：20 parts of modified acroleic acid, 2 parts of bentonite, wollastonite
15 parts, 10 parts of polyvinyl alcohol, 15 parts of light calcium carbonate powder, 3 parts of activating agent, 2 parts of toughener, 3 parts of hydrophobing agent, 1 part of coalescing agent, china clay
70 parts, 30 parts of titanium dioxide, 3 parts of perlite particle, 4 parts of sepiolite, 20 parts of aqueous epoxy resins, 11 parts of waterglass, potassium hydroxide
11 parts, 4 parts of sodium metasilicate, 3 parts of zinc chloride, mixed solvent weight part ratio is as follows：Elastic emulsion：Pigment dispersing agent：Fungicide：Film forming
Solvent：Thickener：Defoaming agent and：Debug agent=35：7：2：4：2.2：3：0.3, it is coated on corresponding object, sees after being sufficiently stirred
Examine its color brightness, water-fast degree, fire resisting degree, degree of thermal insulation.
Specific embodiment 2；
According to weight, the component of the fireproof coating includes 30 parts of modified acroleic acid, 3 parts of bentonite, wollastonite
20 parts, 14 parts of polyvinyl alcohol, 20 parts of light calcium carbonate powder, 5 parts of activating agent, 4 parts of toughener, 5 parts of hydrophobing agent, 2 parts of coalescing agent, china clay
90 parts, 37 parts of titanium dioxide, 5 parts of perlite particle, sea bubble 5 parts, 25 parts of aqueous epoxy resins, 13 parts of waterglass, potassium hydroxide 13
Part, 6 parts of sodium metasilicate, 5 parts of zinc chloride, it is as follows to add mixed solvent weight part ratio：Elastic emulsion：Pigment dispersing agent：Fungicide：
Film forming solvent：Thickener：Defoaming agent and：Debug agent=35：7：2：4：2.2：3：0.3, corresponding object is coated in after being sufficiently stirred
On, observe its color brightness, water-fast degree, fire resisting degree, degree of thermal insulation.
Specific embodiment 3；
According to weight, the component of the fireproof coating includes 40 parts of modified acroleic acid, 5 parts of bentonite, wollastonite
25 parts, 18 parts of polyvinyl alcohol, 25 parts of light calcium carbonate powder, 8 parts of activating agent, 7 parts of toughener, 8 parts of hydrophobing agent, 3 parts of coalescing agent, china clay
110 parts, 45 parts of titanium dioxide, 10 parts of perlite particle, 6 parts of sepiolite, 30 parts of aqueous epoxy resins, 16 parts of waterglass, hydroxide
15 parts of potassium, 9 parts of sodium metasilicate, 8 parts of zinc chloride, mixed solvent weight part ratio is as follows：Elastic emulsion：Pigment dispersing agent：Fungicide：At
Membrane solvent：Thickener：Defoaming agent and：Debug agent=35：7：2：4：2.2：3：0.3, it is coated in after being sufficiently stirred on corresponding object,
Observe its color brightness, water-fast degree, fire resisting degree, degree of thermal insulation.
In the present invention, in use, there is excellent environmental-protecting performance by proportion coating, it is non-toxic and tasteless, it is green safe；And
With good elasticity, flexibility, water resistance and waterproofness, which does not have volatile organic solvent and free formaldehyde, safety
Environmental protection is free of harmful substance, will not damage to human health；Ageing resistance is strong, not easily to fall off, and stability is high；By matching
Stablize than heat-insulating, fire-preventing coating quality, using effect is good, while with excellent flameproof effect, is provided simultaneously with heat-insulated function
Energy.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of green environmental friendly coatings of highly effective flame-retardant, which is characterized in that include the following steps:
S1；It conscientiously checks and quite produces required each equipment, be allowed in intact clean state, operator wears
Good safety protective tools
S2；Fire-resistant composition is configured according to the component ratio of required coating；
S3；Sand mill or ball mill grinding dispersion fire prevention raw material are carried out to required material；
S4；Add mixed solvent, stirring configuration fireproof coating；
S5；Molding coating is repeatedly examined；
S6；Packaging is sealed to molding coating, sticks ingredient, application method, production time and effective time and note
Meaning item.
2. a kind of green environmental friendly coatings of highly effective flame-retardant according to claim 1, which is characterized in that the ingredient of the coating
20-40 parts of proportional arrangement modified acroleic acid, 2-5 parts of bentonite, 15-25 parts of wollastonite, 10-18 parts of polyvinyl alcohol, light calcium carbonate powder 15-
25 parts, 3-8 parts of activating agent, 2-7 parts of toughener, 3-8 parts of hydrophobing agent, 1-3 parts of coalescing agent, 70-110 parts of china clay, titanium dioxide
30-45 parts, 3-10 parts of perlite particle, 4-6 parts of sepiolite, 20-30 parts of aqueous epoxy resins, 11-16 parts of waterglass, hydroxide
11-15 parts of potassium, 4-9 parts of sodium metasilicate, 3-8 parts of zinc chloride.
3. a kind of green environmental friendly coatings of highly effective flame-retardant according to claim 1, which is characterized in that it is described will be with getting ready
China clay, titanium dioxide, perlite particle, the sepiolite of requisite quality are ground through ball mill respectively, and milling time will be
60min or more controls fineness in 100um or less.
4. a kind of green environmental friendly coatings of highly effective flame-retardant according to claim 1, which is characterized in that the mixed solvent packet
It includes：Elastic emulsion, pigment dispersing agent, fungicide, film forming solvent, thickener, defoaming agent and PH debug agent, and weight part ratio is such as
Under：Elastic emulsion：Pigment dispersing agent：Fungicide：Film forming solvent：Thickener：Defoaming agent and：Debug agent=35：7：2：4：2.2：
3：0.3.
5. a kind of green environmental friendly coatings of highly effective flame-retardant according to claim 3, which is characterized in that coating needed for described
Ingredient and high china clay, titanium dioxide, perlite particle, sepiolite are matched according to number, are added to high-speed mixer stirring 30min
More than, while adding water in thinning vessel, the aqueous epoxy resins according to number proportion, water glass are sequentially added under the low speed
Glass, potassium hydroxide, sodium metasilicate, zinc chloride raw material after stirring 15-20min, improve wheel speed, with 1-2 hours shapes of high-speed stirred
At product.