CN108892856A - 一种长玻纤增强聚丙烯复合材料 - Google Patents
一种长玻纤增强聚丙烯复合材料 Download PDFInfo
- Publication number
- CN108892856A CN108892856A CN201810446697.3A CN201810446697A CN108892856A CN 108892856 A CN108892856 A CN 108892856A CN 201810446697 A CN201810446697 A CN 201810446697A CN 108892856 A CN108892856 A CN 108892856A
- Authority
- CN
- China
- Prior art keywords
- long glass
- fiber reinforced
- glass fiber
- composite according
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种长玻纤增强聚丙烯复合材料,属于复合材料领域,提高了复合材料的抗氧化性能,并增加了抗菌性能。本发明包括:按质量百分比各物质为:聚丙烯为50%‑80%,长玻璃纤维为10%‑40%,相容剂为2%‑5%,稳定剂为0.5%‑2%,抗氧化剂为0.2%‑1%,抗菌剂为0.5%‑1%,偶联剂为0.5%‑1%。
Description
技术领域
本发明属于复合材料领域,尤其涉及一种长玻纤增强聚丙烯复合材料。
背景技术
金属在制造过程中不适合成型复杂的形状,很大的限制了其在各种零件中的应用,也增加了成本。聚丙烯(Polypropylene,简称PP)是一种半结晶的热塑性塑料,其具有良好的物理机械性能、化学性能和加工性能,因此,聚丙烯在建筑工程材料、电动工具、汽车和家用电器材料等方面均有广泛的用途。为了得到更广泛的应用,通常将聚丙烯进行改性,例如滑石粉填充、碳酸钙填充、玻纤增强等。玻纤增强聚丙烯作为一种通用工程塑料,具有高强度、高刚性、高韧性、低密度、低翘曲、蠕变性以及抗动态疲劳性能优异的性能,玻纤增强聚丙烯性价比高,因此广泛应用于汽车、家电与电动工具等结构零部件,以取代金属、尼龙等材料。
聚丙烯在存储、加工和使用过程中,极易受热、氧气与紫光线等外界因素引发老化降解,导致其制品表面变色、粉化、力学和机械性能大幅度下降,影响其使用安全。在上述外界因素中热氧老化是最重要的因素。目前较好的解决方法是在聚丙烯熔融挤出阶段加入适量的抗氧剂,来提高其耐热氧化性能。受阻酚、亚磷酸酯及其复合产品是当前聚丙烯抗氧剂的主体,而这些抗氧剂本身是一种有机小分子化合物,上述抗氧剂易从聚烯烃中不断向外迁移,导致聚丙烯的抗氧化效果不理想。
发明内容
本发明提供了一种长玻纤增强聚丙烯复合材料,克服现有技术的问题,提高了复合材料的抗氧化性能。
为实现以上目的,本发明采用以下技术方案:
一种长玻纤增强聚丙烯复合材料,按质量百分比各物质为:
聚丙烯 50%-80%
长玻璃纤维 10%-40%
相容剂 2%-5%
稳定剂 0.5%-2%
抗氧化剂 0.2%-1%
抗菌剂 0.5%-1%
偶联剂 0.5%-1%
以上所述组分中,所述聚丙烯的熔体流动速率为40-100g/10min,所述长玻璃纤维为无碱玻璃纤维,所述相容剂为聚丙烯马来酸酐接枝,恶唑啉改性聚丙烯或丙烯酸缩水甘油酯接枝的聚丙烯,所述稳定剂为无毒有机锡,所述抗氧化剂为芳香胺类抗氧剂、 受阻酚类抗氧剂和亚磷酸酯类抗氧剂中的一种或多种,所述抗菌剂为吸附银、铜或锌的硅胶或沸石,优选吸附银的硅胶或沸石,所述偶联剂为KH-560。
本发明的有益效果:本发明提供了一种长玻纤增强聚丙烯复合材料,通过加入添加剂,并控制各种添加剂组分的含量,使各种组分协同作用,对长玻纤增强聚丙烯复合材料进行改性,使稳定剂不会随环境变化迁移到复合材料表面,从而使复合材料具有较好的长期抗热氧老化性能,并且加入抗菌剂,使复合材料具有杀菌作用,增大了其使用范围。
具体实施方式
实施例1
一种长玻纤增强聚丙烯复合材料,按质量百分比各物质为:
聚丙烯为50%,无碱长玻璃纤维为40%,聚丙烯马来酸酐接枝为5%,无毒有机锡为2%,芳香胺类抗氧剂为1%,吸附银的硅胶为1%,KH-560为1%。
以上所述组分中,所述聚丙烯的熔体流动速率为40g/10min。
实施例2
一种长玻纤增强聚丙烯复合材料,按质量百分比各物质为:
聚丙烯为80%,无碱长玻璃纤维为10%,恶唑啉改性聚丙烯为5%,无毒有机锡为2%,受阻酚类抗氧剂为1%,吸附银的沸石为1%,KH-560为1%。
以上所述组分中,所述聚丙烯的熔体流动速率为60g/10min。
实施例3
一种长玻纤增强聚丙烯复合材料,按质量百分比各物质为:
聚丙烯为60%,无碱长玻璃纤维为30%,丙烯酸缩水甘油酯接枝的聚丙烯为5%,无毒有机锡为2%,亚磷酸酯类抗氧剂为1%,吸附锌的沸石为1%,KH-560为1%。
以上所述组分中,所述聚丙烯的熔体流动速率为80g/10min。
实施例4
一种长玻纤增强聚丙烯复合材料,按质量百分比各物质为:
聚丙烯为70%,无碱长玻璃纤维为20%,丙烯酸缩水甘油酯接枝的聚丙烯为5%,无毒有机锡为2%,亚磷酸酯类抗氧剂为1%,吸附锌的硅胶为1%,KH-560为1%。
以上所述组分中,所述聚丙烯的熔体流动速率为70g/10min。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下还可以作出若干改进,这些改进也应视为本发明的保护范围。
Claims (9)
1.一种长玻纤增强聚丙烯复合材料,其特征在于,按质量百分比各物质为:
聚丙烯 50%-80%
长玻璃纤维 10%-40%
相容剂 2%-5%
稳定剂 0.5%-2%
抗氧化剂 0.2%-1%
抗菌剂 0.5%-1%
偶联剂 0.5%-1%。
2.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述聚丙烯的熔体流动速率为40 g/10min -100g/10min。
3.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述长玻璃纤维为无碱玻璃纤维。
4.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述相容剂为聚丙烯马来酸酐接枝,恶唑啉改性聚丙烯或丙烯酸缩水甘油酯接枝的聚丙烯。
5.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述稳定剂为无毒有机锡。
6.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述抗氧化剂为芳香胺类抗氧剂、受阻酚类抗氧剂和亚磷酸酯类抗氧剂中的一种或多种。
7.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述抗菌剂为吸附银、铜或锌的硅胶或沸石。
8.根据权利要求1或7所述的长玻纤增强聚丙烯复合材料,其特征在于,所述抗菌剂为吸附银的硅胶或沸石。
9.根据权利要求1所述的长玻纤增强聚丙烯复合材料,其特征在于,所述偶联剂为KH-560。