CN105153913A - Weatherable flame-retardant coating material for electric facilities - Google Patents
Weatherable flame-retardant coating material for electric facilities Download PDFInfo
- Publication number
- CN105153913A CN105153913A CN201510654449.4A CN201510654449A CN105153913A CN 105153913 A CN105153913 A CN 105153913A CN 201510654449 A CN201510654449 A CN 201510654449A CN 105153913 A CN105153913 A CN 105153913A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- electric power
- power facility
- weathering resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a weatherable flame-retardant coating material for electric facilities. The coating material comprises the following ingredients by weight: 48 to 52 parts of carboxy modified ternary composite vinyl chloride-vinyl acetate resin, 50 to 54 parts of diphenyl-methane-diisocyanate, 46 to 50 parts of acrylic acid, 50 to 54 parts of mica powder, 46 to 50 parts of PVC resin powder, 50 to 54 parts of a polyurethane copolymer, 46 to 50 parts of diphenyl guanidine zinc-rich epoxy powder, 52 to 56 parts of tricresyl phosphate, 46 to 50 parts of aluminum hydroxide, 50 to 54 parts of ceramic clinker powder, 46 to 50 parts of polyamide, 50 to 54 parts of phenothiazine, 46 to 50 parts of zircon powder, 50 to 54 parts of chloroplatinic acid, 46 to 50 parts of rutile powder, 50 to 54 parts of di-maleimide, 46 to 50 parts of SBS modified asphalt, 50 to 54 parts of vinyl silicon resin, 46 to 50 parts of ammonium polyphosphate, and 50 to 54 parts of hexamethylenetetramine. The coating material is relatively high in weatherability, fire resistance, flame retardancy, and insulating property, thereby being suitable for the field of electric facilities.
Description
Technical field
The present invention relates to a kind of electric power facility weathering resistance anti-flaming dope, belong to electrical facility technical field.
Background technology
Coating, refers to coat body surface and can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins instead of vegetables oil, therefore is called coating.Coating non-liquid, powder coating is the large class of coating variety one.Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.The classification of the Chemicals of passing through according to the modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.Effect mainly contains 4 points: protection, decoration, covers up defect and other special roles of product, the value of improving product.Electric power facility, because the performance requriements of itself, is necessary to adopt suitable mode to improve its performance, and wherein, employing coating is an important approach.
Summary of the invention
The object of the present invention is to provide a kind of electric power facility weathering resistance anti-flaming dope, to realize the weathering resistance anti-flaming function of electric power facility coating better.
To achieve these goals, technical scheme of the present invention is as follows.
A kind of electric power facility weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 48 ~ 52 parts, diphenylmethanediisocyanate 50 ~ 54 parts, 46 ~ 50 parts, vinylformic acid, mica powder 50 ~ 54 parts, PVC resin powder 46 ~ 50 parts, polyurethane copolymer 50 ~ 54 parts, 46 ~ 50 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 52 ~ 56 parts, 46 ~ 50 parts, aluminium hydroxide, pottery 50 ~ 54 parts, ground-slag end, polymeric amide 46 ~ 50 parts, thiodiphenylamine 50 ~ 54 parts, 46 ~ 50 parts, zirconium English powder, Platinic chloride 50 ~ 54 parts, golden red stone flour 46 ~ 50 parts, dimaleimide 50 ~ 54 parts, SBS modifying asphalt 46 ~ 50 parts, vinyl polysiloxane 50 ~ 54 parts, ammonium polyphosphate 46 ~ 50 parts, hexamethylenetetramine 50 ~ 54 parts.
Further, above-mentioned electric power facility weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 48 parts, diphenylmethanediisocyanate 50 parts, 46 parts, vinylformic acid, mica powder 50 parts, PVC resin powder 46 parts, polyurethane copolymer 50 parts, 46 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 52 parts, 46 parts, aluminium hydroxide, 50 parts, pottery ground-slag end, polymeric amide 46 parts, thiodiphenylamine 50 parts, 46 parts, zirconium English powder, Platinic chloride 50 parts, golden red stone flour 46 parts, dimaleimide 50 parts, SBS modifying asphalt 46 parts, vinyl polysiloxane 50 parts, ammonium polyphosphate 46 parts, hexamethylenetetramine 50 parts.
Further, above-mentioned electric power facility weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 50 parts, diphenylmethanediisocyanate 52 parts, 48 parts, vinylformic acid, mica powder 52 parts, PVC resin powder 48 parts, polyurethane copolymer 52 parts, 48 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 54 parts, 48 parts, aluminium hydroxide, 52 parts, pottery ground-slag end, polymeric amide 48 parts, thiodiphenylamine 52 parts, 48 parts, zirconium English powder, Platinic chloride 52 parts, golden red stone flour 48 parts, dimaleimide 52 parts, SBS modifying asphalt 48 parts, vinyl polysiloxane 52 parts, ammonium polyphosphate 48 parts, hexamethylenetetramine 52 parts.
Further, above-mentioned electric power facility weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 52 parts, diphenylmethanediisocyanate 54 parts, 50 parts, vinylformic acid, mica powder 54 parts, PVC resin powder 50 parts, polyurethane copolymer 54 parts, 50 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 56 parts, 50 parts, aluminium hydroxide, 54 parts, pottery ground-slag end, polymeric amide 50 parts, thiodiphenylamine 54 parts, 50 parts, zirconium English powder, Platinic chloride 54 parts, golden red stone flour 50 parts, dimaleimide 54 parts, SBS modifying asphalt 50 parts, vinyl polysiloxane 54 parts, ammonium polyphosphate 50 parts, hexamethylenetetramine 54 parts.
Further, above-mentioned electric power facility weathering resistance anti-flaming dope preparation method step is as follows:
(1) by the carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid of described mass fraction, diphenylmethanediisocyanate, vinylformic acid, mica powder, PVC resin powder, polyurethane copolymer, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate, aluminium hydroxide, polymeric amide, thiodiphenylamine, zirconium English powder, Platinic chloride, dimaleimide, SBS modifying asphalt, vinyl polysiloxane, ammonium polyphosphate, hexamethylenetetramine is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the ceramic ground-slag end of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the golden red stone flour of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.
Above-mentioned each component function is as follows:
(1) carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid: containing carboxyl functional group, has excellent sticking power to smooth substrate and metal.Be usually used in metal parts printing-ink; Metal primer; Tackiness agent main raw material; Beverage bottle cap and food packaging tackiness agent; Cable sticks with glue agent; Protective system; Be coated with in vacuum UV additive color.
(2) diphenylmethanediisocyanate: be widely used in polyurethane coating, in addition, also for water-proof material, sealing material, pottery material etc.; With the urethane foam that this product is made, as the parts of warming, building materials, vehicle, boats and ships; Highly finished product can be made into automobile car bumper, snubber, synthetic leather, non-plastic urethane, polyurethane elastomeric fiber, non-plastic spandex fiber, rich film, tackiness agent etc.
(3) vinylformic acid: important organic synthesis raw material and synthetic resins monomer is polymerization velocity vinyl monomer quickly.Great majority are in order to manufacture the esters of acrylic acids such as methyl acrylate, ethyl ester, butyl ester, hydroxyl ethyl ester.Superpolymer is prepared, for the synthesis of industrial sectors such as resin, sizing agent, synthetic rubber, synthon, super absorbent resin, pharmacy, leather, weaving, chemical fibre, building materials, water treatment, oil production, coating by homopolymerization or copolymerization.
(4) mica powder: be widely used in the chemical engineering industries such as building material industry, fire protection sector, fire-fighting medium, welding electrode, plastics, electrical isolation, papermaking, pitch paper, rubber, pearly pigment.Ultrafine mica powder makes the functional fillers such as plastics, coating, paint, rubber, can improve its physical strength, strengthens toughness, sticking power, anti-aging and erosion resistance etc.
(5) PVC resin powder: physical appearance is white powder, nontoxic, odorless.Water insoluble, gasoline, alcohol and vinylchlorid, be dissolved in acetone, ethylene dichloride, dimethylbenzene equal solvent, and chemical stability is very high, has good plasticity-.Its product has good physicals and chemical property, is widely used in the fields such as industry, building, agricultural, daily life, packaging, electric power, public utilities.
(6) polyurethane copolymer: mechanical property has very large adjustability.By the ratio between the hard section of crystallization control and non crystallized soft section, urethane can obtain different mechanical properties.Therefore its goods have the excellent properties such as wear-resisting, heatproof, sealing, sound insulation, good processability, degradable.Purposes is very wide, can replace rubber, plastics, nylon etc.The coating made has strong tackiness, and film has excellent wear resistance, water tolerance and resistance to chemical reagents etc.Be mainly used in coatings for furniture, building materials coating and industrial printing-ink etc.
(7) diphenylguanidine zinc-riched epoxy powder: high rust resistance, strong adhesion, normal temperature quick-drying, in paint film, zinc content is higher, has galvanic protection effect, and water-fast rust-preventing characteristic is excellent.Be mainly used in shipbuilding, the steel and iron member such as bridge, freight container, offshore drilling platforms, port facilities and chemical industry equipment etc.
(8) Tritolyl Phosphate: colourless or flaxen transparent oily liquid, water insoluble, be dissolved in many organic solvents such as alcohol, benzene.Stick the softening agent of agent as epoxy resin and pressure-sensitive Yin, there is flame retardant properties.Also the flame-retardant plasticizer of polyvinyl acetate emulsion is used as.Also can be used as the tenderizer of rubber-type sizing agent.
(9) aluminium hydroxide: this product is the maximum and most widely used inorganic fire-retarded additive of consumption.This product can not only be fire-retardant as fire retardant, and can prevent from being fuming, do not produce dropping, do not produce toxic gas, and therefore, obtain and apply more widely, usage quantity is also increasing year by year.For industries such as thermosetting resin, thermoplastics, synthetic rubber, coating and building materials.
(10) ceramic ground-slag end: a kind of lightweight non-metallic multifunctional material, good dispersity, opacifying power are high, whiteness is high, suspension is good, chemical stability is good, plasticity-is good, heat resisting temperature is high, density is little, loss on ignition is low, light scattering good, good insulating.The adsorptivity of coating, weathering, weather resistance, scrubbing resistance, corrosion-resistant and high thermal resistance can be improved, improve the mechanical property of paint film, increase transparency, improve fire resistance, can be used for anticorrosion, fire prevention, high temperature resistant, powder, building coating and various industry, civilian coating.
(11) polymeric amide: there is good over-all properties, comprise mechanical property, thermotolerance, wearability, chemical proofing and self lubricity, and frictional coefficient is low, there is certain flame retardant resistance, be easy to processing, be suitable for, by glass fibre and other filler filling enhancing modified, improving performance and broadened application scope.Be widely used in the fields such as machinery, automobile, electrical equipment, textile equipment, chemical industry equipment, aviation, metallurgy.
(12) thiodiphenylamine: yellow or greyish-green powder or little lobate crystal, easy oxidation discoloration.There is faint foreign odor, be placed in oxidizable in air for a long time and darken.This product is widely used in the production of vinylformic acid, acrylate, methacrylic ester, vinyl acetate mainly as the excellent stopper of alkenyl monomer.Also for the synthesis of medicine, dyestuff, polyethers, oxidation inhibitor and rubber antioxidant.Also for livestock insect repellent, fruit tree insecticide.
(13) zirconium English powder: chemical stability is a kind of high-quality, inexpensive opacifying agent, is widely used in the production of various architectural pottery, snitaryware, domestic ceramics, one-level artwork pottery etc.Not by the impact of ceramic firing atmosphere, and significantly can improve the glaze-body bonding performance of pottery, improve Ceramic glaze hardness.The fusing point of zirconium English powder is 2500 degrees Celsius, so be also widely used in refractory materials, glass furnace zirconium ramming mass, mould material, spray material.
(14) Platinic chloride: orange-yellow powder or sorrel crystallization, fusing point 60 DEG C.Easy deliquescence, water-soluble, ethanol and acetone, simultaneously soluble in water, sour, ethanol and ether, water absorbability is extremely strong.Mainly for the preparation of noble metal catalyst and precious metal coating; Precipitation potassium, gallium, ammonium, caesium and thallium, to be separated with sodium; Precipitation alkaloid; Plating; Catalyzer; Manufacture platinized asbestos.For platinum plating and make platinum catalyst, indelible ink and platinum mirror etc.
(15) golden red stone flour: there is high temperature resistant, low temperature resistant, corrosion-resistant, the excellent properties such as high strength, little proportion, be widely used in the aspects such as military project Aeronautics and Astronautics, navigation, machinery, chemical industry, sea water desaltination.Being one of necessary raw material of high-grade welding electrode, is also the optimum feed stock of producing Rutile type Titanium Dioxide.
(16) dimaleimide: a kind of heat-resisting, high-efficiency activated flame-retardant monomer, have improve that thermotolerance degree is high, good flame resistance, consistency are good, toxicity is low, the advantage of Heat stability is good etc., important heat-proof modifier and additive, the resistance toheat of material is improved while material can be made to obtain flame retardant properties, widely applicable, excellent combination property.
(17) SBS modifying asphalt: there is well high temperature resistant, anti-seismic design in the area that the temperature difference is larger; Viscosifying power is strong especially, obviously can improve the resistance to tension after the chance water of road surface, and significantly improve the water stability of pitch; Reduce the ageing of asphalt phenomenon that road surface causes because of ultraviolet radiation; Reduce the destruction of causing because of vehicle seepage diesel oil, machine oil and gasoline.
(18) vinyl polysiloxane: there is good erosion resistance, solvent resistance and high temperature resistant type, the high temperature application such as some smelting, electric power sweeteners can be widely used in, as cooling tower, chimney and chemical line etc., the type resin also has the feature of resistance to strong solvent, strong oxidizing property medium simultaneously.
(19) ammonium polyphosphate: nonpoisonous and tasteless, do not produce etchant gas, water absorbability is little, thermostability is high, be a kind of non-halogen fire retardant of excellent property, be widely used in expanding fire-proof paint, polyethylene, polypropylene, urethane, epoxy resin, rubber item, fiberboard and powder extinguishing agent etc.
(20) hexamethylenetetramine: under normal temperature, these product are the glossiness crystallization of white tool or crystalline powder, taste is sweet rear hardship just, irritant to skin, heating easily distils and decomposes, inflammable, soluble in water, ethanol, chloroform polar solvent, be insoluble in the non-polar solvent such as ether, aromatic hydrocarbon.Main be used as resin and the solidifying agent of plastics, the catalyzer of aminoplastics and whipping agent, the promotor of the vulcanization of rubber, the sanforzing agent etc. of textiles; As inhibiter, for slowing down the corrosion of metallic substance.
This beneficial effect of the invention is: this electric power facility is simple with weathering resistance anti-flaming dope process of preparing, prepared product has good weathering resistance, its fire protection flame retarding, insulating property are relatively good, are adapted at electric power facility field and use, improve product performance.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
Embodiment 1
Electric power facility in the present embodiment weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 48 parts, diphenylmethanediisocyanate 50 parts, 46 parts, vinylformic acid, mica powder 50 parts, PVC resin powder 46 parts, polyurethane copolymer 50 parts, 46 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 52 parts, 46 parts, aluminium hydroxide, 50 parts, pottery ground-slag end, polymeric amide 46 parts, thiodiphenylamine 50 parts, 46 parts, zirconium English powder, Platinic chloride 50 parts, golden red stone flour 46 parts, dimaleimide 50 parts, SBS modifying asphalt 46 parts, vinyl polysiloxane 50 parts, ammonium polyphosphate 46 parts, hexamethylenetetramine 50 parts.
Above-mentioned electric power facility weathering resistance anti-flaming dope preparation method step is as follows:
(1) the carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid of described mass fraction, diphenylmethanediisocyanate, vinylformic acid, mica powder, PVC resin powder, polyurethane copolymer, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate, aluminium hydroxide, polymeric amide, thiodiphenylamine, zirconium English powder, Platinic chloride, dimaleimide, SBS modifying asphalt, vinyl polysiloxane, ammonium polyphosphate, hexamethylenetetramine are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min;
(2) add the ceramic ground-slag end of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) add the golden red stone flour of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min; Mix rear obtained this product.
Embodiment 2
Electric power facility in the present embodiment weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 50 parts, diphenylmethanediisocyanate 52 parts, 48 parts, vinylformic acid, mica powder 52 parts, PVC resin powder 48 parts, polyurethane copolymer 52 parts, 48 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 54 parts, 48 parts, aluminium hydroxide, 52 parts, pottery ground-slag end, polymeric amide 48 parts, thiodiphenylamine 52 parts, 48 parts, zirconium English powder, Platinic chloride 52 parts, golden red stone flour 48 parts, dimaleimide 52 parts, SBS modifying asphalt 48 parts, vinyl polysiloxane 52 parts, ammonium polyphosphate 48 parts, hexamethylenetetramine 52 parts.
Above-mentioned electric power facility weathering resistance anti-flaming dope preparation method step is as follows:
(1) the carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid of described mass fraction, diphenylmethanediisocyanate, vinylformic acid, mica powder, PVC resin powder, polyurethane copolymer, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate, aluminium hydroxide, polymeric amide, thiodiphenylamine, zirconium English powder, Platinic chloride, dimaleimide, SBS modifying asphalt, vinyl polysiloxane, ammonium polyphosphate, hexamethylenetetramine are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min;
(2) add the ceramic ground-slag end of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) add the golden red stone flour of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min; Mix rear obtained this product.
Embodiment 3
Electric power facility in the present embodiment weathering resistance anti-flaming dope, be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 52 parts, diphenylmethanediisocyanate 54 parts, 50 parts, vinylformic acid, mica powder 54 parts, PVC resin powder 50 parts, polyurethane copolymer 54 parts, 50 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 56 parts, 50 parts, aluminium hydroxide, 54 parts, pottery ground-slag end, polymeric amide 50 parts, thiodiphenylamine 54 parts, 50 parts, zirconium English powder, Platinic chloride 54 parts, golden red stone flour 50 parts, dimaleimide 54 parts, SBS modifying asphalt 50 parts, vinyl polysiloxane 54 parts, ammonium polyphosphate 50 parts, hexamethylenetetramine 54 parts.
Above-mentioned electric power facility weathering resistance anti-flaming dope preparation method step is as follows:
(1) the carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid of described mass fraction, diphenylmethanediisocyanate, vinylformic acid, mica powder, PVC resin powder, polyurethane copolymer, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate, aluminium hydroxide, polymeric amide, thiodiphenylamine, zirconium English powder, Platinic chloride, dimaleimide, SBS modifying asphalt, vinyl polysiloxane, ammonium polyphosphate, hexamethylenetetramine are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) add the ceramic ground-slag end of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the golden red stone flour of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min; Mix rear obtained this product.
Carry out performance measurement for the coating in embodiment 1, embodiment 2 and embodiment 3 and certain commercial coating, measured data are as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
Visible, material of the present invention has good weathering resistance, and its fire protection flame retarding, insulating property are relatively good.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
1. an electric power facility weathering resistance anti-flaming dope, it is characterized in that: be made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 48 ~ 52 parts, diphenylmethanediisocyanate 50 ~ 54 parts, 46 ~ 50 parts, vinylformic acid, mica powder 50 ~ 54 parts, PVC resin powder 46 ~ 50 parts, polyurethane copolymer 50 ~ 54 parts, 46 ~ 50 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 52 ~ 56 parts, 46 ~ 50 parts, aluminium hydroxide, pottery 50 ~ 54 parts, ground-slag end, polymeric amide 46 ~ 50 parts, thiodiphenylamine 50 ~ 54 parts, 46 ~ 50 parts, zirconium English powder, Platinic chloride 50 ~ 54 parts, golden red stone flour 46 ~ 50 parts, dimaleimide 50 ~ 54 parts, SBS modifying asphalt 46 ~ 50 parts, vinyl polysiloxane 50 ~ 54 parts, ammonium polyphosphate 46 ~ 50 parts, hexamethylenetetramine 50 ~ 54 parts.
2. electric power facility weathering resistance anti-flaming dope according to claim 1, it is characterized in that: described electric power facility weathering resistance anti-flaming dope is made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 48 parts, diphenylmethanediisocyanate 50 parts, 46 parts, vinylformic acid, mica powder 50 parts, PVC resin powder 46 parts, polyurethane copolymer 50 parts, 46 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 52 parts, 46 parts, aluminium hydroxide, 50 parts, pottery ground-slag end, polymeric amide 46 parts, thiodiphenylamine 50 parts, 46 parts, zirconium English powder, Platinic chloride 50 parts, golden red stone flour 46 parts, dimaleimide 50 parts, SBS modifying asphalt 46 parts, vinyl polysiloxane 50 parts, ammonium polyphosphate 46 parts, hexamethylenetetramine 50 parts.
3. electric power facility weathering resistance anti-flaming dope according to claim 1, it is characterized in that: described electric power facility weathering resistance anti-flaming dope is made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 50 parts, diphenylmethanediisocyanate 52 parts, 48 parts, vinylformic acid, mica powder 52 parts, PVC resin powder 48 parts, polyurethane copolymer 52 parts, 48 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 54 parts, 48 parts, aluminium hydroxide, 52 parts, pottery ground-slag end, polymeric amide 48 parts, thiodiphenylamine 52 parts, 48 parts, zirconium English powder, Platinic chloride 52 parts, golden red stone flour 48 parts, dimaleimide 52 parts, SBS modifying asphalt 48 parts, vinyl polysiloxane 52 parts, ammonium polyphosphate 48 parts, hexamethylenetetramine 52 parts.
4. electric power facility weathering resistance anti-flaming dope according to claim 1, it is characterized in that: described electric power facility weathering resistance anti-flaming dope is made up of the component of following mass fraction: carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid 52 parts, diphenylmethanediisocyanate 54 parts, 50 parts, vinylformic acid, mica powder 54 parts, PVC resin powder 50 parts, polyurethane copolymer 54 parts, 50 parts, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate 56 parts, 50 parts, aluminium hydroxide, 54 parts, pottery ground-slag end, polymeric amide 50 parts, thiodiphenylamine 54 parts, 50 parts, zirconium English powder, Platinic chloride 54 parts, golden red stone flour 50 parts, dimaleimide 54 parts, SBS modifying asphalt 50 parts, vinyl polysiloxane 54 parts, ammonium polyphosphate 50 parts, hexamethylenetetramine 54 parts.
5. the weathering resistance anti-flaming dope of the electric power facility according to Claims 1-4, is characterized in that: described electric power facility weathering resistance anti-flaming dope preparation method step is as follows:
(1) by the carboxy-modified tri compound vinyl chloride-vinyl acetate resin liquid of described mass fraction, diphenylmethanediisocyanate, vinylformic acid, mica powder, PVC resin powder, polyurethane copolymer, diphenylguanidine zinc-riched epoxy powder, Tritolyl Phosphate, aluminium hydroxide, polymeric amide, thiodiphenylamine, zirconium English powder, Platinic chloride, dimaleimide, SBS modifying asphalt, vinyl polysiloxane, ammonium polyphosphate, hexamethylenetetramine is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the ceramic ground-slag end of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the golden red stone flour of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.